WO2010000638A1 - Blends of stabilizers for aliphatic polyesters - Google Patents
Blends of stabilizers for aliphatic polyesters Download PDFInfo
- Publication number
- WO2010000638A1 WO2010000638A1 PCT/EP2009/057766 EP2009057766W WO2010000638A1 WO 2010000638 A1 WO2010000638 A1 WO 2010000638A1 EP 2009057766 W EP2009057766 W EP 2009057766W WO 2010000638 A1 WO2010000638 A1 WO 2010000638A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tert
- bis
- butyl
- hydroxy
- component
- Prior art date
Abstract
Description
Claims