WO2011014068A1 - Cellule photovoltaïque à émetteur sélectif et son procédé de production - Google Patents

Cellule photovoltaïque à émetteur sélectif et son procédé de production Download PDF

Info

Publication number
WO2011014068A1
WO2011014068A1 PCT/NL2010/050489 NL2010050489W WO2011014068A1 WO 2011014068 A1 WO2011014068 A1 WO 2011014068A1 NL 2010050489 W NL2010050489 W NL 2010050489W WO 2011014068 A1 WO2011014068 A1 WO 2011014068A1
Authority
WO
WIPO (PCT)
Prior art keywords
pattern
substrate
dopant source
nozzles
acid solution
Prior art date
Application number
PCT/NL2010/050489
Other languages
English (en)
Inventor
Woutherus Johannes Maria Brok
Emerentius Maria Josephus Antonius Van Dijk
Franciscus Cornelius Dings
Wouterus Johannes Paulus Carolus Van Vugt
Original Assignee
Otb Solar B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Otb Solar B.V. filed Critical Otb Solar B.V.
Priority to EP10740419A priority Critical patent/EP2460188A1/fr
Priority to CN2010800440586A priority patent/CN102549776A/zh
Publication of WO2011014068A1 publication Critical patent/WO2011014068A1/fr

Abstract

L’invention concerne un procédé de production de dispositif à semi-conducteur (1) comprenant un substrat semi-conducteur essentiellement plat (2). Le procédé comprend trois étapes consistant à : 1) appliquer une source de dopant pour sélectivement imprimer par jet d’encre un premier motif d'une solution d’acide phosphorique ou d’acide borique sur une surface principale (2a) du substrat semi-conducteur; 2) chauffer le substrat de façon à diffuser des atomes de phosphore ou de bore provenant de la source de dopant dans le substrat, ce qui permet de former des premières zones de diffusion (4) immédiatement en-dessous du premier motif; et 3) former un motif de contact métallique (10, 11, 12) sensiblement en alignement avec les premières zones de diffusion. L’invention concerne également une cellule photovoltaïque produite à partir de ce procédé.
PCT/NL2010/050489 2009-07-31 2010-07-30 Cellule photovoltaïque à émetteur sélectif et son procédé de production WO2011014068A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP10740419A EP2460188A1 (fr) 2009-07-31 2010-07-30 Cellule photovoltaïque à émetteur sélectif et son procédé de production
CN2010800440586A CN102549776A (zh) 2009-07-31 2010-07-30 具有选择性发射极的光伏电池及其制造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
NL2003324 2009-07-31
NL2003324A NL2003324C2 (en) 2009-07-31 2009-07-31 Photovoltaic cell with a selective emitter and method for making the same.

Publications (1)

Publication Number Publication Date
WO2011014068A1 true WO2011014068A1 (fr) 2011-02-03

Family

ID=42269439

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/NL2010/050489 WO2011014068A1 (fr) 2009-07-31 2010-07-30 Cellule photovoltaïque à émetteur sélectif et son procédé de production

Country Status (5)

Country Link
EP (1) EP2460188A1 (fr)
CN (1) CN102549776A (fr)
NL (1) NL2003324C2 (fr)
TW (1) TW201110404A (fr)
WO (1) WO2011014068A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8912071B2 (en) 2012-12-06 2014-12-16 International Business Machines Corporation Selective emitter photovoltaic device
EP3146015A4 (fr) * 2014-05-20 2018-05-16 Alpha Metals, Inc. Encres pulvérisables pour fabrication de cellule solaire et de semi-conducteurs

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2010012A (en) * 1977-12-09 1979-06-20 Ibm Phosphorus diffusion process for semiconductors
JP2000183379A (ja) * 1998-12-11 2000-06-30 Sanyo Electric Co Ltd 太陽電池の製造方法
DE10150040A1 (de) * 2001-10-10 2003-04-17 Merck Patent Gmbh Kombinierte Ätz- und Dotiermedien
US6552414B1 (en) * 1996-12-24 2003-04-22 Imec Vzw Semiconductor device with selectively diffused regions
US6695903B1 (en) * 1999-03-11 2004-02-24 Merck Patent Gmbh Dopant pastes for the production of p, p+, and n, n+ regions in semiconductors
JP2004221149A (ja) 2003-01-10 2004-08-05 Hitachi Ltd 太陽電池の製造方法
US20070151598A1 (en) 2005-12-21 2007-07-05 Denis De Ceuster Back side contact solar cell structures and fabrication processes
EP1876651A1 (fr) * 2005-04-26 2008-01-09 Shin-Etsu Handotai Co., Ltd Procede de fabrication d' une cellule solaire, cellule solaire et procede de fabrication d' un dispositif semi-conducteur

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0851511A1 (fr) * 1996-12-24 1998-07-01 IMEC vzw Dispositif semi-conducteur avec deux régions diffusées sélectivement

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2010012A (en) * 1977-12-09 1979-06-20 Ibm Phosphorus diffusion process for semiconductors
US6552414B1 (en) * 1996-12-24 2003-04-22 Imec Vzw Semiconductor device with selectively diffused regions
US6825104B2 (en) 1996-12-24 2004-11-30 Interuniversitair Micro-Elektronica Centrum (Imec) Semiconductor device with selectively diffused regions
JP2000183379A (ja) * 1998-12-11 2000-06-30 Sanyo Electric Co Ltd 太陽電池の製造方法
US6695903B1 (en) * 1999-03-11 2004-02-24 Merck Patent Gmbh Dopant pastes for the production of p, p+, and n, n+ regions in semiconductors
DE10150040A1 (de) * 2001-10-10 2003-04-17 Merck Patent Gmbh Kombinierte Ätz- und Dotiermedien
JP2004221149A (ja) 2003-01-10 2004-08-05 Hitachi Ltd 太陽電池の製造方法
EP1876651A1 (fr) * 2005-04-26 2008-01-09 Shin-Etsu Handotai Co., Ltd Procede de fabrication d' une cellule solaire, cellule solaire et procede de fabrication d' un dispositif semi-conducteur
US20070151598A1 (en) 2005-12-21 2007-07-05 Denis De Ceuster Back side contact solar cell structures and fabrication processes

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8912071B2 (en) 2012-12-06 2014-12-16 International Business Machines Corporation Selective emitter photovoltaic device
US8912529B2 (en) 2012-12-06 2014-12-16 International Business Machines Corporation Selective emitter photovoltaic device
US9263616B2 (en) 2012-12-06 2016-02-16 International Business Machines Corporation Selective emitter photovoltaic device
EP3146015A4 (fr) * 2014-05-20 2018-05-16 Alpha Metals, Inc. Encres pulvérisables pour fabrication de cellule solaire et de semi-conducteurs
US10465295B2 (en) 2014-05-20 2019-11-05 Alpha Assembly Solutions Inc. Jettable inks for solar cell and semiconductor fabrication

Also Published As

Publication number Publication date
EP2460188A1 (fr) 2012-06-06
TW201110404A (en) 2011-03-16
CN102549776A (zh) 2012-07-04
NL2003324C2 (en) 2011-02-02

Similar Documents

Publication Publication Date Title
US8420517B2 (en) Methods of forming a multi-doped junction with silicon-containing particles
US7629257B2 (en) Combined etching and doping substances
US6552414B1 (en) Semiconductor device with selectively diffused regions
US8053867B2 (en) Phosphorous-comprising dopants and methods for forming phosphorous-doped regions in semiconductor substrates using phosphorous-comprising dopants
US7615393B1 (en) Methods of forming multi-doped junctions on a substrate
EP0960443B1 (fr) Dispositif semi-conducteur dote de zones diffusees de facon selective
US8394658B2 (en) Methods of using a silicon nanoparticle fluid to control in situ a set of dopant diffusion profiles
US7820532B2 (en) Methods for simultaneously forming doped regions having different conductivity-determining type element profiles
CN110265497B (zh) 一种选择性发射极的n型晶体硅太阳电池及其制备方法
KR20070099840A (ko) 태양 전지 및 이의 제조 방법
KR20110089291A (ko) 기판에 다중 도핑된 접합을 형성하는 방법
US20110244626A1 (en) Method of forming solar cell
US20110183504A1 (en) Methods of forming a dual-doped emitter on a substrate with an inline diffusion apparatus
NL2003324C2 (en) Photovoltaic cell with a selective emitter and method for making the same.
JP2928433B2 (ja) 光電変換素子の製造方法
Nakano et al. Development of a Novel Phosphorus Spray Diffusion System for Low Cost Silicon Solar Cells

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201080044058.6

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10740419

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2010740419

Country of ref document: EP