WO2010043624A2 - Polyesterpolyole auf basis von terephthalsäure - Google Patents
Polyesterpolyole auf basis von terephthalsäure Download PDFInfo
- Publication number
- WO2010043624A2 WO2010043624A2 PCT/EP2009/063358 EP2009063358W WO2010043624A2 WO 2010043624 A2 WO2010043624 A2 WO 2010043624A2 EP 2009063358 W EP2009063358 W EP 2009063358W WO 2010043624 A2 WO2010043624 A2 WO 2010043624A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- oil
- mol
- weight
- fatty
- Prior art date
Abstract
Description
Claims