WO2013161970A1 - Polyamic acid solution composition and polyimide - Google Patents
Polyamic acid solution composition and polyimide Download PDFInfo
- Publication number
- WO2013161970A1 WO2013161970A1 PCT/JP2013/062301 JP2013062301W WO2013161970A1 WO 2013161970 A1 WO2013161970 A1 WO 2013161970A1 JP 2013062301 W JP2013062301 W JP 2013062301W WO 2013161970 A1 WO2013161970 A1 WO 2013161970A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyamic acid
- acid solution
- solution composition
- polyimide
- silica
- Prior art date
Abstract
Description
1. フッ素原子を含有するテトラカルボン酸二無水物を50モル%以上の量で含むテトラカルボン酸成分と、フッ素原子を含有するジアミンを50モル%以上の量で含むジアミン成分とを溶媒中で反応させて得られるポリアミック酸溶液に、シリカの量がテトラカルボン酸成分とジアミン成分の合計量100質量部に対して1~100質量部の量になるように、有機溶媒にコロイダルシリカを分散させてなるコロイド溶液を添加してなるポリアミック酸溶液組成物。
2. 添加されるシリカの量が、テトラカルボン酸成分とジアミン成分の合計量100質量部に対して、5~70質量部の量であることを特徴とする前記項1に記載のポリアミック酸溶液組成物。
3. 前記シリカの粒子径が、1~60nmであることを特徴とする前記項1~2のいずれかに記載のポリアミック酸溶液組成物。 The present invention relates to the following matters.
1. A tetracarboxylic acid component containing a fluorine atom-containing tetracarboxylic dianhydride in an amount of 50 mol% or more and a diamine component containing a fluorine atom-containing diamine in an amount of 50 mol% or more are reacted in a solvent. Colloidal silica is dispersed in an organic solvent so that the amount of silica is 1 to 100 parts by mass with respect to 100 parts by mass of the total amount of the tetracarboxylic acid component and the diamine component. A polyamic acid solution composition obtained by adding a colloidal solution.
2. Item 2. The polyamic acid solution composition according to Item 1, wherein the amount of silica added is 5 to 70 parts by mass with respect to 100 parts by mass of the total amount of the tetracarboxylic acid component and the diamine component. .
3. Item 3. The polyamic acid solution composition according to any one of Items 1 to 2, wherein the silica has a particle size of 1 to 60 nm.
5. ポリアミック酸溶液組成物を加熱処理して得られるポリイミドが、300~400℃の線膨張係数が250ppm/℃以下であることを特徴とする前記項4に記載のポリアミック酸溶液組成物。 4). The polyimide obtained by heat-treating the polyamic acid solution composition has a light transmittance at a wavelength of 400 nm of a film having a thickness of 10 μm of 70% or more, and a linear expansion coefficient of 300 to 400 ° C. is 350 ppm / ° C. or less. Item 4. The polyamic acid solution composition according to any one of Items 1 to 3, wherein
5. Item 5. The polyamic acid solution composition according to item 4, wherein the polyimide obtained by heat-treating the polyamic acid solution composition has a linear expansion coefficient at 300 to 400 ° C of 250 ppm / ° C or less.
前記フッ素原子を含有するジアミンが、2,2’-ビス(トリフルオロメチル)-4,4’-ジアミノビフェニル、及び/又は2,2’-ビス(3-アミノ-4-ヒドロキシフェニル)ヘキサフルオロプロパンであることを特徴とする前記項1~5のいずれかに記載のポリアミック酸溶液組成物。 6). The tetracarboxylic dianhydride containing a fluorine atom is 2,2-bis (3,4-dicarboxyphenyl) hexafluoropropane dianhydride,
The diamine containing a fluorine atom is 2,2′-bis (trifluoromethyl) -4,4′-diaminobiphenyl and / or 2,2′-bis (3-amino-4-hydroxyphenyl) hexafluoro. Item 6. The polyamic acid solution composition according to any one of Items 1 to 5, which is propane.
フッ素原子を含有するテトラカルボン酸二無水物を50モル%以上の量で含むテトラカルボン酸成分と、フッ素原子を含有するジアミンを50モル%以上の量で含むジアミン成分とを溶媒中で反応させてポリアミック酸溶液を製造する工程と、
得られたポリアミック酸溶液に、シリカの量がテトラカルボン酸成分とジアミン成分の合計量100質量部に対して1~100質量部の量になるように、有機溶媒にコロイダルシリカを分散させてなるコロイド溶液を添加し、混合する工程と
を有するポリアミック酸溶液組成物の製造方法。 7). A method for producing the polyamic acid solution composition according to any one of Items 1 to 6,
A tetracarboxylic acid component containing a fluorine atom-containing tetracarboxylic dianhydride in an amount of 50 mol% or more and a diamine component containing a fluorine atom-containing diamine in an amount of 50 mol% or more are reacted in a solvent. Producing a polyamic acid solution,
In the obtained polyamic acid solution, colloidal silica is dispersed in an organic solvent so that the amount of silica is 1 to 100 parts by mass with respect to 100 parts by mass of the total amount of the tetracarboxylic acid component and the diamine component. A method for producing a polyamic acid solution composition comprising the steps of adding and mixing a colloidal solution.
9. 前記項8に記載のポリイミドを含む電気装置、電子装置、光学装置、表示装置、タッチパネル、太陽電池、又はLED照明装置。 8). A polyimide obtained by heat-treating the polyamic acid solution composition according to any one of Items 1 to 6.
9. An electric device, an electronic device, an optical device, a display device, a touch panel, a solar cell, or an LED lighting device including the polyimide according to Item 8.
前記項1~6のいずれかに記載のポリアミック酸溶液組成物をキャリア基板上に塗布し、加熱処理して固体状のポリイミド樹脂膜を形成する工程、前記ポリイミド樹脂膜上に回路を形成する工程、及び、前記回路が表面に形成されたポリイミド樹脂膜を前記キャリア基板から剥離する工程を含むことを特徴とするフレキシブルデバイスの製造方法。
11. 前記項10に記載のフレキシブルデバイスの製造方法により製造された表示デバイス又は受光デバイスであるフレキシブルデバイス。 10. A method of manufacturing a flexible device which is a display device or a light receiving device,
The step of applying the polyamic acid solution composition according to any one of Items 1 to 6 on a carrier substrate and heat-treating it to form a solid polyimide resin film, and the step of forming a circuit on the polyimide resin film And the manufacturing method of the flexible device characterized by including the process of peeling the polyimide resin film in which the said circuit was formed in the surface from the said carrier substrate.
11. A flexible device which is a display device or a light receiving device manufactured by the method for manufacturing a flexible device according to Item 10.
6FDA:2,2-ビス(3,4-ジカルボキシフェニル)ヘキサフルオロプロパン二無水物
2,2’-TFMB:2,2’-ビス(トリフルオロメチル)-4,4’-ジアミノビフェニル
6FAP:2,2’-ビス(3-アミノ-4-ヒドロキシフェニル)ヘキサフルオロプロパン Abbreviations of the compounds used in the following examples are as follows.
6FDA: 2,2-bis (3,4-dicarboxyphenyl) hexafluoropropane dianhydride 2,2′-TFMB: 2,2′-bis (trifluoromethyl) -4,4′-diaminobiphenyl 6FAP: 2,2'-bis (3-amino-4-hydroxyphenyl) hexafluoropropane
ポリアミック酸溶液の固形分濃度は、ポリアミック酸溶液を350℃で30分間乾燥し、乾燥前の重量W1と乾燥後の重量W2とから次式によって求めた値である。 (Solid content concentration)
The solid content concentration of the polyamic acid solution is a value obtained by drying the polyamic acid solution at 350 ° C. for 30 minutes and obtaining the weight W 1 before drying and the weight W 2 after drying by the following formula.
試料溶液を、固形分濃度に基づいて濃度が0.5g/dl(溶媒:N-メチル-2-ピロリドン)になるように希釈した。この希釈液を、30℃にて、キャノンフェンスケNo.100を用いて流下時間(T1)を測定した。対数粘度は、ブランクの水の流下時間(T0)を用いて、次式から算出した。 (Logarithmic viscosity)
The sample solution was diluted to a concentration of 0.5 g / dl (solvent: N-methyl-2-pyrrolidone) based on the solid content concentration. This diluted solution was added to Cannon Fenceke No. The flow-down time (T 1 ) was measured using 100. The logarithmic viscosity was calculated from the following equation using the flow time (T 0 ) of blank water.
膜厚10μmのポリイミド膜を幅4mmの短冊状に切り取って試験片とし、TMA/SS6100(エスアイアイ・テクノロジー社製)を用い、チャック間長15mm、荷重2g、昇温速度20℃/minで400℃まで昇温した。得られたTMA曲線から、50℃から200℃、300℃から400℃までの線膨張係数を求めた。 (Linear expansion coefficient (CTE))
A polyimide film having a thickness of 10 μm is cut into a strip shape having a width of 4 mm to obtain a test piece, and a TMA / SS6100 (manufactured by SII Technology Co., Ltd.) is used. The temperature was raised to ° C. From the obtained TMA curve, linear expansion coefficients from 50 ° C. to 200 ° C. and from 300 ° C. to 400 ° C. were obtained.
分光光度計U-2910(日立ハイテク製)を用いて、ポリイミド膜の波長400nmにおける透過率を測定した。そして、ランバード・ベール(Lambert-Beer Law)を用いて膜厚10μmにおける透過率を算出した。 (Light transmittance)
Using a spectrophotometer U-2910 (manufactured by Hitachi High-Tech), the transmittance of the polyimide film at a wavelength of 400 nm was measured. Then, the transmittance at a film thickness of 10 μm was calculated using a Lambert-Beer Law.
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてN-メチル-2-ピロリドン440gを加え、2,2’-TFMBを25.12g(0.0785モル)と、6FDAを34.88g(0.0785モル)を加え、50℃で撹拌して、固形分濃度11.43%、対数粘度0.60のポリアミック酸溶液を得た。 [Reference Example 1]
440 g of N-methyl-2-pyrrolidone was added as a solvent to a glass reaction vessel having an internal volume of 500 ml equipped with a stirrer and a nitrogen gas introduction / discharge tube, and 25.12 g (0.0785 mol) of 2,2′-TFMB was added as a solvent. ) And 34.88 g (0.0785 mol) of 6FDA were added and stirred at 50 ° C. to obtain a polyamic acid solution having a solid content concentration of 11.43% and a logarithmic viscosity of 0.60.
参考例1で得られたポリアミック酸溶液を、基材のガラス板上にバーコーターによって塗布し、その塗膜を、120℃にて60分間、150℃にて30分間、200℃にて30分間、400℃にて1分間加熱処理し、ガラス板上に厚さが10μmのポリイミド膜を形成した。そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表1に示す。 [Comparative Example 1]
The polyamic acid solution obtained in Reference Example 1 was applied onto a glass plate as a substrate by a bar coater, and the coating film was applied at 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, and 200 ° C. for 30 minutes. Then, heat treatment was performed at 400 ° C. for 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate. And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 1.
参考例1で得られたポリアミック酸溶液に、N,N-ジメチルアセトアミドにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、DMAc-ST;シリカ粒子固形分濃度:20wt%;シリカの粒子径:10~20nm)を6g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して2質量部である。 [Example 1]
Colloidal solution prepared by dispersing colloidal silica in N, N-dimethylacetamide in the polyamic acid solution obtained in Reference Example 1 (manufactured by Nissan Chemical Industries, Ltd., DMAc-ST; silica particle solid content concentration: 20 wt%; silica 6 g) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 2 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表1に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 1.
参考例1で得られたポリアミック酸溶液に、N,N-ジメチルアセトアミドにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、DMAc-ST)を15g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して5質量部である。 [Example 2]
To the polyamic acid solution obtained in Reference Example 1, 15 g of a colloidal solution in which colloidal silica is dispersed in N, N-dimethylacetamide (manufactured by Nissan Chemical Industries, Ltd., DMAc-ST) is added and stirred, and the polyamic acid is stirred. A solution composition was obtained. The addition amount of silica is 5 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表1に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 1.
参考例1で得られたポリアミック酸溶液に、N,N-ジメチルアセトアミドにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、DMAc-ST)を60g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して20質量部である。 Example 3
To the polyamic acid solution obtained in Reference Example 1, 60 g of a colloidal solution in which colloidal silica is dispersed in N, N-dimethylacetamide (manufactured by Nissan Chemical Industries, Ltd., DMAc-ST) is added and stirred, and the polyamic acid is stirred. A solution composition was obtained. The addition amount of silica is 20 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表1に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 1.
参考例1で得られたポリアミック酸溶液に、N,N-ジメチルアセトアミドにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、DMAc-ST)を120g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して40質量部である。 Example 4
To the polyamic acid solution obtained in Reference Example 1, 120 g of a colloidal solution in which colloidal silica is dispersed in N, N-dimethylacetamide (manufactured by Nissan Chemical Industries, Ltd., DMAc-ST) is added and stirred, and the polyamic acid is stirred. A solution composition was obtained. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表1に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 1.
参考例1で得られたポリアミック酸溶液に、プロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカの粒子径:10~20nm)を40g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して20質量部である。 Example 5
Colloidal solution in which colloidal silica is dispersed in propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 1 (manufactured by Nissan Chemical Industries, Ltd., PMA-ST; silica particle solid content concentration: 30 wt%; silica 40 g (particle diameter: 10 to 20 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 20 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
参考例1で得られたポリアミック酸溶液に、プロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST)を80g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して40質量部である。 Example 6
To the polyamic acid solution obtained in Reference Example 1, 80 g of a colloidal solution (PMA-ST, manufactured by Nissan Chemical Industries, Ltd.) in which colloidal silica is dispersed in propylene glycol monomethyl ether acetate is added and stirred, and the polyamic acid solution is stirred. A composition was obtained. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
参考例1で得られたポリアミック酸溶液に、プロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST)を120g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して60質量部である。 Example 7
To the polyamic acid solution obtained in Reference Example 1, 120 g of a colloidal solution (PMA-ST, manufactured by Nissan Chemical Industries, Ltd.) in which colloidal silica is dispersed in propylene glycol monomethyl ether acetate was added and stirred, and the polyamic acid solution was stirred. A composition was obtained. The addition amount of silica is 60 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
参考例1で得られたポリアミック酸溶液に、エチレングリコールモノ-n-プロピルエーテルにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、NPC-ST-30;シリカ粒子固形分濃度:30wt%;シリカの粒子径:10~20nm)を80g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して40質量部である。 Example 8
Colloidal solution obtained by dispersing colloidal silica in ethylene glycol mono-n-propyl ether in the polyamic acid solution obtained in Reference Example 1 (NPC-ST-30, manufactured by Nissan Chemical Industries, Ltd .; solid content concentration of silica particles: 30 wt%; silica particle size: 10 to 20 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
参考例1で得られたポリアミック酸溶液に、エチレングリコールモノ-n-プロピルエーテルにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、NPC-ST-30)を120g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して60質量部である。 Example 9
To the polyamic acid solution obtained in Reference Example 1, 120 g of a colloidal solution (NPC-ST-30, manufactured by Nissan Chemical Industries, Ltd.) in which colloidal silica is dispersed in ethylene glycol mono-n-propyl ether is added and stirred. Thus, a polyamic acid solution composition was obtained. The addition amount of silica is 60 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
参考例1で得られたポリアミック酸溶液に、エチレングリコールにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、EG-ST;シリカ粒子固形分濃度:20wt%;シリカの粒子径:10~20nm)を120g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して40質量部である。 Example 10
Colloidal solution in which colloidal silica is dispersed in ethylene glycol in the polyamic acid solution obtained in Reference Example 1 (manufactured by Nissan Chemical Industries, Ltd., EG-ST; silica particle solid content concentration: 20 wt%; silica particle diameter: 10 to 20 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
参考例1で得られたポリアミック酸溶液に、エチレングリコールにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、EG-ST)を180g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して60質量部である。 Example 11
To the polyamic acid solution obtained in Reference Example 1, 180 g of a colloidal solution in which colloidal silica is dispersed in ethylene glycol (EG-ST, manufactured by Nissan Chemical Industries, Ltd.) was added and stirred to obtain a polyamic acid solution composition. Obtained. The addition amount of silica is 60 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
参考例1で得られたポリアミック酸溶液に、イソプロパノールにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、IPA-ST;シリカ粒子固形分濃度:30wt%;シリカの粒子径:10~20nm)を80g添加して攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+2,2’-TFMB)100質量部に対して40質量部である。 Example 12
Colloidal solution obtained by dispersing colloidal silica in isopropanol in the polyamic acid solution obtained in Reference Example 1 (IPA-ST, manufactured by Nissan Chemical Industries, Ltd .; silica particle solid content concentration: 30 wt%; silica particle size: 10 80 g) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 2,2′-TFMB).
そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表2に示す。 This polyamic acid solution composition was applied to a glass plate of a substrate by a bar coater, and the coating film was heated to 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. For 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate.
And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 2.
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてN-メチル-2-ピロリドン440gを加え、6FAPを27.11g(0.0740モル)と、6FDAを32.89g(0.0740モル)を加え、50℃で攪拌して、固形分濃度11.47%、対数粘度0.19のポリアミック酸溶液を得た。 [Reference Example 2]
440 g of N-methyl-2-pyrrolidone was added as a solvent to a glass reaction vessel having an internal volume of 500 ml equipped with a stirrer and a nitrogen gas inlet / outlet pipe, and 27.11 g (0.0740 mol) of 6FAP and 6FDA 32.89 g (0.0740 mol) was added and stirred at 50 ° C. to obtain a polyamic acid solution having a solid content of 11.47% and a logarithmic viscosity of 0.19.
参考例2で得られたポリアミック酸溶液を、基材のガラス板上にバーコーターによって塗布し、その塗膜を、120℃にて60分間、150℃にて30分間、200℃にて30分間、400℃にて1分間加熱処理し、ガラス板上の厚さが10μmのポリイミド膜を形成した。そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表3に示す。 [Comparative Example 2]
The polyamic acid solution obtained in Reference Example 2 was applied onto a base glass plate by a bar coater, and the coating film was applied at 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, and 200 ° C. for 30 minutes. Then, heat treatment was performed at 400 ° C. for 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate. And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 3.
参考例2で得られたポリアミック酸溶液に、プロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を80g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 13
Colloidal solution prepared by dispersing colloidal silica in propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., PMA-ST; solid content concentration of silica particles: 30 wt%; silica particles) 80 g of 10 to 15 nm in diameter were added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、プロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を160g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して80質量部である。 Example 14
Colloidal solution prepared by dispersing colloidal silica in propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., PMA-ST; solid content concentration of silica particles: 30 wt%; silica particles) 160 g (diameter 10-15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 80 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、メチルエチルケトンにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、MEK-ST-40;シリカ粒子固形分濃度:40wt%;シリカ粒子径10~15nm;表面改質無し)を80g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 15
Colloidal solution prepared by dispersing colloidal silica in methyl ethyl ketone in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., MEK-ST-40; solid content concentration of silica particles: 40 wt%; silica particle diameter 10 80 g of ˜15 nm (no surface modification) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、メチルエチルケトンにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、MEK-AC-2101;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm;表面改質有り)を80g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 16
Colloidal solution prepared by dispersing colloidal silica in methyl ethyl ketone in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., MEK-AC-2101; solid content concentration of silica particles: 30 wt%; silica particle diameter of 10 80 g of ˜15 nm (with surface modification) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、エチレングリコールモノ-n-プロピルエーテルにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、NPC-ST-30;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を80g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 17
Colloidal solution obtained by dispersing colloidal silica in ethylene glycol mono-n-propyl ether in the polyamic acid solution obtained in Reference Example 2 (NPC-ST-30, manufactured by Nissan Chemical Industries, Ltd .; solid content concentration of silica particles: 30 wt%; silica particle diameter 10-15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、イソプロパノールにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、IPA-ST-30;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を80g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 18
Colloidal solution in which colloidal silica is dispersed in isopropanol in the polyamic acid solution obtained in Reference Example 2 (Nissan Chemical Industry Co., Ltd., IPA-ST-30; silica particle solid content concentration: 30 wt%; silica particle diameter 10 ˜15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、イソプロパノールにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、IPA-ST-S;シリカ粒子固形分濃度:25wt%;シリカ粒子径8~10nm)を96g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 19
Colloidal solution in which colloidal silica is dispersed in isopropanol in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., IPA-ST-S; silica particle solid content concentration: 25 wt%; silica particle diameter 8 96 g) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、イソプロパノールにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、IPA-ST-S;シリカ粒子固形分濃度:15wt%;シリカ粒子径9~15nm)を160g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 20
Colloidal solution in which colloidal silica is dispersed in isopropanol in the polyamic acid solution obtained in Reference Example 2 (IPA-ST-S, manufactured by Nissan Chemical Industries, Ltd .; silica particle solid content concentration: 15 wt%; silica particle diameter 9 (About 15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例2で得られたポリアミック酸溶液に、エチレングリコールにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、EG-ST;シリカ粒子固形分濃度:20wt%;シリカ粒子径10~15nm)を120g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP)100質量部に対して40質量部である。 Example 21
Colloidal solution in which colloidal silica is dispersed in ethylene glycol in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., EG-ST; silica particle solid content concentration: 20 wt%; silica particle diameter of 10 to 15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP).
参考例1で得られたポリアミック酸溶液に、参考例2で得られたポリアミック酸溶液を214g加えて攪拌し、ポリアミック酸溶液組成物を得た。このポリアミック酸溶液組成物を基材のガラス板上にバーコーターによって塗布し、その塗膜を、120℃にて60分間、150℃にて30分間、200℃にて30分間、400℃にて1分間加熱処理し、ガラス板上の厚さが10μmのポリイミド膜を形成した。そして、ガラス板からポリイミド膜を剥離し、このポリイミド膜の線膨張係数および光透過率を測定した。その結果を表5に示す。 [Comparative Example 3]
To the polyamic acid solution obtained in Reference Example 1, 214 g of the polyamic acid solution obtained in Reference Example 2 was added and stirred to obtain a polyamic acid solution composition. This polyamic acid solution composition was applied onto a glass plate as a substrate by a bar coater, and the coating film was applied at 120 ° C. for 60 minutes, 150 ° C. for 30 minutes, 200 ° C. for 30 minutes, and 400 ° C. A heat treatment was performed for 1 minute to form a polyimide film having a thickness of 10 μm on the glass plate. And the polyimide film was peeled from the glass plate, and the linear expansion coefficient and light transmittance of this polyimide film were measured. The results are shown in Table 5.
参考例1で得られたポリアミック酸溶液に、参考例2で得られたポリアミック酸溶液を214gおよびプロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を114g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP+2,2’-TFMB)100質量部に対して40質量部である。 [Example 22]
Colloidal solution obtained by dispersing colloidal silica in 214 g of the polyamic acid solution obtained in Reference Example 2 and propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 1 (manufactured by Nissan Chemical Industries, Ltd., PMA- ST: Silica particle solid content concentration: 30 wt%; silica particle diameter 10-15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP + 2,2′-TFMB).
参考例1で得られたポリアミック酸溶液に、参考例2で得られたポリアミック酸溶液を214gおよびプロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を228g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP+2,2’-TFMB)100質量部に対して80質量部である。 Example 23
Colloidal solution obtained by dispersing colloidal silica in 214 g of the polyamic acid solution obtained in Reference Example 2 and propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 1 (manufactured by Nissan Chemical Industries, Ltd., PMA- ST: Silica particle solid content concentration: 30 wt%; silica particle diameter of 10 to 15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 80 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP + 2,2′-TFMB).
参考例1で得られたポリアミック酸溶液に、参考例2で得られたポリアミック酸溶液を500gおよびプロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を160g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP+2,2’-TFMB)100質量部に対して40質量部である。 Example 24
A colloidal solution obtained by dispersing colloidal silica in 500 g of the polyamic acid solution obtained in Reference Example 2 and propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 1 (manufactured by Nissan Chemical Industries, Ltd., PMA- ST: Silica particle solid content concentration: 30 wt%; silica particle diameter of 10 to 15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP + 2,2′-TFMB).
参考例1で得られたポリアミック酸溶液に、参考例2で得られたポリアミック酸溶液を500gおよびプロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を320g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP+2,2’-TFMB)100質量部に対して80質量部である。 Example 25
A colloidal solution obtained by dispersing colloidal silica in 500 g of the polyamic acid solution obtained in Reference Example 2 and propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 1 (manufactured by Nissan Chemical Industries, Ltd., PMA- ST: Silica particle solid content concentration: 30 wt%; silica particle diameter of 10 to 15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 80 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP + 2,2′-TFMB).
参考例2で得られたポリアミック酸溶液に、参考例1で得られたポリアミック酸溶液を214gおよびプロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を114g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP+2,2’-TFMB)100質量部に対して40質量部である。 Example 26
Colloidal solution obtained by dispersing colloidal silica in 214 g of the polyamic acid solution obtained in Reference Example 1 and propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., PMA- ST: Silica particle solid content concentration: 30 wt%; silica particle diameter 10-15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP + 2,2′-TFMB).
参考例2で得られたポリアミック酸溶液に、参考例1で得られたポリアミック酸溶液を56gおよびプロピレングリコールモノメチルエーテルアセテートにコロイダルシリカを分散させてなるコロイド溶液(日産化学工業株式会社製、PMA-ST;シリカ粒子固形分濃度:30wt%;シリカ粒子径10~15nm)を89g加えて攪拌し、ポリアミック酸溶液組成物を得た。シリカの添加量はモノマー成分(6FDA+6FAP+2,2’-TFMB)100質量部に対して40質量部である。 Example 27
Colloidal solution prepared by dispersing colloidal silica in 56 g of the polyamic acid solution obtained in Reference Example 1 and propylene glycol monomethyl ether acetate in the polyamic acid solution obtained in Reference Example 2 (manufactured by Nissan Chemical Industries, Ltd., PMA- ST: Silica particle solid concentration: 30 wt%; silica particle diameter of 10 to 15 nm) was added and stirred to obtain a polyamic acid solution composition. The addition amount of silica is 40 parts by mass with respect to 100 parts by mass of the monomer component (6FDA + 6FAP + 2,2′-TFMB).
The polyimide obtained by heat-treating the polyamic acid solution composition of the present invention has high transparency and has a relatively low linear expansion coefficient, particularly a linear expansion coefficient at high temperatures, so that it can be used in electrical, electronic and optical devices. For example, it can be suitably used as a display device such as a liquid crystal display, EL display, or electronic paper, a touch panel, a solar cell, a substrate of an LED lighting device, or a protective film. In particular, it can be suitably used as a substrate for flexible devices such as display devices such as liquid crystal displays, organic EL displays and electronic paper, and light receiving devices such as light receiving elements of thin film solar cells.
Claims (11)
- フッ素原子を含有するテトラカルボン酸二無水物を50モル%以上の量で含むテトラカルボン酸成分と、フッ素原子を含有するジアミンを50モル%以上の量で含むジアミン成分とを溶媒中で反応させて得られるポリアミック酸溶液に、シリカの量がテトラカルボン酸成分とジアミン成分の合計量100質量部に対して1~100質量部の量になるように、有機溶媒にコロイダルシリカを分散させてなるコロイド溶液を添加してなるポリアミック酸溶液組成物。 A tetracarboxylic acid component containing a fluorine atom-containing tetracarboxylic dianhydride in an amount of 50 mol% or more and a diamine component containing a fluorine atom-containing diamine in an amount of 50 mol% or more are reacted in a solvent. Colloidal silica is dispersed in an organic solvent so that the amount of silica is 1 to 100 parts by mass with respect to 100 parts by mass of the total amount of the tetracarboxylic acid component and the diamine component. A polyamic acid solution composition obtained by adding a colloidal solution.
- 添加されるシリカの量が、テトラカルボン酸成分とジアミン成分の合計量100質量部に対して、5~70質量部の量であることを特徴とする請求項1に記載のポリアミック酸溶液組成物。 2. The polyamic acid solution composition according to claim 1, wherein the amount of silica added is 5 to 70 parts by mass with respect to 100 parts by mass of the total amount of the tetracarboxylic acid component and the diamine component. .
- 前記シリカの粒子径が、1~60nmであることを特徴とする請求項1~2のいずれかに記載のポリアミック酸溶液組成物。 3. The polyamic acid solution composition according to claim 1, wherein the silica has a particle diameter of 1 to 60 nm.
- ポリアミック酸溶液組成物を加熱処理して得られるポリイミドが、膜厚10μmのフィルムでの波長400nmの光透過率が70%以上であり、且つ、300~400℃の線膨張係数が350ppm/℃以下であることを特徴とする請求項1~3のいずれかに記載のポリアミック酸溶液組成物。 The polyimide obtained by heat-treating the polyamic acid solution composition has a light transmittance at a wavelength of 400 nm of a film having a thickness of 10 μm of 70% or more, and a linear expansion coefficient of 300 to 400 ° C. is 350 ppm / ° C. or less. The polyamic acid solution composition according to any one of claims 1 to 3, wherein
- ポリアミック酸溶液組成物を加熱処理して得られるポリイミドが、300~400℃の線膨張係数が250ppm/℃以下であることを特徴とする請求項4に記載のポリアミック酸溶液組成物。 The polyamic acid solution composition according to claim 4, wherein the polyimide obtained by heat-treating the polyamic acid solution composition has a coefficient of linear expansion at 300 to 400 ° C of 250 ppm / ° C or less.
- 前記フッ素原子を含有するテトラカルボン酸二無水物が、2,2-ビス(3,4-ジカルボキシフェニル)ヘキサフルオロプロパン二無水物であり、
前記フッ素原子を含有するジアミンが、2,2’-ビス(トリフルオロメチル)-4,4’-ジアミノビフェニル、及び/又は2,2’-ビス(3-アミノ-4-ヒドロキシフェニル)ヘキサフルオロプロパンであることを特徴とする請求項1~5のいずれかに記載のポリアミック酸溶液組成物。 The tetracarboxylic dianhydride containing a fluorine atom is 2,2-bis (3,4-dicarboxyphenyl) hexafluoropropane dianhydride,
The diamine containing a fluorine atom is 2,2′-bis (trifluoromethyl) -4,4′-diaminobiphenyl and / or 2,2′-bis (3-amino-4-hydroxyphenyl) hexafluoro. 6. The polyamic acid solution composition according to claim 1, which is propane. - 請求項1~6のいずれかに記載のポリアミック酸溶液組成物を製造する方法であって、
フッ素原子を含有するテトラカルボン酸二無水物を50モル%以上の量で含むテトラカルボン酸成分と、フッ素原子を含有するジアミンを50モル%以上の量で含むジアミン成分とを溶媒中で反応させてポリアミック酸溶液を製造する工程と、
得られたポリアミック酸溶液に、シリカの量がテトラカルボン酸成分とジアミン成分の合計量100質量部に対して1~100質量部の量になるように、有機溶媒にコロイダルシリカを分散させてなるコロイド溶液を添加し、混合する工程と
を有するポリアミック酸溶液組成物の製造方法。 A method for producing the polyamic acid solution composition according to any one of claims 1 to 6,
A tetracarboxylic acid component containing a fluorine atom-containing tetracarboxylic dianhydride in an amount of 50 mol% or more and a diamine component containing a fluorine atom-containing diamine in an amount of 50 mol% or more are reacted in a solvent. Producing a polyamic acid solution,
In the obtained polyamic acid solution, colloidal silica is dispersed in an organic solvent so that the amount of silica is 1 to 100 parts by mass with respect to 100 parts by mass of the total amount of the tetracarboxylic acid component and the diamine component. A method for producing a polyamic acid solution composition comprising the steps of adding and mixing a colloidal solution. - 請求項1~6のいずれかに記載のポリアミック酸溶液組成物を加熱処理して得られるポリイミド。 A polyimide obtained by heat-treating the polyamic acid solution composition according to any one of claims 1 to 6.
- 請求項8に記載のポリイミドを含む電気装置、電子装置、光学装置、表示装置、タッチパネル、太陽電池、又はLED照明装置。 An electric device, an electronic device, an optical device, a display device, a touch panel, a solar cell, or an LED lighting device including the polyimide according to claim 8.
- 表示デバイス又は受光デバイスであるフレキシブルデバイスの製造方法であって、
請求項1~6のいずれかに記載のポリアミック酸溶液組成物をキャリア基板上に塗布し、加熱処理して固体状のポリイミド樹脂膜を形成する工程、前記ポリイミド樹脂膜上に回路を形成する工程、及び、前記回路が表面に形成されたポリイミド樹脂膜を前記キャリア基板から剥離する工程を含むことを特徴とするフレキシブルデバイスの製造方法。 A method of manufacturing a flexible device which is a display device or a light receiving device,
A step of applying the polyamic acid solution composition according to any one of claims 1 to 6 on a carrier substrate and heat-treating it to form a solid polyimide resin film, and a step of forming a circuit on the polyimide resin film And the manufacturing method of the flexible device characterized by including the process of peeling the polyimide resin film in which the said circuit was formed in the surface from the said carrier substrate. - 請求項10に記載のフレキシブルデバイスの製造方法により製造された表示デバイス又は受光デバイスであるフレキシブルデバイス。 A flexible device which is a display device or a light receiving device manufactured by the method for manufacturing a flexible device according to claim 10.