WO2011095540A2 - Mousses polymères ignifugées contenant du phosphore et exemptes d'halogène - Google Patents
Mousses polymères ignifugées contenant du phosphore et exemptes d'halogène Download PDFInfo
- Publication number
- WO2011095540A2 WO2011095540A2 PCT/EP2011/051550 EP2011051550W WO2011095540A2 WO 2011095540 A2 WO2011095540 A2 WO 2011095540A2 EP 2011051550 W EP2011051550 W EP 2011051550W WO 2011095540 A2 WO2011095540 A2 WO 2011095540A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- aryl
- alkyl
- alkoxy
- polymer
- different
- Prior art date
Abstract
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020127020471A KR20120120282A (ko) | 2010-02-05 | 2011-02-03 | 할로겐-부재 인-함유 방염 중합체 발포체 |
EP11703640A EP2531552A2 (fr) | 2010-02-05 | 2011-02-03 | Mousses polymères ignifugées contenant du phosphore et exemptes d'halogène |
JP2012551617A JP2013518956A (ja) | 2010-02-05 | 2011-02-03 | ハロゲンを有しない、リン含有の難燃性ポリマーフォーム |
RU2012137856/05A RU2012137856A (ru) | 2010-02-05 | 2011-02-03 | Свободные от галогена фосфорсодержащие огнестойкие полимерные пены |
CN2011800083795A CN102741332A (zh) | 2010-02-05 | 2011-02-03 | 无卤含磷阻燃聚合物泡沫 |
MX2012008974A MX2012008974A (es) | 2010-02-05 | 2011-02-03 | Espumas polimericas retardadoras de llama que contienen fosoro, libres de halogeno. |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP10152842 | 2010-02-05 | ||
EP10152842.0 | 2010-02-05 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2011095540A2 true WO2011095540A2 (fr) | 2011-08-11 |
WO2011095540A3 WO2011095540A3 (fr) | 2011-11-10 |
Family
ID=44281073
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2011/051550 WO2011095540A2 (fr) | 2010-02-05 | 2011-02-03 | Mousses polymères ignifugées contenant du phosphore et exemptes d'halogène |
Country Status (7)
Country | Link |
---|---|
EP (1) | EP2531552A2 (fr) |
JP (1) | JP2013518956A (fr) |
KR (1) | KR20120120282A (fr) |
CN (1) | CN102741332A (fr) |
MX (1) | MX2012008974A (fr) |
RU (1) | RU2012137856A (fr) |
WO (1) | WO2011095540A2 (fr) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2733166A1 (fr) | 2012-11-20 | 2014-05-21 | Basf Se | Procédé de fabrication de granulés de polymère de styrène expansibles et de mousses de polymère de styrène à teneur réduite en monomères résiduels |
EP2733165A1 (fr) | 2012-11-20 | 2014-05-21 | Basf Se | Procédé pour la préparation de mousses de polystyrène retardateurs de flamme et libre d'halogène |
WO2021121485A1 (fr) | 2019-12-19 | 2021-06-24 | Hochschule Hamm-Lippstadt | Copolymères et composés de moulage ignifuges |
WO2022128001A1 (fr) | 2020-12-17 | 2022-06-23 | Hochschule Hamm-Lippstadt | Copolymères ignifugés et composés de moulage |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101539663B1 (ko) * | 2014-11-10 | 2015-07-27 | 손민일 | 폐기물을 이용한 난연성 폴리스티렌계 발포 입자 및 그 제조방법 |
CN104804213A (zh) * | 2015-05-08 | 2015-07-29 | 北京理工大学 | 原位无卤阻燃可发性聚苯乙烯的制备 |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE1694945A1 (de) | 1966-11-29 | 1971-08-05 | Shell Int Research | Verfahren zur Herstellung von schwer entflammbaren Stoffen mit Zellenstruktur |
US4440880A (en) | 1980-11-19 | 1984-04-03 | Saffa S.P.A. | Process for stabilizing by encapsulation red phosphorus to be used as flame retardant of polymeric materials and product so obtained |
US4698215A (en) | 1985-03-19 | 1987-10-06 | Saffa S.P.A. | Stabilized red phosphorus for use as flame-retardant, in particular for compositions on the basis of polymers |
EP0806451A1 (fr) | 1996-05-06 | 1997-11-12 | Albemarle Corporation | Compositions de styrènes-polymères retardatrices de flamme |
WO1999010429A1 (fr) | 1997-08-27 | 1999-03-04 | Albemarle Corporation | Compositions ignifugeantes pour polymeres styreniques |
WO2007058736A1 (fr) | 2005-11-12 | 2007-05-24 | Dow Global Technologies Inc. | Copolymeres de butadiene et de vinyle aromatique bromes, melanges de tels copolymeres avec un polymere de vinyle aromatique et mousses polymeres formees a partir de tels melanges |
Family Cites Families (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CA2673524C (fr) * | 2006-12-21 | 2014-01-28 | Dow Global Technologies Inc. | Additifs phosphore-soufre et systemes polymeriques les contenant |
DK2480598T3 (en) * | 2009-09-24 | 2014-12-15 | Sunpor Kunststoff Gmbh | Flame retardant expandable styrene polymers |
-
2011
- 2011-02-03 EP EP11703640A patent/EP2531552A2/fr not_active Withdrawn
- 2011-02-03 JP JP2012551617A patent/JP2013518956A/ja not_active Withdrawn
- 2011-02-03 WO PCT/EP2011/051550 patent/WO2011095540A2/fr active Application Filing
- 2011-02-03 CN CN2011800083795A patent/CN102741332A/zh active Pending
- 2011-02-03 KR KR1020127020471A patent/KR20120120282A/ko not_active Application Discontinuation
- 2011-02-03 RU RU2012137856/05A patent/RU2012137856A/ru not_active Application Discontinuation
- 2011-02-03 MX MX2012008974A patent/MX2012008974A/es not_active Application Discontinuation
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE1694945A1 (de) | 1966-11-29 | 1971-08-05 | Shell Int Research | Verfahren zur Herstellung von schwer entflammbaren Stoffen mit Zellenstruktur |
US4440880A (en) | 1980-11-19 | 1984-04-03 | Saffa S.P.A. | Process for stabilizing by encapsulation red phosphorus to be used as flame retardant of polymeric materials and product so obtained |
US4698215A (en) | 1985-03-19 | 1987-10-06 | Saffa S.P.A. | Stabilized red phosphorus for use as flame-retardant, in particular for compositions on the basis of polymers |
EP0806451A1 (fr) | 1996-05-06 | 1997-11-12 | Albemarle Corporation | Compositions de styrènes-polymères retardatrices de flamme |
WO1999010429A1 (fr) | 1997-08-27 | 1999-03-04 | Albemarle Corporation | Compositions ignifugeantes pour polymeres styreniques |
WO2007058736A1 (fr) | 2005-11-12 | 2007-05-24 | Dow Global Technologies Inc. | Copolymeres de butadiene et de vinyle aromatique bromes, melanges de tels copolymeres avec un polymere de vinyle aromatique et mousses polymeres formees a partir de tels melanges |
Non-Patent Citations (3)
Title |
---|
J. I. G. CADOGAN; J. B. HUSBAND; H. MCNAB, J. CHEM. SOC. PERKIN TRANS., 1983, pages 1489 - 1495 |
M.G. ZIMIN; N. G. ZABIROV; V. SMIRNOV, ZHOURNAL OBSCHEI KHIMII, vol. 50, no. 1, 1980, pages 24 - 30 |
W. KUCHEN; H. BUCHWALD, CHEM. BER., vol. 91, 1958, pages 2871 - 2877 |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2733166A1 (fr) | 2012-11-20 | 2014-05-21 | Basf Se | Procédé de fabrication de granulés de polymère de styrène expansibles et de mousses de polymère de styrène à teneur réduite en monomères résiduels |
EP2733165A1 (fr) | 2012-11-20 | 2014-05-21 | Basf Se | Procédé pour la préparation de mousses de polystyrène retardateurs de flamme et libre d'halogène |
WO2021121485A1 (fr) | 2019-12-19 | 2021-06-24 | Hochschule Hamm-Lippstadt | Copolymères et composés de moulage ignifuges |
US11851512B2 (en) | 2019-12-19 | 2023-12-26 | Universitat Siegen | Flame-retardant copolymers and molding compounds |
WO2022128001A1 (fr) | 2020-12-17 | 2022-06-23 | Hochschule Hamm-Lippstadt | Copolymères ignifugés et composés de moulage |
Also Published As
Publication number | Publication date |
---|---|
MX2012008974A (es) | 2012-08-23 |
JP2013518956A (ja) | 2013-05-23 |
EP2531552A2 (fr) | 2012-12-12 |
WO2011095540A3 (fr) | 2011-11-10 |
RU2012137856A (ru) | 2014-03-10 |
KR20120120282A (ko) | 2012-11-01 |
CN102741332A (zh) | 2012-10-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1791896B1 (fr) | Mousses polymeres ignifuges sans halogene | |
EP2478044B1 (fr) | Mousses polymères ignifuges exemptes d'halogène contenant au moins un composé oligophosphoré | |
EP1819758B1 (fr) | Polymeres styreniques expansibles, ignifuges et sans halogenes | |
EP2513209A1 (fr) | Mousses polymères ignifugées | |
EP2480598B1 (fr) | Polymères de styrène expansés à l'épreuve du feu | |
EP1694754A1 (fr) | Piece moulee en mousse particulaire composee de granules polymeres expansibles contenant une charge | |
EP2658905B1 (fr) | Systeme ignifugeant | |
WO2011095540A2 (fr) | Mousses polymères ignifugées contenant du phosphore et exemptes d'halogène | |
EP2274369B1 (fr) | Mousses de polystyrene avec une faible teneur en métal | |
AT511395A1 (de) | Flammgeschützte expandierbare polymerisate | |
DE102004034516A1 (de) | Verfahren zur Herstellung von flammgeschütztem, expandierbarem Polystyrol | |
US8691896B2 (en) | Halogen-free, phosphorus-containing flame-retardant polymer foams | |
WO2011113795A2 (fr) | Mousse composite ignifugée | |
DE102004034514A1 (de) | Synergistische Flammschutzmischungen für Polystyrolschaumstoffe | |
EP1846486A1 (fr) | Granules de polystyrene expansible (pse) ignifuges presentant un synergiste d'ignifugation dans le revetement | |
WO2011095552A1 (fr) | Agents ignifuges | |
US20110196052A1 (en) | Flame retardants | |
WO2021121485A1 (fr) | Copolymères et composés de moulage ignifuges | |
EP2574614B1 (fr) | Mousses polymères ignifuges dotées de moyens de protection contre les flammes sans halogène, contenant du phosphore et à base de sucre | |
DE102004034515A1 (de) | Selbstverlöschender Styrolpolymer-Partikelschaumstoff | |
AT508303A1 (de) | Flammgeschützte expandierbare polymerisate | |
EP2957595A1 (fr) | Composition d'agents ignifuges destinée à être utilisée dans des mousses polymères de styrène |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201180008379.5 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 11703640 Country of ref document: EP Kind code of ref document: A1 |
|
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2012551617 Country of ref document: JP Ref document number: 2011703640 Country of ref document: EP Ref document number: MX/A/2012/008974 Country of ref document: MX |
|
ENP | Entry into the national phase |
Ref document number: 20127020471 Country of ref document: KR Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2012137856 Country of ref document: RU |