WO2016107662A1 - Verfahren zum dotieren von halbleitern - Google Patents
Verfahren zum dotieren von halbleitern Download PDFInfo
- Publication number
- WO2016107662A1 WO2016107662A1 PCT/EP2015/002412 EP2015002412W WO2016107662A1 WO 2016107662 A1 WO2016107662 A1 WO 2016107662A1 EP 2015002412 W EP2015002412 W EP 2015002412W WO 2016107662 A1 WO2016107662 A1 WO 2016107662A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- doping
- silicon
- diffusion
- printing
- substrate
- Prior art date
Abstract
Description
Claims