WO2014007461A1 - 터짐불량이 개선된 진공단열재 및 그의 제조방법 - Google Patents
터짐불량이 개선된 진공단열재 및 그의 제조방법 Download PDFInfo
- Publication number
- WO2014007461A1 WO2014007461A1 PCT/KR2013/004296 KR2013004296W WO2014007461A1 WO 2014007461 A1 WO2014007461 A1 WO 2014007461A1 KR 2013004296 W KR2013004296 W KR 2013004296W WO 2014007461 A1 WO2014007461 A1 WO 2014007461A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- vacuum insulation
- vacuum
- heat
- insulation material
- layer
- Prior art date
Abstract
Description
실시예1 | 실시예2 | 비교예1 | 비교예2 | 비교예3 | |
열처리 유/무 | 유 | 유 | 무 | 무 | 무 |
Hole 유/무 | 외피재열용착부 | 진공단열재 하단부 | 무 | 외피재열용착부 | 진공단열재 하단부 |
열전도율(mW/mK) | 2.54 | 2.57 | 2.55 | 터짐 | 터짐 |
실시예1실링강도 측정결과(kgf) | 비교예2실링강도 측정결과(kgf) | |
No.1 | 12.8 | 5.0 |
No.2 | 11.7 | 4.2 |
No.3 | 10.7 | 5.0 |
No.4 | 11.8 | 5.3 |
No.5 | 10.8 | 5.3 |
No.6 | 14.2 | 4.8 |
No.7 | 12.0 | 4.7 |
No.8 | 13.0 | 5.4 |
No.9 | 12.0 | 4.6 |
No.10 | 11.9 | 4.1 |
평균 | 12.1 | 4.84 |
Claims (13)
- 심재; 및상기 심재를 커버하는 외피재를 포함하는 진공단열재에 있어서,상기 외피재가 외부로부터 표면보호층, 금속 베리어층 및 열용착층의 적층 구조를 포함하고,상기 진공단열재의 실링강도가 5kgf 내지 15kgf인 진공단열재.
- 제 1항에 있어서,상기 열용착층이 선형저밀도폴리에틸렌(LLDPE) 또는 연신폴리프로필렌 (CPP)을 포함하는진공단열재.
- 제 1항에 있어서,상기 열용착층의 두께가 30㎛ 내지 80㎛ 인진공단열재.
- 제 1항에 있어서,상기 진공단열재가 하나 이상의 관통홀을 포함하는진공단열재.
- 제 4항에 있어서,상기 관통홀이 심재 또는 외피재의 열용착부에 두께방향으로 형성되는진공단열재.
- 제 4항에 있어서,상기 관통홀이 다각형, 원, 타원 및 이들을 조합한 형상을 포함하는진공단열재.
- 열용착층, 금속 베리어층, 표면보호층을 순차적으로 적층하여 외피재를 준비하는 단계;상기 외피재 사이에 심재를 삽입하는 단계;상기 외피재를 감압 및 밀봉하여 진공단열재를 형성하는 단계; 및상기 진공단열재를 열처리하는 단계를 포함하고,상기 진공단열재의 실링강도는 5kgf 내지 15kgf인 진공단열재 제조방법.
- 제 7항에 있어서,상기 외피재 사이에 심재를 삽입하는 단계 전에 상기 심재에 관통홀을 형성하는 단계를 포함하는진공단열재 제조방법.
- 제 7항에 있어서,상기 열처리는 외피재의 미용착부를 용착하는 것을 특징으로 하는 진공단열재 제조방법.
- 제 7항에 있어서,상기 열처리의 열원은 적외선 복사열, 전기열풍 또는 히터인 것을 특징으로 하는진공단열재 제조방법.
- 제 7항에 있어서,상기 열처리는 100℃ 내지 200℃의 온도에서 1분 내지 30분 동안 수행되는 것을 특징으로 하는진공단열재 제조방법.
- 제 7항에 있어서,상기 열처리는 상압 또는 그 이하의 압력상태에서 수행되는 것을 특징으로 하는진공단열재 제조방법.
- 제 7항에 있어서,상기 진공단열재 열처리 후에 20℃ 내지 90℃의 온도에서 쿨링하는 단계를 추가로 포함하는진공단열재 제조방법.