WO2011085691A1 - Regulation d'humidite pour produits finis a base de bois - Google Patents
Regulation d'humidite pour produits finis a base de bois Download PDFInfo
- Publication number
- WO2011085691A1 WO2011085691A1 PCT/CN2011/070298 CN2011070298W WO2011085691A1 WO 2011085691 A1 WO2011085691 A1 WO 2011085691A1 CN 2011070298 W CN2011070298 W CN 2011070298W WO 2011085691 A1 WO2011085691 A1 WO 2011085691A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- wood
- eucalyptus wood
- eucalyptus
- manufactured
- strips
- Prior art date
Abstract
L'invention concerne des produits finis à base de bois, des systèmes et des procédés de production desdits produits. Les procédés décrits consistent avantageusement à réguler la teneur en humidité des morceaux de bois au niveau d'un ou de plusieurs points. Les produits finis à base de bois présentent avantageusement une apparence ou un aspect de grain de bois et des qualités esthétiques et structurelles qui sont appropriées pour un trafic élevé et des applications à visibilité élevée, telles qu'un plancher en bois.
Applications Claiming Priority (10)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CNPCT/CN2010/000066 | 2010-01-15 | ||
PCT/CN2010/070225 WO2011085556A1 (fr) | 2010-01-15 | 2010-01-15 | Procédés de préparation de bois d'eucalyptus |
PCT/CN2010/070229 WO2011085559A1 (fr) | 2010-01-15 | 2010-01-15 | Procédés de fabrication de produits en bois d'eucalyptus |
CNPCT/CN2010/070219 | 2010-01-15 | ||
PCT/CN2010/070219 WO2011085555A1 (fr) | 2010-01-15 | 2010-01-15 | Systèmes de production de produits de bois manufacturés |
PCT/CN2010/000066 WO2011085518A1 (fr) | 2010-01-15 | 2010-01-15 | Produits de bois d'eucalyptus manufacturés |
PCT/CN2010/070214 WO2011085554A1 (fr) | 2010-01-15 | 2010-01-15 | Procédés de préparation et de fabrication de produits en bois manufacturés |
CNPCT/CN2010/070225 | 2010-01-15 | ||
CNPCT/CN2010/070229 | 2010-01-15 | ||
CNPCT/CN2010/070214 | 2010-01-15 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2011085691A1 true WO2011085691A1 (fr) | 2011-07-21 |
Family
ID=44303837
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2011/070297 WO2011085690A1 (fr) | 2010-01-15 | 2011-01-15 | Produits finis a base de bois utilisant des feuilles minces |
PCT/CN2011/070298 WO2011085691A1 (fr) | 2010-01-15 | 2011-01-15 | Regulation d'humidite pour produits finis a base de bois |
Family Applications Before (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2011/070297 WO2011085690A1 (fr) | 2010-01-15 | 2011-01-15 | Produits finis a base de bois utilisant des feuilles minces |
Country Status (1)
Country | Link |
---|---|
WO (2) | WO2011085690A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN104942908A (zh) * | 2015-06-12 | 2015-09-30 | 柳州市骏马木业有限公司 | 一种环保型桉木胶合板的制造方法 |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102848440A (zh) * | 2011-07-01 | 2013-01-02 | 赵星 | 重组竹地板坯料制造方法的改进 |
CN103878839B (zh) * | 2014-01-27 | 2015-09-09 | 南京林业大学 | 一种竹篾重组竹材制造刨切竹单板的生产方法 |
CN104441190B (zh) * | 2014-11-04 | 2016-06-29 | 深圳市文业装饰设计工程股份有限公司 | 一种复合纤维板材料及其制备方法及用途 |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1460592A (zh) * | 2002-07-02 | 2003-12-10 | 中国国际海运集装箱(集团)股份有限公司 | 集装箱地板用胶合板及其生产方法 |
CN1906030A (zh) * | 2004-01-27 | 2007-01-31 | 利格讷有限公司 | 硬木条产品 |
WO2010032080A1 (fr) * | 2008-09-19 | 2010-03-25 | Style Limited | Produit manufacturé en bois et ses procédés de fabrication |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CA1232728A (fr) * | 1983-11-23 | 1988-02-16 | Commonwealth Scientific And Industrial Research Organization | Production d'articles en agglomere de bois |
CN1180604A (zh) * | 1996-10-21 | 1998-05-06 | 河南农业大学林学系 | 单板条层积材 |
JP4524904B2 (ja) * | 2000-10-30 | 2010-08-18 | 株式会社ニッタクス | 強化木の製造方法 |
US20070111019A1 (en) * | 2005-11-04 | 2007-05-17 | Ainsworth Lumber Co., Ltd. | Methods of manufacturing engineered wood products |
CN101298153B (zh) * | 2008-07-03 | 2010-10-13 | 北京林业大学 | 一种木丝、木丝板的制备方法 |
-
2011
- 2011-01-15 WO PCT/CN2011/070297 patent/WO2011085690A1/fr active Application Filing
- 2011-01-15 WO PCT/CN2011/070298 patent/WO2011085691A1/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1460592A (zh) * | 2002-07-02 | 2003-12-10 | 中国国际海运集装箱(集团)股份有限公司 | 集装箱地板用胶合板及其生产方法 |
CN1906030A (zh) * | 2004-01-27 | 2007-01-31 | 利格讷有限公司 | 硬木条产品 |
WO2010032080A1 (fr) * | 2008-09-19 | 2010-03-25 | Style Limited | Produit manufacturé en bois et ses procédés de fabrication |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN104942908A (zh) * | 2015-06-12 | 2015-09-30 | 柳州市骏马木业有限公司 | 一种环保型桉木胶合板的制造方法 |
Also Published As
Publication number | Publication date |
---|---|
WO2011085690A1 (fr) | 2011-07-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2344309B1 (fr) | Produit manufacturé en bois et ses procédés de fabrication | |
US20060048852A1 (en) | Compressed wood product and manufacture | |
US20100178451A1 (en) | Method for producing bamboo boards and products | |
CN104608228B (zh) | 一种抗菌防霉芳香型定向刨花板及其制备工艺 | |
CN101357470B (zh) | 一种重组木及其制造方法 | |
KR100927170B1 (ko) | 압축판재와 그의 제조방법 | |
US20060093745A1 (en) | Treatment of wood for the production of building structures and other wood products | |
CN103231427B (zh) | 用软质速生林木制造高密度板材的方法 | |
US20110045243A1 (en) | Bamboo composite board and beam product | |
US20100119857A1 (en) | Manufactured wood product and methods for producing the same | |
US20210276218A1 (en) | Method and system for producing an engineered wood | |
Mokhtar et al. | Plywood from oil palm trunks | |
US8221894B2 (en) | Surface reinforced solid wood profiles, flooring and manufacturing method | |
WO2011085691A1 (fr) | Regulation d'humidite pour produits finis a base de bois | |
CN106643012A (zh) | 一种专用于小径木材的干燥方法 | |
AU2010342749B2 (en) | Methods of preparing and making manufactured wood products | |
AU2010342713B2 (en) | Manufactured eucalyptus wood products | |
KR100985034B1 (ko) | 목재 부산물을 이용하여 제조한 압축판재의 제조방법 | |
WO2011085555A1 (fr) | Systèmes de production de produits de bois manufacturés | |
WO2011085559A1 (fr) | Procédés de fabrication de produits en bois d'eucalyptus | |
CN104552529A (zh) | 绿色环保高强度抗变形复合门的制作方法 | |
WO2011085556A1 (fr) | Procédés de préparation de bois d'eucalyptus | |
CN109072016B (zh) | 制造湿胶合木材制品的方法 | |
CN102303336A (zh) | 一种速生材阻燃增强木皮及其生产方法 | |
Chawla et al. | Use of lignocellulosic biomaterials for sustainable development of bamboo strand lumber for structural applications |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
32PN | Ep: public notification in the ep bulletin as address of the adressee cannot be established |
Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112 (1) EPC, EPO FORM 1205A DATED 19.11.12. |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 11732681 Country of ref document: EP Kind code of ref document: A1 |