WO2011079341A2 - Thermomechanisches behandlungsverfahren - Google Patents
Thermomechanisches behandlungsverfahren Download PDFInfo
- Publication number
- WO2011079341A2 WO2011079341A2 PCT/AT2010/000493 AT2010000493W WO2011079341A2 WO 2011079341 A2 WO2011079341 A2 WO 2011079341A2 AT 2010000493 W AT2010000493 W AT 2010000493W WO 2011079341 A2 WO2011079341 A2 WO 2011079341A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- temperature
- heavy plate
- plate
- thermomechanical treatment
- treatment method
- Prior art date
Abstract
Description
Claims