WO2012044368A1 - Rubber composition with low surface area carbon black - Google Patents
Rubber composition with low surface area carbon black Download PDFInfo
- Publication number
- WO2012044368A1 WO2012044368A1 PCT/US2011/031504 US2011031504W WO2012044368A1 WO 2012044368 A1 WO2012044368 A1 WO 2012044368A1 US 2011031504 W US2011031504 W US 2011031504W WO 2012044368 A1 WO2012044368 A1 WO 2012044368A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- phr
- rubber
- rubber composition
- carbon black
- run
- Prior art date
Abstract
Description
Claims