WO2010085764A2 - Procédé, appareil, et compositions de fabrication de revêtements anti-réfléchissants pour des substrats - Google Patents
Procédé, appareil, et compositions de fabrication de revêtements anti-réfléchissants pour des substrats Download PDFInfo
- Publication number
- WO2010085764A2 WO2010085764A2 PCT/US2010/022010 US2010022010W WO2010085764A2 WO 2010085764 A2 WO2010085764 A2 WO 2010085764A2 US 2010022010 W US2010022010 W US 2010022010W WO 2010085764 A2 WO2010085764 A2 WO 2010085764A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- reflective
- deposition
- nanoparticles
- product
- Prior art date
Abstract
Les modes de réalisation du présent système et du présent procédé sont utiles pour le dépôt chimique, notamment le dépôt continu de film anti-réfléchissants. La présente invention concerne des systèmes qui comprennent généralement un micromixeur et un applicateur de microcanaux. Un matériau ou des matériaux de dépôt sont appliqués à un substrat, tel que l'aluminium, le verre, le silicium, ou le polycarbonate, pour former un revêtement anti-réfléchissant nanostructuré. Les morphologies de surface uniformes et hautement orientées des films déposés à l'aide des modes de réalisation décrits sont clairement améliorées par rapport à celles des films déposés par un procédé discontinu habituel. Dans certains modes de réalisation, un revêtement anti-réfléchissant est appliqué à une surface d'un microréacteur catalytique solaire adapté pour réaliser des réactions endothermiques, l'énergie étant fournie au réacteur par absorption des rayons solaires. Le procédé peut être utilisé pour personnaliser la composition et la morphologie du matériau déposé sur un substrat. Le présent procédé peut être utilisé à des températures faibles lorsqu'une étape d'annelage post-dépôt à température élevée est évitée.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US13/189,411 US8553333B2 (en) | 2009-01-23 | 2011-07-22 | Nanostructured anti-reflective coatings for substrates |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US20576609P | 2009-01-23 | 2009-01-23 | |
US61/205,766 | 2009-01-23 |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/189,411 Continuation-In-Part US8553333B2 (en) | 2009-01-23 | 2011-07-22 | Nanostructured anti-reflective coatings for substrates |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2010085764A2 true WO2010085764A2 (fr) | 2010-07-29 |
WO2010085764A3 WO2010085764A3 (fr) | 2010-11-18 |
Family
ID=42356423
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2010/022010 WO2010085764A2 (fr) | 2009-01-23 | 2010-01-25 | Procédé, appareil, et compositions de fabrication de revêtements anti-réfléchissants pour des substrats |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2010085764A2 (fr) |
Cited By (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8236599B2 (en) | 2009-04-09 | 2012-08-07 | State of Oregon acting by and through the State Board of Higher Education | Solution-based process for making inorganic materials |
US20140009834A1 (en) * | 2012-07-05 | 2014-01-09 | Intermolecular, Inc. | Novel antireflective coatings with graded refractive index |
US8801979B2 (en) | 2010-06-10 | 2014-08-12 | State Of Oregon Acting By And Through The State Board Of Higher Education On Behalf Of Oregon State University | Apparatus and method for continuous production of materials |
US9328969B2 (en) | 2011-10-07 | 2016-05-03 | Outset Medical, Inc. | Heat exchange fluid purification for dialysis system |
US9402945B2 (en) | 2014-04-29 | 2016-08-02 | Outset Medical, Inc. | Dialysis system and methods |
US9545469B2 (en) | 2009-12-05 | 2017-01-17 | Outset Medical, Inc. | Dialysis system with ultrafiltration control |
WO2017216592A3 (fr) * | 2016-06-15 | 2018-03-15 | Hungaro Lux Light Kft | Film antireflet et son utilisation sur un substrat |
CN110981208A (zh) * | 2019-12-17 | 2020-04-10 | 河南豫科光学科技股份有限公司 | 一种超白玻璃基板的制备工艺 |
CN114163882A (zh) * | 2021-12-06 | 2022-03-11 | 中科智清生态技术(苏州)有限公司 | 一种河道治理的光伏面板膜层及生产工艺 |
CN114524450A (zh) * | 2022-03-21 | 2022-05-24 | 南京科技职业学院 | 一种纳米氧化铈紫外吸收剂的制备方法 |
US11534537B2 (en) | 2016-08-19 | 2022-12-27 | Outset Medical, Inc. | Peritoneal dialysis system and methods |
US11724013B2 (en) | 2010-06-07 | 2023-08-15 | Outset Medical, Inc. | Fluid purification system |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20010006048A (ko) * | 1997-04-04 | 2001-01-15 | 무네유키 가코우 | 반사방지 필름 및 이를 이용한 화상표시장치 |
JP2001281411A (ja) * | 2000-03-30 | 2001-10-10 | Fuji Photo Film Co Ltd | 防眩性反射防止フィルムおよび画像表示装置 |
US6343865B1 (en) * | 1998-02-17 | 2002-02-05 | Dai Nippon Printing Co., Ltd. | Non-glare film, polarizing device and display device |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20010106048A (ko) * | 2000-05-20 | 2001-11-29 | 서정은 | 스타들로 구성된 상설 라이브 콘서트 |
-
2010
- 2010-01-25 WO PCT/US2010/022010 patent/WO2010085764A2/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20010006048A (ko) * | 1997-04-04 | 2001-01-15 | 무네유키 가코우 | 반사방지 필름 및 이를 이용한 화상표시장치 |
US6343865B1 (en) * | 1998-02-17 | 2002-02-05 | Dai Nippon Printing Co., Ltd. | Non-glare film, polarizing device and display device |
JP2001281411A (ja) * | 2000-03-30 | 2001-10-10 | Fuji Photo Film Co Ltd | 防眩性反射防止フィルムおよび画像表示装置 |
Cited By (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8236599B2 (en) | 2009-04-09 | 2012-08-07 | State of Oregon acting by and through the State Board of Higher Education | Solution-based process for making inorganic materials |
US9545469B2 (en) | 2009-12-05 | 2017-01-17 | Outset Medical, Inc. | Dialysis system with ultrafiltration control |
US11724013B2 (en) | 2010-06-07 | 2023-08-15 | Outset Medical, Inc. | Fluid purification system |
US8801979B2 (en) | 2010-06-10 | 2014-08-12 | State Of Oregon Acting By And Through The State Board Of Higher Education On Behalf Of Oregon State University | Apparatus and method for continuous production of materials |
US9328969B2 (en) | 2011-10-07 | 2016-05-03 | Outset Medical, Inc. | Heat exchange fluid purification for dialysis system |
US20140009834A1 (en) * | 2012-07-05 | 2014-01-09 | Intermolecular, Inc. | Novel antireflective coatings with graded refractive index |
US11305040B2 (en) | 2014-04-29 | 2022-04-19 | Outset Medical, Inc. | Dialysis system and methods |
US9579440B2 (en) | 2014-04-29 | 2017-02-28 | Outset Medical, Inc. | Dialysis system and methods |
US9504777B2 (en) | 2014-04-29 | 2016-11-29 | Outset Medical, Inc. | Dialysis system and methods |
US9402945B2 (en) | 2014-04-29 | 2016-08-02 | Outset Medical, Inc. | Dialysis system and methods |
WO2017216592A3 (fr) * | 2016-06-15 | 2018-03-15 | Hungaro Lux Light Kft | Film antireflet et son utilisation sur un substrat |
US11029514B2 (en) | 2016-06-15 | 2021-06-08 | Hungaro Lux Light Kft. | Antireflection film and its use on a substrate |
US11534537B2 (en) | 2016-08-19 | 2022-12-27 | Outset Medical, Inc. | Peritoneal dialysis system and methods |
US11951241B2 (en) | 2016-08-19 | 2024-04-09 | Outset Medical, Inc. | Peritoneal dialysis system and methods |
CN110981208A (zh) * | 2019-12-17 | 2020-04-10 | 河南豫科光学科技股份有限公司 | 一种超白玻璃基板的制备工艺 |
CN114163882A (zh) * | 2021-12-06 | 2022-03-11 | 中科智清生态技术(苏州)有限公司 | 一种河道治理的光伏面板膜层及生产工艺 |
CN114524450A (zh) * | 2022-03-21 | 2022-05-24 | 南京科技职业学院 | 一种纳米氧化铈紫外吸收剂的制备方法 |
CN114524450B (zh) * | 2022-03-21 | 2024-01-19 | 南京科技职业学院 | 一种纳米氧化铈紫外吸收剂的制备方法 |
Also Published As
Publication number | Publication date |
---|---|
WO2010085764A3 (fr) | 2010-11-18 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2010085764A2 (fr) | Procédé, appareil, et compositions de fabrication de revêtements anti-réfléchissants pour des substrats | |
US8553333B2 (en) | Nanostructured anti-reflective coatings for substrates | |
Henderson et al. | Colloidally stable germanium nanocrystals for photonic applications | |
Guillemin et al. | Controlling the structural properties of single step, dip coated ZnO seed layers for growing perfectly aligned nanowire arrays | |
McPeak et al. | ZnO nanowires grown by chemical bath deposition in a continuous flow microreactor | |
Kumar et al. | Preparation and characterization of CuO nanostructures on copper substrate as selective solar absorbers | |
Wategaonkar et al. | Synthesis of rutile TiO2 nanostructures by single step hydrothermal route and its characterization | |
US9763325B2 (en) | Microreactor-assisted printing of conductive traces with in-situ reactive inks | |
Liu et al. | ZnO tetrakaidecahedrons with coexposed {001},{101}, and {100} facets: shape-selective synthesis and enhancing photocatalytic performance | |
Li et al. | Micro/Nano hierarchical peony-like Al doped ZnO superhydrophobic film: The guiding effect of (100) preferred seed layer | |
CN108761581A (zh) | 一种折射率可调的SiO2减反射膜的制备方法 | |
Wallace et al. | Synthesis and characterization of zinc oxide (ZnO) nanowire | |
CN100376473C (zh) | 一种硒化锌多晶纳米薄膜的制备方法 | |
Park et al. | Synthesis and characterization of polycrystalline CuInS2 thin films for solar cell devices at low temperature processing conditions | |
Chang et al. | Investigate the reacting flux of chemical bath deposition by a continuous flow microreactor | |
Thiyagu et al. | Ultra-low reflectance, high absorption microcrystalline silicon nanostalagmite | |
Vas-Umnuay et al. | Conformal growth of copper sulfide thin films on highly textured surface via microreactor-assisted solution deposition | |
Liufu et al. | Bismuth sulfide thin films with low resistivity on self-assembled monolayers | |
Doddapaneni et al. | Transformation, reaction and organization of functional nanostructures using solution-based microreactor-assisted nanomaterial deposition for solar photovoltaics | |
Önal et al. | Effect of stirring on chemically deposited ZnO thin films | |
CN105645462A (zh) | 一种CdS/ZnO核壳结构纳米线的制备方法 | |
Gayathri et al. | Preparation and effect of complexing agents on ternary FeZnS 2 thin films by chemical bath deposition method for photo catalytic degradation of dye molecules | |
Sankir et al. | Spray Pyrolysis of Nano‐Structured Optical and Electronic Materials | |
KR20130098057A (ko) | 연속흐름마이크로반응법을 이용한 황화구리 박막의 제조방법 | |
Castilla et al. | PbS Nanostructures Thin Films by in situ PbS: Ni and PbS: Cd-Doping |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10733980 Country of ref document: EP Kind code of ref document: A2 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 10733980 Country of ref document: EP Kind code of ref document: A2 |