WO2014022363A2 - Anti-smudge hard coat and anti-smudge hard coat precursor - Google Patents
Anti-smudge hard coat and anti-smudge hard coat precursor Download PDFInfo
- Publication number
- WO2014022363A2 WO2014022363A2 PCT/US2013/052677 US2013052677W WO2014022363A2 WO 2014022363 A2 WO2014022363 A2 WO 2014022363A2 US 2013052677 W US2013052677 W US 2013052677W WO 2014022363 A2 WO2014022363 A2 WO 2014022363A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nanoparticles
- hard coat
- particle size
- meth
- average particle
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/16—Antifouling paints; Underwater paints
- C09D5/1687—Use of special additives
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y40/00—Manufacture or treatment of nanostructures
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D133/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers
- C09D133/04—Homopolymers or copolymers of esters
- C09D133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
- C09D133/16—Homopolymers or copolymers of esters containing halogen atoms
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D4/00—Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/60—Additives non-macromolecular
- C09D7/61—Additives non-macromolecular inorganic
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/65—Additives macromolecular
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/66—Additives characterised by particle size
- C09D7/67—Particle size smaller than 100 nm
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/66—Additives characterised by particle size
- C09D7/68—Particle size between 100-1000 nm
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/66—Additives characterised by particle size
- C09D7/69—Particle size larger than 1000 nm
Definitions
- the present disclosure relates to an anti-smudge hard coat and an anti-smudge hard coat precursor.
- Hard coats are used to protect the surfaces of various hard materials and flexible materials. Hard coats are required to have excellent scratch resistance, impact resistance, and the like, as well as optical characteristics in the case of transparent materials. In addition, there is a strong demand for hard coat surfaces to be provided with anti-smudge properties.
- Hard coat materials containing Si0 2 nanoparticles modified by a photo-curing silane coupling agent are described in U.S. Patent Nos. 5104929 and 7074463.
- an object of the present disclosure is to provide a hard coat and a hard coat precursor with excellent scratch resistance and durability of anti-smudge properties.
- One embodiment of the present disclosure provides a hard coat including a nanoparticle mixture and a binder, the nanoparticles constituting from 40 to 95 mass% of an entire mass of the hard coat; from 10 to 50 mass% of the nanoparticles having an average particle size within a range of 2 to 200 nm; from 50 to 90 mass% of the nanoparticles having an average particle size within a range of 60 to 400 nm; a ratio of the average particle size of nanoparticles having an average particle size within the range of 60 to 400 nm to the average particle size of nanoparticles having an average particle size within the range of 2 to 200 nm being within a range of 2: 1 to 200: 1 ; and the binder including a polyfunctional fluorinated (meth)acrylic compound, a reaction product thereof, or a combination thereof.
- a hard coat precursor including a nanoparticle mixture and a binder, the nanoparticles constituting from 40 to 95 mass% of a total mass of the nanoparticles and the binder; from 10 to 50 mass% of the nanoparticles having an average particle size within the range of 2 to 200 nm; from 50 to 90 mass% of the nanoparticles having an average particle size within the range of 60 to 400 nm; the ratio of the average particle size of nanoparticles having an average particle size within the range of 60 to 400 nm to the average particle size of nanoparticles having an average particle size within the range of 2 to 200 nm being within the range of 2: 1 to 200: 1 ; and the binder including a polyfunctional fluorinated (meth)acrylic compound.
- the anti-smudge hard coat of the present disclosure filled with a high concentration of nanoparticles demonstrates both excellent scratch resistance and impact resistance while maintaining optical transparency. Additionally, since the binder contains a polyfunctional fluorinated (meth)acrylic compound, a reaction product thereof, or a combination thereof, it is possible to prevent the adhesion of fingerprints, grease, dust, smudges, and the like or to easily wash the hard coat in the event of such adhesion, and it is also possible to increase the durability of the anti-smudge properties. In addition, such an anti-smudge hard coat can be formed using the anti-smudge hard coat precursor of the present disclosure.
- FIG. 1 is a graph showing the results of simulations between the mass ratios and filling rates of a small particle group and a large particle group for combinations of several particle sizes (small particle group/large particle group).
- FIG. 2 is a pattern diagram of an abrasion resistance test device used in the embodiments.
- (meth)acrylic refers to “acrylic or methacrylic
- (meth)acrylate refers to "acrylate or methacrylate”.
- the hard coat of one embodiment of the present disclosure contains a nanoparticle mixture and a binder, and the binder contains a polyfunctional fluorinated (meth)acrylic compound, a reaction product thereof, or a combination thereof.
- Examples of representative binders contained in the hard coat include resins obtained by polymerizing a curable monomer and/or a curable oligomer and resins obtained by polymerizing sol-gel glass. More specific examples include acrylic resins, urethane resins, epoxy resins, phenol resins, and polyvinyl alcohol resins.
- the curable monomer or curable oligomer can be selected from known curable monomers or curable oligomers in this technical field, and it is possible to use a mixture of two or more curable monomers, a mixture of two or more curable oligomers, or a mixture of one or two or more curable monomers and one or two or more curable oligomers.
- examples of resins include dipentaerythritol pentaacrylate (available from the Sartomer Company (Exton, PA) under the product name "SR399", for example), pentaerythritol triacrylate isophorone diisocyanate (IPDI) (available from Nippon Kayaku Co., Ltd. (Tokyo Japan) under the product name "UX-5000", for example), urethane acrylate (available from Nippon Synthetic Chemical Industry Co., Ltd.
- IPDI pentaerythritol triacrylate isophorone diisocyanate
- UX-5000 urethane acrylate
- the amount of the binder in the hard coat is typically from approximately 5 to 60 mass% and, in several embodiments, is from approximately 10 to 40 mass% or from approximately 15 to 30 mass% of the total mass of the anti-reflective hard coat. With the present disclosure, it is possible to form a hard coat with a relatively small amount of a binder.
- the hard coat may be further cured with another curable monomer or curable oligomer as necessary.
- curable monomers or curable oligomers include polyfunctional (meth)acrylic monomers and polyfunctional (meth)acrylic oligomers selected from a group comprising: (a) compounds having two (meth)acrylic groups such as 1,3-butylene glycol diacrylate, 1 ,4-butanediol diacrylate, 1 ,6-hexanediol diacrylate, 1 ,6-hexanediol monoacrylate monomethacrylate, ethylene glycol diacrylate, alkoxylated aliphatic diacrylate, alkoxylated cyclohexane dimethanol diacrylate, alkoxylated hexanediol diacrylate, alkoxylated neopentyl glycol diacrylate, caprolactone modified neopentyl glycol hydroxypivalate diacrylate, caprolactone modified
- Such compounds are commercially available, and at least several of these compounds are available from the Sartomer Company, UCB Chemicals Corporation (Smyrna, GA), the Aldrich Chemical Company (Milwaukee, WI), and the like.
- examples of other useful (meth)acrylates include hydantoin portion-containing poly(meth)acrylates, such as are disclosed in U.S. Patent No. 4262072.
- a preferable curable monomer or curable oligomer contains at least three (meth)acrylic groups.
- curable monomers or curable oligomers include those available from the Sartomer Company such as trimethylol propane triacrylate (TMPTA) product name: "SR351 "), pentaerythritol tri/tetraacrylate (PETA) (product names: "SR444" and "SR295"), and dipentaerythritol pentaacrylate (product name: "SR399”).
- TMPTA trimethylol propane triacrylate
- PETA pentaerythritol tri/tetraacrylate
- dipentaerythritol pentaacrylate product name: "SR399”
- mixtures of polyfunctional (meth)acrylates and monofunctional (meth)acrylates such as a mixture of PETA and 2-phenoxyethyl acrylate (PEA) can also be used.
- the nanoparticle mixture contained in the hard coat constitutes from approximately 40 to 95 mass% of the entire mass of the hard coat and, in several embodiments, constitutes from approximately 60 to 90 mass% or from approximately 70 to 85 mass% of the entire mass of the hard coat.
- the nanoparticle mixture contains from approximately 10 to 50 mass% of nanoparticles having an average particle size within the range of approximately 2 to 200 nm (hereafter called the small particle group or the first nanoparticle group) and from approximately 50 to 90 mass% of nanoparticles having an average particle size within the range of approximately 60 to 400 nm (hereafter called the large particle group or the second nanoparticle group).
- the nanoparticle mixture may be obtained by mixing the first nanoparticle group with an average particle size of approximately 2 to 200 nm and the second nanoparticle group with an average particle size of approximately 60 to 400 nm at a mass ratio of approximately 10:90 to 50:50.
- the average particle size of the nanoparticles can be measured with a transmission electron microscope (TEM) using technology commonly used in this technical field.
- TEM transmission electron microscope
- a sol sample for a TEM image can be prepared by dripping a sol sample into a 400-mesh copper TEM grid having an ultra-thin carbon substrate on the upper surface of mesh lace-like carbon (available from Ted Pella Inc. (Redding, CA)).
- Some liquid droplets can be removed by bringing the droplets into contact with filter paper as well as the side or bottom portion of the grid.
- the remaining sol solvent can be removed by heating or allowing the solution to stand at room temperature. This allows the particles to rest on the ultra-thin carbon substrate and to be imaged with the least interference from the substrate.
- the TEM image can be recorded at many positions spanning the entire grid. Sufficient images are recorded to enable the measurement of the particle sizes of 500 to 1000 particles.
- the average particle size of the nanoparticles can be calculated based on the particle size measurements of each of the samples.
- TEM images can be obtained using a high-resolution transmission electron microscope (using an LaB 6 source) operating at 300 KV (available from the Hitachi High Technologies Corporation under the product name "Hitachi H-9000").
- the images can be recorded using a camera (available from Gatan, Inc. (Pleasanton, CA) under the product name "GATAN ULTRASCAN CCD", for example: model No. 895, 2k x 2k chip).
- the images can be taken at a magnification of 50,000 and 100,000 times. Images can be taken at a magnification of 300,000 times for several samples.
- the nanoparticles are typically inorganic particles.
- inorganic particles include inorganic oxides such as alumina, tin oxide, antimony oxide, silica (SiO, Si0 2 ), zirconia, titania, ferrite, and the like, as well as mixtures thereof, or mixed oxides thereof; metal vanadate, metal tungstate, metal phosphate, metal nitrate, metal sulfate, metal carbide, and the like.
- An inorganic oxide sol can be used as inorganic oxide nanoparticles.
- silica nanoparticles for example, a silica sol obtained using liquid glass (sodium silicate solution) as a starting material can be used.
- a silica sol obtained from liquid glass may have a very narrow particle size distribution depending on the manufacturing conditions; therefore, when such a silica sol is used, a hard coat having desired characteristics can be obtained by more accurately controlling the filling rate of nanoparticles in the hard coat.
- the average particle size of the small particle group is within the range of approximately 2 to 200 nm.
- the particle size is preferably from approximately 2 to 150 nm, from approximately 3 to 120 nm, or from approximately 5 to 100 nm.
- the average particle size of the large particle group is within the range of approximately 60 to 400 nm.
- the particle size is preferably from approximately 65 to 350 nm, from approximately 70 to 300 nm, or from approximately 75 to 200 nm.
- the nanoparticle mixture contains a particle size distribution of at least two different types of nanoparticles.
- the particle size distribution of the nanoparticle mixture may exhibit bimodality or multimodality with peaks at the average particle size of the small particle group and the average particle size of the large particle group.
- the nanoparticles may be the same or different from one another (for example, surface-modified or not surface-modified
- a ratio of the average particle size of nanoparticles having an average particle size within the range of approximately 2 to 200 nm to the average particle size of nanoparticles having an average particle size within the range of approximately 60 to 400 nm is within the range of 2: 1 to 200: 1 and, in several embodiments, is within the range of 2.5: 1 to 100: 1 or 2.5: 1 to 25: 1.
- Examples of preferable combinations of average particle sizes include combinations of 5 nm/190 nm, 5 nm/75 nm, 20 nm/190 nm, 5 nm/20 nm, 20 nm/75 nm, 75 nm/190 nm, and 5 nm/20 nm/190 nm.
- the transparency (haze or the like) and hardness can be varied by selecting the type, amount, size, and ratio of the nanoparticles, for example.
- a hard coat having both a desired transparency and hardness can be obtained.
- the mass ratio (%) of the small particle group and the large particle group can be selected in accordance with the particle size used or the combination of particle sizes used.
- a preferable mass ratio can be selected in accordance with the particle size used or the combination of particle sizes used by using software available under the product name "CALVOLD2" and can be selected based on a simulation between the mass ratio and filling rate of the small particle group and the large particle group for the combination of particle sizes (small particle group/large particle group), for example (see also "Verification of a Model for Estimating the Void Fraction in a Three-Component Randomly Packed Bed," M. Suzuki and T. Oshima: Powder Technol., 43, 147- 153 (1985)).
- the simulation results are illustrated in FIG. 1.
- the mass ratio (small particle group: large particle group) for a combination of 5 nm/190 nm is from approximately 45:55 to 13:87 or from approximately 40:60 to 15:85.
- the mass ratio for a combination of 5 nm/75 nm is preferably from approximately 45:55 to 10:90 or from approximately 35:65 to 15:85.
- the mass ratio for a combination of 20 nm/190 nm is preferably from approximately 45:55 to 10:90.
- the mass ratio for a combination of 5 nm/20 nm is preferably from approximately 50:50 to 20:80.
- the mass ratio for a combination of 20 nm/75 nm is preferably from approximately 50:50 to 22:78.
- the mass ratio for a combination of 75 nm/190 nm is preferably from approximately 50:50 to 27:73.
- using a preferable combination of particle sizes and nanoparticles makes it possible to increase the amount of nanoparticles with which the hard coat is filled and to adjust the transparency and hardness of the resulting hard coat.
- the thickness of the hard coat is typically within the range of approximately 80 nm to 30 ⁇ (in several embodiments, from approximately 200 nm to 20 ⁇ or from approximately 1 to 10 ⁇ ), however, the hard coat can sometimes be used effectively even when the thickness deviates from these ranges. Using a mixture of nanoparticles of different sizes sometimes makes it possible to obtain a hard coat with a greater thickness and higher hardness.
- the surface of the nanoparticles may be modified using a surface treatment agent as necessary.
- a surface treatment agent typically has a first terminal bonding to the particle surface (via covalent bonds, ionic bonds, or strong physisorption) and a second terminal which gives the particles
- surface treatment agents include alcohols, amines, carboxylic acids, sulfonic acids, phosphonic acids, silanes, and titanates.
- the preferred type of treatment agent is determined, in part, by the chemical nature of the nanoparticle surface. When silica or another siliceous filler are used as nanoparticles, a silane is preferable.
- Silanes and carboxylic acids are preferred for metal oxides.
- Surface modification may be performed before, during, or after mixing with a curable monomer or a curable oligomer.
- the reaction between the silane and the nanoparticle surface is preferably performed before mixing with the curable monomer or the curable oligomer.
- the required amount of the surface treating agent is determined by several factors such as the particle size and type of the nanoparticles and the molecular weight and type of the surface treating agent. It is typically preferable for one layer of a surface treating agent to be deposited onto the surface of the particles.
- the required deposition procedure or reaction conditions are also determined by the surface treating agent that is used.
- a silane it is preferable to perform surface treatment for approximately 1 to 24 hours at a high temperature under acidic or basic conditions. A high temperature or long period of time is typically unnecessary in the case of a surface treating agent such as a carboxylic acid.
- Representative examples of surface treating agents include compounds such as
- the binder of the anti-smudge hard coat of the present disclosure contains a polyfunctional fluorinated (meth)acrylic compound, a reaction product thereof, or a combination thereof, which provides the hard coat surface with anti-smudge properties and improves the ease of washing (for example, fingerprint prevention, oil resistance, dust prevention, and/or anti-smudge functions).
- the polyfunctional fluorinated (meth)acrylic compound has a plurality of (meth)acrylic groups and can therefore react with a curable monomer or a curable oligomer as a crosslinking agent or can interact non-covalently with functional groups contained in the binder in a plurality of sites. As a result, the durability of the anti-smudge properties can be increased.
- a polyfunctional fluorinated (meth)acrylic compound has a plurality of (meth)acrylic groups and can therefore react with a curable monomer or a curable oligomer as a crosslinking agent or can interact non-covalently with functional
- (meth)acrylic compound it may also be possible to increase scratch resistance by reducing the coefficient of friction of the hard coat surface.
- a polyfunctional fluorinated (meth)acrylic compound having three or more (meth)acrylic groups it is possible to further increase the durability of the anti-smudge properties.
- the polyfunctional fluorinated (meth)acrylic compound is preferably a perfluoroether compound having two or more (meth)acrylic groups.
- 2008-527090 can be used as perfluoroether compounds having two or more (meth)acrylic groups.
- polyfunctional perfluoroether (meth)acrylates include:
- HFPO refers to a perfluoroether site expressed by F(CF(CF3)CF 2 0) n CF(CF 3 )- (n is from 2 to 15) and a compound containing such a perfluoroether site.
- the polyfunctional perfluoropolyether (meth)acrylate described above can be synthesized, for example, via a first step of reacting a poly(hexafluoropropylene oxide) ester such as HFPO-C(0)OCH 3 or a poly(hexafluoropropylene oxide) acid halide: HFPO-C(0)F with a material containing at least three alcohols or primary or secondary amino groups to produce an HFPO-ester having an HFPO-amide polyol or polyamine, an HFPO-ester polyol or polyamine, an HFPO-amide, or a mixed amine and an alcohol group and a second step of (meth)acrylating the alcohol group and/or amine group with a (meth)acryloyl halide, a (meth)acrylic acid anhydride, or a (meth)acrylic acid.
- a poly(hexafluoropropylene oxide) ester such as HFPO-C(0)OCH 3 or
- the polyfunctional perfluoropolyether (meth)acrylate can be synthesized using a Michael- type addition reaction of a reactive perfluoroether such as an adduct of HFPO-C(0)N(H)CH 2 CH 2 CH 2 N(H)CH 3 and trimethylol propane triacrylate (TMPTA) and a poly(meth)acrylate.
- a reactive perfluoroether such as an adduct of HFPO-C(0)N(H)CH 2 CH 2 CH 2 N(H)CH 3 and trimethylol propane triacrylate (TMPTA) and a poly(meth)acrylate.
- a preferable polyfunctional fluorinated (meth)acrylic compound is one in which the perfluoroether site is bivalent and (meth)acrylic groups bond with both terminals directly or via other groups or bonds (ether bonds, ester bonds, amide bonds, urethane bonds, or the like). Although not bound by any particular theory, it is thought that such a compound forms a firm bond with the hard coat so as to improve the durability of the anti-smudge properties, and the perfluoroether site between
- (meth)acrylic groups migrates to the hard coat surface so as to be easily oriented in the in-plane direction. As a result, it may be possible to sufficiently express anti-smudge properties.
- the polyfunctional fluorinated (meth)acrylic compound may contain siloxane units.
- the polyfunctional fluorinated (meth)acrylic compound containing siloxane units is more firmly held onto the hard coat not only by the reaction between the (meth)acrylic groups and the curable monomer or the curable oligomer, but also by interactions between siloxane bonds and the nanoparticles, which is thought to further increase the durability of the anti-smudge properties.
- the nanoparticles are preferably silica nanoparticles which are chemically similar to and have high affinity with siloxane bonds.
- the polyfunctional fluorinated (meth)acrylic compound containing siloxane units can be synthesized, for example, by adding (hydrosilating) a perfluoropolyether compound having one or two or more unsaturated ethylene groups to a straight-chain or cyclic oligosiloxane or polysiloxane (hydrogen siloxane) containing three or more Si-H bonds in the presence of a platinum catalyst or the like at a volume of less than one equivalent with respect to the Si-H bonds, similarly adding (hydrosilating) a hydroxyl group-containing unsaturated ethylene compound to the remaining Si-H bonds in the presence of a platinum catalyst or the like, and then reacting the hydroxyl groups with an epoxy (meth)acrylate, urethane (meth)acrylate, or the like.
- the partial molecular weight of the perfluoroether site calculated from the chemical formula may be from 500 to 30,000.
- the siloxane units In order to sufficiently express the anti-smudge properties imparted by the fluorinated site, it is preferable for the siloxane units to be cyclic siloxane units derived from tetramethyl cyclotetrasiloxane, pentamethyl cyclopentasiloxane, or the like.
- the number of silicon atoms constituting the cyclic siloxane units is preferably from 3 to 7.
- a polyfunctional fluorinated (meth)acrylic compound containing siloxane units is a perfluoropolyether compound having two or more (meth)acrylic groups as described in Japanese Unexamined Patent Application Publication No. 2010-285501 , for example.
- the compounds of formulas (19) and (21) in this publication have structures in which cyclic siloxanes with four silicon atoms respectively bond to both terminals of a bivalent perfluoropolyether group:
- the compound and reaction product are contained in the binder within the range of approximately 0.01 to 20 parts by mass (in several embodiments, from approximately 0.1 to 10 parts by mass or from approximately 0.2 to 5 parts by mass) with respect to a total of 100 parts by mass of the nanoparticles, the curable monomer, and the curable oligomer, for example.
- the binder of the hard coat may further contain known additives such as an ultraviolet absorbent, a defogging agent, a leveling agent, an ultraviolet reflecting agent, an anti-static agent, or the like, or another chemical which provides a function of facilitating cleaning as necessary.
- known additives such as an ultraviolet absorbent, a defogging agent, a leveling agent, an ultraviolet reflecting agent, an anti-static agent, or the like, or another chemical which provides a function of facilitating cleaning as necessary.
- the ultraviolet absorbent is contained in the binder of the hard coat.
- the ultraviolet absorbent can be mixed with the curable monomer or the curable oligomer.
- a known agent may be used as the ultraviolet absorbent.
- ultraviolet absorbents such as benzophenone absorbents (available from BASF AG under the product name "Uvinul 3050", for example), benzotriazole absorbents (available from BASF AG under the product name "Tinuvin 928", for example), triazine absorbents (available from BASF AG under the product name "Tinuvin 1577", for example), salicylate absorbents, diphenylacrylate absorbents, and cyanoacrylate absorbents and hindered amine light stabilizers (HALSs) (available from BASF AG under the product name "Tinuvin 292", for example) may be used.
- HALSs hindered amine light stabilizers
- the amount of the ultraviolet absorbent that is added may be, for example, within the range of approximately 0.01 to 20 parts by mass (in several embodiments, from approximately 0.1 to 15 parts by mass or from approximately 0.2 to 10 parts by mass) with respect to a total of 100 parts by mass of the nanoparticles, the curable monomer, and the curable oligomer.
- the hard coat containing the ultraviolet absorbent can achieve ultraviolet transmittance of less than 3%.
- a defogging agent is contained in the binder of the hard coat.
- the defogging agent can be mixed with the curable monomer or the curable oligomer.
- Anionic, cationic, nonionic or amphoteric surfactants can be used as the defogging agent, examples of which include sorbitan surfactants such as sorbitan monostearate, sorbitan monomyristate, sorbitan monopalmitate, sorbitan monobehenate, and esters of sorbitan, alkylene glycol condensates, and fatty acids; glycerin surfactants such as glycerin monopalmitate, glycerin monostearate, glycerin monolaurate, diglycerin monopalmitate, glycerin dipalmitate, glycerin distearate, glycerin monopalmitate/monostearate, triglycerin monostearate, triglycerin
- the defogging agent may also have functional groups which react with the curable monomer or the curable oligomer.
- the amount of the defogging agent that is added may be, for example, within the range of approximately 0.01 to 20 parts by mass (in several embodiments, from approximately 0.1 to 15 parts by mass or from approximately 0.2 to 10 parts by mass) with respect to a total of 100 parts by mass of the nanoparticles, the curable monomer, and the curable oligomer.
- a hard coat precursor that can be used to form a hard coat contains the nanoparticle mixture described above, a binder containing a curable monomer and/or a curable oligomer and a polyfunctional fluorinated (meth)acrylic compound, a reaction initiator, and, if necessary a solvent such as methyl ethyl ketone (MEK), 1 -methoxy-2-propanol (MP-OH), or the like, and the additives described above such as an ultraviolet absorbent, a defogging agent, a leveling agent, an ultraviolet reflecting agent, an anti-static agent, or the like.
- MEK methyl ethyl ketone
- MP-OH 1 -methoxy-2-propanol
- the hard coat precursors of some embodiments contain a nanoparticle mixture and a binder, wherein the nanoparticles constitute from 40 to 95 mass% of the total mass of the nanoparticles and the binder. From 10 to 50 mass% of the nanoparticles have an average particle size within the range of 2 to 200 nm, and from 50 to 90 mass% of the nanoparticles have an average particle size within the range of 60 to 400 nm.
- the ratio of the average particle size of nanoparticles having an average particle size within the range of 60 to 400 nm to the average particle size of nanoparticles having an average particle size within the range of 2 to 200 nm is within the range of 2: 1 to 200: 1 , and the binder contains a polyfunctional fluorinated (meth)acrylic compound.
- a hard coat precursor can be prepared by combining specific components of the hard coat precursor.
- the hard coat precursor can be prepared by preparing a modified or non-modified nanoparticle sol of two or more different sizes with a desired solid content by mixing a curable monomer and/or a curable oligomer together with a reaction initiator in a solvent and adding a solvent.
- a light initiator or thermal polymerization initiator known in this technical field, for example, may be used as the reaction initiator.
- the hard coat precursor can be prepared as follows, for example. An inhibitor and a surface modifier are added to a solvent in a container (for example, in a glass vial), and the resulting mixture is added to an aqueous solution in which
- nanoparticles are dispersed and is then stirred.
- the container is sealed and placed in an oven for several hours (for example, 16 hours) at a high temperature (for example, 80°C).
- a rotary evaporator for example, is used at a high temperature (for example, 60°C) to remove the water from the solution.
- the concentration of the nanoparticles can be adjusted to a desired concentration (mass%) by adjusting the volume of the solvent.
- the coated hard coat precursor is dried as necessary and can be cured with a known polymerization method in this technical field such as optical polymerization using ultraviolet rays or electron beams, thermal polymerization, or the like. In this way, a hard coat can be formed on a substrate.
- Examples of representative substrates to which the anti-smudge hard coat of the present disclosure is applied include films, plastics (polymer plates), sheet glass, and metal sheets. Films may be transparent or opaque. In the present disclosure, “transparent” means that the total light transmission rate in the visible light range (380 to 780 nm) is at least 90%, and “opaque” means that the total light transmission rate in the visible light range (380 to 780 nm) is less than 90%. Examples of
- representative films include films formed from polyolefins (for example, polyethylene (PE), polypropylene (PP), or the like), polyurethanes, polyesters (for example, polyethylene terephthalate (PET) or the like), poly(meth)acrylates (for example, polymethyl methacrylate (PMMA) or the like), polyvinyl chlorides, polycarbonates, polyamides, polyimides, phenol resins, cellulose diacetates, cellulose triacetates, polystyrenes, styrene-acrylonitrile copolymers, acrylonitrile-butadiene-styrene copolymers (ABS), epoxies, polyacetates, or glass.
- Plastics (polymer plates) may be transparent or opaque. Examples of representative plastics (polymer plates) include plastics formed from
- PC polycarbonates
- PMMA polymethylmethcrylates
- styrene-acrylonitrile copolymers
- Metal sheets may be flexible or rigid.
- a "flexible metal sheet” refers to a metal sheet which does not undergo substantial irreversible changes and can receive mechanical stress such as bending or elongation
- a "rigid metal sheet” refers to a metal sheet which does not undergo substantial irreversible changes and cannot receive mechanical stress such as bending or elongation.
- a representative flexible metal sheet is one made from aluminum.
- Representative rigid metal sheets are sheets made from aluminum, nickel, nickel-chrome, and stainless steel.
- a thickness of the film is within the range of approximately 5 to 500 ⁇ (in several embodiments, from approximately 10 to 200 ⁇ or from approximately 25 to 100 ⁇ ).
- a thickness of the plastic (polymer plate) is within the range of approximately 0.5 mm to 10 cm (in several embodiments, from approximately 0.5 to 5 mm or from approximately 0.5 to 3 mm).
- a thickness of the sheet glass or metal sheet is within the range of approximately 5 to 500 ⁇ or from approximately 0.5 mm to 10 cm (in several embodiments, from approximately 0.5 to 5 mm or from approximately 0.5 to 3 mm).
- the hard coat can be applied to a plurality of surfaces of the substrate.
- a plurality of hard coat layers can be applied to the surface of the substrate.
- the surface of the substrate is primed or a primer layer is disposed on the surface of the substrate in order to improve the adhesion of the hard coat and the substrate.
- a primer layer is particularly effective. Priming is known in this technical field, and examples include plasma treatment, corona discharge treatment, flame treatment, electron beam irradiation, surface roughening, ozone treatment, chemical oxide treatment using chromic acid or sulfuric acid, and the like.
- Examples of materials used for the primer layer include (meth)acrylic resins (homopolymers of
- (meth)acrylates copolymers of two or more types of (meth)acrylates, or copolymers of (meth)acrylates and other polymerizable monomers
- urethane resins for example, 2-solution curable urethane resins consisting of a polyol and an isocyanate curing agent
- (meth)acryl-urethane copolymers for example, acryl-urethane block copolymers
- polyester resins butyral resins, vinyl chloride-vinyl acetate copolymers, ethylene-vinyl acetate copolymers, chlorinated polyolefins such as chlorinated
- polyethylenes or chlorinated polypropylenes, and copolymers and derivatives thereof for example, chlorinated ethylene-propylene copolymers, chlorinated ethylene-vinyl acetate copolymers,
- the substrate is a polypropylene film
- the primer it is advantageous for the primer to contain a chlorinated polypropylene or a modified chlorinated polypropylene.
- the primer layer can be formed by applying a primer solution prepared by dissolving the aforementioned resins in a solvent using a known method in this technical field and then drying the solution.
- a thickness of the primer layer is typically within the range of approximately 0.1 to 20 ⁇ (in several embodiments, from approximately 0.5 to 5 ⁇ ).
- the substrate may also have a printing layer, a coloring layer, a metal thin film layer, or the like with a desired pattern as necessary.
- a product containing the hard coat of the present disclosure may also have an adhesive layer if necessary.
- the adhesive layer can be disposed on the surface of the substrate on the opposite side when viewed from the hard coat, for example.
- a rubber adhesive, acrylic adhesives, polyurethane adhesives, a polyolefin adhesives, polyester adhesives, and silicon adhesives or pressure-sensitive adhesives known in this technical field can be used as adhesive layers.
- An adhesive layer may be formed by directly applying or extruding the adhesive and the pressure-sensitive adhesive onto the substrate, or an adhesive layer formed by applying the adhesive and the pressure-sensitive adhesive to a release liner may be laminated and transferred to the substrate.
- a thickness of the adhesive layer including the adhesive or the pressure-sensitive adhesive is typically within the range of approximately 1 to 100 ⁇ (in several embodiments, from approximately 5 to 75 ⁇ or from approximately 10 to 50 ⁇ ).
- the adhesive or the pressure-sensitive adhesive may also contain the ultraviolet absorbent described above.
- the hard coat and/or the adhesive layer may also be provided with a release liner known in this technical field, as necessary.
- a material known in this technical field and prepared by performing silicon processing or the like on paper or a polymer film can be used as the release liner.
- the anti-smudge hard coat of the present disclosure is useful, for example, in optical displays (for example, cathode ray tube (CRT) and light-emitting diode (LED) displays), plastic cards, the lenses or main bodies of cameras, fans, doorknobs, faucet handles, mirrors, and household electronics such as vacuum cleaners, washing machines, and the like; personal digital assistants (PDAs), mobile telephones, liquid crystal display (LCD) panels, devices with touch sensor screens, detachable computer screens, or the like, and the main bodies of such devices, and the like.
- the anti-smudge hard coat of the present disclosure may also be useful, for example, in furniture, doors and windows, toilets and baths, interiors/exteriors of vehicles, lenses (of cameras or glasses), or solar-powered panels (solar panels).
- Various embodiments are provided that include a hard coat or a hard coat precursor.
- Embodiemnt 1 is a hard coat comprising a nanoparticle mixture and a binder; the nanoparticles constituting from 40 to 95 mass% of an entire mass of the hard coat; from 10 to 50 mass% of the nanoparticles having an average particle size within a range of 2 to 200 nm; from 50 to 90 mass% of the nanoparticles having an average particle size within a range of 60 to 400 nm; a ratio of the average particle size of nanoparticles having an average particle size within the range of 60 to 400 nm to the average particle size of nanoparticles having an average particle size within the range of 2 to 200 nm being within a range of 2: 1 to 200: 1 ; a particle size distribution of the nanoparticles being bimodal or multimodal; the binder comprising a polyfunctional fluorinated (meth)acrylic compound, a reaction product thereof, or a combination thereof; wherein the polyfunctional fluorinated (meth)acrylic compound comprises cyclic siloxane units.
- Embodiment 2 is the hard coat of embodiment 1 , wherein the nanoparticles are
- Embodiment 3 is the hard coat of embodiment 1 or 2, wherein the polyfunctional fluorinated (meth)acrylic compound is a perfluoroether compound having two or more (meth)acrylic groups.
- Embodiment 4 is the hard coat of any of the embodiments 1 to 3, wherein the polyfunctional fluorinated (meth)acrylic compound has 3 or more (meth)acrylic groups.
- Embodiment 5 Is the hard coat of any of the embodiments 1 to 4, wherein the nanoparticles are inorganic oxide nanoparticles, and the polyfunctional fluorinated (meth)acrylic compound comprises siloxane units.
- Embodiment 6 is the hard coat of any of the embodiments 1 to 5, wherein the nanoparticles are silica nanoparticles.
- Embodiment 7 is the hard coat of any of the embodiments 1 to 6, wherein the binder further comprises an ultraviolet absorbent.
- Embodiment 8 is a hard coat precursor comprising a nanoparticle mixture and a binder; the nanoparticles constituting from 40 to 95 mass% of a total mass of the nanoparticles and the binder; from 10 to 50 mass% of the nanoparticles having an average particle size within a range of 2 to 200 nm; from 50 to 90 mass% of the nanoparticles having an average particle size within a range of 60 to 400 nm; a ratio of the average particle size of nanoparticles having an average particle size within the range of 60 to 400 nm to the average particle size of nanoparticles having an average particle size within the range of 2 to 200 nm being within a range of 2: 1 to 200: 1 ; wherein a particle size distribution of the nanoparticles is bimodal or multimodal; and the binder comprising a polyfunctional fluorinated (meth)acrylic compound; wherein the polyfunctional fluorinated (meth)acrylic compound comprises cyclic siloxane units.
- the characteristics of the hard coat of the present disclosure were evaluated in accordance with the following methods.
- a hard coat was formed by applying a hard coat precursor to a substrate and irradiating the precursor with ultraviolet rays. The hard coat was evaluated while supported on the substrate. 1. Pencil Hardness
- the pencil hardness of the surface of the hard coat formed on the substrate was determined using a 750 g weight in accordance with JIS K5600-5-4 (1999).
- the haze of the hard coat was measured using an NDH-5000W haze meter (acquired from
- the water contact angle of the hard coat surface was measured by the Sessile Drop method using a contact angle meter (acquired from Kyowa Kaimen Kagaku Co., Ltd. under the product name "DROPMASTER FACE").
- the volume of liquid droplets was set to 4 ⁇ for static measurements.
- the value of the water contact angle was calculated from the average of five measurements.
- FIG. 2 illustrates a schematic diagram of an abrasion resistance test device 60 (IMC- 157C rubbing tester, acquired from Imoto Machinery Co., Ltd.).
- a sample 10 is fixed to the top of a stage 61, and the load of a weight 63 is applied to the fabric or the steel wool 64 via a stylus 62 so as to rub the surface of the sample by moving the stage 61 back and forth.
- the abrasion resistance test simulates scratching that occurs with wiping and washing.
- a surface-modified silica sol (“sol 1 ”) was prepared as follows. First, 5.95 g of SILQUEST
- PROSTAB A174 and 0.5 g of PROSTAB was added to a mixture of 400 g of NALCO 2329 and 450 g of
- a surface-modified silica sol (“sol 2”) was prepared as follows. Modification was performed with the same method as for sol 1 with the exception of using 400 g of NALCO 2327, 25.25 g of SILQUEST Al 74, and 0.5 g of PROSTAB, and an Si0 2 sol (hereafter called "sol 2") containing 45 mass% of surface-modified Si0 2 nanoparticles having an average particle size of 20 nm was obtained.
- HFPO urethane acrylate is a monofunctional fluorinated (meth)acrylic compound.
- Hard coat precursors HC-3 to HC-8 were prepared in the same manner as HC-2 with the formulas described in Table 2.
- KAYARAD UX-5000 was used as an acrylate oligomer in HC-6 to
- HC-8, and KY-1203 was used as a polyfunctional (meth)acrylic compound (anti-smudge agent) in HC-4, HC-5, and HC-8.
- the compositions of HC-1 to HC-8 are shown in Table 2.
- a PMMA substrate (Acrylite L-001, 100 x 53 x 2 mm, acquired from Mitsubishi Rayon Co., Ltd.) was fixed to the top of a stainless steel table equipped with a level.
- Hard coat precursor HC-4 was applied to the PMMA substrate using a #16 Meyer rod and dried for 5 minutes at 60°C.
- the coating surface was irradiated with ultraviolet rays ten times (irradiance: approximately 1400 mJ/ 2 ) at a line rate of 13 m/minute, in a nitrogen atmosphere, using an H-valve (DRS model) made by Fusion UV System Inc.
- the thickness of the hard coat was approximately 10 ⁇ . In this manner, the hard coat of Example 1 was formed on the PMMA substrate.
- Hard coats were formed on PMMA substrates in the same manner as in Example 1 using hard coat precursors HC-1 to HC-3 and HC-5 to HC-8. The results of evaluating these hard coats are shown in Tables 3 and 4.
- the hard coats containing fluorinated (meth)acrylic compounds as anti-smudge agents demonstrated a pencil hardness of 8 H equivalent to that of a hard coat not containing a fluorinated (meth)acrylic compound (Comparative Example 1).
- the addition of an appropriate amount of a fluorinated (meth)acrylic compound did not affect the pencil hardness of the hard coat.
- the water contact angle increased when a fluorinated (meth)acrylic compound was added.
- HC-4 (Example 1) and HC-5 (Example 2) demonstrated favorable ink repellency even after fabric abrasion resistance tests. On the other hand, the ink repellency became poor after fabric abrasion resistance tests on HC-3
- Table 4 shows the results of performing steel wool abrasion resistance tests in addition to fabric abrasion resistance tests.
- the water contact angle and the ink repellency were compared before and after the fabric abrasion resistance tests, and the water contact angle, the ink repellency, and the optical characteristics were compared before and after the steel wool abrasion resistance tests.
- HC-7
- Example 5 Comparative Example 5
- Example 3 demonstrated water contact angles exceeding 100 degrees as well as favorable ink repellency both at the beginning and after fabric abrasion resistance tests.
- the hard coat of Example 2 containing UX-5000, a polyfunctional acrylate having a plurality of acrylate groups, as a urethane acrylate oligomer had higher scratch resistance than the hard coat of Example 3 containing EBECRYL 4858.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Life Sciences & Earth Sciences (AREA)
- Materials Engineering (AREA)
- Wood Science & Technology (AREA)
- Organic Chemistry (AREA)
- Nanotechnology (AREA)
- Physics & Mathematics (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- General Physics & Mathematics (AREA)
- Manufacturing & Machinery (AREA)
- Crystallography & Structural Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Paints Or Removers (AREA)
- Laminated Bodies (AREA)
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SG11201500748XA SG11201500748XA (en) | 2012-08-01 | 2013-07-30 | Anti-smudge hard coat and anti-smudge hard coat precursor |
KR1020157004809A KR102159140B1 (ko) | 2012-08-01 | 2013-07-30 | 방오성 하드 코트 및 방오성 하드 코트 전구체 |
CN201380040679.0A CN104540900B (zh) | 2012-08-01 | 2013-07-30 | 防污硬涂层和防污硬涂层前体 |
HK15110293.6A HK1209448A1 (en) | 2012-08-01 | 2015-10-20 | Anti-smudge hard coat and anti-smudge hard coat precursor |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2012170999A JP6062680B2 (ja) | 2012-08-01 | 2012-08-01 | 防汚性ハードコートおよび防汚性ハードコート前駆体 |
JP2012-170999 | 2012-08-01 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2014022363A2 true WO2014022363A2 (en) | 2014-02-06 |
WO2014022363A3 WO2014022363A3 (en) | 2014-06-12 |
Family
ID=48998699
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2013/052677 WO2014022363A2 (en) | 2012-08-01 | 2013-07-30 | Anti-smudge hard coat and anti-smudge hard coat precursor |
Country Status (7)
Country | Link |
---|---|
JP (1) | JP6062680B2 (xx) |
KR (1) | KR102159140B1 (xx) |
CN (1) | CN104540900B (xx) |
HK (1) | HK1209448A1 (xx) |
SG (2) | SG11201500748XA (xx) |
TW (1) | TWI623595B (xx) |
WO (1) | WO2014022363A2 (xx) |
Cited By (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2016036507A1 (en) * | 2014-09-04 | 2016-03-10 | 3M Innovative Properties Company | Hardcoat and method of making the same |
WO2016137722A1 (en) * | 2015-02-24 | 2016-09-01 | 3M Innovative Properties Company | 3-d printing surface |
JP2017128114A (ja) * | 2016-01-18 | 2017-07-27 | リケンテクノス株式会社 | ハードコート積層フィルム |
WO2017142744A1 (en) * | 2016-02-18 | 2017-08-24 | 3M Innovative Properties Company | 3-d printing surface |
US20180208793A1 (en) * | 2015-08-03 | 2018-07-26 | Lg Chem, Ltd. | Coating composition for flexible plastic film |
US10118371B2 (en) | 2015-08-03 | 2018-11-06 | Lg Chem, Ltd. | Flexible plastic film |
US20180327626A1 (en) * | 2014-11-21 | 2018-11-15 | Dexerials Corporation | Coating Composition, and Super Water-Repellent Film |
US10233355B2 (en) | 2015-08-03 | 2019-03-19 | Lg Chem, Ltd. | Flexible plastic film |
EP3357078A4 (en) * | 2015-09-30 | 2019-05-15 | 3M Innovative Properties Company | MULTILAYER BARRIER COATINGS |
US11053393B2 (en) * | 2018-08-02 | 2021-07-06 | Benq Materials Corporation | Hard coating layered optical film, polarizer comprising the same, and image display comprising the hard coating layered optical film and/or the polarizer comprising the same |
US11054550B2 (en) * | 2018-08-02 | 2021-07-06 | Benq Materials Corporation | Anti-reflective film, polarizer comprising the same, and image display comprising the anti-reflective film and/or the polarizer comprising the same |
Families Citing this family (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101539262B1 (ko) * | 2014-08-20 | 2015-07-29 | 주식회사 콘텍 | 불소함유 Diol을 이용한 폴리머 조성물 및 이를 이용한 표면처리물 |
EP3272528B1 (en) | 2015-03-18 | 2021-04-14 | Riken Technos Corporation | Multilayer hard coating film |
KR102516912B1 (ko) | 2015-03-18 | 2023-03-31 | 리껭테크노스 가부시키가이샤 | 점착 필름 |
EP3666522B1 (en) | 2015-03-18 | 2022-07-06 | Riken Technos Corporation | Anti-glare hard coat laminated film |
EP3272529B1 (en) | 2015-03-18 | 2022-05-04 | Riken Technos Corporation | Hard coat laminated film |
US11433651B2 (en) | 2015-03-18 | 2022-09-06 | Riken Technos Corporation | Hard coat laminated film |
US11352473B2 (en) | 2015-03-18 | 2022-06-07 | Riken Technos Corporation | Hard coat laminated film and method for producing same |
EP3272513B1 (en) | 2015-03-18 | 2022-06-01 | Riken Technos Corporation | Molded body |
JP6806048B2 (ja) * | 2015-04-07 | 2021-01-06 | 日産化学株式会社 | 防眩性コーティング用硬化性組成物 |
WO2017015885A1 (en) * | 2015-07-29 | 2017-02-02 | 3M Innovative Properties Company | Anti-soiling compositions comprising silica nanopaticles and functional silane compounds and coated articles thereof |
KR101862251B1 (ko) * | 2015-08-03 | 2018-05-29 | 주식회사 엘지화학 | 플렉시블 플라스틱 필름 |
WO2017023120A1 (ko) * | 2015-08-03 | 2017-02-09 | 주식회사 엘지화학 | 플렉시블 플라스틱 필름용 코팅 조성물 |
US11774166B2 (en) | 2015-11-25 | 2023-10-03 | Riken Technos Corporation | Door body |
TWI745316B (zh) | 2015-11-25 | 2021-11-11 | 日商理研科技股份有限公司 | 門體 |
JP6644534B2 (ja) | 2015-12-08 | 2020-02-12 | リケンテクノス株式会社 | ハードコート積層フィルム |
EP3808800B1 (en) | 2016-09-14 | 2022-01-05 | Riken Technos Corporation | Hard coat laminated film |
JP7064313B2 (ja) | 2016-11-25 | 2022-05-10 | リケンテクノス株式会社 | ハードコート積層フィルム |
KR102429958B1 (ko) * | 2017-06-21 | 2022-08-09 | 현대자동차주식회사 | 차량의 전파투과 커버용 자외선 경화형 프라이머 |
DE102019106081B4 (de) * | 2019-03-11 | 2024-05-08 | Joanneum Research Forschungsgesellschaft Mbh | Oligomere Hexafluorpropylenoxidderivate |
CN114231137A (zh) * | 2021-12-27 | 2022-03-25 | 武汉格林鸿业新材料科技有限公司 | 无溶剂型自清洁uv树脂环保涂层及其制备方法 |
TW202348554A (zh) * | 2022-01-13 | 2023-12-16 | 日商日產化學股份有限公司 | 具有粒度分布之氧化矽溶膠及其製造方法 |
CN116656155A (zh) * | 2023-05-22 | 2023-08-29 | 兰州空间技术物理研究所 | 一种太阳能电池表面月尘防护涂层及其制备方法和防尘效率评价方法 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4262072A (en) | 1979-06-25 | 1981-04-14 | Minnesota Mining And Manufacturing Company | Poly(ethylenically unsaturated alkoxy) heterocyclic protective coatings |
US5104929A (en) | 1988-04-11 | 1992-04-14 | Minnesota Mining And Manufacturing Company | Abrasion resistant coatings comprising silicon dioxide dispersions |
US7074463B2 (en) | 2003-09-12 | 2006-07-11 | 3M Innovative Properties Company | Durable optical element |
US20080124555A1 (en) | 2006-11-29 | 2008-05-29 | 3M Innovative Properties Company | Polymerizable composition comprising perfluoropolyether urethane having ethylene oxide repeat units |
JP2008527090A (ja) | 2004-12-30 | 2008-07-24 | スリーエム イノベイティブ プロパティズ カンパニー | 耐汚染性フルオロケミカル組成物 |
JP2008538195A (ja) | 2005-03-23 | 2008-10-16 | スリーエム イノベイティブ プロパティズ カンパニー | (メタ)アクリル基を有するパーフルオロポリエーテルウレタン添加剤およびハードコート |
JP2010285501A (ja) | 2009-06-10 | 2010-12-24 | Shin-Etsu Chemical Co Ltd | パーフルオロポリエーテル基を有するアクリレート化合物 |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4149924B2 (ja) * | 2001-09-11 | 2008-09-17 | スリーエム イノベイティブ プロパティズ カンパニー | 耐汚染性ナノ複合材ハードコートおよびその製造方法 |
US7378136B2 (en) * | 2004-07-09 | 2008-05-27 | 3M Innovative Properties Company | Optical film coating |
JP5433926B2 (ja) * | 2006-04-18 | 2014-03-05 | Jsr株式会社 | 硬化性樹脂組成物及び反射防止膜 |
US20080003420A1 (en) * | 2006-06-29 | 2008-01-03 | 3M Innovative Properties Company | Transfer hardcoat films for graphic substrates |
US7709092B2 (en) * | 2007-01-19 | 2010-05-04 | 3M Innovative Properties Company | Solar control multilayer film |
EP2222463A4 (en) * | 2007-11-28 | 2013-06-05 | 3M Innovative Properties Co | HARD-FILM FILMS FOR GRAPHIC SUBSTRATES |
CN102241899B (zh) * | 2010-05-11 | 2014-05-14 | 3M创新有限公司 | 涂料组合物,改性基体表面的方法和制品 |
JP5477160B2 (ja) * | 2010-05-20 | 2014-04-23 | 信越化学工業株式会社 | 含フッ素(メタ)アクリル変性有機ケイ素化合物及びこれを含む硬化性組成物 |
KR101870473B1 (ko) * | 2011-01-14 | 2018-06-22 | 다이니폰 인사츠 가부시키가이샤 | 반사 방지 필름, 반사 방지 필름의 제조 방법, 편광판 및 화상 표시 장치 |
JP6040936B2 (ja) * | 2011-05-16 | 2016-12-07 | 大日本印刷株式会社 | 反射防止フィルムの製造方法、反射防止フィルム、偏光板、及び画像表示装置 |
US9523795B2 (en) * | 2011-11-25 | 2016-12-20 | Fujifilm Corporation | Antistatic antireflection film, method for manufacturing antistatic antireflection film, polarizing plate and image display device |
-
2012
- 2012-08-01 JP JP2012170999A patent/JP6062680B2/ja active Active
-
2013
- 2013-07-30 WO PCT/US2013/052677 patent/WO2014022363A2/en active Application Filing
- 2013-07-30 SG SG11201500748XA patent/SG11201500748XA/en unknown
- 2013-07-30 CN CN201380040679.0A patent/CN104540900B/zh active Active
- 2013-07-30 KR KR1020157004809A patent/KR102159140B1/ko active IP Right Grant
- 2013-07-30 SG SG10201707666UA patent/SG10201707666UA/en unknown
- 2013-07-31 TW TW102127567A patent/TWI623595B/zh not_active IP Right Cessation
-
2015
- 2015-10-20 HK HK15110293.6A patent/HK1209448A1/xx unknown
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4262072A (en) | 1979-06-25 | 1981-04-14 | Minnesota Mining And Manufacturing Company | Poly(ethylenically unsaturated alkoxy) heterocyclic protective coatings |
US5104929A (en) | 1988-04-11 | 1992-04-14 | Minnesota Mining And Manufacturing Company | Abrasion resistant coatings comprising silicon dioxide dispersions |
US7074463B2 (en) | 2003-09-12 | 2006-07-11 | 3M Innovative Properties Company | Durable optical element |
JP2008527090A (ja) | 2004-12-30 | 2008-07-24 | スリーエム イノベイティブ プロパティズ カンパニー | 耐汚染性フルオロケミカル組成物 |
JP2008538195A (ja) | 2005-03-23 | 2008-10-16 | スリーエム イノベイティブ プロパティズ カンパニー | (メタ)アクリル基を有するパーフルオロポリエーテルウレタン添加剤およびハードコート |
US7718264B2 (en) | 2005-03-23 | 2010-05-18 | 3M Innovative Properties Company | Perfluoropolyether urethane additives having (meth)acryl groups and hard coats |
US20080124555A1 (en) | 2006-11-29 | 2008-05-29 | 3M Innovative Properties Company | Polymerizable composition comprising perfluoropolyether urethane having ethylene oxide repeat units |
JP2010285501A (ja) | 2009-06-10 | 2010-12-24 | Shin-Etsu Chemical Co Ltd | パーフルオロポリエーテル基を有するアクリレート化合物 |
Non-Patent Citations (1)
Title |
---|
M. SUZUKI; T. OSHIMA: "Verification of a Model for Estimating the Void Fraction in a Three-Component Randomly Packed Bed", POWDER TECHNOL., vol. 43, 1985, pages 147 - 153 |
Cited By (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2016036507A1 (en) * | 2014-09-04 | 2016-03-10 | 3M Innovative Properties Company | Hardcoat and method of making the same |
US20180327626A1 (en) * | 2014-11-21 | 2018-11-15 | Dexerials Corporation | Coating Composition, and Super Water-Repellent Film |
US10533110B2 (en) | 2014-11-21 | 2020-01-14 | Dexerials Corporation | Coating composition, and super water-repellent film |
WO2016137722A1 (en) * | 2015-02-24 | 2016-09-01 | 3M Innovative Properties Company | 3-d printing surface |
US10626292B2 (en) | 2015-08-03 | 2020-04-21 | Lg Chem, Ltd. | Coating composition for flexible plastic film |
US11168191B2 (en) | 2015-08-03 | 2021-11-09 | Lg Chem, Ltd. | Flexible plastic film |
US11161951B2 (en) | 2015-08-03 | 2021-11-02 | Lg Chem, Ltd. | Coating composition for flexible plastic film |
US20180208793A1 (en) * | 2015-08-03 | 2018-07-26 | Lg Chem, Ltd. | Coating composition for flexible plastic film |
US10118371B2 (en) | 2015-08-03 | 2018-11-06 | Lg Chem, Ltd. | Flexible plastic film |
US10233355B2 (en) | 2015-08-03 | 2019-03-19 | Lg Chem, Ltd. | Flexible plastic film |
EP3357078A4 (en) * | 2015-09-30 | 2019-05-15 | 3M Innovative Properties Company | MULTILAYER BARRIER COATINGS |
JP2017128114A (ja) * | 2016-01-18 | 2017-07-27 | リケンテクノス株式会社 | ハードコート積層フィルム |
WO2017142744A1 (en) * | 2016-02-18 | 2017-08-24 | 3M Innovative Properties Company | 3-d printing surface |
US11260592B2 (en) | 2016-02-18 | 2022-03-01 | 3M Innovative Properties Company | 3-D printing surface |
US11053393B2 (en) * | 2018-08-02 | 2021-07-06 | Benq Materials Corporation | Hard coating layered optical film, polarizer comprising the same, and image display comprising the hard coating layered optical film and/or the polarizer comprising the same |
US11054550B2 (en) * | 2018-08-02 | 2021-07-06 | Benq Materials Corporation | Anti-reflective film, polarizer comprising the same, and image display comprising the anti-reflective film and/or the polarizer comprising the same |
US11447643B2 (en) * | 2018-08-02 | 2022-09-20 | Benq Materials Corporation | Hard coating layered optical film, polarizer comprising the same, and image display comprising the hard coating layered optical film and/or the polarizer comprising the same |
Also Published As
Publication number | Publication date |
---|---|
WO2014022363A3 (en) | 2014-06-12 |
CN104540900B (zh) | 2017-11-17 |
SG11201500748XA (en) | 2015-02-27 |
KR20150040310A (ko) | 2015-04-14 |
KR102159140B1 (ko) | 2020-09-23 |
TWI623595B (zh) | 2018-05-11 |
SG10201707666UA (en) | 2017-10-30 |
HK1209448A1 (en) | 2016-04-01 |
CN104540900A (zh) | 2015-04-22 |
TW201406877A (zh) | 2014-02-16 |
JP6062680B2 (ja) | 2017-01-18 |
JP2014031397A (ja) | 2014-02-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR102159140B1 (ko) | 방오성 하드 코트 및 방오성 하드 코트 전구체 | |
TWI620949B (zh) | 抗反射硬性塗層及抗反射物件 | |
JP6416964B2 (ja) | ハードコート | |
US7407710B2 (en) | Composition containing fluoroalkyl silicone and hydrosilicone | |
TWI476223B (zh) | 防污組成物、防污膜、防污積層膜、轉印薄膜及樹脂積層體以及樹脂積層體的製造方法 | |
JP5224781B2 (ja) | 硬化性組成物及び硬化皮膜を有する樹脂板 | |
JP5199237B2 (ja) | 硬化性フルオロアルキルシリコーン組成物 | |
US7410704B2 (en) | Composition containing fluoroalkyl hydrosilicone | |
JP2014238614A (ja) | ハードコートフィルム、ハードコート層用硬化性樹脂組成物およびハードコートフィルムの製造方法 | |
JP2010516499A (ja) | 太陽光制御多層フィルム | |
WO2014062652A1 (en) | Vehicle member | |
JP2014030910A (ja) | ハードコートを有するウィンドウフィルム | |
JP7010560B2 (ja) | ハードコートを有する物品 | |
KR102399829B1 (ko) | 고경도 하드코트 적층체 | |
JP4866811B2 (ja) | 反射防止フィルム | |
JP2014032229A (ja) | ハードコート層を有する光学部品、ならびに光学部品を含む光マネジメントユニット、バックライトアセンブリおよびディスプレイ | |
JP2000290535A (ja) | 活性エネルギー線硬化性被覆組成物 | |
JP4948387B2 (ja) | 反射防止フィルム | |
JP7030122B2 (ja) | 紫外線吸収ハードコート | |
JP2019505626A (ja) | 紫外線吸収ハードコート | |
JP6089709B2 (ja) | タッチパネル用前面基板 | |
KR101111415B1 (ko) | 자외선 경화형 고경도 도료 조성물 | |
WO2024122489A1 (ja) | 反射防止フィルム | |
JP2014030908A (ja) | ハードコートを有する保護具 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ENP | Entry into the national phase |
Ref document number: 20157004809 Country of ref document: KR Kind code of ref document: A |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13750423 Country of ref document: EP Kind code of ref document: A2 |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 13750423 Country of ref document: EP Kind code of ref document: A2 |