WO2016189209A1 - Multi-composite reinforcement made from improved glass-resin - Google Patents
Multi-composite reinforcement made from improved glass-resin Download PDFInfo
- Publication number
- WO2016189209A1 WO2016189209A1 PCT/FR2015/051410 FR2015051410W WO2016189209A1 WO 2016189209 A1 WO2016189209 A1 WO 2016189209A1 FR 2015051410 W FR2015051410 W FR 2015051410W WO 2016189209 A1 WO2016189209 A1 WO 2016189209A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composite reinforcement
- reinforcement according
- composite
- measured
- resin
- Prior art date
Abstract
Description
Claims