WO2013092165A1 - Composite and method for producing a composite - Google Patents

Composite and method for producing a composite Download PDF

Info

Publication number
WO2013092165A1
WO2013092165A1 PCT/EP2012/074013 EP2012074013W WO2013092165A1 WO 2013092165 A1 WO2013092165 A1 WO 2013092165A1 EP 2012074013 W EP2012074013 W EP 2012074013W WO 2013092165 A1 WO2013092165 A1 WO 2013092165A1
Authority
WO
WIPO (PCT)
Prior art keywords
fibers
group
composite body
composite
reinforcing fibers
Prior art date
Application number
PCT/EP2012/074013
Other languages
German (de)
French (fr)
Inventor
Jens Ackermann
Dirk Schmiederer
Original Assignee
Robert Bosch Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Robert Bosch Gmbh filed Critical Robert Bosch Gmbh
Publication of WO2013092165A1 publication Critical patent/WO2013092165A1/en

Abstract

The present invention relates to a composite (10), comprising a polymer matrix (12), in which a first group of reinforcing fibres is arranged and in which a second group of reinforcing fibres is arranged, wherein the second group of reinforcing fibres comprises metal fibres (14), and wherein there is a defined concentration gradient with respect to the concentration of the second group of reinforcing fibres. Such a composite (10) has great stability along with good EMC protection and can at the same time be adapted particularly well to the desired application area and, furthermore, can be produced at particularly low cost. The present invention also relates to a method for producing a composite (10), to a component housing comprising a composite (10) and to the use of a composite (10) and/or a method for producing a composite (10) for producing a component housing with EMC protection.

Description

Beschreibung  description
Titel title
Verbundkörper und Verfahren zum Herstellen eines Verbundkörpers Die vorliegende Erfindung betrifft einen Verbundkörper mit EMV-Schutz und ein The present invention relates to a composite body with EMC protection and a composite body
Verfahren zum Herstellen eines derartigen Verbundkörpers mittels Faserspritzen. Method for producing such a composite body by means of fiber spraying.
Stand der Technik State of the art
Für die Herstellung von faserverstärkten Kunststoffbauteilen ist das Verfahren des Faserspritzens beispielsweise thermoplastischer Hybridgarne bekannt. For the production of fiber-reinforced plastic components, the method of fiber spraying, for example, thermoplastic hybrid yarns is known.
Das Dokument DE 26 17 741 C3, beispielsweise, offenbart ein Verfahren zum Herstellen von faserverstärkten, hydraulisch erhärtenden Massen. Bei einem derartigen Verfahren werden die Matrix und die Fasern durch The document DE 26 17 741 C3, for example, discloses a method for producing fiber-reinforced, hydraulically hardening masses. In such a process, the matrix and fibers are through
Übereinanderspritzen unter Bewirkung eines Mischeffektes in einem Overmoulding causing a mixing effect in one
Faserspritzverfahren gegen eine Fläche gesprüht. Dabei wird die faserbewehrte fließfähige Mischung gegen eine als Prallfläche dienende Fläche gesprüht und sodann durch Abtropfenlassen, Abgleitenlassen, Abstreifen, Abschütteln, Abschleudern oder dergleichen von der Prallfläche abgezogen und dem Fiber spraying sprayed against a surface. In this case, the fiber-reinforced flowable mixture is sprayed against serving as a baffle surface and then removed by draining, let slip, wiping, shaking, spin or the like from the baffle and the
Verwendungsort zugeführt. Zur Verwendung als mögliche Matrix sind in diesem Dokument solche genannt, die Verflüssiger und/oder Luftporenbildner, wie beispielsweise Vinsolharz, Ligninsulfonat, Melaminharz und/oder Usage supplied. For use as a possible matrix, this document mentions such as the plasticizers and / or air-entraining agents, such as, for example, Vinsol resin, lignosulfonate, melamine resin and / or
Verarbeitungshilfen, etwa auf Basis von Methylcellulose und/oder Processing aids, for example based on methylcellulose and / or
Polyethylenoxid enthalten. Als mögliche Verstärkungsfasern kommen gemäß diesem Dokument mineralische Fasern, wie etwa Glasfasern, Stein- und Polyethylene oxide included. As possible reinforcing fibers come according to this document mineral fibers, such as glass fibers, stone and
Schlackenwollen sowie Kohlenstofffasern, Metallfasern und organische Fasern in Betracht. Offenbarung der Erfindung Slag wool as well as carbon fibers, metal fibers and organic fibers. Disclosure of the invention
Gegenstand der Erfindung ist ein Verbundkörper, umfassend eine The invention relates to a composite body comprising a
Kunststoffmatrix, in der eine erste Gruppe von Verstärkungsfasern angeordnet ist und in der eine zweite Gruppe von Verstärkungsfasern angeordnet ist, wobei die zweite Gruppe von Verstärkungsfasern Metallfasern umfasst, und wobei bezüglich der Konzentration der zweiten Gruppe von Verstärkungsfasern ein definierter Konzentrationsgradient vorliegt. A plastic matrix in which a first group of reinforcing fibers is arranged and in which a second group of reinforcing fibers is arranged, the second group of reinforcing fibers comprising metal fibers, and wherein there is a defined concentration gradient with respect to the concentration of the second group of reinforcing fibers.
Unter einem Verbundkörper kann im Sinne der vorliegenden Erfindung insbesondere ein Element verstanden werden, das wenigstens zwei In the context of the present invention, a composite body can be understood in particular to be an element which has at least two
unterschiedliche Materialien umfasst, die miteinander verbunden sein können. Gemäß der vorliegenden Erfindung sind dies insbesondere die Kunststoffmatrix sowie die erste und die zweite Gruppe von Verstärkungsfasern. Die includes different materials that may be interconnected. According to the present invention, these are in particular the plastic matrix as well as the first and the second group of reinforcing fibers. The
Verstärkungsfasern können dabei in der Kunststoffmatrix derart eingebettet sein, dass sie beispielsweise durch Adhäsiv- oder Kohäsivkräfte an das Reinforcing fibers can be embedded in the plastic matrix in such a way that they can be attached to the body by adhesive or cohesive forces, for example
Kunststoffmaterial gebunden sind. Plastic material are bound.
Eine Kunststoffmatrix kann somit insbesondere ein Kunststoffmaterial sein, in welchem die Verstärkungsfasern eingebettet und somit von dem A plastic matrix may thus be in particular a plastic material in which the reinforcing fibers are embedded and thus of the
Kunststoffmaterial insbesondere vollständig umgeben sind. Plastic material in particular are completely surrounded.
Eine Verstärkungsfaser kann dabei eine an sich etwa aus einem Faser- Kunststoff-Verbund bekannte Faser sein, welche insbesondere dem Verbund eine vergrößerte Stabilität verleihen kann. Eine Gruppe von Verstärkungsfasern kann im Sinne der vorliegenden Erfindung dabei insbesondere eine Art an Verstärkungsfasern, also Verstärkungsfasern eines bestimmten Materials oder einer bestimmten Materialgruppe bedeuten. In this case, a reinforcing fiber can be a fiber known per se from a fiber-plastic composite, which in particular can impart increased stability to the composite. In the context of the present invention, a group of reinforcing fibers may in particular mean a type of reinforcing fibers, ie reinforcing fibers of a specific material or of a specific material group.
Die zweite Gruppe der Verstärkungsfasern kann dabei Metallfasern umfassen. Somit liegen in dem Verbundkörper neben der ersten Gruppe an The second group of reinforcing fibers may comprise metal fibers. Thus, in the composite body next to the first group
Verstärkungsfasern Metallfasern vor. Diese können insbesondere in Form eines Metallfasergeflechts in dem Verbundkörper vorliegen, wobei durch die Reinforcement fibers metal fibers ago. These can be present in particular in the form of a metal fiber braid in the composite body, wherein by the
Metallfasern beziehungsweise durch das Metallfasergeflecht ein Faradayscher Käfig erzeugbar beziehungsweise ausgestaltet sein kann. Daher kann der erfindungsgemäße Verbundkörper nicht nur eine hohe mechanische Stabilität aufweisen, sondern er kann zusätzlich durch die Metal fibers or by the metal fiber braid a Faraday cage can be generated or configured. Therefore, the composite body according to the invention can not only have a high mechanical stability, but it can additionally by the
Anordnung der Metallfasern einen EMV-Schutz ermöglichen, der mit Arrangement of metal fibers allow EMC protection with
herkömmlichen Kunststoffmaterialien beziehungsweise Faser-Kunststoff- Verbünden nicht möglich ist. Der erfindungsgemäße Verbundkörper kann daher beispielsweise in Form eines Bauteilgehäuses ein Metallgehäuse ersetzen, da neben der mechanischen Stabilität ferner die Anforderung an Gehäuse von elektrischen Schaltungen, beispielsweise, erfüllt werden, einen wirksamen EMV- Schutz bereit zu stellen. conventional plastic materials or fiber-plastic composites is not possible. The composite body according to the invention can therefore replace, for example, in the form of a component housing a metal housing, since in addition to the mechanical stability of the requirement for housing of electrical circuits, for example, are met, to provide effective EMC protection.
Ein EMV-Schutz kann dabei im Sinne der vorliegenden Erfindung insbesondere einen Schutz insbesondere elektronischer Komponenten vor unerwünschten Wechselwirkungen mit elektrischen beziehungsweise elektromagnetischen Strahlungen bedeuten. In the context of the present invention, EMC protection can in particular mean protection, in particular of electronic components, against undesired interactions with electrical or electromagnetic radiation.
Um einen geeigneten EMV-Schutz zu bewirken, können die Metallfasern in einer Ausgestaltung mit einem Durchmesser von > 30 [im bis < 120 [im ausgestaltet sein und/oder Längen von > 0,5 mm bis < 6 mm aufweisen. Bezüglich der zweiten Gruppe von Verstärkungsfasern beziehungsweise derIn order to effect a suitable EMC protection, the metal fibers may be configured in a configuration with a diameter of> 30 [im to <120 [im and / or have lengths of> 0.5 mm to <6 mm. With respect to the second group of reinforcing fibers or the
Metallfasern ist in dem Verbundkörper ein definierter Konzentrationsgradient vorgesehen. Das kann im Sinne der vorliegenden Erfindung insbesondere bedeuten, dass die Konzentration der zweiten Gruppe an Verstärkungsfasern in dem Verbundkörper lokal unterschiedlich gestaltet ist. So kann beispielsweise in einigen Bereichen eine hohe Konzentration an metallischen Verstärkungsfasern vorliegen, wohingegen deren Konzentration in weiteren Bereichen des Metal fibers, a defined concentration gradient is provided in the composite body. For the purposes of the present invention, this may mean, in particular, that the concentration of the second group of reinforcing fibers in the composite body is designed differently locally. For example, in some areas there may be a high concentration of metallic reinforcing fibers, whereas their concentration in other areas of the
Verbundkörpers geringer sein kann. Dadurch kann es erfindungsgemäß möglich werden, durch eine gezielte und definierte Anordnung der Metallfasern den Verbundkörper an das gewollte Anwendungsgebiet anzupassen Composite body may be lower. This makes it possible according to the invention to adapt the composite body to the desired field of application by means of a specific and defined arrangement of the metal fibers
beziehungsweise für eine gewünschte Anwendung maßzuschneidern. Im Detail kann beispielsweise an manchen Positionen des Verbundkörpers eine für Faser- Kunststoff-Verbünde bekannte Stabilität und nur ein geringer EMV-Schutz vorliegen, oder es kann gezielt eine mechanische Verstärkung beziehungsweise ein hoher EMV-Schutz vorgesehen sein, wobei die vorgenannten Beispiele nicht beschränkend sind. Als Verstärkungsfasern der ersten Gruppe können in dem Verbundkörper ohne auf die folgenden Beispiele beschränkt zu sein etwa anorganische or tailor for a desired application. In detail, for example, at some positions of the composite body known for fiber-plastic composites stability and only a low EMC protection, or it can be targeted mechanical reinforcement or high EMC protection provided, the above examples are not limiting , As the reinforcing fibers of the first group, in the composite body, without being limited to the following examples, such as inorganic ones
Verstärkungsfasern, wie beispielsweise Glasfasern oder Keramikfasern, Reinforcing fibers, such as glass fibers or ceramic fibers,
Basaltfasern, Borfasern oder Kieselsäurefasern, oder auch organische Basalt fibers, boron fibers or silica fibers, or organic
Verstärkungsfasern, wie beispielsweise Aramidfasern, Kohlenstofffasern,Reinforcing fibers, such as aramid fibers, carbon fibers,
Polyesterfasern, Nylonfasern, Plexiglasfasern, Polyethylenfasern oder auch Naturfasern, wie beispielsweise Holzfasern, Flachsfasern, Hanffasern oder Sisalfasern Verwendung finden. Diese können beispielsweise in einer Polyester fibers, nylon fibers, Plexiglas fibers, polyethylene fibers or natural fibers such as wood fibers, flax fibers, hemp fibers or sisal fibers use. These can, for example, in one
Konzentration in dem Verbundkörper vorliegen, die in einem Bereich von > 5 Gew.-% bis < 70 Gew.-%, bevorzugt > 10 Gew.-% bis < 60 Gew.-% liegt. Darüber hinaus können die Verstärkungsfasern der ersten Gruppe einen Länge von > 0,3 mm bis < 10 cm und einen Durchmesser von etwa > 10 [im bis < 15 [im aufweisen. Bezüglich der Konzentration der ersten Gruppe an Verstärkungsfasern kann derConcentration in the composite body, which is in a range of> 5 wt .-% to <70 wt .-%, preferably> 10 wt .-% to <60 wt .-%. In addition, the reinforcing fibers of the first group may have a length of> 0.3 mm to <10 cm and a diameter of about> 10 [im to <15 [im. Concerning the concentration of the first group of reinforcing fibers, the
Verbundkörper weiterhin einen Konzentrationsgradienten oder eine im Composite bodies continue to have a concentration gradient or an im
Wesentlichen konstante Konzentration aufweisen. Eine im Wesentlichen konstante Konzentration kann dabei insbesondere eine Konzentration bedeuten, die in einem einheitlichen Bereich liegt, wobei jedoch herstellungsbedingte Abweichungen beispielsweise unbeachtet bleiben können. Somit kann insbesondere an jeder Stelle des Verbundkörpers die gleiche Konzentration an der ersten Gruppe von Verstärkungsfasern vorliegen. Have substantially constant concentration. In this case, a substantially constant concentration may in particular mean a concentration that lies within a uniform range, although deviations due to production, for example, may remain unnoticed. Thus, in particular at any point of the composite, the same concentration of the first group of reinforcing fibers may be present.
Die Konzentration der ersten Gruppe an Verstärkungsfasern kann dabei an den Konzentrationsgradienten der zweiten Gruppe an Verstärkungsfasern angepasst werden. Somit kann beispielsweise ein variabler EMV-Schutz bei gleichzeitig konstanter mechanischer Stabilität vorgesehen sein, indem die Gesamtmenge an Verstärkungsfasern konstant bleiben kann. Ferner können bei einer konstanten Konzentration der ersten Gruppe der Verstärkungsfasern nur dort The concentration of the first group of reinforcing fibers can be adapted to the concentration gradient of the second group of reinforcing fibers. Thus, for example, a variable EMC protection can be provided at the same time constant mechanical stability by the total amount of reinforcing fibers can remain constant. Further, at a constant concentration of the first group of the reinforcing fibers, only there
Verstärkungsfasern der zweiten Gruppe vorgesehen sein, wo eine mechanischeBe provided reinforcing fibers of the second group, where a mechanical
Verstärkung oder ein EMV-Schutz notwendig ist. Darüber hinaus kann eine Anbindung der Metallfasern an andere Bauteile, wie beispielsweise an eine Gehäuserückseite, um einen Faradayschen Käfig zu schließen, realisiert werden, indem an einem Randbereich der Bauteile eine erhöhter Metallfaseranteil vorgesehen ist. Weiterhin können die in dem Verbundkörper verteilten Metallfasern auf ein Minimum reduziert werden, wodurch Kosten bei der Herstellung ebenso eingespart werden können, wie Gewicht, was das Anwendungsgebiet weiter verbreitert und die Verwendbarkeit erleichtert. Reinforcement or EMC protection is necessary. In addition, a connection of the metal fibers to other components, such as on a housing back to close a Faraday cage, can be realized by an increased metal fiber content is provided at an edge region of the components. Furthermore, the metal fibers distributed in the composite body can be reduced to a minimum, whereby costs in the production can be saved as well as weight, which further widens the field of application and facilitates the usability.
Im Rahmen einer Ausgestaltung können die Metallfasern in dem Verbundkörper räumlich begrenzt angeordnet sein. Dadurch kann beispielsweise und As part of an embodiment, the metal fibers may be spatially limited in the composite body. This can, for example, and
insbesondere bei der Verwendung des Verbundkörpers als Bauteilgehäuse die elektrische Abschirmung nur dort vorgesehen sein, wo sie benötigt wird. An Positionen eines nicht benötigten EMV-Schutzes beziehungsweise einer nicht benötigten mechanischen Verstärkung dagegen kann auf das Vorsehen der Metallfasern und damit auf einen EMV-Schutz beziehungsweise auf eine mechanische Verstärkung insbesondere vollständig verzichtet werden. Dadurch kann das Verbundbauteil in dieser Ausgestaltung besonders kostengünstig ausgestaltet sein und ferner eine besonders gute Anpassbarkeit an das gewünschte Anwendungsgebiet bieten. In dieser Ausgestaltung ist der especially when using the composite body as a component housing, the electrical shielding be provided only where it is needed. On the other hand, it is possible to dispense entirely with the provision of the metal fibers and thus with EMC protection or with mechanical reinforcement at positions of an EMC protection which is not required or an unnecessary mechanical reinforcement. As a result, the composite component in this embodiment can be configured particularly cost-effectively and, in addition, offer particularly good adaptability to the desired field of application. In this embodiment, the
Konzentrationsgradient der zweiten Gruppe an Verstärkungsfasern somit derart ausgestaltet, dass lokal in dem Verbundkörper insbesondere vollständig auf die zweite Gruppe der Verstärkungsfasern verzichtet werden kann, die Konzentration also, von herstellungsbedingten Schwankungen abgesehen, lokal im Concentration gradient of the second group of reinforcing fibers thus configured such that locally in the composite body in particular completely can be dispensed with the second group of reinforcing fibers, ie the concentration, apart from manufacturing fluctuations, locally in
Wesentlichen null sein kann. Insgesamt kann der Konzentrationsgradient der Metallfasern in allen Raumrichtungen vorliegen, also beispielsweise entlang der Dicke und/oder entlang der Breite des Verbundkörpers. Can be essentially zero. Overall, the concentration gradient of the metal fibers can be present in all spatial directions, that is, for example along the thickness and / or along the width of the composite body.
Im Rahmen einer weiteren Ausgestaltung können die Metallfasern in einem innenliegenden von der Oberfläche getrennten Bereich des Verbundkörpers oder an der Oberfläche des Verbundkörpers räumlich begrenzt vorliegen. Within the scope of a further embodiment, the metal fibers may be spatially limited in an inner area of the composite body which is separate from the surface or on the surface of the composite body.
Ein auf einen innenliegenden Bereich räumlich begrenztes Vorliegen der zweiten Gruppe an Verstärkungsfasern beziehungsweise der Metallfasern kann im Sinne der vorliegenden Erfindung insbesondere bedeuten, dass die zweite Gruppe an Verstärkungsfasern beispielsweise nur im Kern des Verbundkörpers angeordnet sind, jedoch nicht unmittelbar an der Oberfläche des Verbundkörpers. Hier liegt der Konzentrationsgradient somit insbesondere entlang der Dicke des For the purposes of the present invention, spatially limited presence of the second group of reinforcing fibers or of the metal fibers on an internal area can mean, in particular, that the second group of reinforcing fibers are arranged only in the core of the composite body, but not directly on the surface of the composite body. Here, the concentration gradient is thus in particular along the thickness of the
Verbundkörpers vor. In dieser Ausgestaltung können die Composite body before. In this embodiment, the
Oberflächeneigenschaften des Verbundkörpers insbesondere unabhängig von den Metallfasern ausgestaltet sein, und somit nur durch die Kunststoffmatrix beziehungsweise die erste Gruppe der Verstärkungsfasern beeinflussbar sein. Dadurch können die Oberflächeneigenschaften besonders definiert vorliegen. Beispielsweise kann der Farbeindruck des Verbundkörpers in dieser Surface properties of the composite body in particular independent of be designed to the metal fibers, and thus be influenced only by the plastic matrix or the first group of reinforcing fibers. As a result, the surface properties can be particularly defined. For example, the color impression of the composite in this
Ausgestaltung unabhängig von den Metallfasern sein, ohne jedoch einen EMV-Be independent of the metal fibers, but without an EMC
Schutz in dem Verbundkörper vernachlässigen zu müssen. To neglect protection in the composite body.
Darüber hinaus kann in dieser Ausgestaltung sichergestellt werden, dass der vorgesehene EMV-Schutz nicht durch geringe, an der Oberfläche des In addition, it can be ensured in this embodiment that the proposed EMC protection is not due to low, on the surface of the
Verbundkörpers auftretende Beschädigungen eingeschränkt beziehungsweise reduziert wird. Denn die den EMV-Schutz ausbildende Metallfasern sind durch ihre innenliegende Anordnung vor äußeren Einflüssen geschützt. Dadurch kann ein EMV-Schutz in dieser Ausgestaltung besonders sicher und verlässlich ausgestaltet sein, was insbesondere bei der Verwendung als EMV-schützendes Gehäuse für sensible elektronische Anordnungen von Vorteil sein kann. Compound occurring damage is reduced or reduced. Because the EMC fibers forming metal fibers are protected by their internal arrangement against external influences. As a result, an EMC protection in this embodiment can be designed to be particularly secure and reliable, which can be advantageous in particular when used as an EMC-protective housing for sensitive electronic arrangements.
Ein auf die Oberfläche räumlich begrenztes Vorliegen der zweiten Gruppe an Verstärkungsfasern beziehungsweise der Metallfasern kann im Sinne der vorliegenden Erfindung insbesondere bedeuten, dass die Metallfasern beispielsweise nur an der Oberfläche beziehungsweise in einem an die A spatially limited presence of the second group of reinforcing fibers or of the metal fibers on the surface in the sense of the present invention may mean, in particular, that the metal fibers, for example, only on the surface or in one of the
Oberfläche grenzenden Bereich vorliegen, jedoch nicht durchgängig durch die gesamte Dicke verteilt sind. Beispielsweise kann in dieser Ausgestaltung ein innenliegender Bereich vorgesehen sein, in dem keine Metallfasern angeordnet sind. Somit ist der Konzentrationsgradient in dieser Ausgestaltung insbesondere entlang der Dicke des Verbundkörpers ausgebildet. In dieser Ausgestaltung kann beispielsweise ein besonders gut ausgeprägter elektrostatischer Schutz, also insbesondere ein Schutz vor elektrostatischer Aufladung, umgesetzt werden.  Surface adjacent area, but are not consistently distributed throughout the thickness. For example, in this embodiment, an inner region may be provided in which no metal fibers are arranged. Thus, the concentration gradient is formed in this embodiment, in particular along the thickness of the composite body. In this embodiment, for example, a particularly well-pronounced electrostatic protection, ie in particular protection against electrostatic charge, can be implemented.
Im Rahmen einer weiteren Ausgestaltung kann der Verbundkörper zumindest teilweise eine Konzentration an Metallfasern aufweisen, die in einem Bereich vonIn a further embodiment, the composite body may at least partially have a concentration of metal fibers in a range of
> 0,5 % bis < 60 % liegt. Insbesondere in dieser Ausgestaltung kann ein wirksamer EMV-Schutz realisiert werden, der im Wesentlichen vor > 0.5% to <60%. In particular, in this embodiment, an effective EMC protection can be realized, which is essentially before
elektromagnetischer Strahlung unterschiedlichster Wellenlängen schützen kann. Bedingt durch den Konzentrationsgradienten der Metallfasern in dem electromagnetic radiation of different wavelengths can protect. Due to the concentration gradient of the metal fibers in the
Verbundkörper kann dabei in weiteren Bereichen des Verbundkörpers eine höhere oder niedrigere Konzentration an Metallfasern vorgesehen sein. Im Rahmen einer weiteren Ausgestaltung kann die Kunststoffmatrix aus einem Material ausgebildet sein, das ausgewählt ist aus der Gruppe umfassend oder bestehend aus Polyurethan, thermoplastischen Polymeren und Composite body can be provided in other areas of the composite, a higher or lower concentration of metal fibers. In a further embodiment, the plastic matrix may be formed from a material which is selected from the group consisting of or consisting of polyurethane, thermoplastic polymers and
Polyalkylenterephtalaten. Derartige Polymermaterialien sind in besonders vorteilhafterweise etwa für einen Faserspritzprozess geeignet, indem sie die Verstärkungsfasern fein verteilt aufnehmen können und diese ferner in einem hergestellten Verbundkörper gut durch Adhäsionskräfte beziehungsweise Kohäsionskräfte an sich binden können. Als thermoplastische Polymere können beispielsweise Verwendung finden Polyamide, Polyethylen, Polypropylen und Polyalkylenterephthalat. Bezüglich Polyalkylenterephtalaten können Polyalkylenterephtalaten. Such polymer materials are particularly advantageously suitable for a fiber spraying process, for example, in that they can absorb the reinforcing fibers in a finely distributed manner and can furthermore bind them well in a manufactured composite body by means of adhesion forces or cohesive forces. As thermoplastic polymers, for example, find use polyamides, polyethylene, polypropylene and polyalkylene terephthalate. With respect to polyalkylene terephthalates
beispielsweise Polyethylenterephtalat oder Polybutylenterephtalat Verwendung finden, wie beispielsweise das unter dem Handelsnamen Twintex der Firma Saint Gobain Vetrotex vertriebene Polyalkylenterephtalat. Bezüglich der Verwendung von Polyurethan kann der Verbundkörper in dieser Ausgestaltung durch ein sogenanntes Polyurethan-Faserspritzen (Long Fibre Injection, LFI) hergestellt werden. Dabei können beispielsweise in einem Mischkopf die Komponenten Isocyanat und Polyol vermischt werden, um so stromaufwärts eines Sprühkopfes das Polyurethan zu bilden. For example, polyethylene terephthalate or polybutylene terephthalate can be used, such as the polyalkylene terephthalate marketed under the trade name Twintex by Saint Gobain Vetrotex. With regard to the use of polyurethane, the composite body in this embodiment can be produced by so-called polyurethane fiber spraying (Long Fiber Injection, LFI). In this case, for example, the components isocyanate and polyol can be mixed in a mixing head so as to form the polyurethane upstream of a spray head.
Im Rahmen einer weiteren Ausgestaltung kann die zweite Gruppe von In a further embodiment, the second group of
Verstärkungsfasern beziehungsweise können die Metallfasern Aluminiumfasern und/oder Kupferfaser und/ oder Silberfasern umfassen beziehungsweise sein. Insbesondere derartige Fasern können eine hohe elektrische Leitfähigkeit aufweisen, die in einem Bereich von 30 * 10Λ6 S/m oder höher liegen kann und damit einen besonders effektiven EMV-Schutz bei gleichzeitig hoher Stabilität bieten kann. Darüber hinaus sind derartige Metalle vorteilhaft als Faser insbesondere in einem Faserspritzverfahren verarbeitbar. Insbesondere können derartige Fasern gleichmäßig in eine Kunststoffmatrix verteilt werden und ferner auf einfache Weise durch herkömmliche Schneideapparaturen in eine geeignete Länge geschnitten werden, um so etwa in einem Faserspritzprozess definiert verarbeitet zu werden. Reinforcing fibers or the metal fibers may comprise or be aluminum fibers and / or copper fiber and / or silver fibers. In particular, such fibers can have a high electrical conductivity, which can be in the range of 30 * 10 Λ 6 S / m or higher and thus can provide a particularly effective EMC protection with high stability. In addition, such metals are advantageously processed as a fiber, in particular in a fiber spraying process. In particular, such fibers can be evenly distributed in a plastic matrix and further easily cut by conventional cutting apparatus into an appropriate length so as to be processed as defined in a fiber spraying process.
Gegenstand der Erfindung ist ferner ein Verfahren zum Herstellen eines erfindungsgemäßen Verbundkörpers, wobei eine erste Gruppe von The invention further provides a method for producing a composite body according to the invention, wherein a first group of
Verstärkungsfasern und eine zweite Gruppe von Verstärkungsfasern mit dem Material einer Kunststoffmatrix in einem Faserspritzprozess derart als Reinforcing fibers and a second group of reinforcing fibers with the Material of a plastic matrix in a fiber spraying process such as
Zwischenprodukt auf ein Substrat aufgebracht wird, dass die zweite Gruppe von Verstärkungsfasern einen Konzentrationsgradienten aufweist, wobei die zweite Gruppe von Verstärkungsfasern Metallfasern umfasst, und wobei das Is applied to a substrate such that the second group of reinforcing fibers has a concentration gradient, wherein the second group of reinforcing fibers comprises metal fibers, and wherein the
Zwischenprodukt insbesondere unter Druckanwendung zu einem geformtenIntermediate especially under pressure application to a molded
Verbundkörper verarbeitet wird. Composite body is processed.
Das vorbeschriebene Verfahren, um einen erfindungsgemäßen Verbundkörper herzustellen, basiert auf einem Faserspritzprozess. Eine Ausgestaltung eines Faserspritzprozesses kann dabei im Sinne der vorliegenden Erfindung insbesondere folgendermaßen ablaufen. Bei einem derartigen Verfahren können Endlosfasern der ersten und der zweiten Gruppe als Ausgangsmaterial zusammen mit Kunststofffasern direkt beispielsweise als Roving in eine The method described above for producing a composite body according to the invention is based on a fiber injection process. An embodiment of a fiber spraying process can take place in the following manner in the sense of the present invention, in particular. In such a method, continuous fibers of the first and the second group can be used as starting material together with synthetic fibers directly, for example as a roving in a
Sprüheinheit gezogen werden. Dabei können sie beispielsweise an der Spray unit to be pulled. They can, for example, at the
Sprüheinheit von einem Schneideelement, wie etwa von einem Schnittmesser, in Faserstücke geschnitten werden. Mit Hilfe eines Heißluftstroms, beispielsweise, oder auch in dem sogenannten Airless-Verfahren können die geschnittenen Fasern, also die Verstärkungsfasern und die Kunststofffasern des Matrix- Materials, auf eine luftdurchlässige Form gesprüht werden. Dabei können die Kunststofffasern beispielsweise durch eine Einwirkung von Heißluft zum Teil an der Oberfläche aufgeschmolzen werden, was zu einem ersten Zusammenhaften der Faserbündel führen kann. In einem zweiten Schritt können die aufgesprühten Fasern, beziehungsweise das aufgesprühte Zwischenprodukt beziehungsweise Halbzeug beispielsweise in einer Heißpresse in die endgültige Form, wie etwa in eine Form eines Bauteilgehäuses, gebracht werden. Spray unit from a cutting element, such as a cutting knife, are cut into pieces of fiber. By means of a hot air flow, for example, or in the so-called airless method, the cut fibers, ie the reinforcing fibers and the plastic fibers of the matrix material, can be sprayed onto an air-permeable mold. In this case, the plastic fibers can be partially melted, for example, by the action of hot air on the surface, which can lead to a first cohesion of the fiber bundles. In a second step, the sprayed-on fibers, or the sprayed-on intermediate product or semifinished product, for example, in a hot press in the final shape, such as in a form of a component housing can be brought.
Dabei kann beispielsweise durch eine Einstellung der Konzentration It can, for example, by adjusting the concentration
beziehungsweise Menge der zugeführten Metallfasern, insbesondere im or amount of the supplied metal fibers, in particular in
Verhältnis zu der ersten Gruppe der Verstärkungsfasern beziehungsweise der Kunststoffmatrixfasern, und/oder durch eine zeitliche begrenzte Zufuhr derRelative to the first group of reinforcing fibers or the plastic matrix fibers, and / or by a time-limited supply of
Metallfasern und/oder durch eine Relativbewegung von Substrat und Düse beziehungsweise Sprühvorrichtung ein Konzentrationsgradient in dem hergestellten Verbundbauteil realisiert werden. Durch das erfindungsgemäße Verfahren können entkonturnahe Bauteile hergestellt werden, die durch das gezielte Einbringen von Metallfasern hohe mechanische Eigenschaften besitzen und gleichzeitig einen guten EMV-Schutz ermöglichen. Dadurch ist es realisierbar, mechanisch stabile beziehungsweise steife, leichte und kostengünstige EMV-geschützte Kunststoff-Verbundkörper, wie etwa Bauteilgehäuse, herzustellen, wobei bei der Herstellung für den EMV- Schutz kein weiterer Verfahrensschritt, wie etwa eine zusätzliche Beschichtung, notwendig ist. Es ist damit beispielsweise eine kostengünstige Herstellung von Langfaser gefüllten Bauteilen möglich, die hohe mechanische Eigenschaften aufweisen. Das erfindungsgemäße Verfahren kann daher den Vorteil bieten, dass in nur einem Verfahrensschritt beispielsweise ein Bauteilgehäuse automatisiert gefertigt werden kann, dass sowohl hohe mechanische als auch EMV-Schutz- Eigenschaften aufweist. Dabei können zudem Bauteile mit geringen bis hin zu großen Dimensionen ermöglicht werden. Ein weiterer Vorteil dieses Verfahrens kann darin gesehen werden, dass durch die ermöglichte kostengünstige Metal fibers and / or by a relative movement of the substrate and nozzle or spraying a concentration gradient in the composite component produced can be realized. By means of the method according to the invention, it is possible to produce components close to the entontankment, which are high due to the targeted introduction of metal fibers possess mechanical properties and at the same time allow good EMC protection. As a result, it is possible to produce mechanically stable or stiff, lightweight and cost-effective EMC-protected plastic composite bodies, such as component housings, wherein no further process step, such as an additional coating, is necessary during production for the EMC protection. It is thus possible, for example, a cost-effective production of long fiber filled components that have high mechanical properties. The method according to the invention can therefore offer the advantage that in one method step, for example, a component housing can be produced automatically, which has both high mechanical and EMC protection properties. In addition, components with small to large dimensions can be made possible. Another advantage of this method can be seen in the fact that made possible by the cost-effective
Prozess- und Maschinentechnik und die ferner möglichen kurzen Zykluszeiten ein Verfahren sowohl mit hoher Stückzahlflexibilität als auch mit  Process and machine technology and the further possible short cycle times a method with both high-volume flexibility and with
Großserientauglichkeit realisierbar ist. Dabei ist es ferner möglich, eine lokal gezielte Aufdickung durch eine verlängerteMass production suitability is feasible. It is also possible, a locally targeted thickening by a prolonged
Sprühzeit an Stellen der Bauteile vorzusehen, die einer höheren mechanischen Last ausgesetzt sind. Dadurch kann eine weiter verbesserte Anpassbarkeit an das gewünschte Anwendungsgebiet realisiert werden. Ferner kann durch die definierte Anordnung der Metallfasern ein Verbund mit einer elektrischen To provide spraying time at parts of the components that are exposed to a higher mechanical load. As a result, a further improved adaptability to the desired field of application can be realized. Furthermore, by the defined arrangement of the metal fibers, a composite with an electrical
Leitfähigkeit erzielt werden. Conductivity can be achieved.
Im Rahmen einer Ausgestaltung kann die erste Gruppe von Verstärkungsfasern und die zweite Gruppe von Verstärkungsfasern gleichzeitig und/oder In one embodiment, the first group of reinforcing fibers and the second group of reinforcing fibers can be used simultaneously and / or
abwechselnd insbesondere gemeinsam mit dem Material der Kunststoffmatrix auf das Substrat aufgebracht werden. Somit kann in dieser Ausgestaltung die erste Gruppe an Verstärkungsfasern etwa gemeinsam mit dem Material der Kunststoffmatrix wie insbesondere Kunststofffasern beispielsweise kontinuierlich etwa in den Sprühkopf eingetragen werden und dadurch beispielsweise eine konstante Konzentration dieser Verstärkungsfasern ermöglicht werden. Dabei können die Metallfasern in variierender Konzentration beziehungsweise Menge zusätzlich dem Sprühkopf zugetragen und zusammen mit den weiteren Verstärkungsfasern beziehungsweise den Matrixfasern versprüht werden. alternately in particular be applied to the substrate together with the material of the plastic matrix. Thus, in this embodiment, the first group of reinforcing fibers, for example, together with the material of the plastic matrix, such as in particular plastic fibers, for example, be continuously introduced into the spray head, thereby allowing, for example, a constant concentration of these reinforcing fibers. In this case, the metal fibers in varying concentration or amount can be added to the spray head and together with the other Reinforcing fibers or the matrix fibers are sprayed.
Alternativ oder zusätzlich ist es in einer Ausgestaltung möglich, lediglich eine Art an Verstärkungsfasern dem Sprühkopf zuzuführen und so zu versprühen. Alternatively or additionally, it is possible in one embodiment to supply only one type of reinforcing fibers to the spray head and thus to spray.
Folglich werden die unterschiedlichen Gruppen von Verstärkungsfasern abwechselnd beziehungsweise jeweils nacheinander versprüht. So ist es beispielsweise möglich, einen elektrisch leitfähigen Kern darzustellen bei gleichzeitigem Erhalt der elektrisch isolierenden Eigenschaften des Consequently, the different groups of reinforcing fibers are sprayed alternately or in succession. Thus, it is possible, for example, to represent an electrically conductive core while maintaining the electrically insulating properties of the
Gesamtverbunds. Gegenstand der Erfindung ist ferner ein Bauteilgehäuse, wobei das Total network. The invention further relates to a component housing, wherein the
Bauteilgehäuse einen erfindungsgemäßen Verbundkörper aufweist  Component housing has a composite body according to the invention
beziehungsweise aus diesem ausgebildet ist. Ein erfindungsgemäßes or is formed from this. An inventive
Bauteilgehäuse kann insbesondere die bezüglich des Verbundbauteils beschriebenen Vorteile aufweisen. Insbesondere kann ein derartiges Component housing may in particular have the advantages described with respect to the composite component. In particular, such a
Bauteilgehäuse auf einfache Weise hergestellt werden, eine hohe mechanischeComponent housings are easily manufactured, a high mechanical
Stabilität zusammen mit einer guten EMV-Schutz bieten und dabei bezüglich des gewünschten Anwendungsgebiets maßgeschneidert werden. Provide stability along with good EMC protection while tailoring to the desired application area.
Somit kann auch für komplexe Bauteile ein einteiliges Gehäuse mit lokal unterschiedlichen Eigenschaften hergestellt werden, was eine besonders großeThus, even for complex components, a one-piece housing with locally different properties can be produced, which is a particularly large
Variabilität verbunden mit einer kostengünstigen Herstellung ermöglicht. Der EMV-Schutz kann dabei von der Frequenz und der Stärke beispielsweise von elektromagnetischer Strahlung abhängen. Erfindungsgemäß kann daher das Bauteilgehäuse durch einen Konzentrationsgradienten der Metallfasern an unterschiedliche Bauteile beziehungsweise an unterschiedliche Anforderungen angepasst werden. So kann an unterschiedlichen Bereichen etwa eines Variability combined with a cost-effective production allows. The EMC protection can depend on the frequency and the strength of, for example, electromagnetic radiation. According to the invention, therefore, the component housing can be adapted by a concentration gradient of the metal fibers to different components or to different requirements. So can in different areas about one
Gehäuses ein geringer EMV-Schutz, ein hoher EMV-Schutz oder die Housing low EMC protection, high EMC protection or the
Abwesenheit eines EMV-Schutzes erwünscht sein. Entsprechendes gilt für eine mechanische Verstärkung. Als zu schützendes Bauteil, für welches das erfindungsgemäße Bauteilgehäuse Verwendung finden kann, können Absence of EMC protection may be desirable. The same applies to a mechanical reinforcement. As a component to be protected, for which the component housing according to the invention can be used, can
beispielsweise und nicht beschränkend Steuergeräte, Sensoren, Batteriepacks, beispielsweise von Lithium-Ionen-Batterien, oder auch elektrische Schaltungen genannt werden. Hier kann das erfindungsgemäße Bauteilgehäuse insbesondere Metallgehäuse ersetzen oder Kunststoffgehäuse, um beispielsweise einen leiterplattenseitig bestehenden EMV-Schutz in das Gehäuse integrieren zu können. Gegenstand der Erfindung ist ferner die Verwendung eines erfindungsgemäßen Verbundkörpers und/oder eines erfindungsgemäßen Verfahrens zum Herstellen eines Verbundkörpers zum Herstellen eines Bauteilgehäuses mit EMV-Schutz. In dieser Ausgestaltung der Erfindung kann ein EMV-Schutz auf besonders einfache und kostengünstige Weise durch ein Faserspritzverfahren erzeugt werden. Auf das Vorsehen einer Beschichtung für eine EMV-Abschirmung kann somit verzichtet werden, so dass weitere Arbeitsschritte eingespart werden können. Darüber hinaus kann durch die Verwendung eines wie vorstehend beschrieben ausgestalteten Verbundkörpers auf das Verwenden von For example, and not limiting control devices, sensors, battery packs, for example, lithium-ion batteries, or electrical circuits are called. Here, the component housing according to the invention can in particular replace metal housing or plastic housing in order, for example, to be able to integrate an EMC protection on the circuit board side into the housing. The invention further relates to the use of a composite body according to the invention and / or a method according to the invention for producing a composite body for producing a component housing with EMC protection. In this embodiment of the invention, an EMC protection can be generated in a particularly simple and cost-effective manner by a fiber spraying process. The provision of a coating for an EMC shield can thus be dispensed with so that further work steps can be saved. Moreover, by using a composite body configured as described above, it is possible to use
Stahlgehäusen, beispielsweise, verzichtet werden. Dadurch können Kosten eingespart werden, da der Verbundkörper im Vergleich zu Metallgehäusen kostengünstiger geformt werden kann. Darüber hinaus bietet die Steel housings, for example, be waived. As a result, costs can be saved, since the composite body can be formed cheaper compared to metal housings. In addition, the
erfindungsgemäße Verwendung eines derartigen Verbundkörpers zu EMV- Schutzzwecken eine deutliche Gewichtsersparnis, was eine besonders große Anwendungsvielfalt mit sich bringt. inventive use of such a composite body for EMC protection purposes a significant weight savings, which brings a particularly wide variety of applications with it.
Zeichnungen und Beispiele Drawings and examples
Weitere Vorteile und vorteilhafte Ausgestaltungen der erfindungsgemäßen Gegenstände werden durch die Zeichnungen veranschaulicht und in der nachfolgenden Beschreibung erläutert. Dabei ist zu beachten, dass die Further advantages and advantageous embodiments of the subject invention are illustrated by the drawings and explained in the following description. It should be noted that the
Zeichnungen nur beschreibenden Charakter haben und nicht dazu gedacht sind, die Erfindung in irgendeiner Form einzuschränken. Es zeigen Drawings are descriptive only and are not intended to limit the invention in any way. Show it
Fig. 1 eine schematische Darstellung einer Ausführungsform eines Fig. 1 is a schematic representation of an embodiment of a
erfindungsgemäßen Verbundkörpers;  composite body according to the invention;
Fig. 2 eine schematische Darstellung einer weiteren Ausführungsform eines erfindungsgemäßen Verbundkörpers; und Fig. 2 is a schematic representation of another embodiment of a composite body according to the invention; and
Fig. 3 eine schematische Darstellung einer Ausführungsform einer  Fig. 3 is a schematic representation of an embodiment of a
Faserspritzvorrichtung geeignet zum Herstellen eines  Fiber injection device suitable for producing a
erfindungsgemäßen Verbundkörpers.  composite body according to the invention.
In Figur 1 ist eine Ausführungsform eines erfindungsgemäßen Verbundkörpers 10 gezeigt. Der Verbundkörper 10 umfasst eine Kunststoffmatrix 12, in der eine erste Gruppe von Verstärkungsfasern angeordnet ist und in der eine zweite Gruppe von Verstärkungsfasern angeordnet ist. Dabei umfasst die zweite Gruppe von Verstärkungsfasern Metallfasern 14. Darüber hinaus liegt bezüglich der Konzentration der zweiten Gruppe von Verstärkungsfasern ein definierter Konzentrationsgradient vor. FIG. 1 shows an embodiment of a composite body 10 according to the invention. The composite body 10 comprises a plastic matrix 12 in which a first group of reinforcing fibers is arranged and in which a second group of reinforcing fibers is arranged. In this case, the second group of reinforcing fibers comprises metal fibers 14. In addition, there is a defined concentration gradient with respect to the concentration of the second group of reinforcing fibers.
Die Kunststoffmatrix 12 kann dabei aus einem Material ausgebildet sein, das ausgewählt ist aus der Gruppe umfassend Polyurethan, thermoplastischen Polymeren und Polyalkylenterephtalaten. Ferner kann die zweite Gruppe von Verstärkungsfasern beziehungsweise können die Metallfasern 14 The plastic matrix 12 may be formed from a material which is selected from the group comprising polyurethane, thermoplastic polymers and polyalkylene terephthalates. Furthermore, the second group of reinforcing fibers or the metal fibers 14 may be used
Aluminiumfasern und/oder Kupferfasern und/oder Silberfasern umfassen.  Aluminum fibers and / or copper fibers and / or silver fibers include.
Ein derartiger Verbundkörper 10 kann beispielsweise ein Bauteilgehäuse sein oder einen Teil des Bauteilgehäuses bilden. Durch die Metallfasern 14 kann der Verbundkörper 10 beziehungsweise das Bauteilgehäuse neben einer hohenSuch a composite body 10 may for example be a component housing or form part of the component housing. By the metal fibers 14, the composite body 10 and the component housing in addition to a high
Stabilität einen effektiven EMV-Schutz realisieren. Stability an effective EMC protection realize.
Darüber hinaus kann der Konzentrationsgradient derart ausgestaltet sein, dass die Metallfasern 14 in dem Verbundkörper 10 räumlich begrenzt vorliegen beziehungsweise angeordnet sind. In der Ausgestaltung gemäß Figur 1 liegen die Metallfasern 14 in einem innenliegenden Bereich 16 des Verbundkörpers 10 begrenzt vor, wobei der innenliegende Bereich 16 von einer Oberfläche 18, 28 etwa durch einen Bereich ohne Metallfasern 14, getrennt ist. Dementsprechend kann der innenliegende Bereich14 von beispielsweise zwei außenliegenden Bereichen beziehungsweise Oberflächenbereichen 20, 22 umgeben sein, so dass die Metallfasern 14 im Wesentlichen nicht an der Oberfläche 18, 28 des Verbundkörpers 10 vorliegen. In addition, the concentration gradient can be configured such that the metal fibers 14 are spatially limited or arranged in the composite body 10. In the embodiment according to FIG. 1, the metal fibers 14 are limited in an inner region 16 of the composite body 10, wherein the inner region 16 is separated from a surface 18, 28 approximately by a region without metal fibers 14. Accordingly, the inner region 14 may be surrounded by, for example, two outer regions or surface regions 20, 22, such that the metal fibers 14 are substantially not present on the surface 18, 28 of the composite body 10.
In Figur 2 ist eine weitere Ausgestaltung des erfindungsgemäßen FIG. 2 shows a further embodiment of the invention
Verbundkörpers 10 gezeigt. In der Ausgestaltung gemäß Figur 2 liegen dieComposite body 10 shown. In the embodiment of Figure 2 are the
Metallfasern 14 an der Oberfläche 18 beziehungsweise an einem Metal fibers 14 on the surface 18 or on a
Oberflächenbereich 24 des Verbundkörpers 10 räumlich begrenzt vor. In einem darunterliegenden Bereich 26, der beispielsweise ein innenliegender Bereich oder ein Bereich, der die gegenüberliegende Oberfläche 28 bildet, sein kann, liegen dagegen keine Metallfasern 14 vor. Somit können die Metallfasern 14 in anderen Worten nur einseitig beziehungsweise außenliegend in dem Surface region 24 of the composite body 10 limited in space. In contrast, no metal fibers 14 are present in an underlying region 26, which may be an internal region or an area that forms the opposite surface 28, for example. Thus, the metal fibers 14 in other words only one-sided or outboard in the
Verbundkörper 10 vorliegen. Composite body 10 is present.
Unabhängig von der konkreten Ausgestaltung können die Metallfasern 14 zumindest teilweise, also in einem Bereich, in dem ein EMV-Schutz oder eine mechanische Verstärkung erwünscht ist, in einem Konzentrationsbereich von wenigen Prozenten bis 50 % und mehr vorliegen, beispielsweise in einem Regardless of the specific embodiment, the metal fibers 14 may be present at least partially, ie in a region in which EMC protection or mechanical reinforcement is desired, in a concentration range of a few percent to 50 percent or more, for example in one
Bereich von > 0,5% bis < 60%. In Figur 3 ist eine beispielhafte Vorrichtung 30 zum Faserspritzen gezeigt, mit der ein erfindungsgemäßes Verfahren zum Herstellen eines erfindungsgemäßen Verbundbauteils 10 realisierbar ist. Range from> 0.5% to <60%. FIG. 3 shows an exemplary apparatus 30 for fiber spraying with which a method according to the invention for producing a composite component 10 according to the invention can be realized.
Die Vorrichtung 30 kann eine Sprüheinheit umfassen, in welche beispielsweise Endlosfasern beziehungsweise Langfasern der ersten und der zweiten Gruppe der Verstärkungsfasern als Ausgangsmaterial der jeweiligen Verstärkungsfasern zusammen mit Kunststofffasern als Ausgangsmaterial für die Kunststoffmatrix 12, beispielsweise als Roving, gezogen werden können. Als Sprüheinheit kann beispielsweise eine Venturi-Düse 32 dienen, in welcher die einzelnen Fasern nach einem Schneiden der Fasern in geeignete Längen durch einen Luftstrom angesaugt und versprüht werden. Die Fasern werden dann, beispielsweise unter Zuhilfename von Leitblechen 34, auf ein insbesondere luftdurchlässiges Substrat 36 gesprüht. Stromaufwärts des Substrats 36 können die Fasern durch einen von Lufterhitzern 38 erzeugten heißen Luftstrom 40 erhitzt und so angeschmolzen werden. Somit können die erste Gruppe von Verstärkungsfasern und die zweite Gruppe von Verstärkungsfasern mit dem Material einer Kunststoffmatrix in einem Faserspritzprozess als Zwischenprodukt auf das Substrat 36 aufgebracht beziehungsweise aufgesprüht werden. Unterhalb des Substrats 36 kann eine Absaugung 42 vorgesehen sein, um den Luftstrom abzusaugen, was durch den Pfeil 44 angedeutet sein soll. The device 30 may comprise a spray unit into which, for example, continuous fibers or long fibers of the first and second groups of reinforcing fibers may be drawn as the starting material of the respective reinforcing fibers together with plastic fibers as the starting material for the plastic matrix 12, for example as a roving. As a spray unit, for example, a Venturi nozzle 32 serve in which the individual fibers are sucked and sprayed after cutting the fibers in suitable lengths by an air flow. The fibers are then sprayed, for example, with the aid of baffles 34, on a particular air-permeable substrate 36. Upstream of the substrate 36, the fibers may be heated and fused by a hot air stream 40 generated by air heaters 38. Thus, the first group of reinforcing fibers and the second group of reinforcing fibers with the material of a plastic matrix can be applied or sprayed onto the substrate 36 as an intermediate product in a fiber spraying process. Below the substrate 36, a suction 42 may be provided to suck the air flow, which should be indicated by the arrow 44.
Bei der Verwendung von Polyurethan als Kunststoffmatrix 12, beispielsweise, können dabei die Rovings der Verstärkungsfasern der ersten und/oder der zweiten Gruppe gefördert werden. Parallel hierzu können in einer Mischkammer aus zwei Polyurethan-Komponenten, beispielsweise einem Isocyanat und einemWhen using polyurethane as a plastic matrix 12, for example, while the rovings of the reinforcing fibers of the first and / or the second group can be promoted. In parallel, in a mixing chamber of two polyurethane components, such as an isocyanate and a
Polyol, beispielsweise nach dem Gegenstrom-Hochdruck-Mischprinzip vermischt werden, wodurch sich Polyurethan bilden kann, welches als Matrixmaterial dienen kann. Polyol, for example, mixed according to the countercurrent high pressure mixing principle become, which can form polyurethane, which can serve as a matrix material.
Der Mischkopf, beispielsweise ein LFI-Mischkopf, kann dann mittels eines Roboters über eine offene Form verfahren und das Faser/Polyurethan-Gemisch in die Form eingetragen werden. Der Eintrag kann dabei entsprechend der Bauteilgeometrie und den Anforderungen innerhalb des Verbundkörpers frei wählbar sein. Nach Beendigung des Materialeintrags kann die Form geschlossen werden und durch das Einwirken von Druck und/oder Hitze die endgültige Form erzeugt werden. Nach Aushärten kann das erzeugte Verbundbauteil entformt werden. The mixing head, for example an LFI mixing head, can then be moved by means of a robot over an open mold and the fiber / polyurethane mixture can be introduced into the mold. The entry can be freely selectable according to the component geometry and the requirements within the composite body. After completion of the material entry, the mold can be closed and the final shape created by the application of pressure and / or heat. After curing, the composite component produced can be removed from the mold.
Ein derartiges Verfahren verwendend Polyurethan kann dabei beispielsweise bei Großserien, etwa in der Automobilindustrie, eingesetzt werden. Denn durch das zeitgleiche, automatisierte Eintragen von Matrix und Fasern und durch eine recht schnelle Reaktionszeit insbesondere einer Matrix umfassend Polyurethan ist ein kostengünstiger Reaktionszyklus realisierbar. Such a method using polyurethane can be used for example in large series, such as in the automotive industry. Because by the simultaneous, automated entry of matrix and fibers and by a fairly fast reaction time, in particular a matrix comprising polyurethane, a cost-effective reaction cycle can be realized.
Um zu ermöglichen, dass die zweite Gruppe von Verstärkungsfasern To allow the second group of reinforcing fibers
beziehungsweise die Metallfasern 14, einen Konzentrationsgradienten aufweist, kann die zweite Gruppe von Verstärkungsfasern beispielsweise in einer variierenden Menge oder zeitlich begrenzt in die Sprühvorrichtung eingeführt werden. Dabei kann die erste Gruppe von Verstärkungsfasern und die zweite Gruppe von Verstärkungsfasern gleichzeitig und/oder abwechselnd in der Kunststoffmatrix 12 auf das Substrat 36 aufgebracht werden. Darüber hinaus kann das Substrat 36 unter der Sprüheinheit verfahren werden, was die Formung vereinfacht und ferner eine Konzentrationssteuerung der Faseranteile zulässt. or the metal fibers 14, a concentration gradient, the second group of reinforcing fibers, for example, in a varying amount or for a limited time in the spray device can be introduced. In this case, the first group of reinforcing fibers and the second group of reinforcing fibers can be applied to the substrate 36 simultaneously and / or alternately in the plastic matrix 12. In addition, the substrate 36 can be moved under the spray unit, which simplifies molding and further permits concentration control of the fiber portions.
Bezüglich der Länge der Fasern kann hier auch eine definierte Längenverteilung von vorzugsweise 0,2 - 50 mm von Vorteil sein, um beispielsweise ein verbessertes Sturzverhalten beziehungsweise eine verbesserte Stabilität und/oder eine punktuelle Verstärkung der Verbundkörper 10 zu realisieren. With regard to the length of the fibers, a defined length distribution of preferably 0.2-50 mm may be advantageous here, in order to realize, for example, an improved camber behavior or an improved stability and / or a punctiform reinforcement of the composite body 10.
In einem weiteren Schritt können die aufgesprühten Fasern, beziehungsweise das aufgesprühte Zwischenprodukt beziehungsweise Halbzeug, von dem Substrat 36 entfernt werden und, beispielsweise in einer nicht dargestellten Heißpresse, in die endgültige Form, wie etwa in eine Form eines In a further step, the sprayed-on fibers, or the sprayed intermediate product or semifinished product, can be removed from the substrate 36 and, for example, in a not shown Hot press, in the final form, such as in a form of a
Bauteilgehäuses, gebracht werden, also unter Druckanwendung zu einem geformten Verbundkörper 10 verarbeitet werden. Dazu kann das Substrat beispielsweise bereits in einer Form angeordnet sein, so dass durch Schließen der Form und durch Anwendung von Druck und/oder Hitze die gewünschte Form erzeugbar sein kann. Component housing, are brought, so be processed under pressure application to a molded composite body 10. For this purpose, for example, the substrate may already be arranged in a mold, so that the desired shape can be produced by closing the mold and applying pressure and / or heat.

Claims

Ansprüche claims
1. Verbundkörper, umfassend eine Kunststoffmatrix (12), in der eine erste A composite body comprising a plastic matrix (12) in which a first
Gruppe von Verstärkungsfasern angeordnet ist und in der eine zweite Gruppe von Verstärkungsfasern angeordnet ist, wobei die zweite Gruppe von Verstärkungsfasern Metallfasern (14) umfasst, und wobei bezüglich der Konzentration der zweiten Gruppe von Verstärkungsfasern ein definierter Konzentrationsgradient vorliegt.  Group of reinforcing fibers is arranged and in which a second group of reinforcing fibers is arranged, wherein the second group of reinforcing fibers comprises metal fibers (14), and wherein there is a defined concentration gradient with respect to the concentration of the second group of reinforcing fibers.
2. Verbundkörper nach Anspruch 1 , wobei die Metallfasern (14) in dem 2. A composite according to claim 1, wherein the metal fibers (14) in the
Verbundkörper (10) räumlich begrenzt angeordnet sind.  Composite body (10) are arranged spatially limited.
3. Verbundkörper nach Anspruch 2, wobei die Metallfasern (14) in einem 3. A composite according to claim 2, wherein the metal fibers (14) in one
innenliegenden von der Oberfläche (18, 28) getrennten Bereich (16) des Verbundkörpers (10) oder an der Oberfläche (18, 28) des Verbundkörpers (10) räumlich begrenzt vorliegen.  internal region (16) of the composite body (10) separated from the surface (18, 28) or spatially limited on the surface (18, 28) of the composite body (10).
4. Verbundkörper nach einem der Ansprüche 1 bis 3, wobei der Verbundkörper (10) zumindest teilweise eine Konzentration an Metallfasern (14) aufweist, die in einem Bereich von > 0,5 bis < 60% liegt. 4. A composite according to any one of claims 1 to 3, wherein the composite body (10) at least partially has a concentration of metal fibers (14), which is in a range of> 0.5 to <60%.
5. Verbundkörper nach einem der Ansprüche 1 bis 4, wobei die 5. A composite according to any one of claims 1 to 4, wherein the
Kunststoffmatrix (12) aus einem Material ausgebildet ist, das ausgewählt ist aus der Gruppe umfassend Polyurethan, thermoplastischen Polymeren und Polyalkylenterephtalaten.  Plastic matrix (12) is formed of a material which is selected from the group comprising polyurethane, thermoplastic polymers and polyalkylene terephthalates.
6. Verbundkörper nach einem der Ansprüche 1 bis 5, wobei die zweite Gruppe von Verstärkungsfasern Aluminiumfasern und/oder Kupferfasern und/oder Silberfasern umfasst. A composite according to any one of claims 1 to 5, wherein the second group of reinforcing fibers comprises aluminum fibers and / or copper fibers and / or silver fibers.
7. Verfahren zum Herstellen eines Verbundkörpers (10) nach einem der 7. A method for producing a composite body (10) according to one of
Ansprüche 1 bis 6, wobei eine erste Gruppe von Verstärkungsfasern u eine zweite Gruppe von Verstärkungsfasern mit dem Material einer Claims 1 to 6, wherein a first group of reinforcing fibers u a second group of reinforcing fibers with the material of a
Kunststoffmatrix (12) in einem Faserspritzprozess derart als  Plastic matrix (12) in a fiber spraying process such as
Zwischenprodukt auf ein Substrat (36) aufgebracht wird, dass die zweite Gruppe von Verstärkungsfasern einen Konzentrationsgradienten aufweist, wobei die zweite Gruppe von Verstärkungsfasern Metallfasern (14) umfasst, und wobei das Zwischenprodukt insbesondere unter Druckanwendung zu einem geformten Verbundkörper (10) verarbeitet wird.  Intermediate product is applied to a substrate (36) such that the second group of reinforcing fibers has a concentration gradient, wherein the second group of reinforcing fibers comprises metal fibers (14), and wherein the intermediate product is processed into a molded composite body (10), in particular under pressure application.
8. Verfahren nach Anspruch 7, wobei die erste Gruppe von Verstärkungsfasern und die zweite Gruppe von Verstärkungsfasern gleichzeitig und/oder abwechselnd insbesondere gemeinsam mit dem Material der 8. The method of claim 7, wherein the first group of reinforcing fibers and the second group of reinforcing fibers at the same time and / or alternately in particular together with the material of
Kunststoffmatrix (12) auf das Substrat (36) aufgebracht werden.  Plastic matrix (12) are applied to the substrate (36).
9. Bauteilgehäuse, wobei das Bauteilgehäuse einen Verbundkörper (10) nach einem der Ansprüche 1 bis 6 aufweist. 9. component housing, wherein the component housing has a composite body (10) according to one of claims 1 to 6.
10. Verwendung eines Verbundkörpers (10) nach einem der Ansprüche 1 bis 6 und/oder eines Verfahren zum Herstellen eines Verbundkörpers (10) nach einem der Ansprüche 7 oder 8 zum Herstellen eines Bauteilgehäuses mit EMV-Schutz. 10. Use of a composite body (10) according to any one of claims 1 to 6 and / or a method for producing a composite body (10) according to any one of claims 7 or 8 for producing a component housing with EMC protection.
PCT/EP2012/074013 2011-12-19 2012-11-30 Composite and method for producing a composite WO2013092165A1 (en)