WO2017011381A1 - Production de biocarburant utilisant un catalyseur nanozéolithique - Google Patents
Production de biocarburant utilisant un catalyseur nanozéolithique Download PDFInfo
- Publication number
- WO2017011381A1 WO2017011381A1 PCT/US2016/041724 US2016041724W WO2017011381A1 WO 2017011381 A1 WO2017011381 A1 WO 2017011381A1 US 2016041724 W US2016041724 W US 2016041724W WO 2017011381 A1 WO2017011381 A1 WO 2017011381A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- nanozeolite
- zeolite
- less
- biovapors
- Prior art date
Abstract
L'invention concerne un procédé de conversion de bio-vapeurs en biocarburant consistant à diriger des bio-vapeurs dérivées de la décomposition de biomasse, lesdites bio-vapeurs comprenant au moins des composés C5 et C6, dans une chambre de réaction catalytique; et à mettre en contact les bio-vapeurs avec une composition de catalyseur comprenant une nanozéolithe.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201562191166P | 2015-07-10 | 2015-07-10 | |
US62/191,166 | 2015-07-10 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2017011381A1 true WO2017011381A1 (fr) | 2017-01-19 |
Family
ID=57758184
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2016/041724 WO2017011381A1 (fr) | 2015-07-10 | 2016-07-11 | Production de biocarburant utilisant un catalyseur nanozéolithique |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2017011381A1 (fr) |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100041932A1 (en) * | 2008-07-25 | 2010-02-18 | Conocophillips Company | Process for converting an oxygenated feed to high octane gasoline |
US20120203042A1 (en) * | 2009-09-09 | 2012-08-09 | Anellotech, Inc. | Systems and processes for catalytic pyrolysis of biomass and hydrocarbonaceous materials for production of aromatics with optional olefin recycle, and catalysts having selected particle size for catalytic pyrolysis |
WO2015061736A1 (fr) * | 2013-10-25 | 2015-04-30 | Cool Planet Energy Systems, Inc. | Composition de catalyseur à zéolite |
-
2016
- 2016-07-11 WO PCT/US2016/041724 patent/WO2017011381A1/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100041932A1 (en) * | 2008-07-25 | 2010-02-18 | Conocophillips Company | Process for converting an oxygenated feed to high octane gasoline |
US20120203042A1 (en) * | 2009-09-09 | 2012-08-09 | Anellotech, Inc. | Systems and processes for catalytic pyrolysis of biomass and hydrocarbonaceous materials for production of aromatics with optional olefin recycle, and catalysts having selected particle size for catalytic pyrolysis |
WO2015061736A1 (fr) * | 2013-10-25 | 2015-04-30 | Cool Planet Energy Systems, Inc. | Composition de catalyseur à zéolite |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US9333494B2 (en) | Biomass catalytic cracking catalyst and process of preparing the same | |
US20140007493A1 (en) | Hybrid silica and alumina as catalyst matrix and/or binder in biomass conversion catalysts and bio-oil upgrading | |
Naqvi et al. | Catalytic fast pyrolysis of rice husk: Influence of commercial and synthesized microporous zeolites on deoxygenation of biomass pyrolysis vapors | |
AU2017279755B2 (en) | Catalyst Compositions And Use Thereof In Catalytic Biomass Pyrolysis | |
US20130261355A1 (en) | Catalyst Compositions for Use in a Two-Stage Reactor Assembly Unit for the Thermolysis and Catalytic Conversion of Biomass | |
US20160017238A1 (en) | Mesoporous Zeolite-Containing Catalysts For The Thermoconversion Of Biomass And For Upgrading Bio-Oils | |
US9649624B2 (en) | Catalyst for thermocatalytic conversion of biomass to liquid fuels and chemicals | |
US10155908B2 (en) | Catalyst compositions and use thereof in catalytic biomass pyrolysis | |
US20150027871A1 (en) | Catalyst Compositions Comprising In Situ Grown Zeolites on Clay Matrixes Exhibiting Hierarchical Pore Structures | |
Socci et al. | The role of catalyst acidity and shape selectivity on products from the catalytic fast pyrolysis of beech wood | |
Mirshafiee et al. | A green approach for template free synthesis of Beta zeolite incorporated in ZSM-5 zeolite to enhance catalytic activity in MTG reaction: Effect of seed nature and temperature | |
Zhang et al. | Catalytic deoxygenation during cellulose fast pyrolysis using acid–base bifunctional catalysis | |
Dada et al. | Thermo-catalytic co-pyrolysis of ironbark sawdust and plastic waste over strontium loaded hierarchical Y-zeolite | |
US20160237356A1 (en) | Zeolite catalyst composition | |
US20170009142A1 (en) | Biofuel production using nanozeolite catalyst | |
Ahmed et al. | Tailoring ZSM-5 zeolite porosity and acidity for efficient conversion of municipal solid waste to fuel | |
Wang et al. | In situ synthesis, characterization and catalytic activity of ZSM-5 zeolites on kaolin microspheres from amine-free system | |
WO2017011381A1 (fr) | Production de biocarburant utilisant un catalyseur nanozéolithique | |
US20150045208A1 (en) | Catalysts For Thermo-Catalytic Conversion Of Biomass, And Methods Of Making and Using | |
WO2017066521A1 (fr) | Production de biocarburant utilisant un catalyseur de zéolite dopé | |
Jae | Production of green aromatics and olefins from lignocellulosic biomass by catalytic fast pyrolysis: Chemistry, catalysis, and process development | |
López Renau | Ex-situ catalytic fast pyrolysis of wheat straw over acid-base catalysts for the production of high-added value bio-based chemicals | |
Bonetto et al. | From peanut shell to 2, 5-dimethylfuran: the role of Zr-micro/mesoporous zeolites | |
RO134307B1 (ro) | Procedeu de sinteză a unui catalizator sub formă de material compozit metal/zeolit şi catalizatorul astfel obţinut |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 16824985 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 16824985 Country of ref document: EP Kind code of ref document: A1 |