WO2012077553A1 - ガスバリア性フィルム、ガスバリア性フィルムの製造方法及び電子デバイス - Google Patents
ガスバリア性フィルム、ガスバリア性フィルムの製造方法及び電子デバイス Download PDFInfo
- Publication number
- WO2012077553A1 WO2012077553A1 PCT/JP2011/077668 JP2011077668W WO2012077553A1 WO 2012077553 A1 WO2012077553 A1 WO 2012077553A1 JP 2011077668 W JP2011077668 W JP 2011077668W WO 2012077553 A1 WO2012077553 A1 WO 2012077553A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- barrier layer
- film
- gas
- group
- Prior art date
Abstract
Description
本発明のガスバリア性フィルムでは、基材の少なくとも一方の面側に、ガスバリア層ユニットを有する。
本発明においては、本発明のガスバリア性フィルムを構成する第1のバリア層が、化学蒸着法で形成されたことを特徴の1つとする。第1のバリア層の存在により、基材からの水分移行を妨げることができ、第2のバリア層を形成する際の改質処理が進行しやすくなる。
次に、大気圧プラズマ処理について好ましい形態を説明する。
V1≧IV>V2 または V1>IV≧V2
を満たし、第2の高周波電界の出力密度が、1W/cm2以上であることが好ましい。
本発明に係る第2のバリア層は、化学蒸着法で形成した第1のバリア層上に珪素化合物を含有する塗布液を用いて積層塗布した後、改質処理することによって形成される。
本発明に係る珪素化合物としては、珪素化合物を含有する塗布液の調製が可能であれば特に限定はされないが、成膜性、クラック等の欠陥が少ない事、残留有機物の少なさの点で、パーヒドロポリシラザン、オルガノポリシラザン等のポリシラザン;シルセスキオキサン等のポリシロキサン等が好ましい。
ポリシラザン含有の塗布液等により形成された珪素化合物を塗布して形成された塗膜(以下、単に珪素化合物塗膜とする)は、改質処理前または改質処理中に水分が除去されていることが好ましい。そのために、第2のバリア層の製造においては、珪素化合物塗膜中の有機溶媒の除去を目的とする第一工程と、それに続く珪素化合物塗膜中の水分の除去を目的とする第二工程とを含むことが好ましい。改質処理前または改質処理中に水分が除去されることによって、その後の改質処理の効率が向上する。
珪素化合物塗膜の含水率は、以下に示す分析方法に従って測定することができる。
装置:HP6890GC/HP5973MSD
オーブン:40℃(2min)、その後、10℃/minの速度で150℃まで昇温
カラム:DB-624(0.25mmid×30m)
注入口:230℃
検出器:SIM m/z=18
HS条件:190℃・30min
珪素化合物塗膜中の含水率は、上記の分析方法により得られる含水量(g)から、第2のバリア層の体積(L)で除した値として定義され、第二工程により水分が取り除かれた状態においては、好ましくは0.1%(g/L)以下であり、さらに好ましい含水率は、0.01%(g/L)以下(検出限界以下)である。
本発明における改質処理とは、珪素化合物の酸化ケイ素または酸化窒化珪素への転化反応を指し、具体的には本発明のガスバリア性フィルムが全体としてガスバリア性(水蒸気透過率が、1×10-3g/(m2・24h)以下)を発現するに貢献できるレベルの無機薄膜を形成する処理をいう。
本発明において、改質処理として用いることのできるプラズマ処理は、公知の方法を用いることができるが、好ましくは前述の大気圧プラズマ処理等をあげることが出来る。
珪素化合物を含有する塗膜を後述するエキシマ照射処理等と組み合わせて、加熱処理することで、前記改質処理を行うことが出来る。
本発明において、改質処理の方法の1つとして、紫外線照射による処理も好ましい。紫外線(紫外光と同義)によって生成されるオゾンや活性酸素原子は高い酸化能力を有しており、低温で高い緻密性と絶縁性を有する酸化ケイ素膜または酸化窒化珪素膜を形成することが可能である。
本発明において、最も好ましい改質処理方法は、真空紫外線照射による処理(エキシマ照射処理)である。真空紫外線照射による処理は、ポリシラザン化合物内の原子間結合力より大きい100~200nmの光エネルギーを用い、好ましくは100~180nmの波長の光エネルギーを用い、原子の結合を光量子プロセスと呼ばれる光子のみの作用により、直接切断しながら活性酸素やオゾンによる酸化反応を進行させることで、比較的低温(約200℃以下)で、酸化珪素膜の形成を行う方法である。なお、エキシマ照射処理を行う際は、上述したように熱処理を併用することが好ましく、その際の熱処理条件の詳細は上述したとおりである。
e+Xe→e+Xe*
Xe*+Xe+Xe→Xe2 *+Xe
となり、励起されたエキシマ分子であるXe2 *が基底状態に遷移するときに172nmのエキシマ光を発光する。
図1に示す如く本発明の好ましい態様においては、第2のバリア層4Aは基材2面側に低改質領域(非改質領域)を、また表層側に高改質領域(改質領域)を有するが、改質処理によって形成される改質領域は、様々な方法で確認することができる。改質処理後の第2のバリア層の断面を透過型電子顕微鏡(TEM)により観察することにより確認する方法が最も有効である。
ガスバリア性フィルムを、以下のFIB加工装置により薄片を作製した後、断面TEM観察を行う。このとき試料に電子線を照射し続けると、電子線ダメージを受ける部分とそうでない部分にコントラスト差が現れる。本発明に係る改質領域は、改質処理によって緻密化するために電子線ダメージを受けにくいが、非改質領域では電子線ダメージを受け変質が確認される。このようにして確認できた断面TEM観察により、改質領域と非改質領域の膜厚の算出が可能になる。
装置:SII製SMI2050
加工イオン:(Ga 30kV)
試料厚み:100nm~200nm
〈TEM観察〉
装置:日本電子製JEM2000FX(加速電圧:200kV)
電子線照射時間:5秒から60秒
このようにして見積もる改質領域の膜厚は、第2のバリア層4Aの厚みに対する膜厚比率として、0.2以上、0.9以下であることが好ましい。より好ましくは0.3以上、0.9以下であり、さらに好ましくは0.4以上、0.8以下である。第2のバリア層4Aの総膜厚に対する改質領域の膜厚が、0.2以上であると、第2のバリア層のバリア性能および屈曲性が向上し、0.9以下であると、バリア性能および屈曲性が向上するため好ましい。
本発明のガスバリア性フィルムの好ましい態様においては、化学蒸着法で形成された第1のバリア層4Bが、酸化珪素または酸窒化珪素から構成され、第1のバリア層4Bの弾性率をE1とし、第2のバリア層4Aにおける改質領域の弾性率をE2とし、第2のバリア層4Aにおける非改質領域の弾性率をE3としたときに、E1>E2>E3の関係を満たすことが好ましい。
本発明においては、好ましくは第1のバリア層が珪素酸化物、珪素窒化物または酸化窒化珪素化合物を有する膜から形成されており、第2のバリア層の処理表面側の改質領域の膜密度d1と、改質されていない非改質領域の膜密度d2は、以下の方法に従って求めることができる。
・X線反射率測定装置:理学電気製薄膜構造評価装置ATX-G
・X線源ターゲット:銅(1.2kW)
・測定:4結晶モノクロメータを用いてX線反射率曲線を測定し、密度分布プロファイルのモデルを作成、フィッティングを行い、膜厚方向の密度分布を算出。
本発明に係る第2のバリア層の改質処理側の表面の表面粗さ(Ra)は、2nm以下であることが好ましく、さらに好ましくは1nm以下である。表面粗さが上記で規定する範囲にあることで、電子デバイス用の樹脂基材として使用する際に、凹凸が少ない平滑な膜面により光透過効率の向上と、電極間リーク電流の低減によりエネルギー変換効率が向上するので好ましい。本発明に係るガスバリア層の表面粗さ(Ra)は以下の方法で測定することができる。
表面粗さは、AFM(原子間力顕微鏡)、例えば、Digital Instruments社製DI3100で、極小の先端半径の触針を持つ検出器で連続測定した凹凸の断面曲線から算出され、極小の先端半径の触針により測定方向が数十μmの区間内を多数回測定し、微細な凹凸の振幅に関する粗さである。
本発明のガスバリア性フィルムは、断裁加工適性に優れる。すなわち、断裁しても断裁面でのほつれや破断等がなく、有効な面積を稼げる。
断裁の方法として、特に限定するところではないが、紫外線レーザー(例えば、波長266nm)、赤外線レーザー、炭酸ガスレーザー等の高エネルギーレーザーによるアブレーション加工で行うことが好ましい。ガスバリア性フィルムは、割れやすい無機薄膜を有しているため、通常のカッターで断裁すると断細部で亀裂が発生することがある。さらには第1のバリア層表面に有機成分を含む保護層を設置することでも、断裁時のヒビ割れを抑制することが可能である。
(基材:基材)
本発明のガスバリア性フィルムの基材(以下、基材ともいう)としては、ガスバリア性を有するガスバリア層(第1のバリア層+第2のバリア層)を保持することができる有機材料で形成されたものであれば特に限定されるものではない。
本発明のガスバリア性フィルムにおいては、基材と第1のバリア層との間に中間層を有していることを特徴の一つとする。
本発明に係る基材表面には、第1のバリア層との密着性の向上を目的として、中間層としてアンカーコート層を形成することが好ましい。このアンカーコート層に用いられるアンカーコート剤としては、ポリエステル樹脂、イソシアネート樹脂、ウレタン樹脂、アクリル樹脂、エチレンビニルアルコール樹脂、ビニル変性樹脂、エポキシ樹脂、変性スチレン樹脂、変性シリコン樹脂、及びアルキルチタネート等を、1または2種以上併せて使用することができる。この中でも特にエポキシ樹脂が好ましい。これらのアンカーコート剤には、従来公知の添加剤を加えることもできる。そして、上記のアンカーコート剤は、ロールコート、グラビアコート、ナイフコート、ディップコート、スプレーコート等の公知の方法により基材上にコーティングし、溶剤、希釈剤等を乾燥除去することによりコーティングすることができる。上記のアンカーコート剤の塗布量としては、0.1~5g/m2(乾燥状態)程度が好ましい。
さらに、本発明に係る基材表面には、中間層として平滑層を設けることが望ましい。特に表面が、JIS K 5600-5-4で規定する鉛筆硬度がH以上であることが好ましい。また、中間層の表面粗さがJIS B 0601:2001で規定される最大断面高さRt(p)で10nm<Rt(p)<30nmとなる様な平滑層を設けることが好ましい。
本発明のガスバリア性フィルムにおいては、中間層としてブリードアウト防止層を設けることができる。ブリードアウト防止層は、平滑層を有するフィルムを加熱した際に、フィルム基材中から未反応のオリゴマー等が表面へ移行して、接触する面を汚染する現象を抑制する目的で、平滑層を有する基材の反対面に設けられる。ブリードアウト防止層は、この機能を有していれば、基本的に平滑層と同じ構成をとっても構わない。
本発明のガスバリア性フィルムは、連続生産しロール形態に巻き取ることができる(いわゆるロール・トゥ・ロール生産)。その際、ガスバリア層を形成した面に保護シートを貼合して巻き取ることが好ましい。特に、本発明のガスバリア性フィルムを有機薄膜デバイスの封止材として用いる場合、表面に付着したゴミ(例えば、パーティクル)が原因で欠陥となる場合が多く、クリーン度の高い場所で保護シートを貼合してゴミの付着を防止することは非常に有効である。併せて、巻取り時に入るガスバリア層表面への傷の防止に有効である。
本発明のガスバリア性フィルムの各特性値は、下記の方法に従って測定することができる。
前述のJIS K 7129(1992年)に記載のB法に従って水蒸気透過率を測定するには、種々の方法が提案されている。例えば、カップ法、乾湿センサー法(Lassy法)、赤外線センサー法(mocon法)が代表として挙げられるが、ガスバリア性が向上するに伴って、これらの方法では測定限界に達する場合があり、以下に示す方法も提案されている。
1.Ca法
ガスバリア性フィルムに金属Caを蒸着し、該フィルムを透過した水分で金属Caが腐食される現象を利用する方法。腐食面積とそこに到達する時間から水蒸気透過率を算出する。
蒸着装置:日本電子(株)製真空蒸着装置JEE-400
恒温恒湿度オーブン:Yamato Humidic ChamberIG47M
水分と反応して腐食する金属:カルシウム(粒状)
水蒸気不透過性の金属:アルミニウム(φ3~5mm、粒状)
水蒸気バリア性評価用セルの作製
バリアフィルム試料のガスバリア層面に、真空蒸着装置(日本電子製真空蒸着装置JEE-400)を用い、透明導電膜を付ける前のバリアフィルム試料の蒸着させたい部分(12mm×12mmを9箇所)以外をマスクし、金属カルシウムを蒸着させた。その後、真空状態のままマスクを取り去り、シート片側全面にアルミニウムをもう一つの金属蒸着源から蒸着させた。アルミニウム封止後、真空状態を解除し、速やかに乾燥窒素ガス雰囲気下で、厚さ0.2mmの石英ガラスに封止用紫外線硬化樹脂(ナガセケムテックス製)を介してアルミニウム封止側と対面させ、紫外線を照射することで、評価用セルを作製した。また、屈曲前後のガスバリア性の変化を確認するために、上記屈曲の処理を行わなかったバリアフィルムについても同様に、水蒸気バリア性評価用セルを作製した。
温度23℃、湿度0%RHの条件で、米国、モコン(MOCON)社製の酸素透過率測定装置(機種名、“オキシトラン”(登録商標)(“OXTRAN”2/20))を使用して、JIS K7126(1987年)に記載のB法(等圧法)に基づいて測定する。また、2枚の試験片について測定を各々1回行い、2つの測定値の平均値を酸素透過率の値とする。
本発明のガスバリア性フィルムは、電子デバイスに適用することができる。有機薄膜光電変換素子や有機エレクトロルミネッセンス素子の様な有機薄膜デバイスばかりでなく、製造工程に高温処理が含まれるようなフレキシブルLCDや電子ペーパー等のディスプレイ電子デバイスにも好適に用いることが可能である。
本発明のガスバリア性フィルムは、種々の封止用材料、封止用フィルムとして用いることができ、例えば、有機光電変換素子の封止用フィルムに用いることができる。
本発明において、封止フィルムに、本発明のガスバリア性フィルムを基板として用いることができる。
本発明では、本発明のガスバリア層ユニットを有する樹脂フィルム(ガスバリア性フィルム)上に透明導電膜を形成し、作製した有機光電変換素子用樹脂基材上に、有機光電変換素子各層を形成した後、上記封止フィルムを用いて、不活性ガスによりパージされた環境下で、上記封止フィルムで陰極面を覆うようにして、有機光電変換素子を封止することができる。
本発明のガスバリア性フィルムにおいては、上述のように、有機光電変換素子を封止するにあたって、ガスバリア性を一層高める等の観点から、無機酸化物、窒化物、炭化物、等による化合物により形成されるセラミック層を設けることができる。
本発明の有機光電変換素子の好ましい態様を説明するが、これに限定されるものではない。
ここで、発電層は、正孔を輸送できるp型半導体材料と電子を輸送できるn型半導体材料を含有していることが必要であり、これらは実質2層でヘテロジャンクションを形成していてもよいし、1層の内部で混合された状態となっているバルクヘテロジャンクションを形成してもよいが、バルクヘテロジャンクション構成の方が、光電変換効率が高いため、好ましい。発電層に用いられるp型半導体材料、n型半導体材料については後述する。
(p型半導体材料)
有機光電変換素子において、発電層(バルクヘテロジャンクション層)に用いられるp型半導体材料としては、種々の縮合多環芳香族低分子化合物や共役系ポリマーやオリゴマーが挙げられる。
有機光電変換素子において、バルクヘテロジャンクション層に用いられるn型半導体材料としては、特に限定されないが、例えば、フラーレン、オクタアザポルフィリン等、p型半導体の水素原子をフッ素原子に置換したパーフルオロ体(パーフルオロペンタセンやパーフルオロフタロシアニン等)、ナフタレンテトラカルボン酸無水物、ナフタレンテトラカルボン酸ジイミド、ペリレンテトラカルボン酸無水物、ペリレンテトラカルボン酸ジイミド等の芳香族カルボン酸無水物やそのイミド化物を骨格として含む高分子化合物等を挙げることができる。
有機光電変換素子10は、バルクヘテロジャンクション層で発生した電荷をより効率的に取り出すことが可能となるため、バルクヘテロジャンクション層と陽極との中間には正孔輸送層17を有していることが好ましい。
有機光電変換素子10は、バルクヘテロジャンクション層で発生した電荷をより効率的に取り出すことが可能となるため、バルクヘテロジャンクション層と陰極との中間には電子輸送層18を有していることが好ましい。
有機光電変換素子においては、エネルギー変換効率の向上や、素子寿命の向上を目的に、各種中間層を素子内に有する構成としてもよい。中間層の例としては、正孔ブロック層、電子ブロック層、正孔注入層、電子注入層、励起子ブロック層、UV吸収層、光反射層、波長変換層等を挙げることができる。
有機光電変換素子において、透明電極は、陰極あるいは陽極のいずれあっても良く、有機光電変換素子構成により選択することができるが、好ましくは透明電極を陽極として用いることである。例えば、陽極として用いる場合、好ましくは380~800nmの光を透過する電極である。材料としては、例えば、インジウムチンオキシド(ITO)、SnO2、ZnO等の透明導電性金属酸化物、金、銀、白金等の金属薄膜、金属ナノワイヤ、カーボンナノチューブ用いることができる。
対電極は、導電材料の単独層であってもよいが、導電性を有する材料に加えて、これらを保持する樹脂を併用してもよい。対電極の導電材料としては、仕事関数の小さい(4eV以下)金属、合金、電気伝導性化合物及びこれらの混合物を電極物質とするものが用いられる。このような電極物質の具体例としては、ナトリウム、ナトリウム-カリウム合金、マグネシウム、リチウム、マグネシウム/銅混合物、マグネシウム/銀混合物、マグネシウム/アルミニウム混合物、マグネシウム/インジウム混合物、アルミニウム/酸化アルミニウム(Al2O3)混合物、インジウム、リチウム/アルミニウム混合物、希土類金属等が挙げられる。これらの中で、電子の取り出し性能及び酸化等に対する耐久性の点から、これら金属とこれより仕事関数の値が大きく安定な金属である第二金属との混合物、例えば、マグネシウム/銀混合物、マグネシウム/アルミニウム混合物、マグネシウム/インジウム混合物、アルミニウム/酸化アルミニウム(Al2O3)混合物、リチウム/アルミニウム混合物、アルミニウム等が好適である。対電極はこれらの電極物質を蒸着やスパッタリング等の方法により薄膜を形成させることにより、作製することができる。また、(平均)膜厚は通常10nm~5μm、好ましくは50~200nmの範囲で選ばれる。
また、前記(v)(または図5)に記載したようなタンデム構成の場合に必要となる中間電極の材料としては、透明性と導電性を併せ持つ化合物を用いた層であることが好ましく、前記透明電極で用いたような材料(ITO、AZO、FTO、酸化チタン等の透明金属酸化物、Ag、Al、Au等の非常に薄い金属層またはナノ粒子・ナノワイヤを含有する層、PEDOT:PSS、ポリアニリン等の導電性高分子材料等)を用いることができる。
有機光電変換素子では導電性繊維を用いることができ、導電性繊維としては、金属でコーティングした有機繊維や無機繊維、導電性金属酸化物繊維、金属ナノワイヤ、炭素繊維、カーボンナノチューブ等を用いることができるが、金属ナノワイヤが好ましい。
本発明の有機光電変換素子は、太陽光のより効率的な受光を目的として、各種の光学機能層を有していてよい。光学機能層としては、例えば、反射防止膜、マイクロレンズアレイ等の集光層、陰極で反射した光を散乱させて再度発電層に入射させることができるような光拡散層等を設けてもよい。
〈各種の層の形成方法〉
電子受容体と電子供与体とが混合されたバルクヘテロジャンクション層、及び輸送層・電極の形成方法としては、蒸着法、塗布法(キャスト法、スピンコート法を含む)等を例示することができる。このうち、バルクヘテロジャンクション層の形成方法としては、蒸着法、塗布法(キャスト法、スピンコート法を含む)等を例示することができる。このうち、前述の正孔と電子が電荷分離する界面の面積を増大させ、高い光電変換効率を有する素子を作製するためには、塗布法が好ましい。また塗布法は、製造速度にも優れている。
本発明の有機光電変換素子の製造において、電極、発電層、正孔輸送層、電子輸送層等をパターニングする方法やプロセスには特に制限はなく、公知の手法を適宜適用することができる。
《試料1(ガスバリア性フィルム)の作製》
〔第1のバリア層1の形成〕
大気圧プラズマ製膜装置(特開2008-56967号の図3に記載、ロールツーロール形態の大気圧プラズマCVD装置)を用いて、大気圧プラズマ法により、ハードコート層(中間層)付き透明樹脂基材(きもと社製クリアハードコート層(CHC)付ポリエチレンテレフタレート(PET)フィルム、、ハードコート層はアクリル樹脂を主成分としたUV硬化樹脂より構成、PETの厚さ125μm、CHCの厚さ6μm)上に、以下の薄膜形成条件で酸化珪素の第1のバリア層1(100nm)を形成した。
放電ガス:窒素ガス 94.9体積%
薄膜形成ガス:テトラエトキシシラン 0.1体積%
添加ガス:酸素ガス 5.0体積%
(成膜条件)
〈第1電極側〉
電源種類:ハイデン研究所 100kHz(連続モード) PHF-6k
周波数 :100kHz
出力密度:10W/cm2
電極温度:120℃
〈第2電極側〉
電源種類:パール工業 13.56MHz CF-5000-13M
周波数 :13.56MHz
出力密度:10W/cm2
電極温度:90℃
上記方法に従って形成した第1のバリア層1は、酸化珪素(SiO2)で構成され、膜厚は100nmであり、弾性率E1は、膜厚方向で一様に30GPaであった。
上記方法で形成した第1のバリア層1上に、パーヒドロポリシラザン(アクアミカ NN120-10、無触媒タイプ、AZエレクトロニックマテリアルズ(株)製)の10質量%ジブチルエーテル溶液をワイヤレスバーにて、乾燥後の(平均)膜厚が、0.10μmとなるように塗布し、塗布試料を得た。
得られた塗布試料を、温度85℃、湿度55%RHの雰囲気下で1分間処理し、乾燥試料を得た。
乾燥試料をさらに温度25℃、湿度10%RH(露点温度-8℃)の雰囲気下に10分間保持し、除湿処理を行った。このようにして得られた層の含水率は、0.01%以下(検出限界以下)であった。
除湿処理を行った試料に対し、下記の条件で改質処理を施した。改質処理時の露点温度は-8℃で実施した。
装置:株式会社 エム・ディ・コム製エキシマ照射装置MODEL:MECL-M-1-200
波長:172nm
ランプ封入ガス:Xe
(改質処理条件)
稼動ステージ上に固定した試料を、以下の条件で改質処理を行って、第2のバリア層1を形成した。
試料と光源の距離 :1mm
ステージ加熱温度 :70℃
照射装置内の酸素濃度:1.0%
エキシマ照射時間 :5秒
以上により、ガスバリア性フィルムである試料1を作製した。
上記作製した試料1を、後述の方法に従って断面のTEMによる観察を行った結果、第2のバリア層1において、改質領域が表面から深さ方向で30nmまで存在していることを確認した。
〔第1のバリア層2の形成〕
上記試料1におけるバリア層1の形成において、製膜条件を下記のように代えた以外は同様にして、酸窒化珪素の第1のバリア層2(100nm)を形成した。
放電ガス:窒素ガス 94.9体積%
薄膜形成ガス:テトラエトキシシラン 0.1体積%
添加ガス:水素ガス 1.0体積%
(成膜条件)
〈第1電極側〉
電源種類:ハイデン研究所 100kHz(連続モード) PHF-6k
周波数 :100kHz
出力密度:12W/cm2
電極温度:120℃
〈第2電極側〉
電源種類:パール工業 13.56MHz CF-5000-13M
周波数 :13.56MHz
出力密度:12W/cm2
電極温度:90℃
得られた第1のバリア層2は酸窒化珪素(SiON)で、膜厚は100nmであり、窒素含有率は元素比率で0.8%であった。弾性率は、膜厚方向で一様に45GPa(=E1)であった。
引き続き、得られた第1のバリア層2上に、パーヒドロポリシラザン(アクアミカ NN120-10、無触媒タイプ、AZエレクトロニックマテリアルズ(株)製)の10質量%ジブチルエーテル溶液をワイヤレスバーにて、乾燥後の(平均)膜厚が、0.10μmとなるように塗布し、塗布試料を得た。
得られた塗布試料を、温度85℃、湿度55%RHの雰囲気下で1分間処理し、乾燥試料を得た。
乾燥試料を、さらに温度25℃、湿度10%RH(露点温度-8℃)の雰囲気下に10分間保持し、除湿処理を行った。このようにして得られた層の含水率は、0.01%以下(検出限界以下)であった。
除湿処理を行った試料に対し、下記の条件で改質処理を施した。改質処理時の露点温度は-8℃で実施した。
装置:株式会社 エム・ディ・コム製エキシマ照射装置MODEL:MECL-M-1-200
波長:172nm
ランプ封入ガス:Xe
(改質処理条件)
稼動ステージ上に固定した試料を以下の条件で改質処理を行って、第2のバリア層2を形成した。
試料と光源の距離 :1mm
ステージ加熱温度 :90℃
照射装置内の酸素濃度:0.1%
エキシマ照射時間 :3秒
以上により、ガスバリア性フィルムの試料2を作製した。
〔第1のバリア層3の形成〕
サムコ社製プラズマCVD装置Model PD-270STPを用いて、透明樹脂基材(きもと社製クリアハードコート層(CHC)付ポリエチレンテレフタレート(PET)フィルム(PETの厚さ125μm、CHCの厚さ6μm))上に、以下の薄膜形成条件で第1のバリア層3を形成した。
酸素圧力:53.2Pa
反応ガス:テトラエトキシシラン(TEOS)5sccm(standard cubic centimeter per minute)濃度0.5%
電力:13.56MHzで100W
基材保持温度:120℃
得られた第1のバリア層3は、酸化珪素(SiO2)で、膜厚は100nmであり、弾性率は膜厚方向で一様に30GPa(=E1)であった。
引き続き、得られた第1のバリア層3に、第2のバリア層1の形成と同様の処理を施した第2のバリア層3を形成し、ガスバリア性フィルムの試料3を作製した。
〔第1のバリア層4の形成〕
試料2における第1のバリア層1と同様の形成方法より、酸窒化珪素の第1のバリア層4(100nm)を形成した。
試料1の作製において、第2のバリア層1の改質処理で用いた改質処理Aを、下記の改質処理Cに変更したした以外は同様にして、第1のバリア層4上に第2のバリア層4を形成し、ガスバリア性フィルムの試料4を作製した。
除湿処理を行った試料を下記の条件でプラズマ処理を行い、第2のバリア層4を形成した。また、製膜時の基材保持温度は、120℃とした。
反応ガス:酸素ガスを全ガスに対し7%
低周波側電源電力:100kHzを6W/cm2
高周波側電源電力:13.56MHzを10W/cm2
プラズマ処理時間;20秒
試料4の断面をTEMにより観察を行った結果、第2のバリア層4の表面より深さ方向で10nmの領域で改質領域が存在していることを確認した。
〔第1のバリア層5の形成〕
試料2における第1のバリア層1の形成と同様にして、酸窒化珪素の第1のバリア層5(100nm)を形成した。
試料1の第2のバリア層1の形成において、第2のバリア層の膜厚を0.06μmとし、改質処理Aを下記の改質処理Dに変更した以外は同様にして、第1のバリア層5上に第2のバリア層5を形成し、ガスバリア性フィルムの試料5を作製した。
除湿処理を行った試料を下記の条件で改質処理を行い、第2のバリア層5を形成した。改質処理時の露点温度は-8℃で実施した。
装置:株式会社 ウシオ電機製、紫外照射装置 型式UVH-0252C
〈改質処理条件〉
稼動ステージ上に固定した試料を以下の条件で改質処理を行った。
試料と光源の距離 :30mm
ステージ加熱温度 :40℃
照射装置内の酸素濃度:5%
UV照射時間 :180秒
試料5の断面をTEMにより観察した結果、第2のバリア層5における改質領域が、表面から深さ方向で55nmの厚みで存在していることが確認された。
特開2009-255040号公報に記載の実施例1の条件で、厚さ100nmの第2のバリア層を2層積層し、これを試料6とした。試料6には、断面をTEMにより観察した結果、改質領域は確認されなかった。
特許第3511325号公報の実施例1に記載の条件で、プラズマCVD法により厚さ100nmの第1のバリア層(酸化珪素)を形成し、第1のバリア層上に、同様に第2のバリア層を0.1μmの厚さで形成し、試料7を得た。試料7の断面をTEMにより観察した結果、改質領域の存在は確認されなかった。
特開2008-235165号公報の実施例に記載のバリア膜に積層する平坦化膜として、前記試料1の第2のバリア層1の形成に用いた塗布条件を適用し、更に改質処理を90℃で10分間の加熱処理とした以外は同様にして、試料8とした。試料8の断面をTEMにより観察した結果、改質領域の存在は確認されなかった。
上記作製した各ガスバリア性フィルムである各試料について、以下の方法で特性値の測定と性能評価を行った。
上記作製した各ガスバリア性フィルムについて、以下のFIB加工装置により超薄切片を作製した後、TEM観察を行った。このとき、試料に電子線を照射し続けると、電子線によりダメージを受ける部分(非改質領域)とそうでない部分(改質領域)にコントラスト差が現れるため、その領域を測定することで、改質領域の厚さを算出した。
装置:SII製SMI2050
加工イオン:(Ga 30kV)
試料厚み:200nm
(TEM観察)
装置:日本電子製JEM2000FX(加速電圧:200kV)
電子線照射時間:30秒
〔第1のバリア層、第2のバリア層における改質領域及び非改質領域の弾性率の測定〕
上記と同様にして、FIB加工により、各ガスバリア性フィルムの断面を露出させた後、MTSシステム社製のナノインデンター(Nano Indenter TMXP/DCM)を用いて、断面部の各領域に対し、超微小な三角錐の圧子を押し込んで、第1のバリア層、第2のバリア層における改質領域、非改質領域の弾性率を測定した。
以下の測定方法に従って、各ガスバリア性フィルムの水蒸気バリア性を評価した。
蒸着装置:日本電子(株)製真空蒸着装置JEE-400
恒温恒湿度オーブン:Yamato Humidic ChamberIG47M
水分と反応して腐食する金属:カルシウム(粒状)
水蒸気不透過性の金属:アルミニウム(φ3~5mm、粒状)
(水蒸気バリア性評価用セルの作製)
試料のガスバリア層面に、真空蒸着装置(日本電子製真空蒸着装置 JEE-400)を用い、透明導電膜を付ける前のガスバリア性フィルム試料の蒸着させたい部分(12mm×12mmを9箇所)以外をマスクし、金属カルシウムを蒸着させた。その後、真空状態のままマスクを取り去り、シート片側全面にアルミニウムをもう一つの金属蒸着源から蒸着させた。アルミニウム封止後、真空状態を解除し、速やかに乾燥窒素ガス雰囲気下で、厚さ0.2mmの石英ガラスに封止用紫外線硬化樹脂(ナガセケムテックス製)を介してアルミニウム封止側と対面させ、紫外線を照射することで、評価用セルを作製した。また、屈曲前後のガスバリア性の変化を確認するために、上記屈曲の処理を行わなかったガスバリア性フィルムについても同様に、水蒸気バリア性評価用セルを作製した。
4:水分量が1×10-4g/m2/day以上、1×10-3g/m2/day未満
3:水分量が1×10-3g/m2/day以上、1×10-2g/m2/day未満
2:水分量が1×10-2g/m2/day以上、1×10-1g/m2/day未満
1:水分量が1×10-1g/m2/day以上
〔折り曲げ耐性の評価〕
各ガスバリア性フィルムを、半径が10mmの曲率になるように、180度の角度で100回の屈曲を繰り返した後、上記と同様の方法で水蒸気透過率を測定し、屈曲処理前後での水蒸気透過率の変化より、下式に従って耐劣化度を測定し、下記の基準に従って折り曲げ耐性を評価した。
5:耐劣化度が、90%以上である
4:耐劣化度が、80%以上、90%未満である
3:耐劣化度が、60%以上、80%未満である
2:耐劣化度が、30%以上、60%未満である
1:耐劣化度が、30%未満である
〔断裁加工適性の評価〕
各ガスバリア性フィルムを、ディスクカッターDC-230(CADL社)を用いてB5サイズに断裁した後、断裁した各端部をルーペ観察し、四辺のクラックの総発生数を確認し、下記の基準に従って断裁加工適性を評価した。
4:クラックの発生数が、1本以上、2本以下である
3:クラックの発生数が、3本以上、5本以下である
2:クラックの発生数が、6本以上、10本以下である
1:クラックの発生数が、11本以上である。
《有機光電変換素子の作製》
実施例1で作製したガスバリア性フィルム1~8に、それぞれ、インジウム・スズ酸化物(ITO)透明導電膜を150nm堆積したもの(シート抵抗10Ω/□)を、通常のフォトリソグラフィ技術と湿式エッチングとを用いて2mm幅にパターニングして第1電極を形成した。パターン形成した第1電極を、界面活性剤と超純水による超音波洗浄、超純水による超音波洗浄の順で洗浄後、窒素ブローで乾燥させ、最後に紫外線オゾン洗浄を行った。
窒素ガス(不活性ガス)によりパージされた環境下で、ガスバリアフィルム1~8の二枚を用い、ガスバリア層を設けた面に、シール材としてエポキシ系光硬化型接着剤を塗布した。上述した方法によって得られたガスバリアフィルム1~8に対応する有機光電変換素子を、上記接着剤を塗布した二枚のガスバリアフィルム1~8の接着剤塗布面の間に挟み込んで密着させた後、片側の基板側からUV光を照射して硬化させ、それぞれ有機光電変換素子1~8とした。
上記作製した有機光電変換素子について、以下の方法で耐久性の評価を行った。
〈エネルギー変換効率〉
ソーラーシミュレーター(AM1.5Gフィルタ)の100mW/cm2の強度の光を照射し、有効面積を4.0mm2にしたマスクを受光部に重ね、IV特性を評価することで、短絡電流密度Jsc(mA/cm2)、開放電圧Voc(V)及びフィルファクターFF(%)を、同素子上に形成した4箇所の受光部をそれぞれ測定し、下記式1に従って求めたエネルギー変換効率PCE(%)の4点平均値を見積もった。
PCE(%)=〔Jsc(mA/cm2)×Voc(V)×FF(%)〕/100mW/cm2
初期電池特性としての変換効率を測定し、性能の経時的低下の度合いを温度60℃、湿度90%RH環境で1000時間保存した加速試験後の変換効率残存率により評価した。
5:変換効率残存率が90%以上
4:変換効率残存率が70%以上、90%未満
3:変換効率残存率が40%以上、70%未満
2:変換効率残存率が20%以上、40%未満
1:変換効率残存率が20%未満
以上により得られた結果を、表3に示す。
《ガスバリア性フィルムの作製》
〔試料3-1の作製〕
実施例1に記載の試料2の作製において、樹脂基材をポリエチレンテレフタレートからポリイミド系耐熱フィルム(三菱瓦斯化学(株)製ネオプリムL3430、厚み200μm)に変更し、中間層(平滑層)としてUV硬化型のアクリル樹脂((株)JSR製オプスターZ7501)を紫外線により硬化後、5μmとなる様に塗布し、N2パージ雰囲気中で、高圧水銀ランプを用いて1J/cm2のUV光照射により硬化した硬化膜を設けた以外は実施例1に記載の試料2と同様にしてガスバリア性フィルムを作製した後、ガスバリア性ユニットの上にスパッタ法(室温)によりITOを100nm成膜し、ITOの抵抗率を下げるため空気中で220℃1hrの熱処理を行って、ガスバリア性フィルムである試料3-1を作製した。加熱処理後にITO表面の表面比抵抗を測定したところ20Ω/□であり、低抵抗な表面になっている事を確認した。
上記試料3-1の作製において、中間層を以下の中間層塗布液を用いて形成した以外は同様にしてガスバリア性フィルムである試料3-2を作製した。
トリメチロールプロパントリグリシジルエーテル(エポライト100MF 共栄社化学社製)を8.0g、エチレングリコールジグリシジルエーテル(エポライト40E 共栄社化学社製)を5.0g、オキセタニル基を有するシルセスキオキサン:OX-SQ-H(東亞合成社製)(熱硬化により有機無機ハイブリッド樹脂となる)を12.0g、3-グリシドキシプロピルトリメトキシシランを32.5g、Al(III)アセチルアセトネートを2.2g、メタノールシリカゾル(日産化学社製、固形分濃度30質量%)134.0g、BYK333(BYKケミー社製)を0.1g、ブチルセロソルブを125.0g、0.1モル/Lの塩酸水15.0gを混合し、充分に攪拌した。これを室温でさらに静置脱気して、中間層塗布液を得た。
上記基材の片面に、定法によりコロナ放電処理を行った後、上記調製した中間層塗布液を、乾燥後の膜厚が4.0μmになるように塗布した後、80℃で3分間乾燥した。さらに120℃で10分間加熱処理を行って、中間層1を形成した。
得られた中間層1の表面粗さは、JIS B 0601で規定されるRzで約20nmであった。
上記試料3-2の作製において、基材の中間層1を形成した面とは反対側の面にも、中間層1と同様にして中間層2を形成した以外は同様にして、ガスバリア性フィルムである試料3-3を作製した。
上記試料3-2の作製において、フィルム基材を高透明性ポリイミド系耐熱フィルム(東洋紡(株)製 タイプHM、Tg=225℃、厚み18μm)に変更した以外は同様にして、ガスバリア性フィルムである試料3-4を作製した。
上記試料3-4の作製において、基材の中間層1を形成した面とは反対側の面にも、中間層1と同様にして中間層2を形成した以外は同様にして、ガスバリア性フィルムである試料3-5を作製した。
上記試料3-2の作製において、中間層1に代えて、熱硬化型エポキシ系樹脂(DIC(株)製EPICLON EXA-4710、硬化剤イミダゾール(2E4MZ)2phr添加)に変更し、硬化条件を200℃1hrとした中間層3を用いた以外は同様にして、ガスバリア性フィルムである試料3-6を作製した。
上記試料3-6の作製において、基材の中間層3を形成した面とは反対側の面にも、中間層3と同様にして中間層4を形成した以外は同様にして、ガスバリア性フィルムである試料3-7を作製した。
形成した中間層3および中間層4の表面粗さは、JIS B 0601で規定されるRzで約25nmであった。
上記作製した各試料について、実施例1に記載の方法と同様にして、改質領域の膜厚測定、弾性率の測定と、水蒸気バリア性、折り曲げ耐性及び断裁加工適性の評価と共に、下記の膜面耐久性の評価を行った。
各試料を220℃の熱処理を行った前後で、目視による膜面品質(層間剥離、変形、変色、ひび割れ)の評価を行い、下記の基準に従って膜面耐久性を評価した。
○:熱処理前後でいずれの項目劣化が殆ど認められない。
△:熱処理前後で若干ではあるが劣化した項目がある。
×:目視で明らかに劣化した項目が1つ以上ある。
上記方法により作製したガスバリア性フィルムである試料3-1~3-7を用いて、実施例2に記載の方法と同様にして光電変換素子3-1~3-7を作製した。作製した光電変換素子3-1~3-7を、JIS C8938(1995)に準拠した条件で温湿度サイクル試験を行い、60℃90%RHで1000hr調湿後、光電変換効率を測定し、実施例2に記載の方法と同様にして、温湿度サイクル試験前後の変換効率の劣化度合い(耐久性2)を評価し、得られた結果を表6に示す。
実施例3で作製したガスバリア性フィルムである試料3-1~3-7を用いて作製した光電変換素子3-1~3-7を、JIS C8938(1995)に準拠した条件で温湿度サイクル試験を行い、25℃50%RHで15hr調湿後、光電変換効率を測定し、温湿度サイクル試験前後の変換効率の劣化度合い(耐久性3)を、実施例2に記載の方法と同様にして評価し、得られた結果を表7に示す。
2 基材
3 中間層
4 ガスバリア層ユニット
4A 第2のバリア層
4B 第1のバリア層
L 改質処理手段
10 バルクヘテロジャンクション型の有機光電変換素子
11 基板
12 透明電極
13 対極
14 発電層
14p p層
14i i層
14n n層
14′ 第1の発電層
15 電荷再結合層
16 第2の発電層
17 正孔輸送層
18 電子輸送層
101 本発明で使用できるプラズマCVD装置
102 真空槽
103 カソード電極
105 サセプタ
106 熱媒体循環系
107 真空排気系
108 ガス導入系
109 高周波電源
110 基板
160 加熱冷却装置
Claims (7)
- 基材の少なくとも一方の面側にガスバリア層ユニットを有し、該ガスバリア層ユニットは、化学蒸着法で形成された第1のバリア層と、該第1のバリア層上に珪素化合物を塗布して形成された塗膜に改質処理が施された第2のバリア層とを有し、かつ該第1のバリア層と該基材との間に中間層を有するガスバリア性フィルム。
- 前記化学蒸着法で形成された第1のバリア層が、酸化珪素、酸窒化珪素及び窒化珪素から選ばれる少なくとも1種を有する、請求項1に記載のガスバリア性フィルム。
- 前記第1のバリア層上に形成される前記第2のバリア層が、ポリシラザン含有液を塗布して形成された塗膜に改質処理が施されたもので、前記基材面側に非改質領域を、表層側に改質領域を有する、請求項1または2に記載のガスバリア性フィルム。
- 前記第2のバリア層の表層側に位置する改質領域の厚みが、該第2のバリア層の全膜厚に対し、厚み比率で0.2以上、0.9以下である、請求項3に記載のガスバリア性フィルム。
- 前記化学蒸着法で形成された第1のバリア層が、酸化珪素または酸窒化珪素を有し、該第1のバリア層の弾性率をE1とし、前記第2のバリア層における改質領域の弾性率をE2とし、前記第2のバリア層における非改質領域の弾性率をE3としたときに、E1>E2>E3の関係を満たす、請求項3または4に記載のガスバリア性フィルム。
- 請求項3から5のいずれか1項に記載のガスバリア性フィルムを製造するガスバリア性フィルムの製造方法であって、第2のバリア層を形成する際に施される改質処理が、180nm以下の波長成分を有する真空紫外線を照射する処理である、ガスバリア性フィルムの製造方法。
- 請求項1から5のいずれか1項に記載のガスバリア性フィルムを用いる電子デバイス。