WO2012121972A2 - Sheet wafer growth stabilization - Google Patents
Sheet wafer growth stabilization Download PDFInfo
- Publication number
- WO2012121972A2 WO2012121972A2 PCT/US2012/027280 US2012027280W WO2012121972A2 WO 2012121972 A2 WO2012121972 A2 WO 2012121972A2 US 2012027280 W US2012027280 W US 2012027280W WO 2012121972 A2 WO2012121972 A2 WO 2012121972A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- wafer
- channel
- sheet
- afterheater
- crucible
- Prior art date
Abstract
Description
Claims