WO2011028206A1 - Masterbatch composition having a high polymer processing aid - Google Patents
Masterbatch composition having a high polymer processing aid Download PDFInfo
- Publication number
- WO2011028206A1 WO2011028206A1 PCT/US2009/056009 US2009056009W WO2011028206A1 WO 2011028206 A1 WO2011028206 A1 WO 2011028206A1 US 2009056009 W US2009056009 W US 2009056009W WO 2011028206 A1 WO2011028206 A1 WO 2011028206A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- masterbatch composition
- weight
- colorant
- masterbatch
- processing aid
- Prior art date
Abstract
Description
Claims