WO2011107273A1 - Composition de polymère de carbonate ignifuge à écoulement amélioré - Google Patents
Composition de polymère de carbonate ignifuge à écoulement amélioré Download PDFInfo
- Publication number
- WO2011107273A1 WO2011107273A1 PCT/EP2011/001035 EP2011001035W WO2011107273A1 WO 2011107273 A1 WO2011107273 A1 WO 2011107273A1 EP 2011001035 W EP2011001035 W EP 2011001035W WO 2011107273 A1 WO2011107273 A1 WO 2011107273A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- polymer
- parts
- ignition resistant
- polymer composition
- Prior art date
Abstract
La présente invention porte sur une composition de polymère de carbonate ignifuge, sur un procédé pour fabriquer ladite composition et sur des articles fabriqués formés à partir de celle-ci. La composition de polymère de carbonate ignifuge est constituée de : (i) un polycarbonate aromatique ou un polyestercarbonate aromatique, (ii) un (co)polymère greffé produit par polymérisation en masse, (iii) un polymère poly(dicarboxylate d'alkylène) semi-cristallin thermoplastique ayant une viscosité intrinsèque de 0,4 à 0,7 dl/g, (iv) un composé phosphate aromatique représenté par la formule (I) : dans laquelle, R1, R2, R3 et R4 représentent chacun indépendamment des autres un alkyle en C1 à C8 éventuellement halogéné ou cycloalkyle en C5 à C6, aryle en C6 à C20 ou aralkyle en C7 à C12, dans chaque cas éventuellement substitué par un alkyle et/ou halogène, X désigne un radical aromatique mononucléaire ou polynucléaire ayant 6 à 30 atomes de C, chaque n représente indépendamment des autres 0 ou 1 et N représente des valeurs de 0 à 30, (v) un polymère polytétrafluoroéthylène, un thermoplastique fluoré, ou un mélange de ceux-ci, et (vi) un ou plusieurs composants parmi un (co)polymère vinylique thermoplastique, un modificateur de la résistance au choc, une charge, un matériau de renforcement, un stabilisant, un pigment, un colorant, un agent de démoulage, un lubrifiant ou un agent antistatique.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN2011800183420A CN102834460A (zh) | 2010-03-02 | 2011-03-02 | 流动性改进的阻燃碳酸酯聚合物组合物 |
EP11706760A EP2542622A1 (fr) | 2010-03-02 | 2011-03-02 | Composition de polymère de carbonate ignifuge à écoulement amélioré |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US30963410P | 2010-03-02 | 2010-03-02 | |
USUS61/309,634 | 2010-03-02 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2011107273A1 true WO2011107273A1 (fr) | 2011-09-09 |
Family
ID=43985826
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2011/001035 WO2011107273A1 (fr) | 2010-03-02 | 2011-03-02 | Composition de polymère de carbonate ignifuge à écoulement amélioré |
Country Status (4)
Country | Link |
---|---|
EP (1) | EP2542622A1 (fr) |
CN (1) | CN102834460A (fr) |
TW (1) | TW201137033A (fr) |
WO (1) | WO2011107273A1 (fr) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015052114A1 (fr) * | 2013-10-08 | 2015-04-16 | Bayer Materialscience Ag | Matériau composite renforcé de fibres, son utilisation et son procédé de fabrication |
WO2016149400A1 (fr) * | 2015-03-16 | 2016-09-22 | Sabic Global Technologies B.V. | Compositions polymères fibrillées et leurs procédés de fabrication |
WO2018046697A1 (fr) | 2016-09-09 | 2018-03-15 | Trinseo Europe Gmbh | Article composite multicouche comprenant une couche de polyuréthane et une couche pc/abs |
WO2019106124A1 (fr) * | 2017-12-01 | 2019-06-06 | Lego A/S | Élément de jeu de construction en matériau pet polymère |
US10639870B2 (en) | 2014-11-17 | 2020-05-05 | Hewlett-Packard Development Company, L.P. | Polymer fiber composite |
EP3786226A1 (fr) | 2019-08-27 | 2021-03-03 | Trinseo Europe GmbH | Compositions stabilisées de polycarbonates et de composés aromatiques substitués par du vinylidène |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015135958A1 (fr) * | 2014-03-14 | 2015-09-17 | Bayer Materialscience Ag | Compositions thermoplastiques conductrices thermiquement ayant une transformabilité équilibrée |
CN108884308A (zh) * | 2016-04-06 | 2018-11-23 | 株式会社钟化 | 聚碳酸酯树脂组合物及其成型品 |
CN109306187B (zh) * | 2018-08-23 | 2021-02-05 | 苏州普科环境技术有限公司 | 一种新能源汽车用高阻燃复合材料及其制备方法 |
TWI810751B (zh) * | 2021-12-21 | 2023-08-01 | 南亞塑膠工業股份有限公司 | 耐衝擊的聚酯組成物及其製品 |
Citations (38)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2465319A (en) | 1941-07-29 | 1949-03-22 | Du Pont | Polymeric linear terephthalic esters |
US2720502A (en) | 1952-10-03 | 1955-10-11 | Eastman Kodak Co | Organo-metallic titanium catalysts for the preparation of polyesters |
US2727881A (en) | 1952-10-03 | 1955-12-20 | Eastman Kodak Co | Organo-titanium catalysts for the preparation of polyesters |
US2822348A (en) | 1951-11-14 | 1958-02-04 | Du Pont | Ester interchange catalysts |
US3028365A (en) | 1953-10-16 | 1962-04-03 | Bayer Ag | Thermoplastic aromatic polycarbonates and their manufacture |
US3047539A (en) | 1958-11-28 | 1962-07-31 | Goodyear Tire & Rubber | Production of polyesters |
US3169121A (en) | 1957-08-22 | 1965-02-09 | Gen Electric | Carbonate-carboxylate copolyesters of dihydric phenols and difunctional carboxylic acids |
US3243481A (en) | 1962-01-08 | 1966-03-29 | Dow Chemical Co | Process for making graft copolymers of vinyl aromatic compounds and stereospecific rubbers |
US3419634A (en) | 1966-01-03 | 1968-12-31 | Gen Electric | Organopolysiloxane polycarbonate block copolymers |
US3660535A (en) | 1970-09-23 | 1972-05-02 | Dow Chemical Co | Process for the production of alkenyl aromatic polymers containing a reinforcing polymer therein |
US3692744A (en) | 1968-01-04 | 1972-09-19 | Rhodiaceta | Injection molded branched polyesters |
US4156069A (en) | 1976-04-02 | 1979-05-22 | Allied Chemical Corporation | Bisphenol-A/terephthalate/carbonate melt processable copolymers |
US4239863A (en) | 1979-06-28 | 1980-12-16 | The Dow Chemical Company | Process for the polymerization of acrylonitrile-butadiene-styrene resins |
US4260731A (en) | 1978-09-11 | 1981-04-07 | Mitsubishi Chemical Industries, Ltd. | Aromatic polyester-polycarbonate |
US4401804A (en) | 1982-05-24 | 1983-08-30 | Eastman Kodak Company | Deactivation of polyester catalyst residues |
US4529791A (en) | 1981-01-28 | 1985-07-16 | The Dow Chemical Company | Interfacial polycarbonate preparation by adding additional solvent |
US4532290A (en) | 1984-05-02 | 1985-07-30 | General Electric Company | Stabilized polycarbonate-polyester compositions |
US4558141A (en) | 1981-11-19 | 1985-12-10 | E. I. Du Pont De Nemours And Company | Perfluorodioxole and its polymers |
US4677162A (en) | 1983-04-15 | 1987-06-30 | Mobay Corporation | Polycarbonate blends having low gloss |
EP0363608A1 (fr) | 1988-09-22 | 1990-04-18 | General Electric Company | Mélange de polymères comprenant un polycarbonate aromatique, un copolymère et/ou polymère greffé contenant du styrène et un ignifugeant à base de phosphate, articles formés à partir de ce mélange |
US4937285A (en) | 1987-11-10 | 1990-06-26 | Bayer Aktiengesellschaft | Use of redox graft polymers to improve the petroleum-resistance of thermoplastic, aromatic polycarbonate and/or polyester carbonate moulding compositions |
US5061745A (en) | 1988-06-04 | 1991-10-29 | Bayer Aktiengesellschaft | Flame-retardant, high-impact polycarbonate molding compounds |
EP0640655A2 (fr) | 1993-08-26 | 1995-03-01 | Bayer Ag | Compositions à mouler de polycarbonate et d'ABS ignifigues et résistant à la fissuration |
US5714262A (en) | 1995-12-22 | 1998-02-03 | E. I. Du Pont De Nemours And Company | Production of poly(ethylene terephthalate) |
USRE36188E (en) | 1989-09-20 | 1999-04-06 | General Electric Company | Polymer mixture having aromatic polycarbonate styrene I containing copolymer and/or graft polymer and a flame-retardant, articles formed therefrom |
US5922816A (en) | 1992-06-02 | 1999-07-13 | General Electric Company | Polyester-polycarbonate compositions stabilized against ester-carbonate interchange |
WO2001027197A1 (fr) | 1999-10-14 | 2001-04-19 | Dyneon Llc | Additif de traitement pour polymeres pouvant etre travailles a l'etat de fusion |
US6380304B1 (en) | 1999-09-30 | 2002-04-30 | The Dow Chemical Company | Mass polymerized rubber-modified monovinylidene aromatic copolymer compositions |
US6545089B1 (en) | 1997-09-04 | 2003-04-08 | General Electric Company | Impact modified carbonnate polymer composition having improved resistance to degradation and improved thermal stability |
US6596794B1 (en) | 1998-11-18 | 2003-07-22 | Bayer Aktiengesellschaft | Flame-resistant polycarbonate ABS moulding material |
US6727301B1 (en) | 1999-03-27 | 2004-04-27 | Bayer Aktiengesellschaft | Flame-resistant, impact-resistant modified polycarbonate molding and extrusion masses |
US6753366B1 (en) | 1997-08-11 | 2004-06-22 | Bayer Aktiengesellschaft | Flame resistant ABS polycarbonate mouldable materials |
US20070060678A1 (en) * | 2005-09-14 | 2007-03-15 | Eckhard Wenz | Thermoplastic molding composition and articles thermoformed therefrom |
US20070155857A1 (en) | 2005-12-30 | 2007-07-05 | Cheil Industries Inc. | Flame Retardant Polycarbonate Resin Composition Having Good Impact, High Heat Resistance |
US20070225441A1 (en) | 2006-03-22 | 2007-09-27 | Bayer Materialscience Ag | Flame resistant, impact modified polycarbonate compositions |
US20080090961A1 (en) | 2006-10-13 | 2008-04-17 | Bayer Materialscience Llc | Impact resistant, flame retardant thermoplastic molding composition |
US20090203819A1 (en) | 2006-11-23 | 2009-08-13 | Cheil Industries Inc. | Flameproof Thermoplastic Resin Composition |
WO2010017067A1 (fr) * | 2008-08-06 | 2010-02-11 | Dow Global Technologies Inc. | Composition de polymère de carbonate résistante à l'allumage |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN101104731A (zh) * | 2006-07-14 | 2008-01-16 | 上海普利特复合材料有限公司 | 一种无卤阻燃聚碳酸酯/热塑性聚酯树脂组合物 |
-
2011
- 2011-03-01 TW TW100106660A patent/TW201137033A/zh unknown
- 2011-03-02 CN CN2011800183420A patent/CN102834460A/zh active Pending
- 2011-03-02 EP EP11706760A patent/EP2542622A1/fr not_active Ceased
- 2011-03-02 WO PCT/EP2011/001035 patent/WO2011107273A1/fr active Application Filing
Patent Citations (38)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2465319A (en) | 1941-07-29 | 1949-03-22 | Du Pont | Polymeric linear terephthalic esters |
US2822348A (en) | 1951-11-14 | 1958-02-04 | Du Pont | Ester interchange catalysts |
US2720502A (en) | 1952-10-03 | 1955-10-11 | Eastman Kodak Co | Organo-metallic titanium catalysts for the preparation of polyesters |
US2727881A (en) | 1952-10-03 | 1955-12-20 | Eastman Kodak Co | Organo-titanium catalysts for the preparation of polyesters |
US3028365A (en) | 1953-10-16 | 1962-04-03 | Bayer Ag | Thermoplastic aromatic polycarbonates and their manufacture |
US3169121A (en) | 1957-08-22 | 1965-02-09 | Gen Electric | Carbonate-carboxylate copolyesters of dihydric phenols and difunctional carboxylic acids |
US3047539A (en) | 1958-11-28 | 1962-07-31 | Goodyear Tire & Rubber | Production of polyesters |
US3243481A (en) | 1962-01-08 | 1966-03-29 | Dow Chemical Co | Process for making graft copolymers of vinyl aromatic compounds and stereospecific rubbers |
US3419634A (en) | 1966-01-03 | 1968-12-31 | Gen Electric | Organopolysiloxane polycarbonate block copolymers |
US3692744A (en) | 1968-01-04 | 1972-09-19 | Rhodiaceta | Injection molded branched polyesters |
US3660535A (en) | 1970-09-23 | 1972-05-02 | Dow Chemical Co | Process for the production of alkenyl aromatic polymers containing a reinforcing polymer therein |
US4156069A (en) | 1976-04-02 | 1979-05-22 | Allied Chemical Corporation | Bisphenol-A/terephthalate/carbonate melt processable copolymers |
US4260731A (en) | 1978-09-11 | 1981-04-07 | Mitsubishi Chemical Industries, Ltd. | Aromatic polyester-polycarbonate |
US4239863A (en) | 1979-06-28 | 1980-12-16 | The Dow Chemical Company | Process for the polymerization of acrylonitrile-butadiene-styrene resins |
US4529791A (en) | 1981-01-28 | 1985-07-16 | The Dow Chemical Company | Interfacial polycarbonate preparation by adding additional solvent |
US4558141A (en) | 1981-11-19 | 1985-12-10 | E. I. Du Pont De Nemours And Company | Perfluorodioxole and its polymers |
US4401804A (en) | 1982-05-24 | 1983-08-30 | Eastman Kodak Company | Deactivation of polyester catalyst residues |
US4677162A (en) | 1983-04-15 | 1987-06-30 | Mobay Corporation | Polycarbonate blends having low gloss |
US4532290A (en) | 1984-05-02 | 1985-07-30 | General Electric Company | Stabilized polycarbonate-polyester compositions |
US4937285A (en) | 1987-11-10 | 1990-06-26 | Bayer Aktiengesellschaft | Use of redox graft polymers to improve the petroleum-resistance of thermoplastic, aromatic polycarbonate and/or polyester carbonate moulding compositions |
US5061745A (en) | 1988-06-04 | 1991-10-29 | Bayer Aktiengesellschaft | Flame-retardant, high-impact polycarbonate molding compounds |
EP0363608A1 (fr) | 1988-09-22 | 1990-04-18 | General Electric Company | Mélange de polymères comprenant un polycarbonate aromatique, un copolymère et/ou polymère greffé contenant du styrène et un ignifugeant à base de phosphate, articles formés à partir de ce mélange |
USRE36188E (en) | 1989-09-20 | 1999-04-06 | General Electric Company | Polymer mixture having aromatic polycarbonate styrene I containing copolymer and/or graft polymer and a flame-retardant, articles formed therefrom |
US5922816A (en) | 1992-06-02 | 1999-07-13 | General Electric Company | Polyester-polycarbonate compositions stabilized against ester-carbonate interchange |
EP0640655A2 (fr) | 1993-08-26 | 1995-03-01 | Bayer Ag | Compositions à mouler de polycarbonate et d'ABS ignifigues et résistant à la fissuration |
US5714262A (en) | 1995-12-22 | 1998-02-03 | E. I. Du Pont De Nemours And Company | Production of poly(ethylene terephthalate) |
US6753366B1 (en) | 1997-08-11 | 2004-06-22 | Bayer Aktiengesellschaft | Flame resistant ABS polycarbonate mouldable materials |
US6545089B1 (en) | 1997-09-04 | 2003-04-08 | General Electric Company | Impact modified carbonnate polymer composition having improved resistance to degradation and improved thermal stability |
US6596794B1 (en) | 1998-11-18 | 2003-07-22 | Bayer Aktiengesellschaft | Flame-resistant polycarbonate ABS moulding material |
US6727301B1 (en) | 1999-03-27 | 2004-04-27 | Bayer Aktiengesellschaft | Flame-resistant, impact-resistant modified polycarbonate molding and extrusion masses |
US6380304B1 (en) | 1999-09-30 | 2002-04-30 | The Dow Chemical Company | Mass polymerized rubber-modified monovinylidene aromatic copolymer compositions |
WO2001027197A1 (fr) | 1999-10-14 | 2001-04-19 | Dyneon Llc | Additif de traitement pour polymeres pouvant etre travailles a l'etat de fusion |
US20070060678A1 (en) * | 2005-09-14 | 2007-03-15 | Eckhard Wenz | Thermoplastic molding composition and articles thermoformed therefrom |
US20070155857A1 (en) | 2005-12-30 | 2007-07-05 | Cheil Industries Inc. | Flame Retardant Polycarbonate Resin Composition Having Good Impact, High Heat Resistance |
US20070225441A1 (en) | 2006-03-22 | 2007-09-27 | Bayer Materialscience Ag | Flame resistant, impact modified polycarbonate compositions |
US20080090961A1 (en) | 2006-10-13 | 2008-04-17 | Bayer Materialscience Llc | Impact resistant, flame retardant thermoplastic molding composition |
US20090203819A1 (en) | 2006-11-23 | 2009-08-13 | Cheil Industries Inc. | Flameproof Thermoplastic Resin Composition |
WO2010017067A1 (fr) * | 2008-08-06 | 2010-02-11 | Dow Global Technologies Inc. | Composition de polymère de carbonate résistante à l'allumage |
Non-Patent Citations (1)
Title |
---|
PANG: "REVIEW of CONVENTIONAL and NOVEL POLYMERIZATION PROCESSES for POLYESTERS, PROGRESS in POLYMER SCIENCE", vol. 31, 2006, ELSEVIER, pages: 1009 - 1037 |
Cited By (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10808086B2 (en) | 2013-10-08 | 2020-10-20 | Covestro Deutschland Ag | Fiber composite material, use therefor, and method for the production thereof |
US20160257794A1 (en) * | 2013-10-08 | 2016-09-08 | Covestro Deutschland Ag | Fiber composite material, use therefor, and method for the production thereof |
WO2015052114A1 (fr) * | 2013-10-08 | 2015-04-16 | Bayer Materialscience Ag | Matériau composite renforcé de fibres, son utilisation et son procédé de fabrication |
US10639870B2 (en) | 2014-11-17 | 2020-05-05 | Hewlett-Packard Development Company, L.P. | Polymer fiber composite |
WO2016149400A1 (fr) * | 2015-03-16 | 2016-09-22 | Sabic Global Technologies B.V. | Compositions polymères fibrillées et leurs procédés de fabrication |
US11339263B2 (en) | 2015-03-16 | 2022-05-24 | Shpp Global Technologies B.V. | Fibrillated polymer compositions and methods of their manufacture |
US10400080B2 (en) | 2015-03-16 | 2019-09-03 | Sabic Global Technologies B.V. | Fibrillated polymer compositions and methods of their manufacture |
WO2018046697A1 (fr) | 2016-09-09 | 2018-03-15 | Trinseo Europe Gmbh | Article composite multicouche comprenant une couche de polyuréthane et une couche pc/abs |
WO2018046698A1 (fr) | 2016-09-09 | 2018-03-15 | Trinseo Europe Gmbh | Article composite multicouche comprenant une couche de revêtement et une couche pc/abs et procédés associés |
CN111417445A (zh) * | 2017-12-01 | 2020-07-14 | 乐高公司 | 由pet聚合物材料制成的玩具搭建元件 |
JP2021504064A (ja) * | 2017-12-01 | 2021-02-15 | レゴ エー/エス | 高分子pet材料でできた玩具組立要素 |
CN111417445B (zh) * | 2017-12-01 | 2022-05-17 | 乐高公司 | 由pet聚合物材料制成的玩具搭建元件 |
WO2019106124A1 (fr) * | 2017-12-01 | 2019-06-06 | Lego A/S | Élément de jeu de construction en matériau pet polymère |
JP7303193B2 (ja) | 2017-12-01 | 2023-07-04 | レゴ エー/エス | 高分子pet材料でできた玩具組立要素 |
EP3786226A1 (fr) | 2019-08-27 | 2021-03-03 | Trinseo Europe GmbH | Compositions stabilisées de polycarbonates et de composés aromatiques substitués par du vinylidène |
WO2021037729A1 (fr) | 2019-08-27 | 2021-03-04 | Trinseo Europe Gmbh | Compositions stabilisées de polycarbonates et de composés de vinylidène aromatiques substitués |
US11781007B2 (en) | 2019-08-27 | 2023-10-10 | Trinseo Europe Gmbh | Stabilized compositions of polycarbonates and vinylidene substituted aromatic compounds |
Also Published As
Publication number | Publication date |
---|---|
EP2542622A1 (fr) | 2013-01-09 |
CN102834460A (zh) | 2012-12-19 |
TW201137033A (en) | 2011-11-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8357441B2 (en) | Ignition resistant carbonate polymer composition | |
EP2545122B1 (fr) | Composition polymère de type carbonate résistant à l'inflammation et ayant une résistance aux chocs modifiée | |
EP2542622A1 (fr) | Composition de polymère de carbonate ignifuge à écoulement amélioré | |
JP4343439B2 (ja) | 難燃性ポリカーボネート/abs成形用組成物 | |
CN100408629C (zh) | 阻燃的聚碳酸酯模塑组合物 | |
EP2074177B1 (fr) | Composition de moulage thermoplastique résistante aux flammes et résistante aux impacts | |
JP4216593B2 (ja) | 難燃性のポリカーボネート含有組成物 | |
KR100954005B1 (ko) | 내충격성이 개질된 폴리카르보네이트 블렌드 | |
JP4294227B2 (ja) | グラフトポリマー変性された熱可塑性ポリカーボネート成形用組成物 | |
JP2010270338A (ja) | グラフトポリマーを用いて変性した難燃性ポリカーボネート成形配合物 | |
US20150307707A1 (en) | Flame-retardant polycarbonate molding materials vi | |
EP2481774A1 (fr) | Composition de moulage thermoplastique ignifuge | |
US20160185956A1 (en) | Flame-retardant polycarbonate molding materials v | |
KR102204271B1 (ko) | 할로겐 무함유 난연성 폴리카르보네이트 | |
TW201811918A (zh) | 具有良好之熱與化學抗性之pc/abs組成物 | |
US20020147256A1 (en) | Flame-resistant polycarbonate compositions | |
CA2368188C (fr) | Matieres moulables a base de polycarbonate, modifiees a l'aide de polymeres greffes et resistantes aux flammes | |
KR102135992B1 (ko) | 난연성 폴리카르보네이트 성형 물질 iii | |
JP4394290B2 (ja) | 熱可塑性成型用組成物 | |
MXPA03005117A (es) | Composiciones de policarbonato ignifugas, resistentes a deformacion por calor. | |
MXPA01004971A (en) | Flame resistant thermostable polycarbonate abs moulding compounds |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201180018342.0 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 11706760 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2011706760 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |