WO2013177211A1 - Endoprothèse à élution de médicament sûre dotée d'un enrobage absorbable - Google Patents
Endoprothèse à élution de médicament sûre dotée d'un enrobage absorbable Download PDFInfo
- Publication number
- WO2013177211A1 WO2013177211A1 PCT/US2013/042093 US2013042093W WO2013177211A1 WO 2013177211 A1 WO2013177211 A1 WO 2013177211A1 US 2013042093 W US2013042093 W US 2013042093W WO 2013177211 A1 WO2013177211 A1 WO 2013177211A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- stent
- months
- coating
- less
- struts
- Prior art date
Abstract
La présente invention concerne un dispositif comportant : a) une endoprothèse; b) plusieurs couches sur la structure de ladite endoprothèse pour former ledit dispositif; au moins une desdites couches comprenant un polymère bioabsorbable et au moins une desdites couches comprenant un ou plusieurs principes actifs se présentant au moins en partie sous forme cristalline.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US14/402,839 US20150134047A1 (en) | 2011-11-07 | 2013-05-21 | Safe drug eluting stent with absorbable coating |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201261649832P | 2012-05-21 | 2012-05-21 | |
US61/649,832 | 2012-05-21 | ||
US201261716437P | 2012-10-19 | 2012-10-19 | |
US61/716,437 | 2012-10-19 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2013177211A1 true WO2013177211A1 (fr) | 2013-11-28 |
Family
ID=49624300
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2013/042093 WO2013177211A1 (fr) | 2011-11-07 | 2013-05-21 | Endoprothèse à élution de médicament sûre dotée d'un enrobage absorbable |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2013177211A1 (fr) |
Cited By (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8900651B2 (en) | 2007-05-25 | 2014-12-02 | Micell Technologies, Inc. | Polymer films for medical device coating |
US9415142B2 (en) | 2006-04-26 | 2016-08-16 | Micell Technologies, Inc. | Coatings containing multiple drugs |
US9433516B2 (en) | 2007-04-17 | 2016-09-06 | Micell Technologies, Inc. | Stents having controlled elution |
US9486431B2 (en) | 2008-07-17 | 2016-11-08 | Micell Technologies, Inc. | Drug delivery medical device |
US9510856B2 (en) | 2008-07-17 | 2016-12-06 | Micell Technologies, Inc. | Drug delivery medical device |
US9539593B2 (en) | 2006-10-23 | 2017-01-10 | Micell Technologies, Inc. | Holder for electrically charging a substrate during coating |
US9687864B2 (en) | 2010-03-26 | 2017-06-27 | Battelle Memorial Institute | System and method for enhanced electrostatic deposition and surface coatings |
US9737642B2 (en) | 2007-01-08 | 2017-08-22 | Micell Technologies, Inc. | Stents having biodegradable layers |
US9789233B2 (en) | 2008-04-17 | 2017-10-17 | Micell Technologies, Inc. | Stents having bioabsorbable layers |
US9827117B2 (en) | 2005-07-15 | 2017-11-28 | Micell Technologies, Inc. | Polymer coatings containing drug powder of controlled morphology |
US9981072B2 (en) | 2009-04-01 | 2018-05-29 | Micell Technologies, Inc. | Coated stents |
US10117972B2 (en) | 2011-07-15 | 2018-11-06 | Micell Technologies, Inc. | Drug delivery medical device |
US10188772B2 (en) | 2011-10-18 | 2019-01-29 | Micell Technologies, Inc. | Drug delivery medical device |
US10232092B2 (en) | 2010-04-22 | 2019-03-19 | Micell Technologies, Inc. | Stents and other devices having extracellular matrix coating |
US10272606B2 (en) | 2013-05-15 | 2019-04-30 | Micell Technologies, Inc. | Bioabsorbable biomedical implants |
US10464100B2 (en) | 2011-05-31 | 2019-11-05 | Micell Technologies, Inc. | System and process for formation of a time-released, drug-eluting transferable coating |
WO2020028437A1 (fr) * | 2018-08-01 | 2020-02-06 | Boston Scientific Scimed, Inc. | Compositions de revêtement à libération de médicament |
US10835396B2 (en) | 2005-07-15 | 2020-11-17 | Micell Technologies, Inc. | Stent with polymer coating containing amorphous rapamycin |
US11039943B2 (en) | 2013-03-12 | 2021-06-22 | Micell Technologies, Inc. | Bioabsorbable biomedical implants |
US11369498B2 (en) | 2010-02-02 | 2022-06-28 | MT Acquisition Holdings LLC | Stent and stent delivery system with improved deliverability |
US11426494B2 (en) | 2007-01-08 | 2022-08-30 | MT Acquisition Holdings LLC | Stents having biodegradable layers |
US11904118B2 (en) | 2010-07-16 | 2024-02-20 | Micell Medtech Inc. | Drug delivery medical device |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1995006487A2 (fr) * | 1993-08-30 | 1995-03-09 | Med Institute, Inc. | Dispositif medical intravasculaire |
US20100055145A1 (en) * | 2008-08-29 | 2010-03-04 | Biosensors International Group | Stent coatings for reducing late stent thrombosis |
US20100198330A1 (en) * | 2009-02-02 | 2010-08-05 | Hossainy Syed F A | Bioabsorbable Stent And Treatment That Elicits Time-Varying Host-Material Response |
US20100198331A1 (en) * | 2009-02-02 | 2010-08-05 | Richard Rapoza | Bioabsorbable Stent That Modulates Plaque Geometric Morphology And Chemical Composition |
US20110160751A1 (en) * | 2006-06-06 | 2011-06-30 | Luiz Gonzaga Granja Filho | Extraluminal stent type prosthesis for anastomosis |
US20110301697A1 (en) * | 2009-04-10 | 2011-12-08 | Hemoteq Ag | Manufacture, method and use of drug-eluting medical devices for permanently keeping blood vessels open |
US20120101566A1 (en) * | 2009-06-22 | 2012-04-26 | Biotronik Vi Patent Ag | Stent having improved stent design |
-
2013
- 2013-05-21 WO PCT/US2013/042093 patent/WO2013177211A1/fr active Application Filing
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1995006487A2 (fr) * | 1993-08-30 | 1995-03-09 | Med Institute, Inc. | Dispositif medical intravasculaire |
US20110160751A1 (en) * | 2006-06-06 | 2011-06-30 | Luiz Gonzaga Granja Filho | Extraluminal stent type prosthesis for anastomosis |
US20100055145A1 (en) * | 2008-08-29 | 2010-03-04 | Biosensors International Group | Stent coatings for reducing late stent thrombosis |
US20100198330A1 (en) * | 2009-02-02 | 2010-08-05 | Hossainy Syed F A | Bioabsorbable Stent And Treatment That Elicits Time-Varying Host-Material Response |
US20100198331A1 (en) * | 2009-02-02 | 2010-08-05 | Richard Rapoza | Bioabsorbable Stent That Modulates Plaque Geometric Morphology And Chemical Composition |
US20110301697A1 (en) * | 2009-04-10 | 2011-12-08 | Hemoteq Ag | Manufacture, method and use of drug-eluting medical devices for permanently keeping blood vessels open |
US20120101566A1 (en) * | 2009-06-22 | 2012-04-26 | Biotronik Vi Patent Ag | Stent having improved stent design |
Non-Patent Citations (1)
Title |
---|
MATSUMOTO, D ET AL.: "Neointimal Coverage of Sirolimus-Eluting Stents at 6-month Follow-up: Evaluated by Optical Coherence Tomography", EUROPEAN HEART JOURNAL., 29 November 2006 (2006-11-29), pages 962 * |
Cited By (35)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9827117B2 (en) | 2005-07-15 | 2017-11-28 | Micell Technologies, Inc. | Polymer coatings containing drug powder of controlled morphology |
US10835396B2 (en) | 2005-07-15 | 2020-11-17 | Micell Technologies, Inc. | Stent with polymer coating containing amorphous rapamycin |
US10898353B2 (en) | 2005-07-15 | 2021-01-26 | Micell Technologies, Inc. | Polymer coatings containing drug powder of controlled morphology |
US11911301B2 (en) | 2005-07-15 | 2024-02-27 | Micell Medtech Inc. | Polymer coatings containing drug powder of controlled morphology |
US9415142B2 (en) | 2006-04-26 | 2016-08-16 | Micell Technologies, Inc. | Coatings containing multiple drugs |
US11007307B2 (en) | 2006-04-26 | 2021-05-18 | Micell Technologies, Inc. | Coatings containing multiple drugs |
US9737645B2 (en) | 2006-04-26 | 2017-08-22 | Micell Technologies, Inc. | Coatings containing multiple drugs |
US11850333B2 (en) | 2006-04-26 | 2023-12-26 | Micell Medtech Inc. | Coatings containing multiple drugs |
US9539593B2 (en) | 2006-10-23 | 2017-01-10 | Micell Technologies, Inc. | Holder for electrically charging a substrate during coating |
US11426494B2 (en) | 2007-01-08 | 2022-08-30 | MT Acquisition Holdings LLC | Stents having biodegradable layers |
US9737642B2 (en) | 2007-01-08 | 2017-08-22 | Micell Technologies, Inc. | Stents having biodegradable layers |
US10617795B2 (en) | 2007-01-08 | 2020-04-14 | Micell Technologies, Inc. | Stents having biodegradable layers |
US9775729B2 (en) | 2007-04-17 | 2017-10-03 | Micell Technologies, Inc. | Stents having controlled elution |
US9486338B2 (en) | 2007-04-17 | 2016-11-08 | Micell Technologies, Inc. | Stents having controlled elution |
US9433516B2 (en) | 2007-04-17 | 2016-09-06 | Micell Technologies, Inc. | Stents having controlled elution |
US8900651B2 (en) | 2007-05-25 | 2014-12-02 | Micell Technologies, Inc. | Polymer films for medical device coating |
US9789233B2 (en) | 2008-04-17 | 2017-10-17 | Micell Technologies, Inc. | Stents having bioabsorbable layers |
US10350333B2 (en) | 2008-04-17 | 2019-07-16 | Micell Technologies, Inc. | Stents having bioabsorable layers |
US9981071B2 (en) | 2008-07-17 | 2018-05-29 | Micell Technologies, Inc. | Drug delivery medical device |
US9510856B2 (en) | 2008-07-17 | 2016-12-06 | Micell Technologies, Inc. | Drug delivery medical device |
US9486431B2 (en) | 2008-07-17 | 2016-11-08 | Micell Technologies, Inc. | Drug delivery medical device |
US10350391B2 (en) | 2008-07-17 | 2019-07-16 | Micell Technologies, Inc. | Drug delivery medical device |
US10653820B2 (en) | 2009-04-01 | 2020-05-19 | Micell Technologies, Inc. | Coated stents |
US9981072B2 (en) | 2009-04-01 | 2018-05-29 | Micell Technologies, Inc. | Coated stents |
US11369498B2 (en) | 2010-02-02 | 2022-06-28 | MT Acquisition Holdings LLC | Stent and stent delivery system with improved deliverability |
US9687864B2 (en) | 2010-03-26 | 2017-06-27 | Battelle Memorial Institute | System and method for enhanced electrostatic deposition and surface coatings |
US10232092B2 (en) | 2010-04-22 | 2019-03-19 | Micell Technologies, Inc. | Stents and other devices having extracellular matrix coating |
US11904118B2 (en) | 2010-07-16 | 2024-02-20 | Micell Medtech Inc. | Drug delivery medical device |
US10464100B2 (en) | 2011-05-31 | 2019-11-05 | Micell Technologies, Inc. | System and process for formation of a time-released, drug-eluting transferable coating |
US10729819B2 (en) | 2011-07-15 | 2020-08-04 | Micell Technologies, Inc. | Drug delivery medical device |
US10117972B2 (en) | 2011-07-15 | 2018-11-06 | Micell Technologies, Inc. | Drug delivery medical device |
US10188772B2 (en) | 2011-10-18 | 2019-01-29 | Micell Technologies, Inc. | Drug delivery medical device |
US11039943B2 (en) | 2013-03-12 | 2021-06-22 | Micell Technologies, Inc. | Bioabsorbable biomedical implants |
US10272606B2 (en) | 2013-05-15 | 2019-04-30 | Micell Technologies, Inc. | Bioabsorbable biomedical implants |
WO2020028437A1 (fr) * | 2018-08-01 | 2020-02-06 | Boston Scientific Scimed, Inc. | Compositions de revêtement à libération de médicament |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20230181802A1 (en) | Stents Having Biodegradable Layers | |
US20160271303A1 (en) | Stents having controlled elution | |
US10653820B2 (en) | Coated stents | |
WO2013177211A1 (fr) | Endoprothèse à élution de médicament sûre dotée d'un enrobage absorbable | |
US9775729B2 (en) | Stents having controlled elution | |
EP2696815B1 (fr) | Endoprothèses présentant une élution régulée | |
US20180000996A1 (en) | Stents having biodegradable layers | |
CA2794704C (fr) | Endoprotheses vasculaires ayant une elution controlee | |
AU2017200794B2 (en) | Stents having biodegradable layers | |
US20150134047A1 (en) | Safe drug eluting stent with absorbable coating | |
AU2012203577B2 (en) | Stents having biodegradable layers | |
US11426494B2 (en) | Stents having biodegradable layers |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13794507 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 14402839 Country of ref document: US |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 13794507 Country of ref document: EP Kind code of ref document: A1 |