WO2016004611A1 - Textile texturing machine - Google Patents
Textile texturing machine Download PDFInfo
- Publication number
- WO2016004611A1 WO2016004611A1 PCT/CN2014/081998 CN2014081998W WO2016004611A1 WO 2016004611 A1 WO2016004611 A1 WO 2016004611A1 CN 2014081998 W CN2014081998 W CN 2014081998W WO 2016004611 A1 WO2016004611 A1 WO 2016004611A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- parts
- texturing machine
- frame
- butanone
- ethyl ketone
- Prior art date
Abstract
A textile texturing machine. A frame is formed by adjacent plastic plates adhered to each other. An adhesive used consists of diglycidyl ether of linoleic acid dimer, polysulfide rubber, butanone, methyl methacrylate, acetone, and methyl ethyl ketone peroxide. The plates are connected firmly, and a long working life is achieved.
Description
技术领域 Technical field
本发明涉及一种纺织加弹机。 The invention relates to a textile texturing machine.
背景技术 Background technique
现有的纺织加弹机，其机架各板块之间连接牢固性不理想，易出现脱离现象。 In the existing textile texturing machine, the connection between the plates of the frame is not satisfactory, and the separation phenomenon is easy to occur.
发明内容 Summary of the invention
本发明的目的在于提供一种各板块连接牢固，工作寿命长的纺织加弹机。 It is an object of the present invention to provide a textile texturing machine in which the plates are firmly connected and have a long working life.
本发明的技术解决方案是： The technical solution of the present invention is:
一种纺织加弹机，包括机架，其特征是：机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成：
A textile texturing machine comprising a frame, characterized in that: the frame is made of adjacent plastic plates bonded to each other, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 50~60 份 Linoleic acid dimerized diglycidyl ether 50~60 parts
聚硫橡胶 10~20 份 Polysulfide rubber 10~20 parts
丁酮 5~10 份。 Butanone 5~10 parts.
甲基丙烯酸甲酯 5~10 份 Methyl methacrylate 5~10 parts
丙酮 3~6 份 Acetone 3~6 parts
过氧化甲乙酮 2~8 份。 2 to 8 parts of methyl ethyl ketone peroxide.
所述的纺织加弹机，机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成： In the textile texturing machine, the frame is formed by bonding adjacent plastic plates to each other, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 52 份 Linoleic acid dimerized diglycidyl ether 52 parts
聚硫橡胶 19 份 Polysulfide rubber 19 parts
丁酮 10 份。 10 parts of butanone.
甲基丙烯酸甲酯 6 份 Methyl methacrylate 6 parts
丙酮 5 份 Acetone 5 parts
过氧化甲乙酮 6 份。 6 parts of methyl ethyl ketone peroxide.
所述的纺织加弹机，机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成： In the textile texturing machine, the frame is formed by bonding adjacent plastic plates to each other, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 57 份 Linoleic acid dimerized diglycidyl ether 57 parts
聚硫橡胶 15 份 Polysulfide rubber 15 parts
丁酮 7 份。 7 parts of butanone.
甲基丙烯酸甲酯 8 份 Methyl methacrylate 8 parts
丙酮 3 份 Acetone 3 parts
过氧化甲乙酮 3 份。 3 parts of methyl ethyl ketone peroxide.
本发明各板块连接牢固，工作寿命长。 The plates of the invention are firmly connected and have a long working life.
下面结合实施例对本发明作进一步说明。 The invention is further illustrated by the following examples.
具体实施方式 detailed description
实施例 1 ： Example 1
纺织加弹机，机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成： Textile texturing machine, the frame is made of adjacent plastic plates bonded together, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 52 份 Linoleic acid dimerized diglycidyl ether 52 parts
聚硫橡胶 19 份 Polysulfide rubber 19 parts
丁酮 10 份。 10 parts of butanone.
甲基丙烯酸甲酯 6 份 Methyl methacrylate 6 parts
丙酮 5 份 Acetone 5 parts
过氧化甲乙酮 6 份。 6 parts of methyl ethyl ketone peroxide.
实施例 2 ： Example 2:
纺织加弹机，机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成： Textile texturing machine, the frame is made of adjacent plastic plates bonded together, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 57 份 Linoleic acid dimerized diglycidyl ether 57 parts
聚硫橡胶 15 份 Polysulfide rubber 15 parts
丁酮 7 份。 7 parts of butanone.
甲基丙烯酸甲酯 8 份 Methyl methacrylate 8 parts
丙酮 3 份 Acetone 3 parts
过氧化甲乙酮 3 份。 3 parts of methyl ethyl ketone peroxide.
Claims (1)
1.
一种纺织加弹机，包括机架，其特征是：机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成：1.
A textile texturing machine comprising a frame, characterized in that: the frame is made of adjacent plastic plates bonded to each other, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 50~60 份Linoleic acid dimerized diglycidyl ether 50~60 parts
聚硫橡胶 10~20 份Polysulfide rubber 10~20 parts
丁酮 5~10 份。Butanone 5~10 parts.
甲基丙烯酸甲酯 5~10 份Methyl methacrylate 5~10 parts
丙酮 3~6 份Acetone 3~6 parts
过氧化甲乙酮 2~8 份。2 to 8 parts of methyl ethyl ketone peroxide.
2. 根据权利要求 1
所述的纺织加弹机，其特征是：机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成：2. According to claim 1
The textile texturing machine is characterized in that: the frame is made of adjacent plastic plates bonded to each other, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 52 份Linoleic acid dimerized diglycidyl ether 52 parts
聚硫橡胶 19 份Polysulfide rubber 19 parts
丁酮 10 份。10 parts of butanone.
甲基丙烯酸甲酯 6 份Methyl methacrylate 6 parts
丙酮 5 份Acetone 5 parts
过氧化甲乙酮 6 份。6 parts of methyl ethyl ketone peroxide.
3. 根据权利要求 1
所述的纺织加弹机，其特征是：机架由相邻塑料板体相互粘合而成，所用粘合剂由下列重量份的组分组成：3. According to claim 1
The textile texturing machine is characterized in that: the frame is made of adjacent plastic plates bonded to each other, and the adhesive used is composed of the following parts by weight:
亚油酸二聚二环氧甘油醚 57 份Linoleic acid dimerized diglycidyl ether 57 parts
聚硫橡胶 15 份Polysulfide rubber 15 parts
丁酮 7 份。7 parts of butanone.
甲基丙烯酸甲酯 8 份Methyl methacrylate 8 parts
丙酮 3 份Acetone 3 parts
过氧化甲乙酮 3 份。3 parts of methyl ethyl ketone peroxide.