WO2011032193A2 - Insulation part - Google Patents

Insulation part Download PDF

Info

Publication number
WO2011032193A2
WO2011032193A2 PCT/AT2010/000331 AT2010000331W WO2011032193A2 WO 2011032193 A2 WO2011032193 A2 WO 2011032193A2 AT 2010000331 W AT2010000331 W AT 2010000331W WO 2011032193 A2 WO2011032193 A2 WO 2011032193A2
Authority
WO
WIPO (PCT)
Prior art keywords
insulating part
profiles
part according
polyether
profile
Prior art date
Application number
PCT/AT2010/000331
Other languages
German (de)
French (fr)
Other versions
WO2011032193A3 (en
Inventor
Franz Matauschek
Original Assignee
Alutechnik Matauschek Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alutechnik Matauschek Gmbh filed Critical Alutechnik Matauschek Gmbh
Priority to EP10770503A priority Critical patent/EP2478029A2/en
Publication of WO2011032193A2 publication Critical patent/WO2011032193A2/en
Publication of WO2011032193A3 publication Critical patent/WO2011032193A3/en

Abstract

The invention relates to an insulation part (6), preferably for connecting two moulded parts or sections optionally consisting of sub-sections, in particular wood, plastic or metal sections, such as aluminium sections. Said insulation part consists of at least 55 to 75, preferably 63 to 69 wt. % of at least one glycerol-based raw polyether polyol, 25 to 45, preferably 32 to 37 wt. % saccharose/amine-based raw polyether polyol and 120 to 160, preferably 135 to 145, wt. % polymeric diphenyl methane diisocyanate. The insulation part (6) is preferably suitable for use in a casement and/or block frame for windows or doors.

Description

Isolierteil  Insulation
Die Erfindung betrifft einen Isolierteil, vorzugsweise zum Verbinden zweier, gegebenenfalls aus Teilprofilen bestehender, Formteile oder Profile, insbesondere Holz-, Kunststoff- oder Metallprofile, wie Aluminiumprofile. Ferner betrifft die Erfindung auch eine Einrichtung zur Herstellung eines Profilstabes, vorzugsweise für einen Flügel- und/oder Stockrahmen eines Fensters oder einer Tür, mit einem Isolierteil. The invention relates to an insulating part, preferably for joining two, optionally consisting of part profiles, moldings or profiles, in particular wood, plastic or metal profiles, such as aluminum profiles. Furthermore, the invention also relates to a device for producing a profile bar, preferably for a sash and / or floor frame of a window or a door, with an insulating part.
Aus der AT 412 798 B ist ein Verfahren und eine Einrichtung zur Herstellung eines Flügel- und Stockrahmens für Fenster oder Türen bekannt. Zwei Hohlprofile, nämlich das Außenprofil und das Innenprofil werden mit einem Verbindungsprofil zum Profilstab zusammengefügt. Der im Querschnitt U-förmige Profilstab wird in dem durch die Schenkel gebildeten Freiraum mit einem Klimablocker, also mit einem Isolierteil, gefüllt. Dieser Klimablocker ist ein Zwei-Komponenten- Kunststoffschaum, beispielsweise ein Zwei-Komponenten-Polyurethan-Schaum. Aus dieser AT 412 798 B ist auch eine Einrichtung zur Herstellung eines derartigen Profilstabes bekannt. From AT 412 798 B a method and a device for producing a sash and floor frame for windows or doors is known. Two hollow sections, namely the outer profile and the inner profile are joined together with a connecting profile to the profile bar. The cross-sectionally U-shaped profile bar is filled in the space formed by the legs with a climate blocker, ie with an insulating part. This climate blocker is a two-component plastic foam, for example a two-component polyurethane foam. From this AT 412 798 B, a device for producing such a profile bar is also known.
Weiters ist aus der DE 98 02 148 A1 ein Profilstab mit einem Klimablocker bekannt. Auch die US 4 525 408 A1 offenbart einen Klimablocker aus einem Zwei- Komponenten Kunststoffschaum. Ebenso ist aus der DE 42 35 687 A1 ein Furthermore, from DE 98 02 148 A1 a profile bar with a climatic blocker known. US Pat. No. 4,525,408 A1 also discloses a climate blocker made of a two-component plastic foam. Likewise, from DE 42 35 687 A1 a
Profilstab mit einem Klimablocker bekannt. Profile bar with a climate blocker known.
Bei Rahmen gemäß dem Stand der Technik werden Kennwerte gemäß EN-ISO 10077-2 von u = 1 ,2 bis 1 ,9 W/m2K erreicht. In frame according to the prior art characteristics according to EN-ISO 10077-2 of u = 1, 2 to 1, 9 W / m 2 K are achieved.
Aufgabe der vorliegenden Erfindung ist es, einen Isolierteil zum Verbinden von Profilen zu schaffen, mit dem noch bessere wärmetechnische Kennwerte erreicht werden können. Object of the present invention is to provide an insulating part for connecting profiles, with the even better thermal characteristics can be achieved.
Die Aufgabe wird durch die Erfindung gelöst. Der erfindungsgemäße Isolierteil ist dadurch gekennzeichnet, dass dieser mindestens aus The object is achieved by the invention. The insulating part according to the invention is characterized in that this at least from
55 bis 75, vorzugsweise 63 bis 69, Gew. % mindestens eines Polyether Rohpolyol auf Basis Glycerol,  55 to 75, preferably 63 to 69,% by weight of at least one polyether based on glycerol,
25 bis 45, vorzugsweise 32 bis 37, Gew. % Polyether Rohpolyol auf 25 to 45, preferably 32 to 37, wt.% Polyether raw polyol on
Saccharose/Amin Basis und Sucrose / amine base and
120 bis 160, vorzugsweise 135 bis 145, Gew. % polymerischen  120 to 160, preferably 135 to 145, wt.% Of polymeric
Diphenylmethandiisocyanat besteht. Mit dem erfindungsgemäßen Isolierteil ist es erstmals möglich, ein hochwertiges Dämmmaterial mit einer Wärmeleitzahl λ < 0,024 W/mK herzustellen, wobei der Isolierteil eine Ein-Zonen-Dämmung zwischen den beiden Hohlprofilen mit einer Wärmedurchgangszahl u= 0,5 W/m2K pro etwa 5 cm Dicke bildet. Auf Grund dieser ausgezeichneten Wärmedurchgangszahl wird beispielsweise bei einer Verwendung in Innen- und Außenatmosphäre trennenden Elementen der Gesamt- u-Wert drastisch gesenkt, so dass auch nur eine geringste Wärmeabstrahlung gegeben ist. Diphenylmethane diisocyanate exists. With the insulating part according to the invention, it is now possible to produce a high-quality insulating material with a thermal conductivity λ <0.024 W / mK, the insulating part a one-zone insulation between the two hollow sections with a heat transfer coefficient u = 0.5 W / m 2 K per about 5 cm thick forms. Due to this excellent heat transfer coefficient, for example, when used in indoor and outdoor atmosphere separating elements of the total u value is drastically reduced, so that even a slight heat radiation is given.
Gemäß einem weiteren Merkmal der Erfindung sind zwei, verschiedene According to a further feature of the invention are two different
Eigenschaften aufweisende, Polyether Rohpolyol auf Basis Glycerol enthalten. Die Verwendung von zwei verschiedenen Polyethern hat sich bei praktischen Properties containing polyether raw polyol based on glycerol. The use of two different polyethers has come in handy
Versuchen als überaus vorteilhaft herausgestellt. Try proved to be extremely beneficial.
Nach einem besonderen Merkmal der Erfindung sind 28 bis 32 Gew. % Polyether Rohpolyol auf Basis Glycerol mit einer Dichte von 1 ,08 gr/cm3, einer Viskosität 740 mPa, einem Hxdroxylwert 625 mg KOH/g, einem Wassergehalt < 0,7, einem Flammpunkt 200° und einer Säurezahl < 0,1 enthalten. According to a particular feature of the invention are 28 to 32 wt.% Polyether raw polyol based on glycerol with a density of 1, 08 gr / cm3, a viscosity 740 mPa, a Hxdroxylwert 625 mg KOH / g, a water content <0.7, a Flash point 200 ° and an acid number <0.1.
Gemäß einem weiteren besonderen Merkmal der Erfindung sind 33 bis 37 Gew. % Polyether Rohpolyol auf Basis Glycerol mit einer Dichte von 1 ,07 gr/cm3, einer Viskosität 625 mPa, einem Hxdroxylwert 565 mg KOH/g, einem Wassergehalt < 0,7, einem Flammpunkt 215° und einer Säurezahl < 0, 1 enthalten. Nach einem weiteren Merkmal der Erfindung sind Polyether Rohpolyol auf According to a further particular feature of the invention, 33 to 37% by weight of polyether are crude polyol based on glycerol with a density of 1.70 g / cm 3, a viscosity of 625 mPa, a Hxdroxyl value 565 mg KOH / g, a water content <0.7, a flash point 215 ° and an acid number <0, 1 included. According to a further feature of the invention, polyethers are crude polyol
Sacharose/Amin Basis mit einer Dichte von 1 ,09 gr/cm3, einer Viskosität von 4 400 mPa, einem Hxdroxylwert von 575 mg KOH/g, einem Sacharose / amine base with a density of 1, 09 gr / cm3, a viscosity of 4 400 mPa, a Hxdroxylwert of 575 mg KOH / g, a
Wassergehalt < 0,1 , einem Flammpunkt 200° und einer Säurezahl < 0, 1 enthalten.  Water content <0.1, a flash point 200 ° and an acid number <0, 1 included.
Gemäß einem weiteren Merkmal der Erfindung sind polymerisches According to a further feature of the invention are polymeric
Diphenylmethandiisocyanat mit einer Dichte von 1 ,23 gr/cm3, einer Viskosität von 220 mPas bei 25°, einem NCO-Gehalt von 30,75 %, einem Eisengehalt < 20 ppm, einem Säuregrad von 200 ppm max, einem hydrolysiertem Chlor < 2 000 ppm und einem Flammpunkt von 230° enthalten. Diphenylmethane diisocyanate with a density of 1, 23 gr / cm3, a viscosity of 220 mPas at 25 °, an NCO content of 30.75%, an iron content <20 ppm, an acidity of 200 ppm max, a hydrolyzed chlorine <2,000 ppm and a flashpoint of 230 °.
Wie bereits dargelegt, ergeben die oben aufgezeigten Komponenten einen As already stated, the components shown above give a
Isolierteil mit hervorragenden wärmetechnischen Kenndaten. So wird dadurch auch die OIB 6-Richtlinie betreffend Energieeinsparung und Wärmeschutz bereits mit einer Zweifach-Verglasung erreicht. Insulating part with excellent thermal characteristics. Thus, the OIB 6 guideline regarding energy saving and heat protection is already achieved with a double glazing.
Ein weiterer gravierender Vorteil dieses erfindungsgemäßen Isolierteiles ist darin zu sehen, dass dieser hundertprozentig recyclebar ist. Nach einer besonderen Ausgestaltung der Erfindung sind 8 bis 5, vorzugsweise 9 bis 1 1 , Gew. % eines Flammschutzmittels enthalten. Dadurch wird ein Another serious advantage of this insulating part according to the invention is the fact that it is 100% recyclable. According to a particular embodiment of the invention are 8 to 5, preferably 9 to 1 1, wt.% Of a flame retardant. This will be a
Flammpunkt von etwa 180 °C erreicht, wobei auch eine selbst verlöschende Eigenschaft gegeben ist. Gemäß einer Weiterbildung der Erfindung sind 5 bis 7 Gew. % eines Emulgators enthalten. Dadurch wird ein fein verteiltes Gemisch der Grundkomponenten erreicht. Flash point of about 180 ° C reached, which is given a self-extinguishing property. According to one embodiment of the invention, 5 to 7 wt.% Of an emulsifier are included. As a result, a finely divided mixture of the basic components is achieved.
Nach einer weiteren Ausgestaltung der Erfindung sind 0,5 bis 3 Gew. % eines Katalysators enthalten. Dadurch wird eine ausgezeichnete Reaktionszeit bei der Herstellung erreicht. Gemäß einer weiteren besonderen Ausgestaltung der Erfindung sind 1 bis 3 Gew. % eines Stabilisators enthalten. Derartige Stabilisatoren erhöhen natürlich die Lebenszeit des Isolierteiles. Nach einer besonderen Weiterbildung der Erfindung sind 4 bis 6 Gew. % einer Farbpaste, insbesondere einer Schwarzkonzentrat-Farbpaste, enthalten. According to a further embodiment of the invention, 0.5 to 3 wt.% Of a catalyst are included. This achieves an excellent reaction time in the production. According to a further particular embodiment of the invention, 1 to 3% by weight of a stabilizer are contained. Of course, such stabilizers increase the lifetime of the insulating part. According to a particular embodiment of the invention, 4 to 6 wt.% Of a color paste, in particular a black concentrate color paste, included.
Entsprechend dieser Weiterbildung kann die Farbe des Isolierteiles wunschgemäß hergestellt werden. Gemäß einem ganz besonderen Merkmal der Erfindung ist der erfindungsgemäße Isolierteil in einem Flügel- und/oder Stockrahmen für Fenster oder Türen, vorgesehen, wobei zwei, gegebenenfalls aus Teilprofilen bestehende, Hohlprofile, das Stock- bzw. Flügelrahmenaußenprofil und das Stock- bzw. According to this development, the color of the insulating part can be made as desired. According to a very particular feature of the invention, the insulating part according to the invention in a sash and / or floor frame for windows or doors, provided, wherein two, possibly consisting of sub-profiles, hollow profiles, the floor or wing frame outer profile and the stick or
Flügelrahmeninnenprofil zum Profilstab mit dem Isolierteil verbunden sind. Die mit dem erfindungsgemäßen Isolierteil hergestellten Fenster und Türen erreichen wärmetechnische Werte, die eine hohe Energieeinsparung gewährleisten. So ist in der Winterszeit praktisch keine Kälteabstrahlung nach innen gegeben. Ebenso wird eine Kondensatbildung vermieden. Ein weiterer Vorteil ist vor allem dadurch gegeben, dass auch das so genannte„Zug-Gefühl" im Bereich des Fensters oder der Tür spürbar ist. Natürlich nimmt auch die globale Wärmeabstrahlung nach außen vehement ab. Dieser Effekt ist jederzeit mit einer Wärmekamera Sash inner profile are connected to the profile bar with the insulating part. The windows and doors produced with the insulating part according to the invention achieve thermal values which ensure high energy savings. Thus, in the winter time, virtually no cold radiation is given to the inside. Likewise, condensation is avoided. Another advantage is the fact that the so-called "train feeling" in the area of the window or the door is noticeable.Of course, the global heat radiation to the outside decreases vehemently.This effect is always with a thermal camera
nachweisbar. detectable.
Mit derart hergestellten Fenstern oder Türen wird, natürlich unter anderem, mit einfachster Bauweise Passivhaus-Qualität erreicht. Natürlich wird auch derWith such manufactured windows or doors, of course, among other things, achieved with the simplest construction passive house quality. Of course, too
Umweltfreundlichkeit, die im Zuge der Passivhaus-Qualität gefordert ist, Rechnung getragen. Environmental friendliness, which is required in the course of passive house quality, taken into account.
Es liegt jedoch auch im Rahmen der Erfindung, den erfindungsgemäßen Isolierteil bei Fassaden- oder Dachprofilen einzusetzen. However, it is also within the scope of the invention to use the insulating part according to the invention in facade or roof profiles.
Es ist aber auch Aufgabe der Erfindung eine Einrichtung zur Herstellung eines Profilstabes zu schaffen. Auch diese Aufgabe wird durch die Erfindung gelöst. However, it is also an object of the invention to provide a device for producing a profile bar. This object is also achieved by the invention.
Die Einrichtung zur Herstellung eines Profilstabes, vorzugsweise für einen Flügel- und/oder Stockrahmen eines Fensters oder einer Tür, mit einem Isolierteil umfasst eine Zuführvorrichtung, ein Transportband, eine Befü llstation, eine The device for producing a profile bar, preferably for a sash and / or floor frame of a window or a door, with an insulating part comprises a feed device, a conveyor belt, a Befü llstation, a
Aushärtestrecke, eine Abtrageinheit und eine Ablängvorrichtung. Die Curing line, a removal unit and a cutting device. The
erfindungsgemäße Einrichtung ist dadurch gekennzeichnet, dass nach der Abtrageinheit oder nach der Ablängvorrichtung eine Härterauftragseinheit zum Auftragen eines Härters auf die abgetragenen Flächen vorgesehen ist. Dadurch erhalten die rauen Flächen nach dem Abtragen von Material eine glatte Device according to the invention is characterized in that a hardener application unit for applying a hardener to the removed surfaces is provided after the removal unit or after the cutting device. This gives the rough surfaces after the removal of material a smooth
Oberfläche. Surface.
Nach einem weiteren Merkmal der Erfindung ist im Bereich der Zuführvorrichtung eine Heizeinrichtung für die metallischen Profile vorgesehen. Dadurch wird im Zuge der Herstellung ein Temperaturschock durch die verschiedenen According to a further feature of the invention, a heating device for the metallic profiles is provided in the region of the feeding device. As a result, in the course of manufacturing a temperature shock by the various
Temperaturen von den Profilteilen zum Polyurethanschaum vermieden. Eine homogene Verbindung wird dadurch ermöglicht.  Avoid temperatures from the profile parts to the polyurethane foam. A homogeneous connection is made possible.
Gemäß einer weiteren Ausgestaltung der Erfindung ist das Transportband aus einem endlosen Band gebildet, wobei die dem Profilstab zugewandte Seite dieses Endlosbandes mit Tetrafluorethylen beschichtet ist. Dadurch wird eine etwaige Verklebung im Zuge der Herstellung vermieden. According to a further embodiment of the invention, the conveyor belt is formed from an endless belt, wherein the profiled bar side facing this endless belt is coated with tetrafluoroethylene. As a result, any adhesion during production is avoided.
Nach einer Weiterbildung der Erfindung sind als Abtrageinheit mindestens eine, vorzugsweise zwei, Fräsmaschinen vorgesehen. Mit derartigen Maschinen ist eine genaue Maßhaltigkeit des in den Profilstab eingebrachten Isolierteiles zu erreichen. Zwei Fräsmaschinen deshalb, weil beide freie Flächen des Isolierteiles Maßhaltigkeit aufweisen sollten. Die Erfindung wird an Hand von Ausführungsbeispielen, die in der Zeichnung dargestellt sind, näher erläutert. Es zeigen: According to a development of the invention, at least one, preferably two, milling machines are provided as a removal unit. With such machines, an accurate dimensional accuracy of the introduced into the profile bar insulating part can be achieved. Two milling machines, because both free surfaces of the insulating part should have dimensional accuracy. The invention will be explained in more detail with reference to exemplary embodiments, which are illustrated in the drawing. Show it:
Fig. 1 einen Schnitt durch ein Stock- und Flügelprofil bei geschlossenen Zustand, beispielsweise eines Fensters,  1 shows a section through a floor and wing profile in the closed state, for example, a window,
Fig. 2 schematisch eine Einrichtung an Hand der einzelne Schritte der Herstellung eines Profilstabes aufgezeigt werden,  FIG. 2 schematically shows a device on the basis of the individual steps of producing a profile bar, FIG.
Gemäß der Fig. 1 ist ein Schnitt durch einen Flügelrahmen 1 und einen 1 is a section through a sash 1 and a
Stockrahmen 2 eines Fensters im geschlossenen Zustand dargestellt. Im Stock frame 2 of a window shown in the closed state. in the
Flügelrahmen 1 ist eine Glasscheibe 3, insbesondere eine Verbundglasscheibe, vorgesehen. Sash 1 is a glass sheet 3, in particular a laminated glass pane provided.
Der Flügelrahmen 1 besteht aus zwei Teilprofilen, wobei ein The sash 1 consists of two sub-profiles, with a
Flügelrahmenaußenprofil 4 und ein Flügelrahmeninnenprofil 5 mit einem Isolierteil 6 zu einem Profilstab verbunden werden. Sash outer profile 4 and a sash inner profile 5 are connected to an insulating part 6 to a profile bar.
Ebenso besteht der Stockrahmen 2 aus zwei Teilprofilen, wobei wieder ein Stockrahmenaußenprofil 7 und ein Stockrahmeninnenprofil 8 mit dem Isolierteil 6 zu einem Profilstab verbunden werden. Sowohl das Flügelrahmenaußenprofil 4, wie auch das Flügelrahmeninnenprofil 5 als auch das Stockrahmenaußenprofil 7 und das Stockrahmeninnenprofil 8 sind als Hohlprofile, vorzugsweise aus Aluminium, hergestellt. Aus Festigkeitsgründen sind diese Hohlprofile als Mehrkammernprofile ausgebildet. Um gegebenenfalls dem heutigen Trend Rechnung zu tragen, kann vorzugsweise das Flügelrahmeninnenprofil 5 und das Stockrahmeninnenprofil 8 aus Holz oder auch aus Kunststoff bestehen. Natürlich sind hier den kreativen Variationen keine Grenzen gesetzt. Es könnte auch bei einer Holzfassade umgekehrt sein, oder alle Außen- und Innenprofile aus Holz gefertigt werden. Likewise, the floor frame 2 consists of two sub-profiles, again a floor frame outer profile 7 and a floor frame inner profile 8 are connected to the insulating part 6 to form a profile bar. Both the sash outer profile 4, as well as the sash inner profile 5 and the outer frame frame profile 7 and the floor frame inner profile 8 are made as hollow profiles, preferably made of aluminum. For reasons of strength, these hollow profiles are designed as multi-chamber profiles. To possibly take into account the current trend, preferably the wing frame inner profile 5 and the floor frame inner profile 8 made of wood or plastic. Of course, there are no limits to creative variations. It could also be reversed in a wooden facade, or all exterior and interior profiles are made of wood.
Um jeweils die Außen- und Innenprofile miteinander über die Isolierteile 6 verbinden zu können, weisen diese Teilprofile Verankerungsleisten 9 für die Aufnahme des flüssigen Polyurethanschaumes auf. Im Isolierteil 6 des Stockrahmens 2 ist eine Profildichtung 10, vorzugsweise aus Polyvenylchlorid, angeordnet. In order to be able to connect the outer and inner profiles to one another via the insulating parts 6, these partial profiles have anchoring strips 9 for receiving the liquid polyurethane foam. In the insulating part 6 of the pole frame 2, a profile seal 10, preferably made of polyvinyl chloride, is arranged.
Da aus wärmetechnischen Gründen insbesondere eine dreifache Abdichtung erwünscht wird, sind noch eine Stockaußendichtung 1 1 und eine Since, for reasons of thermal engineering, in particular a triple seal is desired, there is still an outer seal 1 1 and a
Flügelinnendichtung 12 angeordnet. Die Stockaußendichtung 1 1 vermeidet einen eventuellen Wassereintritt und die Flügelinnendichtung 12 verhindert einen Wärmeaustritt. Als Haupt- oder Mitteldichtung wird eine Dichtlippe 13 vorgesehen, die mit der Profildichtung 10 integriert ist und im geschlossenen Zustand des Fensters am Isolierteil 6 des Flügelrahmens 1 dicht anliegt. Durch das Aufeinanderpressen von Gummi auf den aus Polyurethanschaum bestehenden Isolierteil 6 wird ein erhöhter Dichtungseffekt erreicht.  Wing inner seal 12 is arranged. The Stockaußendichtung 1 1 avoids any water ingress and the wing inner seal 12 prevents heat leakage. As a main or center seal, a sealing lip 13 is provided, which is integrated with the profile seal 10 and in the closed state of the window on the insulating part 6 of the sash 1 tightly. By pressing rubber onto the polyurethane foam insulating part 6, an increased sealing effect is achieved.
Zur Halterung der Glasscheibe 3 weist das Flügelrahmenaußenprofil 4 eine Glashaltedichtung 13 und das Flügelrahmeninnenprofil 5 eine Glasleiste 14, in die ebenfalls eine Glashaltedichtung 13 eingesetzt ist, auf. Um nun die erwähnten wärmetechnischen Kennzahlen zu erzielen, wird der Isolierteil 6 des Profilstabes aus nachstehenden Komponenten hergestellt. For holding the glass pane 3, the casement outer profile 4 has a glass-holding seal 13 and the casement inner profile 5 has a glass strip 14 into which a glass-sealing seal 13 is likewise inserted. In order to achieve the aforementioned thermal characteristics, the insulating part 6 of the profile bar is made from the following components.
Der Isolierteil 6 besteht mindestens aus: The insulating part 6 consists at least of:
55 bis 75, vorzugsweise 63 bis 69, Gew. % mindestens eines Polyether Rohpolyol auf Basis Glycerol,  55 to 75, preferably 63 to 69,% by weight of at least one polyether based on glycerol,
25 bis 45, vorzugsweise 32 bis 37, Gew. % Polyether Rohpolyol auf  25 to 45, preferably 32 to 37, wt.% Polyether raw polyol on
Saccharose/Amin Basis und Sucrose / amine base and
120 bis 160, vorzugsweise 135 bis 145, Gew. % polymerischen  120 to 160, preferably 135 to 145, wt.% Of polymeric
Diphenylmethandiisocyanat. Diisocyanate.
Vorteilhafterweise sind zwei, verschiedene Eigenschaften aufweisende, PolyetherAdvantageously, two different properties are polyethers
Rohpolyol auf Basis Glycerol enthalten. Containing crude polyol based on glycerol.
Ein Polyether Rohpolyol auf Basis Glycerol ist: 28 bis 32 Gew. % Polyether Rohpolyol auf Basis Glycerol mit einer Dichte von 1 ,08 gr/cm3, einer Viskosität 740 mPa, einem Hxdroxylwert 625 mg KOH/g, einem Wassergehalt < 0,7, einem Flammpunkt 200° und einer Säurezahl < 0,1 . Der zweite Teil Polyether Rohpolyol auf Basis Glycerol ist: A polyether raw polyol based on glycerol is: 28 to 32 wt.% Polyether raw polyol based on glycerol with a density of 1, 08 gr / cm3, a viscosity 740 mPa, a Hxdroxylwert 625 mg KOH / g, a water content <0.7, a flash point 200 ° and an acid number < 0.1. The second part of polyether raw polyol based on glycerol is:
33 bis 37 Gew. % Polyether Rohpolyol auf Basis Glycerol mit einer Dichte von 33 to 37 wt.% Polyether raw polyol based on glycerol with a density of
I , 07 gr/cm3, einer Viskosität 625 mPa, einem Hxdroxylwert 565 mg KOH/g, einem Wassergehalt < 0,7, einem Flammpunkt 215° und einer Säurezahl < 0,1 . Weiters ist in dem Isolierteil 6 Polyether Rohpolyol auf Sacharose/Amin Basis mit einer Dichte von 1 ,09 gr/cm3, einer Viskosität von 4 400 mPa, einem Hxdroxylwert von 575 mg KOH/g, einem Wassergehalt < 0, 1 , einem Flammpunkt 200° und einer Säurezahl < 0,1 enthalten. Diese 100 Gew. % Polyether Rohpolyolen werden für die Polyadditionsreaktion mit 120 bis 160 Gew. % polymerisches Diphenylmethandiisocyanat mit einer Dichte von 1 ,23 gr/cm3, einer Viskosität von 220 mPas bei 25°, einem NCO- Gehalt von 30,75 %, einem Eisengehalt < 20 ppm, einem Säuregrad von 200 ppm max, einem hydrolysiertem Chlor < 2 000 ppm und einem Flammpunkt von 230° vermischt. I, 07 gr / cm3, a viscosity of 625 mPa, a Hxdroxylwert 565 mg KOH / g, a water content <0.7, a flash point 215 ° and an acid number <0.1. Further, in the insulator 6 polyether raw polyol on a sucrose / amine basis with a density of 1, 09 gr / cm3, a viscosity of 4,400 mPa, a Hxdroxylwert of 575 mg KOH / g, a water content <0, 1, a flash point 200 ° and an acid number <0.1. These 100 wt.% Polyether raw polyols are used for the polyaddition reaction with 120 to 160 wt.% Of polymeric diphenylmethane diisocyanate having a density of 1, 23 gr / cm3, a viscosity of 220 mPas at 25 °, an NCO content of 30.75%, an iron content <20 ppm, an acidity of 200 ppm max, a hydrolyzed chlorine <2,000 ppm and a flash point of 230 ° mixed.
Um ein fein verteiltes Gemisch der Grundkomponenten zu erreichen werden 5 bis 7 Gew. % eines Emulgators beigemengt. Weiters wird, um eine schnelle In order to achieve a finely divided mixture of the basic components, 5 to 7% by weight of an emulsifier are added. It will continue to be a fast
Reaktionszeit bei der Herstellung zu erreichen, 0,5 bis 3 Gew. % eines Reaction time to achieve in the production, 0.5 to 3 wt.% Of a
Katalysators beigemengt. Um die Lebenszeit des Isolierteiles zu erhöhen, sind 1 bis 3 Gew. % eines Stabilisators enthalten. Catalyst added. To increase the lifetime of the insulating part, 1 to 3 wt.% Of a stabilizer are included.
Ferner kann auch zur Erhöhung des Flammpunktes 8 bis 15, vorzugsweise 9 bisFurthermore, it is also possible to increase the flash point 8 to 15, preferably 9 to
I I , Gew. % eines Flammschutzmittels beigemengt werden. I I, wt.% Of a flame retardant are added.
Darüber hinaus können zur Farbwahl des Isolierteiles 6, 4 bis 6 Gew. % einer Farbpaste, insbesondere einer Schwarzkonzentrat-Farbpaste, enthalten sein. Ein aus obigen Komponenten hergestellter Isolierteil 6 weist nachstehende Eigenschaften auf: In addition, the color selection of the insulating part 6, 4 to 6 wt.% Of a color paste, in particular a black concentrate color paste may be included. An insulating member 6 made of the above components has the following properties:
Entsprechend seiner Grundkomponenten ist er hochisolierend, bearbeitbar, schraubenfest, feinporig, homogen, wasserfest und schwer entflammbar bzw. selbst verlöschend. Ein derartiger Isolierteil 6 weist eine Wärmeleitfähigkeit im Bereich von λ < 0,024 W/mK auf, wobei der Isolierteil 6 eine Ein-Zonen-Dämmung zwischen den beiden Hohlprofilen mit einer Wärmedurchgangszahl u= 0,5 W/m2K pro etwa 5 cm Dicke bildet. Die Druckfestigkeit liegt bei 140 bis 160 kg/cm3. Die Schlagzähigkeit des Isolierteiles 6 beträgt etwa 25 mJ/mm2. According to its basic components, it is highly insulating, workable, screw-resistant, fine-pored, homogeneous, water-resistant and flame-retardant or even extinguishing. Such an insulating member 6 has a thermal conductivity in the range of λ <0.024 W / mK, wherein the insulating member 6 is a one-zone insulation between the two hollow profiles with a heat transfer coefficient u = 0.5 W / m 2 K per about 5 cm thickness forms. The compressive strength is 140 to 160 kg / cm 3 . The impact resistance of the insulating part 6 is about 25 mJ / mm 2 .
Gemäß der Fig. 2 ist - schematisch - eine Einrichtung dargestellt, mit der der Profilstab für einen Flügel- 1 oder Stockrahmen 2 eines Fensters oder einer Tür, in diesem Ausführungsbeispiel ein Flügelrahmen 1 , hergestellt wird. According to FIG. 2, a device is shown schematically, with which the profile bar for a wing 1 or floor frame 2 of a window or a door, in this embodiment, a casement 1, is produced.
Die metallischen Teilprofile, nämlich das Flügelrahmenaußenprofil 4 und das Flügelrahmeninnenprofil 5, werden entsprechend ihrem Abstand zueinander mittels der Zuführvorrichtung 24, die auch aus Stehern mit Rollen bestehen kann, einer Befüllstation 27 zugeführt. Im Bereich der Zuführvorrichtung 24 ist eine Heizeinrichtung 25 vorgesehen. The metallic sub-profiles, namely the sash outer profile 4 and the sash inner profile 5, according to their distance from each other by means of the feeder 24, which can also consist of uprights with rollers, fed to a filling station 27. In the area of the feeder 24, a heater 25 is provided.
Zur Verbindung von Flügelrahmeninnenprofil 5 und Flügelrahmenaußenprofil 4 zu einem Profilstab für den Flügelrahmen 2 werden die erwärmten Profile nun mit einem Transportband 26 zur Befüllstation 27 transportiert. Das Transportband 26 ist aus einem endlosen Band gebildet, wobei die dem Profilstab zugewandte Seite dieses Endlosbandes mit Tetrafluorethylen beschichtet ist. To connect sash inner profile 5 and sash outer profile 4 to a profile bar for the sash 2, the heated profiles are now transported by a conveyor belt 26 to the filling station 27. The conveyor belt 26 is formed from an endless belt, wherein the profiled bar side facing this endless belt is coated with tetrafluoroethylene.
In der Befüllstation 27 wird der, gegebenenfalls aus Teilprofilen bestehender, Profilstab im Freiraum mit einem flüssigen Polyurethanschaum gefüllt. Dieser Polyurethanschaum, entsprechend den obigen Ausführungen, ist ein Zwei- Komponenten-Polyurethanschaum, der auf der Aushärtestrecke 28 seine entsprechende Festigkeit erreicht. Da dieser Polyurethanschaum im Zuge seiner Aushärtung aufquillt und den Freiraum ausfüllt, jedoch im ausgehärteten Zustand voraussichtlich leicht über seinem Soll-Maß stehen wird, ist eine Abtrageinheit 29, in Form einer Fräsmaschine vorgesehen. Mit dieser Abtrageinheit 29 wird der nun ausgehärtete Isolierteil 6 exakt auf sein Maß, vorzugsweise bis auf den durch die Profile gebildeten Freiraum, reduziert. Da der Isolierteil 6 ja bekanntlich spezielle Konturen aufweist, ist eine weitere Fräsmaschine für die Fertigung dieser In the filling station 27, the optionally consisting of sub-profiles, profile bar is filled in the free space with a liquid polyurethane foam. This polyurethane foam, as discussed above, is a two-part polyurethane foam that achieves its equivalent strength on the curing line 28. As this polyurethane foam swells in the course of its curing and fills the space, but in the cured state is expected to be slightly above its target size, a removal unit 29, provided in the form of a milling machine. With this removal unit 29, the now cured insulating part 6 is reduced to its exact size, preferably down to the free space formed by the profiles. Since the insulating part 6 is known to have special contours, another milling machine for the production of this is
Konturen in der Abtrageinheit 29 vorgesehen. Um die Fertigungsvorgabe, Contours provided in the removal unit 29. To the production specification,
Maßfertigung oder B-Teil-Fertigung, erfüllen zu können, ist nach der Abtrageinheit 29 eine Ablängvorrichtung 30 vorgesehen. Um äußerst glatte Flächen, also der gefrästen Flächen, des Isolierteiles 6 zu erreichen, ist nach der Abtrageinheit 29 oder nach der Ablängvorrichtung 30 eine Härterauftragseinheit 23 zum Auftragen eines Härters auf die abgetragenen Flächen vorgesehen. Zum Transport des Profilstabes können natürlich noch Führungsrollen 33 vorgesehen werden. Made-to-measure or B-part production to meet, a Ablängvorrichtung 30 is provided after the removal unit 29. In order to achieve extremely smooth surfaces, ie the milled surfaces, of the insulating part 6, after the removal unit 29 or after the cutting device 30, a hardener application unit 23 is provided for applying a hardener to the removed surfaces. Of course, still guide rollers 33 can be provided for transporting the profile bar.
Wie bereits aufgezeigt, ist es natürlich auch möglich, den Isolierteil 6 mit seinen Eigenschaften im Zuge der Herstellung von Fassaden- oder Dachprofilen zu verwenden. As already indicated, it is of course also possible to use the insulating part 6 with its properties in the course of the production of facade or roof profiles.

Claims

Patentansprüche: claims:
Isolierteil, vorzugsweise zum Verbinden zweier, gegebenenfalls aus Teilprofilen bestehender, Formteile oder Profile, insbesondere Holz-, Kunststoff- oder Metallprofile, wie Aluminiumprofile, dadurch Insulating part, preferably for joining two, optionally consisting of part profiles, moldings or profiles, in particular wood, plastic or metal profiles, such as aluminum profiles, characterized
gekennzeichnet, dass dieser mindestens aus  characterized in that this at least
55 bis 75, vorzugsweise 63 bis 69, Gew. % mindestens eines Polyether Rohpolyol auf Basis Glycerol,  55 to 75, preferably 63 to 69,% by weight of at least one polyether based on glycerol,
25 bis 45, vorzugsweise 32 bis 37, Gew. % Polyether Rohpolyol auf Saccharose/Amin Basis und  25 to 45, preferably 32 to 37, wt.% Polyether raw polyol based on sucrose / amine and
120 bis 160, vorzugsweise 135 bis 145, Gew. % polymerischen  120 to 160, preferably 135 to 145, wt.% Of polymeric
Diphenylmethandiisocyanat  diisocyanate
besteht.  consists.
Isolierteil nach Anspruch 1 , dadurch gekennzeichnet, dass zwei, Insulating part according to claim 1, characterized in that two,
verschiedene Eigenschaften aufweisende, Polyether Rohpolyol auf Basis Glycerol enthalten sind.  containing various properties, polyether raw polyol based glycerol are included.
Isolierteil nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass 28 bis 32 Gew. % Polyether Rohpolyol auf Basis Glycerol mit einer Dichte von 1 ,08 gr/cm3, einer Viskosität 740 mPa, einem Hxdroxylwert 625 mg KOH/g, einem Wassergehalt < 0,7, einem Flammpunkt 200° und einer Säurezahl < 0,1 enthalten sind. Isolierteil according to claim 1 or 2, characterized in that 28 to 32 wt.% Polyether crude polyol based on glycerol with a density of 1, 08 gr / cm3, a viscosity 740 mPa, a Hxdroxylwert 625 mg KOH / g, a water content <0 , 7, a flash point 200 ° and an acid number <0.1 are included.
Isolierteil nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass 33 bis 37 Gew. % Polyether Rohpolyol auf Basis Glycerol mit einer Dichte von 1 ,07 gr/cm3, einer Viskosität 625 mPa, einem Hxdroxylwert 565 mg KOH/g, einem Wassergehalt < 0,7, einem Flammpunkt 215° und einer Säurezahl < 0,1 enthalten ist. Isolierteil according to any one of claims 1 to 3, characterized in that 33 to 37 wt.% Polyether raw polyol based on glycerol with a density of 1, 07 gr / cm3, a viscosity 625 mPa, a Hxdroxylwert 565 mg KOH / g, a water content <0.7, a flash point 215 ° and an acid number <0.1 is included.
5. Isolierteil nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass Polyether Rohpolyol auf Sacharose/Amin Basis mit einer Dichte von 1 ,09 gr/cm3, einer Viskosität von 4 400 mPa, einem Hxdroxylwert von 575 mg KOH/g, einem Wassergehalt < 0,1 , einem Flammpunkt 200° und einer Säurezahl < 0, 1 enthalten sind. 6. Isolierteil nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass polymerisches Diphenylmethandiisocyanat mit einer Dichte von 1 ,23 gr/cm3, einer Viskosität von 220 mPas bei 25°, einem NCO-Gehalt von 30,75 %, einem Eisengehalt < 20 ppm, einem Säuregrad von 200 ppm max, einem hydrolysiertem Chlor < 2 000 ppm und einem Flammpunkt von 230° enthalten sind. 5. Insulating part according to one of claims 1 to 4, characterized in that the polyether sarcosine / amine based raw polyol with a density of 1, 09 gr / cm3, a viscosity of 4,400 mPa, a Hxdroxylwert of 575 mg KOH / g, a water content <0.1, a flash point 200 ° and an acid number <0, 1 are included. 6. Insulating according to one of claims 1 to 5, characterized in that polymeric diphenylmethane diisocyanate having a density of 1, 23 gr / cm3, a viscosity of 220 mPas at 25 °, an NCO content of 30.75%, an iron content < 20 ppm, an acidity of 200 ppm max, a hydrolyzed chlorine <2,000 ppm and a flash point of 230 ° are included.
7. Isolierteil nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass 8 bis 15, vorzugsweise 9 bis 1 1 , Gew. % eines Flammschutzmittels enthalten sind. 7. insulating part according to one of claims 1 to 6, characterized in that 8 to 15, preferably 9 to 1 1, wt.% Of a flame retardant are included.
8. Isolierteil nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass 5 bis 7 Gew. % eines Emulgators enthalten sind. 8. insulating part according to one of claims 1 to 7, characterized in that 5 to 7 wt.% Of an emulsifier are included.
9. Isolierteil nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass 0,5 bis 3 Gew. % eines Katalysators enthalten sind. 9. insulating part according to one of claims 1 to 8, characterized in that 0.5 to 3 wt.% Of a catalyst are included.
10. Isolierteil nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass 1 bis 3 Gew. % eines Stabilisators enthalten sind. 1 1 . Isolierteil nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass 4 bis 6 Gew. % einer Farbpaste, insbesondere einer 10. Insulating part according to one of claims 1 to 9, characterized in that 1 to 3 wt.% Of a stabilizer are included. 1 1. Insulating part according to one of claims 1 to 10, characterized in that 4 to 6 wt.% Of a color paste, in particular a
Schwarzkonzentrat-Farbpaste, enthalten sind.  Black concentrate color paste, are included.
12. Isolierteil nach einem der Ansprüche 1 bis 1 1 , dadurch gekennzeichnet, dass dieser in einem Flügel- (1 ) und/oder Stockrahmen (2) für Fenster oder12. insulating part according to one of claims 1 to 1 1, characterized in that this in a wing (1) and / or floor frame (2) for windows or
Türen, vorgesehen ist, wobei zwei, gegebenenfalls aus Teilprofilen bestehende, Hohlprofile, das Stock- (7) bzw. Flügelrahmenaußenprofil (4) und das Stock- (8) bzw. Flügelrahmeninnenprofil (5) zum Profilstab mit dem Isolierteil (6) verbunden sind. Doors, is provided, wherein two, possibly consisting of sub-profiles, hollow profiles, the floor (7) or wing frame outer profile (4) and the floor (8) or wing frame inner profile (5) are connected to the profile bar with the insulating part (6).
13. Einrichtung zur Herstellung eines Profilstabes, vorzugsweise für einen 13. Device for producing a profile bar, preferably for a
Flügel- und/oder Stockrahmen eines Fensters oder einer Tür, mit einem Isolierteil nach einem der Ansprüche 1 bis 12, die eine Zuführvorrichtung, ein Transportband, eine Befü llstation, eine Aushärtestrecke, eine  Wing and / or floor frame of a window or door, comprising an insulating part according to any one of claims 1 to 12, comprising a feeder, a conveyor belt, a filling station, a curing line, a
Abtrageinheit und eine Ablängvorrichtung umfasst, dadurch  Removal unit and a cutting device comprises, characterized
gekennzeichnet, dass nach der Abtrageinheit (29) oder nach der  in that after the removal unit (29) or after the
Ablängvorrichtung (30) eine Härterauftragseinheit (23) zum Auftragen eines Härters auf die abgetragenen Flächen vorgesehen ist.  Ablängvorrichtung (30) a hardener application unit (23) for applying a hardener is provided on the ablated surfaces.
14. Einrichtung nach Anspruch 13, dadurch gekennzeichnet, dass im Bereich der Zuführvorrichtung (24) eine Heizeinrichtung (25) für die metallischen Profile vorgesehen ist. 14. Device according to claim 13, characterized in that in the region of the feed device (24) a heating device (25) is provided for the metallic profiles.
15. Einrichtung nach Anspruch 13 oder 14, dadurch gekennzeichnet, dass das Transportband (26) aus einem endlosen Band gebildet ist, wobei die dem Profilstab zugewandte Seite dieses Endlosbandes mit Tetrafluorethylen beschichtet ist. 15. Device according to claim 13 or 14, characterized in that the conveyor belt (26) is formed from an endless belt, wherein the profile bar facing side of this endless belt is coated with tetrafluoroethylene.
16. Einrichtung nach einem der Ansprüche 13 bis 15, dadurch gekennzeichnet, dass als Abtrageinheit (29) mindestens eine, vorzugsweise zwei, 16. Device according to one of claims 13 to 15, characterized in that as a removal unit (29) at least one, preferably two,
Fräsmaschinen vorgesehen sind.  Milling machines are provided.
PCT/AT2010/000331 2009-09-16 2010-09-14 Insulation part WO2011032193A2 (en)