WO2011070147A1 - Impact resistant freight container - Google Patents
Impact resistant freight container Download PDFInfo
- Publication number
- WO2011070147A1 WO2011070147A1 PCT/EP2010/069364 EP2010069364W WO2011070147A1 WO 2011070147 A1 WO2011070147 A1 WO 2011070147A1 EP 2010069364 W EP2010069364 W EP 2010069364W WO 2011070147 A1 WO2011070147 A1 WO 2011070147A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- impact resistant
- container according
- impact
- container
- resistant portion
- Prior art date
Abstract
Description
Claims