WO2013002532A2 - 산소 원자 분산된 금속 기지 복합재 및 그 제조 방법 - Google Patents
산소 원자 분산된 금속 기지 복합재 및 그 제조 방법 Download PDFInfo
- Publication number
- WO2013002532A2 WO2013002532A2 PCT/KR2012/005030 KR2012005030W WO2013002532A2 WO 2013002532 A2 WO2013002532 A2 WO 2013002532A2 KR 2012005030 W KR2012005030 W KR 2012005030W WO 2013002532 A2 WO2013002532 A2 WO 2013002532A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- composite
- matrix
- oxide
- powder
- Prior art date
Abstract
본 발명에 따라서, 산화물 나노 입자가 분산된 금속기지 복합재 제조 방법이 제공된다. 상기 방법은 금속 기지 분말 내부에 기지 금속의 산화물보다 깁스 자유 에너지 (Gibbs free energy)가 더 큰 산화물 나노 입자가 분산되어 있는 복합 분말을 준비하는 단계와, 상 기 복합 분말을 열간 성형 공정을 이용하여 벌크 가공재를 제조하거나, 상기 복합 분말을 금속 모재 용탕에 투입한 후 급속 교반하여 주조재를 제조하는 단계와, 상기 벌크 가공재 또는 주조재에 대해 열처리를 하여, 상기 산화물 나노입자가 기지 금속과의 계면에서 확산 하도록 하여, 상기 산화물 나노입자와 상기 기지 금속 사이에 새로운 계면 층을 생성하는 단계와, 상기 열처리와 동일한 조건 하에서 그 열처리 시간올 연장시켜, 상기 기지 금속의 원자들과 상기 산화물 나노입자의 원자들이 상호 확산하도록 하여, 상기 산화물 나노입자에서 비롯되는 산소원자를 상기 금속 기지 내부로 확산 및 분산시키는 단계를 포함하는 것을 특징으로 한다.
Description
【명세서】
【발명의 명칭】
산소 원자 분산된 금속 기지 복합재 및 그 제조 방법
【기술분야】
본 발명은 금속기지 복합재 및 그 제조 방법에 관한 것으로서, 보다 구체적으로는 나노 산화물 입자 또는 산소 원자를 금속 기지 중에 분산 /확산시켜, 기계적 특성 및 내부식 성과 같은 특성을 대폭 향상시킨 금속기지 복합재 및 그 제조 방법에 관한 것이다.
【발명의 배경이 되는 기술】
금속기지 복합재료는 금속기지의 우수한 연성과 강화재의 고경도, 고탄성, 내마모성 둥의 특성과 결합하여 기존의 금속재료에 비해 우수한 기계적 성질을 나타내기 때문에 자동 차, 항공 관련 소재산업에서 크게 각광받고 있는 재료이다. 나노 입자 혹은 나노 파이버가 분산된 금속기지 복합재료를 제조하기 위한 기존의 방법은 액상법 (Noguchi T, Magario A, Fukazawa S, Mater Trans 2004;45:602, Yanagi H, Kawai Y, Kita K, Japanese Journal of Applied Physics 2006:45:L650— 3)ᅳ고상법 (Sie Chin Tjong, Advanced Engineering Materials, 9(8), 2007, pp.639~652), 분무성형법 (S.K. Chaudhury, C.S. Sivaramakrishnan, S.C. Panigrahi, Journal of Materials Processing Technology 145 (2004) 385—390)의 세 가지로 구분될 수 있다. 고상법에 있어서, 강화재는 분말 내부에 균일하게 분산되기 어렵고 금속 분말 표면 에 혼합되어 있는 수준에 그치게 된다. 이로 인해 분말 표면 둥에 강화재의 편석 현상이 발생하여 분산도가 떨어지며 복합재의 특성이 저하된다. 또한, 이들은 일체화 시 표면에 존 재하는 강화재가 분말과 분말의 결합을 방해하기 때문에, 양질의 벌크재를 제조하기가 어렵 고, 제조 단가가 높아 경제성의 측면에서 제한적으로 웅용되고 있는 것이 현재의 실정이다. 또한, 분무성형법의 경우에는 미적층 분말이 형성될 수 있고, 고난도 형상 및 미세조직 제어 기술의 확보가 필요해 아직 연구단계에 있으몌 제조 단가 또한 높아 경제성의 측면에서도 많은 제한을 받고 있다. 액상법의 종류에는 스터 캐스팅 (stir casting), 스퀴즈 캐스팅 (squeeze casting), 레오 캐스팅 (rheocasting), 식소캐스팅 (thixocasting) 등이 있으며, 이중 입자 혹은 불연속적인 분 산 강화형 금속기지 복합재료를 제조하는 방법으로 스터 캐스팅법이 간편함, 웅용성, 경제성 및 생산성의 측면에서 가장 각광받는 방법이다ᅳ 그러나 기존 스터 캐스팅 법에서 임펠러를 이용한 단순 혼합 및 강화재의 단순 주 입방법은 강화재와 용탕 사이의 낮은 젖음성 (wetting)의 문제, 용탕과 강화재의 비중차의 문 제, 주조 시 다공질 입자 혹은 나노 파이버가 용탕 표면으로 떠오르는 문제 등 극복해야 할 문제가 있으며, 강화재의 크기가 나노 크기까지 감소할 경우 그 문제점은 더욱 커져 복합재 제조에 어려움이 있다. 한편, 최근 IT 기기 둥이 널리 사용됨에 따라 마그네슘에 대한 관심이 증대되고 있 다. 마그네슘은 단위 중량당 강도가 높아 자동차 등의 수송기기 산업에서 경량화 재료로 기대되고 있다. 그러나, 마그네슘은 부식과 관련하여 매우 취약한 특성을 나타내는 재료이 기 때문에, 휴대전화, PC 등의 상자나 자동차의 외장 등에 적용하는 경우 도장과 같은 표면 처리를 필수적으로 해야 한다. 마그네슘 제품의 양극 산화 처리에는 DOW17, HAE 번 등 이 있으나, 원가가 너무 높아 새로운 방식의 여러 가지 표면 처리 방법이 모색되고 있으나, 마그네슘 재료의 특성을 근본적으로 향상시키는 기술이 여전히 필요한 실정이다.
【발명의 상세한 설명】
【기술적 과제】
본 발명은 전술한 종래 기술에서 나타나는 문제점을 해결하기 위한 것으로서, 한 가 지 목적은 제조 공정이 분말 공법에 비해 쉽고 단순하여 산업적 웅용 가능성이 우수한 캐스 팅법, 바람직하게는 스터 캐스팅법을 통하여 금속기지 복합재를 제조하는 방법 및 금속기지 복합재를 제공하는 것이다. 본 발명의 다른 목적은 나노 입자가 용해 시 모재 용탕과 잘 섞이도록 하여 주조 시 나노 입자가 편석 및 웅집 현상 없이 균일 분산된 금속기지 복합재 및 그 제조 방법을 제공하는 것이다. 본 발명의 또 다른 목적은 모재 금속과 나노 입자의 계면 처리를 통하여 금속기지 와 이종 (異種)의 나노 입자의 계면 특성을 제어하는 방법을 제공하는 것이다. 본 발명의 또 다른 목적은 모재 금속과 나노 입자의 계면 처리를 통하여 우수한 기 계적 특성을 구현할 수 있는 방법을 제공하는 것이다. 본 발명의 또 다른 목적은 단순한 기계적 공정올 이용하여 대형의 벌크재가 대량으 로 제조될 수 있고 우수한 기계적 특성을 지닌 주조용 금속기지 복합재 및 그 제조 방법을 제공하는 것이다. 본 발명의 또 다른 목적은 나노 산화물 입자와 금속 기지와의 계면 반응 증의 확산 을 제어하여, 산소 원자를 금속 기지 내로 확산 /분산시켜, 새로운 특성을 갖는 금속기지 복 합재 및 그 제조 방법을 제공하는 것이다. 본 발명의 또 다른 목적은 나노 산화물 입자와 금속 기지 사이의 신규 계면층 및 이로부터 비롯되는 산소 원자의 확산을 통해, 내부식성과 같은 특성이 획기적으로 개선된 금속 기지 복합재 및 그 제조 방법을 제공하는 것이다.
[기술적 해결 방법】
상기 목적을 달성하기 위하여 , 본 발명에 따라서, 산화물 나노 입자가 분산된 금속 기지 복합재 제조 방법이 제공되는데, 상기 방법은 금속 기지 분말 내부에 기지 금속의 산 화물보다 깁스 자유 에너지 (Gibbs free energy)가 더 큰 산화물 나노 입자가 분산되어 있는 복합 분말을 준비하는 단계와, 상기 복합 분말을 열간 성형 공정을 이용하여 벌크 가공재를 제조하거나, 상기 복합 분말을 금속 모재 용탕에 투입한 후 급속 교반하여 주조재를 제조하 는 단계와, 상기 벌크 가공재 또는 주조재에 대해 열처리를 하여, 상기 기지 금속의 원자들 과 상기 산화물 나노입자의 원자들이 상호 확산하도록 하여, 상기 산화물 나노입자에서 비 롯되는 산소원자를 상기 금속 기지 내부로 확산 및 분산시키는 단계를 포함하는 것을 특징 으로 한다. 한 가지 실시예에 있어서, 상기 산화물 나노 입자들은 상기 확산을 하기에 낮은 에 너지 배리어를 갖는 크기로 되어 있는 것을 특징으로 한다ᅳ 한 가지 실시예에 있어서, 상기 나노 입자는 그 크기가 약 100 nm 이하일 수 있다. 한 가지 실시예에 있어서, 상기 열처리는 0.5~lTm(Tm: 금속 기지 분말의 융점)의 은도에서 수행할 수 있다. 한 가지 실시예에 있어서, 상기 금속 기지 분말은 알루미늄, 구^ 철, 티타늄 또는
마그네슘의 순금속 또는 이중 선택된 하나 이상을 기지로 하는 소성변형 가능한 합금일 수 있다. 한 가지 실시예에 있어서, 상기 산화물 나노 입자는 티타니아 (Ti02), 알루미나
(AI2O3), 실리카 (Si02), 징크옥사이드 (Zn02), 지르코니아 (Ζ1Ό2) 및 틴옥사이드 (Sn02)로부터 선택되는 산화물 나¾입자일 수 있다. 본 발명에 있어서, 상기 산소 원자들이 금속 기지 내부로 확산 및 분산됨에 따라 상기 복합재의 내부식성을 향상시킨다. 본 발명의 다른 실시예에 따른 나노 입자가 분산된 금속기지 복합재 제조 방법은 금속 기지 분말 내부에 기지 금속의 산화물보다 깁스 자유 에너지 (Gibbs free energy)가 더 큰 산화물 나노 입자가 분산되어 있는 복합 분말을 준비하는 단계와, 상기 복합 분말에 대' 해 열처리를 하여, 상기 기지 금속의 원자들과 상기 산화물 나노입자의 원자들이 상호 확산 하도록 하여, 상기 산화물 나노입자에서 비롯되는 산소원자를 상기 금속 기지 내부로 확산 및 분산시키는 단계와, 상기 복합 분말을 열간 성형 공정을 이용하여 벌크 가공재를 제조하 거나, 상기 복합 분말을 금속 모재 용탕에 투입한 후 교반하여 주조재를 제조하는 단계를 포함하는 것을 특징으로 한다. 본 발명의 다른 양태에 따라 금속 기지 복합재가 제공된다. 상기 복합재는 산화물 나노 입자가 금속 기지 내부에 분산되어 있는 복합체와, 모재 금속을 포함하고, 상기 산화물 나노 입자는 상기 기지 금속의 산화물보다 큰 깁스 자유 에너지를 갖고 있으며, 상기 복합 체에서 상기 나노 입자와 기지 금속 사이에 계면층이 형성되어, 상기 계면층을 매개로 상기 나노 입자와 기지 금속이 결합되어 있고, 상기 기지 금속 중에는 상기 산화물 나노입자에서 비롯된 산소 원자들이 분산되어 있는 것을 특징으로 한다. 한 가지 실시예에 있어서, 상기 복합재는 상기 복합체를 상기 모재 금속의 용탕에 투입한 후 교반하여 제조된 주조재일 수 있다. 본 발명의 다른 실시예에 따라 금속 기지 복합재는 산화물 나노 입자가 금속 기지 내부에 분산되어 있는 복합체를 포함하고, 상기 산화물 나노 입자는 상기 기지 금속의 산하 물보다 큰 깁스 자유 에너지를 갖고 있으며, 상기 복합체의 기지 금속 중에는 상기 산화물 나노입자에서 비롯된 산소 원자들이 분산되어 있는 것을 특징으로 한다. 한 가지 실시예에 있어서, 상기 복합재는 상기 복합체를 열간 성형 공정을 이용하여 제조한 벌크 가공재일 수 있다. 본 발명의 다른 실시예에 따라 제공되는 마그네슘 기지 복합재에서 마그네슘 산화 물보다 큰 깁스 자유 에너지를 갖는 산화물 나노 입자가 마그네슘 기지 내부로 삽입되어 있 고, 상기 마그네슘 기지 중에는 상기 산화물 나노입자에서 비롯된 산소 원자들이 분산되어 있는 것을 특징으로 한다. 한 가지 실시예에 있어서, 상기 산화물 나노 입자는 티타니아 (Ti02)일 수 있다.
【유리한 효과】
본 발명의 제조방법에 따르면, 나노크기의 산화물 입자가 균일하게 분산된 재료를 소정의 온도 및 시간 동안 열처리 해즘으로써 산화물 나노입자의 산소 원자들이 계면에서 확산하여 금속기지 내부로 분산된다. 본 발명에 따라 금속기지에 산소 원자들이 확산, 분산
될 경우 내부식성이 획기적으로 향상 될 뿐만 아니라, 분산되는 정도를 손쉽게 제어하여 우 수한 기계적 특성을 동시에 구현할 수 있다.
【도면의 간단한 설명】
도 1은 본 발명의 한 가지 실시예에 따른 제조 방법에 있어서, 복합 분말을 열간 성 형을 통해 일체화하여 벌크 가공재를 제조하는 공정을 간략하게 도식화한 그림이다.
도 2는 본 발명의 한 가지 실시예에 따른 제조 방법에 있어서, 주조 공정의 다른 양 태를 간략하게 도식화한 그림이다.
도 3은 본 발명에 따른 제조 방법에 있어서, 기계적 밀링 과정 증 알루미늄 분말 내 부로 티타니아가 삽입, 분산되는 과정을 주사전자현미경으로 촬영한 사진이다.
도 4는 열간 성형을 통하여 복합 분말을 일체화 한 판재의 사진이다.
도 5는 본 발명에 따른 제조 방법에 있어서, 열간 성형을 통하여 복합 분말을 일체 화 한 후 열 에너지를 인가하였을 때 생성된 새로운 계면 층의 미세구조를 투과전자현미경 으로 촬영한 사진이다.
도 6은 본 발명에 따른 제조 방법에 있어세 복합 분말에 열 에너지를 인가하였을 때, 알루미늄 기지와 티타니아의 패턴을 통해 새로운 층이 생성된 것을 확인할 수 있는 투 과전자현미경 사진이다.
도 7은 본 발명에 따른 제조 방법에 있어서, 티타니아 나노 입자의 크기가 300나노 미터인 입자를 사용하였을 경우 열처리 공정 이후 알루미늄 기지와 티타니아 나노입자의 계 면에 계면 층이 생성되지 않은 것을 확인 할 수 있는 투과전자현미경 사진이다.
도 8은 본 발명의 제조 방법에 따라, 알루미늄 합금 (A1 5083)과 복합분말 (Al/Ti02) 을 용융 상태 (750°C)에서 교반, 주조한 복합재의 미세 구조를 촬영한 주사전자현미경 사진으 로세 Ti02 입자들이 알루미늄 합금 증에 고르게 분산되어 있음을 확인할 수 있다.
도 9는 본 발명에 따른 제조 방법에 있어서, 알루미늄 합금 (A1 5083)과 복합분말 (Al/Ti02)을 용융 상태 (750°C)에서 교반, 주조한 복합재를 5% 변형 시켰을 경우의 미세구조 를 투과전자현미경으로 촬영한 사진으로서, 티타니아 나노 입자를 하얀색 화살표를 통하여 나타내었다.
도 10은 본 발명에 따른 제조 방법으로 제조된 금속기지 복합재의 변형 거동을 개 략적으로 나타낸 그림이다.
도 11은 본 발명에 따른 제조 방법에 있어서, 알루미늄 합금 (A1 5083)과 복합분말 (AI/Ti02)을 용융 상태 (750°C)에서 교반, 주조한 복합재에서 나노 입자의 분을을 1 vol%에 서 5 vol% 까지 증가시키며 제조한 벌크재의 경도를 단순 주조한 알루미늄 합금 (A15083) 과 비교하여 나타낸 그래프이다.
도 12는 본 발명에 따른 제조 방법에 있어서, 알루미늄 합금 (A1 5083)과 복합분말 (Al/Ti02)을 용융 상태 (750 °C)에서 교반, 주조한 복합재에서 나노 입자의 분율이 3 vol% 포 함된 주조재를 압연하여 가공한 판재의 사진이다.
도 13은 본 발명의 변형예에 따라, 복합 분말을 금속 모재 용탕에 첨가하여 주조한 후 고온에서 열처리를 수행한 결과 금속 모재와 나노 입자 사이에 새로운 계면 층이 형성 된 것을 보여주는 투과전자현미경 사진이다.
도 14는 본 발명의 실시예 2의 제조 방법에 있어서, 500°C, 24시간 열처리한 Al/Ti02 금속재료에서 Ti02 나노 입자 주변을 라인 스캔 (Line scan)을 통하여 원소 구배를 측정한 사진이다.
도 15는 본 발명의 실시예 2에 따른 금속재료 제조방법에 적용 가능한 알루미늄 산 화입자 (A1203) 보다 자유에너지가 큰 산화물 나노 입자들과, 그 산화 입자들과 알루미늄 간 의 환원 반웅식을 나타낸 표이다.
도 16은 본 발명의 실시예 2에 따른 금속재료 제조방법에 있어서 알루미늄 산화입 자 (A1203)와 다른 산화 입자들의 온도에 따른 자유에너지를 나타낸 그래프이다.
도 17은 본 발명의 실시예 2에서, 알루미늄 기지 재료를 500°C에서 열처리 시 시간
에 따라 변하는 기계적 특성을 보여주는 그래프이다.
도 18은 본 발명의 실시예 2에 따른 알루미늄 기지 재료를 500°C에서 열처리 시 시 간에 따라 변하는 항복 강도 값을 보여주는 그래프이다.
도 19는 본 발명의 실시예 2에 따른 알루미늄 기지 재료를 500°C에서 열처리 시 시 간에 따라 변하는 부식 전위 값을 보여주는 그래프이다.
도 20은 본 발명의 실시예 2에 따른 알루미늄 기지 재료를 500°C에서 열처리 시 시 간에 따라 변하는 부식 전위와 순 알루미늄의 부식 전위의 차이를 보여주는 그래프이다. 도 21은 본 발명의 실시예 2에 따른 마그네슘 기지 재료를 400°C에서 열처리 시 시 간에 따라 변하는 경도 값을 보여주는 그래프이다.
도 22는 본 발명의 실시예 2에 따른 마그네슘 기지 재료를 40C C에서 열처리 시 시 간에 따라 변하는 부식 전위를 보여주는 그래프와 그 값을 나타낸 표이다.
도 23은 본 발명의 실시예 2에 따른 제조 방법에 있어서, 볼 밀링한 Al/Ti02 복합분 말을 A1용탕에 탐침하여 제조한 주조재를 500°C, 24시간 열처리한 후 Ti02 나노 입자 주변 을 라인 스캔 (Line scan)을 통하여 원소 구배를 측정한 사진이다.
【발명의 실시를 위한 최선의 형태】
이하에서는, 본 발명을 바람직한 실시예를 참조하여 더욱 구체적으로 설명한다. 이 하의 설명에 있어서, 당업계에서 널리 알려진 기술 둥에 대한 설명은 생략한다. 그러나 당업 자라면 이하의 실시예를 통해 본 발명의 특징적 구성 내지 그 효과를 쉽게 이해할 수 있을 것이고, 또 특별한 어려움 없이 본 발명을 구현할 수 있을 것이다.
A. 실시예 1
1. 기계적 밀링 공정을 이용하여 나노 입자가 분산된 복합 분말 제조
도 1에는 본 발명의 한 가지 실시예에 따라 금속기지 복합재를 제조하는 과정이 순 서도의 형태로 도시되어 있다. 본 발명자는 알루미늄과 티타니아 (TK)2, 20nm)를 각각 금속기지, 나노 입자로 선정 하여, 이하의 과정에 따라 복합재를 제조하고 그 특성을 평가하였다 한편, 본 발명에서 금속기지 재료는 후술하는 바와 같이, 나노 입자의 원활한 삽입 을 위해 일반적으로 탄성 및 소성 변형이 가능한 재료인 것이 바람직한데, 예컨대 알루미늄, 구리, 철, 티타늄 둥의 순금속 또는 이증 선택된 하나 이상을 기지로 하는 소성 변형이 가능 한 합금인 것이 특히 바람직하다. 한편, 나노입자의 금속 기지 내부로의 분산을 위해, 기계 적 밀링법을 예시하지만, 본 발명은 이에 제한되지 않는다는 것에 유의하여야 한다ᅳ 즉 나 노입자를 금속 기지 내부에 분산시킬 수 있다면, 그 방법과 관련하여 특별히 제한되지 않는 다. 먼제 본 발명자는 일반적 볼밀링 (planetary ball milling) 법을 통하여 금속 기지 분 말 내부로 나노 입자를 물리적으로 삽입, 분산시키는 방법을 선택하였다. 즉 스테인리스 용 기 내에 알루미늄 분말 대 티타니아를 10%의 부피 분율로 혼합하였다. 다음에 상기 혼합 재료가 들어 있는 용기에 혼합 분말 무게 (약 50g)의 15배에 해당하는 지름 5 mm 크기의 스테인리스 볼 (약 750 g)을 추가한 후, 3시간 동안 200 rpm의 속도로 용기를 회전시켜 물리 적 에너지, 즉 운동 에너지를 인가하였다. 이때, 용기 내의 분위기를 아르곤 가스로 유지하 여 금속 분말의 산화를 방지하였으며 분말 오염을 방지하고 분말의 콜드웰딩 (cold-welding) 현상을 증가시켜주기 위하여 공정제어제 (process control agent)는 첨가하지 않았다. 공정 후 체를 이용하여 분말과 볼을 분리하여 흔합 분말을 수거하였다. 공정 후 티타니아 나노 입자가 알루미늄 분말 내부로 삽입된 것을 관찰할 수 있었
는데, 이를 도 3에 나타내었다. 즉, 도 3(a)에서는 밀링 시간이 충분하게 주어지지 않아 분 말 표면에 잔류하는 티타니아 입자를 볼 수 있으나 밀링 시간이 충분하게 주어진 경우 (도 3(b)) 티타니아 나노 입자는 분말 내부로 완전히 삽입되어 더 이상 표면에 존재하지 않는 것을 확인할 수 있다. 구체적으로 본 발명의 한 가지 실시예에 따르면, 실험적으로 정해지는 조건하에서 스테인레스 볼에 의해 주어지는 충격 에너지로 인한 소성변형이 가능한 기지금속 분말의 지 속적인 소성변형, 콜드웰딩, 파쇄의 과정을 통해 나노 입자는 기지금속 분말 내부로 점차 삽 입 분산된다. 한편, 본 발명의 실시예에 있어서, 볼밀링 또는 핸드밀링법에서 사용되는 기계적 에 너지는 금속 기지의 종류 및 미세구조에 따라 달라질 수 있으며, 밀링 매체의 종류 /크기 /무 게, 밀링 속도, 밀링 용기의 크기 등에 의해 제어될 수 있다.
2. 복합 분말 일체화를 통한 금속기지 복합재 제조
(1) 컴팩트 성형체 제조
본 발명자는 상기한 것과 같은 공정을 통해, 금속기지 중에 Ti02 나노입자를 균일 하게 분산시킬 수 있다는 것올 확인하고, 이러한 공정을 통해 제조한 복합 분말을 이용하여 최종 복합재를 보다 단순화된 공정을 통해 제조하였다. 즉 본 발명자는 분말에 일차적으로 압력만을 인가하거나 혹은 분말이 손상되지 않 는 범위의 온도, 즉 분말이 산화되지 않는 범위의 온도에서 압력을 가하여 중간체 (컴팩트 성형체)를 제조하고, 상기 중간체를 열간 가공하여 최종 벌크재를 제조하였다. 구체적으로, 본 발명자는 전술한 밀링 공정에서 제조한 알루미늄ᅳ Ti02 복합 분말에 압력을 가하여 중간체를 제조하는 방법으로서 상온가압법을 채용하였다. 복합 분말을 구리 류브에 장입한 후 500 MPa의 압력을 가하여 증간체를 제조하였으며, 상기 과정에 따라 제 조된 중간체를 열간 가공하기 위하여 480°C에서 열간 압연하였으며, 12%의 압하율로 27회 압연을 실시하여 최종 판재의 두께는 초기 중간체의 두께에 비해 97% 감소하였다. 한편, 이러한 열간 성형 공정으로서, 열간 압연뿐만 아니라, 열간 압출, hot pressing 등 열과 압력 을 가하여 분말을 일체화하는 등 다양한 열간 성형 공정이 이용될 수 있다. 상기 과정을 통해 제조한 판재를 도 4에 나타내었다.
(2) 열처리를 통한 새로운 계면 층이 형성된 금속기지 복합재 제조
본 발명자는 상기한 과정에 따라 제조한 알루미늄ᅳ Ti02 복합재에 대해 약 500°C (0.8Tm, Tm: 알루미늄의 융점)의 온도에서 열처리를 수행하였다. 그 결과 나노 입자가 기 지금속과의 계면에서 확산하여 새로운 층을 형성한다는 것을 발견하였다. 즉 상기 복합재를 진공 분위기에서 500°C에서 5시간 동안 열처리 하였는데, 그 결과 놀람게도 나노 입자와 기 지 금속 사이에 새로운 층이 생성된 것을 발견하였으며, 이를 도 5 및 도 6에 나타내었다. 특히 도 6에 나타낸 바와 같이, 알루미늄 기지 패턴과 티나이아 패턴을 통해, 그 사이에 새 로운 영역이 형성되었다는 것을 확인할 수 있다. 즉 티타니아 나노 입자가 알루미늄 기지 금속과의 계면에서 확산하여, 티타니아 혹은 알루미늄과는 다른 새로운 층을 형성하는 것으 로 보인다. 일반적으로 알려진 바와 같이, 입자의 크기가 작을수록 입자 표면의 자유 에너 지는 증가한다. 이는 표면의 화학 포텐설로 설명될 수 있으며, Gibbs-Thomson 식으로 표 현된다. 즉
U(r) μ(∞) = 2ΚΩ/Γ
상기 식에서, (r)과 μ(∞)는 입자 반지름이 r인 경우와 표면이 평평할 경우, 각각의
화학 포텐셜 값이며, K는 표면 자유 에너지, Ω는 원자 부피를 의미한다. 화학 포텐셜이 입 자 반지름에 반비례하므로, 입자의 크기가 작아질수록 화학 포텐셜이 증가함을 알 수 있으 며, 이는 자유 에너지가 매우 높은 상태를 의미한다.
100 nm 이하의 나노 입자의 경우 표면 자유 에너지가 매우 높은 상태이므로 확산 을 위한 에너지 배리어 (energy barrier)가 매우 낮아진 상태이다. 또한, 티타니아보다 알루 미늄 산화물의 깁스 자유 에너지 (Gibbs free energy)가 낮기 때문에, 적절한 열 에너지가 인 가될 경우 계면에서 원자들이 단범위 확산을 하여 새로운 층을 형성하는 것으로 보인다. 반면, 100 nm 보다 큰 입자의 경우 에너지 배리어가 층분히 낮아지지 못하여 열 에너지가 인가되어도 계면에서 확산을 하지 못하였으며, 이를 도 7에 나타내었다. 도 7의 티타니아 나노입자는 그 크기가 약 300 nm 이었으며, 상기한 방법과 동일한 과정에 따라 제조하였다. 도 7의 사진을 통해 알 수 있는 바와 같이, 알루미늄과 티타니아의 계면은 선명하게 나타나 며, 다른 새로운 영역이 생성된 것은 확인할 수 없다. 따라서, 본 발명에 따른 제조 방법에 서는 에너지 배리어와 관련하여, 나노입자는 그 크기가 약 100 nm 이하의 것을 사용하는 것이 바람직하다. 한편, 100 nm 이하의 나노입자들이 기지 금속과 계면 층을 형성하는 경 우, 기지 금속과 나노 입자간의 열팽창 계수가 다르기 때문에 웅력이 집증되며, 후술하는 바 와 같이, 재료에 힘이 가해질 경우 계면을 형성하고 있는 나노 입자로부터 전위가 생성되어 전파되에 기계적 특성의 향상에 기여하는 것으로 보인다. 한편, 상기 열처리는 알루미늄과 티타니아 나노 입자들이 단범위 확산을 할 수 있지 만 금속간 화합물 (intermetallic compound)은 생성하지 않는 온도 범위, 바람직하게는 0.5~lTm (금속 기지 융점)의 온도에서 수행하는 것이 바람직하다. 0.5Tm 미만인 경우, 단범 위 확산을 하기에 층분한 구동력이 제공되지 않으며, lTm보다 높은 경우 금속간 화합물이 형성될 수 있으며, 상기 온도 범위에서 열처리를 수행하는 것이 바람직하다. 다시 말하면, 알루미늄 Ti02 복합재에 대해 500°C의 온도에서 5시간 열처리를 수행한 것은 하나의 예시 적인 열처리 조건에 불과하며, 본 발명이 상기 실시예의 열처리 조건에 제한되지 않는다는 것을 이해하여야 한다. 한편, 상기 실시예에서는 벌크 가공재에 대해 열처리를 하여 새로운 계면 층을 형성 하였으나, 나노 입자가 금속 기지 분말에 삽입된 복합 분말에 대해 열처리를 하여, 나노 입 자와 기지 금속 사이에 새로운 계면 층이 형성된 복합 분말을 이용하여, 열간 성형 공정을 통해 벌크 가공재를 제조할 수도 있으며, 이 역시 본 발명의 범위 내에 속하는 것이다.
3. 나노 입자가 분산된 금속기지 복합재 (주조재) 제조
도 2에는 본 발명의 다른 실시예에 따라 금속기지 복합재를 제조하는 과정이 도시 되어 있는데, 이 실시예는 도 1의 실시예와 달리 주조의 과정을 통해 복합재를 제조하는 것 과 관련된 것으로서, 다음과 같이 두 가지 양태로 구분될 수 있다.
(1) 복합 분말의 새로운 층 형성 후 주조를 통한 금속기지 복합재 제조
본 발명자는 상기한 실시예와 관련하여 설명한 새로운 층 형성 방법과 상기 층이 생성됨에 따라 나타나는 특성을 바탕으로, 이를 주조 공정에 웅용하였다. 다시 말하면, 본 실시예는 금속기지 복합재를 제조하는 방법과 관련하여, 열처리 과정을 통해 새로운 층을 형성시킨 복합 분말을 모재 금속의 용탕에 탐침하는 방법으로 금속기지 복합재를 제조하는 방법을 제시한다. 본 발명자는 금속기지 복합재의 제조시 액상법에서 나노 입자가 용해 시 ¾석 및 응집되는 문제를 해결하기 위하여, 고상법과 액상법을 흔합 적용하였다. 즉 상기 실시예에
따라 제조된 알루미늄— ΉΟ2 복합 분말을 xrc에서 5시간 동안 열처리하였으며, 이에 따라 벌크재에 대해 열처리를 수행한 것과 마찬가지로 새로운 층이 형성되었으며, 이와 같이 층 이 형성된 복합 분말을 주조 공정에 이용하였다. 구체적으로, 본 발명자는 알루미늄 합금 모재 (A1 5083)를 전기 용해로를 이용하여 용해한 후 용탕 내부로 상기 과정에 따라 제조한 복합 분말 (Al/Ti02)을 5 vol%의 비율로 첨가하였다. 복합 분말을 첨가하는 온도는 모재가 완전히 용해된 약 750°C 이었으며, 복합 분말을 첨가함과 동시에 교반을 실시하였다. 이때 상기 교반 수단은 터빈형 임펠러를 사용 하였고, 교반 속도는 500 rpm 이었으며, 당업계에 이미 널리 알려진 용해로 및 교반장치를 이용하였다. 한편, 교반 속도는 기지금속 도가니의 크기와 용탕의 점도, 임펠러의 모양에 따라 100 rpm~1000 rpm으로 실험적으로 결정될 수 있다. 복합 분말 첨가시 도가니 주변 은 아르곤 분위기로 유지하여 복합 분말 및 용탕이 산화되는 것을 방지하였다. 상기 복합 분말을 첨가하는 온도, 즉 주조 공정을 수행하는 온도는 모재 금속의 종류에 따라 다르게 할 수 있다. 예컨대, 상기 알루미늄 합금의 경우 반용융 상태 구간이 있으며, 그 온도 구간 에서 복합 분말을 첨가할 수도 있다. 한편, 상기한 바와 같이, 복합 분말은 기계적 밀링 공정을 통해 분말 내부로 나노 입자가 삽입되어 있고 더욱이 열처리 공정을 통하여 금속 기지 분말과 나노입자 사이에 새 로운 층이 형성되어 있으므로, 용탕에 복합 분말 첨가시, 고온 용탕과의 직접적인 접촉을 지 연시킬 수 있으며, 상기 새로운 층으로 인해 모재 금속과 나노 입자가 단단하게 결합되어 젖음성이 향상되어, 이에 따라 후속되는 스터 캐스팅 시에 용융 금속 내에서 나노 입자가 편석이나 응집 현상 없이 균일하게 분산될 수 있다. 구체적으로, 도 8은 상기한 과정에 따라, 알루미늄 합금 (A1 5083)과 복합분말 (Al/Ti02)을 용융 상태 (750°C)에서 교반, 주조한 복합재의 미세 구조를 촬영한 현미경 사진 으로 Ti02 입자들이 알루미늄 합금 중에 고르게 분산되어 있음을 확인할 수 있다. 한편, 도 9는 상기 용해법으로 제조한 벌크 주조재를 5% 변형시킨 후 미세구조를 주사전자현미경 을 이용하여 관찰한 사진으로서, 티타니아 나노 입자를 하얀색 화살표로 나타내었다. 나노 입자와 모재 사이의 층에서 전위가 생성되어 전파되는 것을 확인할 수 있는데, 이는 본 발 명에 따른 복합재의 기계적 특성을 향상시키는 요인으로 작용한다. 구체적으로, 도 10은 본 발명에 따른 제조 방법으로 제조된 금속기지 복합재의 변형 거동을 개략적으로 나타낸 그림 이다. 상기한 바와 같이, 본 발명에 따르면, 나노 입자와 금속 기지 사이에 새로운 층이 형 성되고, 이 층에 웅력이 집중되어 전위가 생성되고, 그 층으로부터 생성된 전위가 전파되어 간다. 따라서, 전위가 생성될 수 있는 소스가 많아지고, 입자로부터 전위가 전파되어 나가 기 때문에, 변형능을 개선할 수가 있다. 도 11은 상기 용해법으로 나노 입자의 분율을 1 vol%에서 5 vol% 까지 증가시키며 제조한 벌크재의 경도를 단순 주조한 알루미늄 합금 (A15083)과 비교하여 나타낸 그래프이 다. 단순 주조 알루미늄 합금의 경도 (σ0)보다 본 발명에 따라 제조한 벌크재의 경도가 더 큼 을 알 수 있으며 (도 12의 y축 참조), 또한 티타니아의 분율이 높아짐에 따라 복합재의 강도 가 증가함을 알 수 있다. 본 발명자는 상기 실시예를 통해 제조된 복합재 증 나노 입자의 분율이 3 vol%인 복합재를 열간 압연 공정을 통해 판재로 가공하였으며, 그 판재의 사진을 도 12에 나타내었 다. 이는 주조 공정을 통해 제조한 복합재를 압연, 압출과 같은 후가공을 통해 자유롭게 가 공하여 웅용할 수 있다는 것을 보여주는 것으로서, 산업적 이용가능성이 매우 크다는 것을 의미한다.
한편, 상기 실시예에서는 주조 공정 전에만 열처리를 통해 계면을 형성해 주었으나, 도 2에 도시한 바와 같이 주조 공정 후 얻어지는 주조재 혹은 가공재에 대하여 목표로 하는 요구 특성에 맞추어 추가적인 계면 층 형성을 위한 열처리 공정을 선택적으로 적용할 수도 있으며, 이 역시 본 발명의 범위 내에 속하는 것이다.
(2) 복합 분말을 이용한 주조 공정 후 새로운 층 형성을 통한 금속기지 복합재 제조 상기 실시예에서는 주조 공정 전에 복합 분말을 열처리하여 새로운 층을 형성하였 다. 이와 관련하여, 본 발명자는 상기한 과정에 따라 형성한 복합 분말에 대해 열처리를 수 행하지 않고 그 복합 분말을 금속 모재의 용탕에 투입한 후, 급속 교반을 실시하여 주조하 였다. 이어서, 얻어진 복합재에 대해 열처리를 수행하였다. 이때, 열처리 온도는 대략 50 0°C(0.5~lTm)에서 수행하였다. 그 결과, 도 13의 전자현미경 사진으로 나타낸 바와 같이, 상기한 실시예와 마찬가지로, 금속기지와 나노입자 사이에 새로운 층이 형성된 것을 확인할 수 있다. 본 실시예에서는 주조 공정에 있어서, 아직 새로운 층이 형성되지 않은 복합 분말을 이용하기 때문에, 기지금속과 나노 입자 간의 계면 결합력이 약해 주조 공정 중에 편석 및 부유 현상이 일어날 수 있으므로, 급속 교반을 실시하여 주조하였다. 급속 교반 장치는 그 라파이트 실린더 내부에 스크류를 장착하여 용해 중 스크류 회전을 통해 교반력을 극대화할 수 있도록 설계, 제작하였다. 본 실시예에서도 상기 실시예와 마찬가지로 열처리한 주조재를 가공한 후 가공재에 있어서 목표로 하는 요구 특성에 맞추어 추가적인 층 형성을 위한 열처리 공정을 선택적으 로 적용할 수도 있으며, 이 역시 본 발명의 범위 내에 속하는 것이다. 이와 같이, 본 발명에 따라서 복합 분말을 열처리하거나, 그렇지 않은 경우 최종 주 조 복합재에 대해 나노입자의 확산이 가능할 정도의 은도에서 열처리를 수행한다면, 금속 기지와 나노 입자 사이에 새로운 층을 형성할 수 있다는 것을 확인할 수 있으며, 이러한 기 술적 사상을 다양하게 확대할 수 있다.
B. 실시예 2
상기 실시예 1에서 설명한 바와 같이, 금속 기지와 산화물 나노입자 사이에 새로운 층이 형성되어, 기계적 특성이 향상되었다. 본 발명자는 상기 실시예 1과 실질적으로 실질 상 동일한 과정에 따라 제조한 복합재에 대해 추가 열처리를 수행하였으며, 그 결과 예기치 못한 놀라운 결과가 발견되었으며, 이 발견이 본 발명의 중요한 기술적 사상을 구성한다. 이하에서는 이 실시예에 대해 구체적으로 설명한다.
1. 기계적 밀링 공정을 이용하여 산화물 나노 입자가 분산된 복합 분말 제조 실시예 2에서도, 실시예 1과 실질상 동일한 프로세스를 이용하여 복합 분말을 제조 하였다. 구체적으로, 본 발명자는 일반적 볼밀링 (attrition ball milling) 법을 통하여 금속 기지 분말 내부로 나노 산화물 입자를 물리적으로 삽입, 분산시키는 방법을 선택하였다. 즉 스테인리스 용기 내에 알루미늄 분말 대 티타니아를 3%의 부피 분율로 혼합하였다. 다음 에 상기 혼합 재료가 들어 있는 용기에 혼합 분말 무게 (약 100g)의 15배에 해당하는 지름 5 mm 크기의 스테인리스 볼 (약 1500 g)을 추가한 후, 6시간 동안 500 rpm의 속도로 블레이 드를 회전시켜 용기 내 물질들이 충돌할 수 있도록 에너지를 가하였다. 기타의 과정은 실 시예 1과 동일하므로, 그 설명은 생략한다.
2. 복합 분말 일체화를 통한 금속기지 복합재 제조
(1) 컴팩트 성형체 제조
실시예 1과 동일한 과정에 따라 상기 제조한 복합 분말을 일체화하여, 컴팩트 성형 체를 제조하고, 이를 열간 가공하여 최종 벌크재를 제조하였다. 기타 실시예 1에서 설명한 기술적 구성이 본 실시예에 적용되므로, 그 증복되는 설명은 생략한다.
(2) 열처리를 통해 산소 원자가 확산 /분산된 금속기지 복합재 제조
상기 제조한 알루미늄 -Ti02 복합재에 대해 약 500°C(0.8Tm, Tm: 알루미늄의 융점) 의 은도에서 열처리를 수행하였다. 그 결과 나노 입자가 기지금속과의 계면에서 확산하여 새로운 층을 형성하였으며, 이는 실시예 1과 마찬가지이다. 그러나, 본 실시예에서는 실시 예 1과 달리, 실시예 1과 실질상 동일한 조건에서 9시간 내지 24시간의 열처리, 즉 열처리 시간을 연장하여 수행하였는데, 그 결과 예상하지 못한 결과가 발견되었다. 즉 실시예 1(열 처리 시간: 대략 5시간)과 달리 열처리 시간이 증가함에 따라, 상기 층을 사이에 두고 산화 물 나노입자의 원자들과 금속기지의 원자들이 상호 확산하여, 상기 산화물 나노입자로부터 비롯되는 산소 원자들이 금속기지 내부로 확산되었으며, 또한 상기 층은 층이라고 부르기에 는 명확히 구분되지 않았다. 구체적으로, 상기 복합재를 일반 노 (furnace)에서 500 °C의 은도에서 대략 9시간 내지 최대 24시간까지 열처리를 하였는데, 그 결과 놀람게도 나노 산화물 입자의 형태가 변화하 여 산화물 나노입자의 산소 원자들이 분리되어, 알루미늄 기지의 원자들과의 상호 확산을 통해 알루미늄 기지 내부로 확산해 가는 것이 발견되었으며, 그 결과 실시예 1의 명확한 층 대신에 산화물 나노입자와 기지 금속 사이에 소정의 확산 영역 (diffused area)이 형성되었으 며, 이를 도 14에 나타내었다. 도 14에 나타낸 바와 같이, 산화물 나노입자 주변을 STEM 을 이용하여 라인 스캔 (Line scan)해본 결과 입자 주변으로부터 산소 원자들이 확산되었다 는 것을 확인할 수 있었다. 즉 실시예 1의 명확한 새로운 층은 거의 사라지고, 대신에 상기 층을 사이에 두고 산화물 나노입자의 원자와 기지 금속의 원자가 상호 확산하여, 소정의 확 산 영역을 형성한 것으로 보인다. 이때, 산화물 나노입자와 기지 금속과 명확히 구별되는 층은 사라지고, 대신에 산화물 나노입자의 원자와 기지 금속의 원자가 상호 확산하고, 산화 물 나노입자에서 비롯되는 산소원자들이 기지 금속 중으로 확산하여, 소정의 영역을 형성한 것으로 보이며, 이를 본 발명에서는 층 대신에 확산 영역이라 지칭하기로 한다. 실시예 1에서 새로운 층 형성과 관련하여 설명한 바와 같이, 입자의 크기가 작을수 록 입자 표면의 자유 에너지는 증가하며, 따라서 100 nm 이하의 나노 산화물 입자의 경우 표면 자유 에너지가 매우 높은 상태이므로 확산을 위한 에너지 배리어가 매우 낮아진 상태 이다. 또한, 티타니아보다 알루미늄 산화물의 깁스 자유 에너지가 낮기 때문에, 열역학적으 로 환원 반응이 일어날 것임을 예상할 수 있다. 이와 같은 환원 반웅이 완벽하게 일어난다 고 가정할 경우 이 반웅식은 다음과 같이 표현할 수 있다.
3Ti02 + 4A1→ 3Ti + 2A1203 그러나, 투과전자현미경을 통한 관찰 결과 이와 같은 완전한 반응이 일어나지 않았 다는 것을 확인할 수 있었다. 즉, 열 에너지가 충분하지 않기 때문에 완전한 환원 반웅이 일 어나지 않고 산소 원자들이 티타니아에서 분리되어, 알루미늄 기지의 금속 원자와의 상호 확산을 통해 알루미늄 기재 내로 단범위 확산을 통해 분산되어 가는 것으로 판단된다. 이 와 같은 단범위 확산은 입자 크기가 100 nm 보다 클 경우 에너지 배리어가 충분히 낮아지 지 못하여 열 에너지가 인가되어도 계면에서 확산을 하지 못하는 것으로 보인다. 따라서, 본 발명에 따른 제조 방법에서는 에너지 배리어와 관련하여, 실시예 1과 마찬가지로, 산화물 나노 입자는 그 크기가 약 100 nm 이하의 것을 사용하는 것이 바람직하다. 한편, 본 실시 예에서는 티타니아 나노 산화물 입자를 사용하였으나, 도 15 및 도 16에 나타낸 바와 같이
알루미늄과의 환원 반웅이 열역학적으로 가능한 : 즉 알루미늄 산화물보다 깁스 자유 에너지 가 더 큰 모든 산화물 나노입자가 사용될 수도 있으며, 이들은 모두 본 발명의 범위 내에 속한다. 한편, 상기 열처리는 알루미늄과 티타니아 나노 산화물 입자들이 단범위 확산을 할 수 있지만 금속간 화합물은 생성하지 않는 은도 범위, 바람직하게는 0.5~lTm (금속 기지 융 점)의 온도에서 수행하는 것이 바람직하다. 0.5Tm 미만인 경우, 단범위 확산을 하기에 충 분한 구동력이 제공되지 않으며, lTm보다 높은 경우 금속간 화합물이 형성될 수 있으며, 상기 온도 범위에서 열처리를 수행하는 것이 바람직하다ᅳ 다시 말하면, 실시예 1과 마찬가 지로, 알루미늄 -Ti02 복합재에 대해 500 °C의 온도에서 열처리를 수행한 것은 하나의 예시적 인 열처리 조건에 불과하며, 본 발명이 상기 실시예의 열처리 조건에 제한되지 않는다는 것 을 이해하여야 한다.
3. 산소 원자 확산 정도에 따른 금속기지 복합재의 특성 평가
본 발명자는 상기와 같이 제조한 알루미늄 기지 재료의 기계적 특성에 대해 실험을 하였으며, 그 결과를 도 Γ7 및 도 18에 나타내었다. 도 17은 상기 과정에 따라 제조한 금속재료를 500°C의 온도에서 유지한 후 유지 시 간에 따라 인장 시험을 실시한 결과를 나타낸 그래프이다. 초기 250°C에서 2시간 열처리 한 경우쎄는 열에너지가 층분하지 않아 알루미늄 기지와 티타니아 나노 산화물 입자 사이의 계 면에서 단범위 확산이 일어나지 않아 결합력이 약하기 때문에 연신률이 작은 것을 확인할 수 있다. 하지만 500°C에서 열처리를 할 경우 기지금속과 산화물 나노입자 사이의 계면에서 단범위 확산이 진행되고 이로 인해 결합력이 강해지며, 결과적으로 연신률이 크게 증가된 것을 그래프를 통해 확인할 수 있다. 또한, 열처리 시간이 6시간 까지 증가함에 따라 전술 한 현상이 계속적으로 진행되어 강도 및 연신률 모두 증가하는 결과를 얻을 수 있었다. 도 18은 상기 금속재료의 열처리 시간 별 항복 강도 값을 그래프로 나타낸 것으로 9시간의 열처리 시간 동안 계속적으로 항복 강도가 증가하는 것을 확인할 수 있으며, 9시간 이상의 열처리를 할 경우 항복 강도가 약간 감소하였지만, 여전히 우수한 기계적 특성을 나 타내는 것을 확인할 수 있다ᅳ 또한, 본 발명자는 상기 기계적 특성 외에 산소 원자 확산에 따른 내부식 특성에 대 해 실험을 하였으며, 그 결과를 도 19 및 도 20에 나타내었다. 도 19 및 도 20으로부터 확 인할 수 있듯이, 3 vol%의 티타니아 나노 산화물 입자를 첨가해 준 것 만으로도 순 알루미 늄에 비하여 획기적으로 향상된 내부식 특성을 나타내었고, 또한 열처리를 통하여 산소 원 자를 확산시켜줌에 따라 내부식 특성이 더욱 향상되는 것을 확인하였다.
• 본 발명자는 기지금속이 알루미늄 이외의 다른 금속기지일 경우에도 전술한 바와 같이 산소 원자가 확산 가능하고 이에 따라 내부식성 등의 향상이 이루어질 수 있다는 것을 증명하기 위하여, 부식에 대해 취약한 마그네슘을 기지 금속으로 선정하여 상기 제시된 금 속재료 제조 방법에 따라 재료를 제조하고 특성을 평가하였다. 볼밀링 속도, 분말 일체화 온 도 그리고 열처리 은도 등은 상기 알루미늄 금속재료의 제조 공정과 약간 차이가 있으며, 이는 마그네슘에 적합한 공정 변수들을 선택하였기 때문이다. 먼저, 알루미늄의 경우와 마찬가지로 일반적 볼밀링 (attrition ball milling) 법을 사용 하였으며, 마그네슘 분말 대 티타니아 나노 산화물 입자를 5%의 부피 분율로 혼합하였다. 다음에 상기 혼합 재료가 들어 있는 용기에 혼합 분말 무게 (약 100g)의 15배에 해당하는 지
름 5 mm크기의 스테인리스 볼 (약 1500 g)을 추가한 후, 6시간 동안 300 rpm의 속도로 블 레이드를 회전시켜 용기 내 물질들이 충돌할 수 있도록 에너지를 가하였다. 이외의 조건은 실시예 2의 알루미늄 기지 복합재를 제조할 때와 동일하며, 복합 분말 제조 후 분말 일체화 의 과정에서 열간 압연 공정의 온도는 40CTC이었다. 도 16에서 확인할 수 있는 바와 같이, 산화 마그네슘 (MgO)의 경우에도 산화 알루미 늄 (A1203)의 경우와 마찬가지로 티타니아 (Ti02) 보다 낮은 깁스 자유 에너지를 가지기 때문 에 적절한 열에너지 인가 시 마그네슘 기지와 티타니아 나노 산화물 의 원자들의 상호 확산 에 따른 산소 원자의 확산이 가능하다. 상기 제조한 마그네슘 기지 복합재의 기계적 특성에 대해 실험을 하였으며, 그 결과 를 도 21에 나타내었다.
도 21은 상기 과정에 따라 제조한 복합재를 40C C의 온도에서 유지하면서 열처리를 하여, 열처리 유지 시간에 따른 경도 변화를 나타낸 것이다. 초기 4시간까지는 결정립 성장 및 잔류 웅력의 해소 등 희복 (recovery) 현상에 의해 경도가 떨어지는 것을 확인할 수 있다. 그러나, 이 후의 열처리 동안에는 복합재의 경도가 열처리 시간이 증가함에 따라 향상되는 현상을 관찰할 수 있다. 또한, 본 발명자는 상기 마그네슘 기지 복합재의 내부식 특성에 대해 실험을 하였으 며, 그 결과를 도 22에 나타내었다. 도 22에서 확인할 수 있듯이, 알루미늄 기지 재료의 경 우와 마찬가지로 본 발명에 따라 열처리를 해준 결과 순 마그네슘의 내부식 특성에 비해 매 우 향상된 부식 전위 값을 나타내는 것을 알 수 있다. 따라서, 본 발명에 따라 마그네슘 기 지 복합재를 제조하는 경우, 마그네슘이 갖고 있는 단점, 즉 부식 취약성을 개선할 수 있어, 마그네슘의 활용 용도를 확장할 수 있다는 것을 예측할 수 있다. 한편, 상기 실시예에서는 복합 분말을 열간 성형을 통하여 일체화하여 금속재료를 제조하였으나, 실시예 1과 마찬가지로 복합 분말을 기지금속 용탕에 탐침한 후 교반하여 제 조되는 주조재 혹은 가공재에 대해서도 열처리를 통하여 산소 원자를 확산, 분산시켜 줄 수 있으며, 이를 도 23을 통해 확인할 수 있다. 또한, 실시예 1과 마찬가지로, 벌크 가공재 또는 주조재를 제조하기 전에, 복합 분말 에 대해 열처리를 수행하여, 원자들의 상호 확산을 통한 산소원자의 기지 금속 내부로의 확 산 및 분산이 일어나도록 할 수도 있으며, 이 역시 본 발명의 범위 내에 속하는 것이다. 이상 본 발명을 바람직한 실시예를 참조하여 설명하였지만, 본 발명은 상기한 실시 예에 제한되지 않는다는 것을 이해하여야 한다. 예컨대, 상기 실시예에서 티타니아 (Ti02)를 예로 들어 설명하였지만, 기지 금속의 산화물보다 Gibbs 자유 에너지가 크다면, 알루미나 (A Os), 실리카 (Si02), 징크옥사이드 (Zn02), 지르코니아 (Zr02), 틴옥사이드 (Sn02) 등의 산화 물 나노입자 역시 본 발명에 적용할 수 있으며, 이들 입자 역시 상기 본 발명에 따라 열에 너지 인가 시 (열처리) 기지 금속과의 계면에서 확산하여 새로운 층을 생성함과 아울러, 그 계면층을 통한 기지금속의 원자들과 산화물 나노입자의 원자들의 상호 확산을 통해, 산화물 나노입자에서 비롯되는 산소 원자들이 기지 금속 내로 확산되어 분산될 수 있다. 이와 같 이, 본 발명은 후술하는 특허청구범위 내에서 다양하게 변형 및 수정할 수 있으며, 이들은 모두 본 발명의 범위 내에 속한다. 따라서 본 발명은 특허청구범위 및 그 균등물에 의해서 만 제한된다ᅳ
Claims
【청구항 1】
산화물 나노 입자가 분산된 금속기지 복합재 제조 방법으로서,
금속 기지 분말 내부에 기지 금속의 산화물보다 깁스 자유 에너지 (Gibbs free energy)가 더 큰 산화물 나노 입자가 분산되어 있는 복합 분말을 준비하는 단계와,
상기 복합 분말을 열간 성형 공정을 이용하여 벌크 가공재를 제조하거나, 상기 복합 분말을 금속 모재 용탕에 투입한 후 급속 교반하여 주조재를 제조하는 단계와,
상기 벌크 가공재 또는 주조재에 대해 열처리를 하여, 상기 기지 금속의 원자들과 상기 산화물 나노입자의 원자들이 상호 확산하도록 하여, 상기 산화물 나노입자에서 비롯되 는 산소원자를 상기 금속 기지 내부로 확산 및 분산시키는 단계
를 포함하는 것을 특징으로 하는 금속기지 복합재 제조 방법ᅳ
【청구항 2】
청구항 1에 있어세 상기 산화물 나노 입자들은 상기 확산을 하기에 낮은 에너지 배 리어를 갖는 크기로 되어 있는 것을 특징으로 하는 금속기지 복합재 제조 방법.
【청구항 3】
청구항 2에 있어세 상기 나노 입자는 그 크기가 약 100 nm 이하인 것을 특징으로 하는 금속기지 복합재 제조 방법.
【청구항 4】
청구항 1 내지 청구항 3 중 어느 한 항에 있어서, 상기 열처리는 0.5~lTm(Tm: 금 속 기지 분말의 융점)의 온도에서 수행하는 것을 특징으로 하는 금속기지 복합재 제조 방
【청구항 5]
청구항 4에 있어서, 상기 금속 기지 분말은 알루미늄, 구리, 철, 티타늄 또는 마그네슘의 순금속 또는 이중 선택된 하나 이상을 기지로 하는 소성변형 가능한 합금인 것을 특징으로 하는 금속기지 복합재 제조 방법.
【청구항 6】
청구항 5에 있어서, 상기 산화물 나노 입자는 티타니아 (Ti02), 알루미나 (A1203), 실 리카 (Si02), 징크옥사이드 (Zn02), 지르코니아 (Zr02) 및 틴옥사이드 (Sn02)로부터 선택되는 산 화물 산화 나노입자인 것을 특징으로 하는 주조용 금속기지 복합재 제조 방법.
【청구항 7】
청구항 1 내지 청구항 3중 어느 한 항에 있어서, 상기 산소 원자들이 금속 기지 내부로 확산 및 분산됨에 따라 상기 복합재의 내부식성을 향상시키는 것을 특징으로 하는 금속기지 복합재 제조 방법.
【청구항 8】
나노 입자가 분산된 금속기지 복합재 제조 방법으로서,
금속 기지 분말 내부에 기지 금속의 산화물보다 깁스 자유 에너지 (Gibbs free energy)가 더 큰 산화물 나노 입자가 분산되어 있는 복합 분말을 준비하는 단계와,
상기 복합 분말에 대해 열처리를 하여, 상기 기지 금속의 원자들과 상기 산화물 나 노입자의 원자들이 상호 확산하도록 하여, 상기 산화물 나노입자에서 비롯되는 산소원자를 상기 금속 기지 내부로 확산 및 분산시키는 단계와,
상기 복합 분말을 열간 성형 공정을 이용하여 벌크 가공재를 제조하거나, 상기 복합 분말을 금속 모재 용탕에 투입한 후 교반하여 주조재를 제조하는 단계
를 포함하는 것을 특징으로 하는 금속기지 복합재 제조 방법.
【청구항 9】
청구항 8에 있어서, 상기 산화물 나노 입자들은 상기 확산을 하기에 낮은 에너지 배 리어를 갖는 크기로 되어 있는 것을 특징으로 하는 금속기지 복합재 제조 방법.
【청구항 10】
청구항 8에 있어서, 상기 나노 입자는 그 크기가 약 100 nm이하인 것을 특징으로 하는 금속기지 복합재 제조 방법.
【청구항 11】
청구항 8 내지 청구항 10 중 어느 한 항에 있어서, 상기 열처리는 0.5~lTm(Tm: 금 속 기지 분말의 점)의 온도에서 수행하는 것을 특징으로 하는 금속기지 복합재 제조 방 법
【청구항 12】
청구항 11에 있어서, 상기 금속 기지 분말은 알루미늄, 구리, 철, 티타늄 또는 마그네슘의 순금속 또는 이중 선택된 하나 이상을 기지로 하는 소성변형 가능한 합금인 것을 특징으로 하는 금속기지 복합재 제조 방법ᅳ
【청구항 13】
청구항 12에 있어서, 상기 산화물 나노 입자는 티타니아 (Ti02), 알루미나 (A1203), 실 리카 (Si02), 징크옥사이드 (Ζηθ2), 지르코니아 (Zr02) 및 틴옥사이드 (Sn02)로부터 선택되는 산 화물 산화 나노입자인 것을 특징으로 하는 주조용 금속기지 복합재 제초 방법.
【청구항 14】
금속 기지 복합재로서, 상기 복합재는 산화물 나노 입자가 금속 기지 내부에 분산되어 있는 복합체와, 모재 금속을 포함하고,
상기 산화물 나노 입자는 상기 기지 금속의 산화물보다 큰 깁스 자유 에너지를 갖 고 있으며,
상기 복합체의 기지 금속 증에는 상기 산화물 나노입자에서 비롯된 산소 원자들이 분산되어 있는 것을 특징으로 하는 금속 기지 복합재.
【청구항 15】
청구항 14에 있어서, 상기 복합재는 상기 복합체를 상기 모재 금속의 용탕에 투입한 후 교반하여 제조된 주조재인 것올 특징으로 하는 금속 기지 복합재.
【청구항 16】
금속 기지 복합재로서,
상기 복합재는 산화물 나노 입자가 금속 기지 내부에 분산되어 있는 복합체를 포함 하고,
상기 산화물 나노 입자는 상기 기지 금속의 산하물보다 큰 김스 자유 에너지를 갖 고 있으며,
상기 복합체의 기지 금속 중에는 상기 산화물 나노입자에서 비롯된 산소 원자들이 분산되어 있는 것을 특징으로 하는 금속 기지 복합재.
【청구항 17]
청구항 16에 있어세 상기 복합재는 상기 복합체를 열간 성형 공정을 이용하여 제조한 벌크 가공재인 것을 특징으로 하는 금속 기지 복합재.
【청구항 18】
마그네슘 기지 복합재로서,
상기 복합재에서 마그네슘 산화물보다 큰 깁스 자유 에너지를 갖는 산화물 나노 입 자가 마그네슘 기지 내부로 삽입되어 있고,
상기 마그네슘 기지 중에는 상기 산화물 나노입자에서 비롯된 산소 원자들이 분산 되어 있는 것을 특징으로 하는 마그네슘 기지 복합재.
【청구항 19]
청구항 18에 있어서, 상기 산화물 나노 입자는 티타니아 (Ti02)인 것을 특징으로 하는 마그네슘 기지 복합재.