WO2009124229A1 - Method for applying a pressure sensitive shrink label to an article - Google Patents
Method for applying a pressure sensitive shrink label to an article Download PDFInfo
- Publication number
- WO2009124229A1 WO2009124229A1 PCT/US2009/039398 US2009039398W WO2009124229A1 WO 2009124229 A1 WO2009124229 A1 WO 2009124229A1 US 2009039398 W US2009039398 W US 2009039398W WO 2009124229 A1 WO2009124229 A1 WO 2009124229A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- label
- film
- article
- heat
- edge
- Prior art date
Abstract
Description
Claims