WO2011129928A1 - Microporous material - Google Patents
Microporous material Download PDFInfo
- Publication number
- WO2011129928A1 WO2011129928A1 PCT/US2011/027471 US2011027471W WO2011129928A1 WO 2011129928 A1 WO2011129928 A1 WO 2011129928A1 US 2011027471 W US2011027471 W US 2011027471W WO 2011129928 A1 WO2011129928 A1 WO 2011129928A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- microporous material
- microporous
- coating
- molecular weight
- percent
- Prior art date
Abstract
Description
Claims