WO2011143825A1 - 含二噻吩并吡咯喹喔啉类共轭聚合物及其制备方法和应用 - Google Patents
含二噻吩并吡咯喹喔啉类共轭聚合物及其制备方法和应用 Download PDFInfo
- Publication number
- WO2011143825A1 WO2011143825A1 PCT/CN2010/073036 CN2010073036W WO2011143825A1 WO 2011143825 A1 WO2011143825 A1 WO 2011143825A1 CN 2010073036 W CN2010073036 W CN 2010073036W WO 2011143825 A1 WO2011143825 A1 WO 2011143825A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- alkyl
- quinoxaline
- conjugated polymer
- organic
- Prior art date
Description
Claims