WO2009036953A1 - Produit en alliage ai-cu-li qui convient pour une application aérospatiale - Google Patents
Produit en alliage ai-cu-li qui convient pour une application aérospatiale Download PDFInfo
- Publication number
- WO2009036953A1 WO2009036953A1 PCT/EP2008/007731 EP2008007731W WO2009036953A1 WO 2009036953 A1 WO2009036953 A1 WO 2009036953A1 EP 2008007731 W EP2008007731 W EP 2008007731W WO 2009036953 A1 WO2009036953 A1 WO 2009036953A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- aluminium alloy
- range
- alloy product
- product
- stock
- Prior art date
Abstract
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2010110350/02A RU2481412C2 (ru) | 2007-09-21 | 2008-09-16 | ПРОДУКТ ИЗ Al-Cu-Li СПЛАВА, ПРИГОДНЫЙ ДЛЯ ПРИМЕНЕНИЯ В АВИАЦИИ И КОСМОНАВТИКЕ |
CA2700250A CA2700250C (fr) | 2007-09-21 | 2008-09-16 | Produit en alliage ai-cu-li qui convient pour une application aerospatiale |
CN200880107556.3A CN101855376B (zh) | 2007-09-21 | 2008-09-16 | 适于航空应用的Al-Cu-Li合金产品 |
DE112008002522T DE112008002522T5 (de) | 2007-09-21 | 2008-09-16 | Al-Cu-Li Legierungsprodukt, welches für eine Luftfahrzeuganwendung geeignet ist |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP07018595 | 2007-09-21 | ||
EP07018595.4 | 2007-09-21 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2009036953A1 true WO2009036953A1 (fr) | 2009-03-26 |
Family
ID=38754771
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2008/007731 WO2009036953A1 (fr) | 2007-09-21 | 2008-09-16 | Produit en alliage ai-cu-li qui convient pour une application aérospatiale |
Country Status (5)
Country | Link |
---|---|
CN (2) | CN101855376B (fr) |
CA (1) | CA2700250C (fr) |
DE (2) | DE202008018370U1 (fr) |
RU (2) | RU2481412C2 (fr) |
WO (1) | WO2009036953A1 (fr) |
Cited By (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2010149873A1 (fr) * | 2009-06-25 | 2010-12-29 | Alcan Rhenalu | Alliage aluminium cuivre lithium a resistance mecanique et tenacite ameliorees |
US8118950B2 (en) | 2007-12-04 | 2012-02-21 | Alcoa Inc. | Aluminum-copper-lithium alloys |
AU2011226797B2 (en) * | 2010-09-08 | 2012-04-19 | Alcoa Inc. | Improved aluminum-lithium alloys, and methods for producing the same |
US20120152415A1 (en) * | 2010-12-20 | 2012-06-21 | Constellium France | Aluminum copper lithium alloy with improved resistance under compression and fracture toughness |
EP2558564A1 (fr) | 2010-04-12 | 2013-02-20 | Alcoa Inc. | Alliages d'aluminium lithium de série 2xxx à faible différentiel de résistance |
WO2013153292A1 (fr) | 2012-04-11 | 2013-10-17 | Constellium France | Alliage aluminium cuivre lithium à résistance au choc améliorée |
WO2013169901A1 (fr) * | 2012-05-09 | 2013-11-14 | Alcoa Inc. | Alliages d'aluminium lithium de série 2xxx |
EP2675933A2 (fr) * | 2011-02-17 | 2013-12-25 | Alcoa Inc. | Alliages d'aluminium-lithium de la série 2xxx |
KR20160040464A (ko) * | 2013-06-21 | 2016-04-14 | 콩스텔리움 이수와르 | 알루미늄 구리 리튬 합금으로 제조된 외호면 구조 요소 |
EP2937435A4 (fr) * | 2012-12-21 | 2016-09-07 | Kawasaki Heavy Ind Ltd | Procédé de fabrication d'un composant façonné en alliage d'aluminium destiné à un aéronef et composant façonné destiné à un aéronef |
US9587298B2 (en) | 2013-02-19 | 2017-03-07 | Arconic Inc. | Heat treatable aluminum alloys having magnesium and zinc and methods for producing the same |
CN106795595A (zh) * | 2014-10-03 | 2017-05-31 | 伊苏瓦尔肯联铝业 | 用于制造飞机机身的各向同性铝‑铜‑锂合金板 |
CN106884129A (zh) * | 2017-03-14 | 2017-06-23 | 广州金邦液态模锻技术有限公司 | 一种用于挤压铸造铝合金转向节的热处理工艺 |
CN106893911A (zh) * | 2017-02-27 | 2017-06-27 | 广东省材料与加工研究所 | 一种高强耐热Al‑Cu系铝合金及其制备方法 |
EP3072984B1 (fr) | 2015-03-27 | 2017-07-05 | Otto Fuchs KG | Alliage d'al-cu-mg-li et produit allié ainsi produit |
EP2981632B1 (fr) | 2013-04-03 | 2017-08-02 | Constellium Issoire | Tôles minces en alliage d'aluminium-cuivre-lithium pour la fabrication de fuselages d'avion |
WO2017137260A1 (fr) * | 2016-02-09 | 2017-08-17 | Aleris Rolled Products Germany Gmbh | Produit d'alliage corroyé à base d'al-cu-li-mg-mn-zn |
US9926620B2 (en) | 2012-03-07 | 2018-03-27 | Arconic Inc. | 2xxx aluminum alloys, and methods for producing the same |
DE202017100517U1 (de) | 2017-01-31 | 2018-05-03 | Aleris Rolled Products Germany Gmbh | Al-Cu-Li-Mg-Mn-Zn Knetlegierungsprodukt |
CN108118271A (zh) * | 2017-12-08 | 2018-06-05 | 北京星航机电装备有限公司 | 一种异形铝合金舱段热处理变形控制方法 |
WO2019211546A1 (fr) | 2018-05-02 | 2019-11-07 | Constellium Issoire | Procede de fabrication d'un alliage aluminium cuivre lithium a resistance en compression et tenacite ameliorees |
WO2019211547A1 (fr) | 2018-05-02 | 2019-11-07 | Constellium Issoire | Alliage aluminium cuivre lithium a resistance en compression et tenacite ameliorees |
RU2716722C2 (ru) * | 2014-10-26 | 2020-03-16 | КАЙЗЕР АЛЮМИНУМ ФАБРИКЕЙТЕД ПРОДАКТС, ЭлЭлСи | Алюминиево-литиевые сплавы с высокой прочностью, высокой деформируемостью и низкой стоимостью |
EP3411508B1 (fr) | 2016-02-03 | 2020-04-08 | Constellium Issoire | Tôles épaisses en alliage al cu li à propriétés en fatigue améliorées |
CN111020425A (zh) * | 2019-12-25 | 2020-04-17 | 辽宁忠旺集团有限公司 | 一种2系铝合金热处理工艺 |
WO2020097169A1 (fr) * | 2018-11-07 | 2020-05-14 | Arconic Inc. | Alliages d'aluminium-lithium de la série 2xxx |
WO2020102441A3 (fr) * | 2018-11-14 | 2020-08-20 | Arconic Inc. | Alliages d'aluminium 7xxx améliorés |
CN113981280A (zh) * | 2021-11-01 | 2022-01-28 | 北京理工大学 | 一种低密度高强高弹性模量的铝锂合金及制备方法 |
CN115584403A (zh) * | 2015-12-18 | 2023-01-10 | 诺维尔里斯公司 | 高强度6xxx铝合金和其制备方法 |
US11920229B2 (en) | 2015-12-18 | 2024-03-05 | Novelis Inc. | High strength 6XXX aluminum alloys and methods of making the same |
Families Citing this family (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN101967588B (zh) * | 2010-10-27 | 2012-08-29 | 中国航空工业集团公司北京航空材料研究院 | 一种耐损伤铝锂合金及其制备方法 |
CN102021457B (zh) * | 2010-10-27 | 2012-06-27 | 中国航空工业集团公司北京航空材料研究院 | 一种高强韧铝锂合金及其制备方法 |
CN101967589B (zh) * | 2010-10-27 | 2013-02-20 | 中国航空工业集团公司北京航空材料研究院 | 一种中强高韧铝锂合金及其制备方法 |
FR2975403B1 (fr) * | 2011-05-20 | 2018-11-02 | Constellium Issoire | Alliage aluminium magnesium lithium a tenacite amelioree |
CN102634706A (zh) * | 2012-04-28 | 2012-08-15 | 中南大学 | 一种高强、高韧、耐蚀Al-Cu-Mg铝合金 |
US20140050936A1 (en) * | 2012-08-17 | 2014-02-20 | Alcoa Inc. | 2xxx series aluminum lithium alloys |
CN103352146B (zh) * | 2013-08-02 | 2015-04-08 | 贵州合润铝业高新科技发展有限公司 | 铝合金 |
CN103397229B (zh) * | 2013-08-02 | 2015-04-08 | 贵州合润铝业高新科技发展有限公司 | 一种铝合金的制备方法 |
CN104018043B (zh) * | 2014-06-19 | 2016-08-24 | 芜湖市泰美机械设备有限公司 | 一种高强度航空用铸造铝合金及其热处理方法 |
RU2698242C1 (ru) * | 2015-11-25 | 2019-08-23 | Отто Фукс-Коммандитгезельшафт | Труба для использования совместно с глубоко пробуренной скважиной |
CN106131720B (zh) * | 2016-08-30 | 2019-02-05 | 宁波泊人艾电子有限公司 | 一种多功能便携音箱 |
CN106131719B (zh) * | 2016-08-30 | 2019-02-05 | 宁波泊人艾电子有限公司 | 一种便携音箱 |
CN106358115A (zh) * | 2016-08-30 | 2017-01-25 | 宁波大诚和电子有限公司 | 一种多功能便携音箱的扬声控制单元 |
CN106591649A (zh) * | 2016-12-14 | 2017-04-26 | 沈阳工业大学 | 一种高强Al‑Cu‑Mg‑Mn‑Er变形铝合金及其制备方法 |
CN110423927A (zh) * | 2019-07-17 | 2019-11-08 | 中南大学 | 一种超高强铝锂合金及其制备方法 |
CN111575561B (zh) * | 2020-05-25 | 2022-02-08 | 江苏豪然喷射成形合金有限公司 | 一种大深度承压壳体用铝锂合金及其制备方法 |
CN114214548A (zh) * | 2021-12-17 | 2022-03-22 | 中南大学 | 一种高强高淬透性铝锂合金及其制备方法 |
CN115386818A (zh) * | 2022-08-25 | 2022-11-25 | 中南大学 | 一种Al-Cu-Li系合金热轧板坯的形变热处理方法 |
CN115505807B (zh) * | 2022-09-21 | 2023-06-27 | 郑州轻研合金科技有限公司 | 一种高比强铝锂合金及其制备方法和应用 |
CN115710662B (zh) * | 2022-11-21 | 2024-02-06 | 郑州轻研合金科技有限公司 | 一种高强高韧铝锂合金板材及其生产工艺 |
Citations (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1989001531A1 (fr) * | 1987-08-10 | 1989-02-23 | Martin Marietta Corporation | Alliages d'aluminium-lithium soudables a resistance ultra elevee |
JPH03107440A (ja) * | 1989-09-20 | 1991-05-07 | Showa Alum Corp | ロードセル用アルミニウム合金 |
WO1992020830A1 (fr) * | 1991-05-14 | 1992-11-26 | Reynolds Metals Company | ALLIAGE DE Al-Li A RESISTANCE ELEVEE ET A FAIBLE DENSITE |
US5211910A (en) * | 1990-01-26 | 1993-05-18 | Martin Marietta Corporation | Ultra high strength aluminum-base alloys |
US5389165A (en) * | 1991-05-14 | 1995-02-14 | Reynolds Metals Company | Low density, high strength Al-Li alloy having high toughness at elevated temperatures |
US5393357A (en) * | 1992-10-06 | 1995-02-28 | Reynolds Metals Company | Method of minimizing strength anisotropy in aluminum-lithium alloy wrought product by cold rolling, stretching and aging |
WO2002063059A1 (fr) * | 2000-10-20 | 2002-08-15 | Pechiney Rolled Products, Llc | Alliage d'aluminium a haute resistance |
US20040071586A1 (en) * | 1998-06-24 | 2004-04-15 | Rioja Roberto J. | Aluminum-copper-magnesium alloys having ancillary additions of lithium |
RU2237098C1 (ru) * | 2003-07-24 | 2004-09-27 | Федеральное государственное унитарное предприятие "Всероссийский научно-исследовательский институт авиационных материалов" | Сплав на основе алюминия и изделие, выполненное из него |
WO2004106570A1 (fr) * | 2003-05-28 | 2004-12-09 | Pechiney Rolled Products | Nouvel alliage de al-cu-li-mg-ag-mn-zr utilise comme elements structurels exigeant une haute resistance ainsi qu'une grande tenacite a la rupture |
US20070181229A1 (en) * | 2005-12-20 | 2007-08-09 | Bernard Bes | High fracture toughness aluminum-copper-lithium sheet or light-gauge plates suitable for fuselage panels |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2415202B (en) * | 2003-04-10 | 2007-08-29 | Corus Aluminium Walzprod Gmbh | An Al-Zn-Mg-Cu alloy |
-
2008
- 2008-09-16 DE DE202008018370U patent/DE202008018370U1/de not_active Expired - Lifetime
- 2008-09-16 CA CA2700250A patent/CA2700250C/fr not_active Expired - Fee Related
- 2008-09-16 CN CN200880107556.3A patent/CN101855376B/zh not_active Expired - Fee Related
- 2008-09-16 CN CN201310124663.XA patent/CN103266246B/zh not_active Expired - Fee Related
- 2008-09-16 RU RU2010110350/02A patent/RU2481412C2/ru not_active IP Right Cessation
- 2008-09-16 WO PCT/EP2008/007731 patent/WO2009036953A1/fr active Application Filing
- 2008-09-16 DE DE112008002522T patent/DE112008002522T5/de not_active Withdrawn
-
2013
- 2013-01-18 RU RU2013102512A patent/RU2627085C2/ru not_active IP Right Cessation
Patent Citations (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1989001531A1 (fr) * | 1987-08-10 | 1989-02-23 | Martin Marietta Corporation | Alliages d'aluminium-lithium soudables a resistance ultra elevee |
JPH03107440A (ja) * | 1989-09-20 | 1991-05-07 | Showa Alum Corp | ロードセル用アルミニウム合金 |
US5211910A (en) * | 1990-01-26 | 1993-05-18 | Martin Marietta Corporation | Ultra high strength aluminum-base alloys |
WO1992020830A1 (fr) * | 1991-05-14 | 1992-11-26 | Reynolds Metals Company | ALLIAGE DE Al-Li A RESISTANCE ELEVEE ET A FAIBLE DENSITE |
US5389165A (en) * | 1991-05-14 | 1995-02-14 | Reynolds Metals Company | Low density, high strength Al-Li alloy having high toughness at elevated temperatures |
US5393357A (en) * | 1992-10-06 | 1995-02-28 | Reynolds Metals Company | Method of minimizing strength anisotropy in aluminum-lithium alloy wrought product by cold rolling, stretching and aging |
US20040071586A1 (en) * | 1998-06-24 | 2004-04-15 | Rioja Roberto J. | Aluminum-copper-magnesium alloys having ancillary additions of lithium |
WO2002063059A1 (fr) * | 2000-10-20 | 2002-08-15 | Pechiney Rolled Products, Llc | Alliage d'aluminium a haute resistance |
WO2004106570A1 (fr) * | 2003-05-28 | 2004-12-09 | Pechiney Rolled Products | Nouvel alliage de al-cu-li-mg-ag-mn-zr utilise comme elements structurels exigeant une haute resistance ainsi qu'une grande tenacite a la rupture |
RU2237098C1 (ru) * | 2003-07-24 | 2004-09-27 | Федеральное государственное унитарное предприятие "Всероссийский научно-исследовательский институт авиационных материалов" | Сплав на основе алюминия и изделие, выполненное из него |
US20070181229A1 (en) * | 2005-12-20 | 2007-08-09 | Bernard Bes | High fracture toughness aluminum-copper-lithium sheet or light-gauge plates suitable for fuselage panels |
Non-Patent Citations (1)
Title |
---|
DATABASE WPI Derwent World Patents Index; AN 2004-755565, XP002461605 * |
Cited By (70)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8118950B2 (en) | 2007-12-04 | 2012-02-21 | Alcoa Inc. | Aluminum-copper-lithium alloys |
US9587294B2 (en) | 2007-12-04 | 2017-03-07 | Arconic Inc. | Aluminum-copper-lithium alloys |
AU2013257457B2 (en) * | 2007-12-04 | 2016-03-31 | Arconic Inc. | Improved aluminum-copper-lithium alloys |
CN102459671B (zh) * | 2009-06-25 | 2014-03-19 | 法国肯联铝业 | 具有改进的机械强度和韧性的铝-铜-锂合金 |
FR2947282A1 (fr) * | 2009-06-25 | 2010-12-31 | Alcan Rhenalu | Alliage aluminium cuivre lithium a resistance mecanique et tenacite ameliorees |
US20110209801A2 (en) * | 2009-06-25 | 2011-09-01 | Alcan Rhenalu | Aluminum-Copper-Lithium Alloy With Improved Mechanical Strength and Toughness |
US11111562B2 (en) | 2009-06-25 | 2021-09-07 | Constellium Issoire | Aluminum-copper-lithium alloy with improved mechanical strength and toughness |
CN102459671A (zh) * | 2009-06-25 | 2012-05-16 | 法国肯联铝业 | 具有改进的机械强度和韧性的铝-铜-锂合金 |
EP2449142B1 (fr) | 2009-06-25 | 2017-05-03 | Constellium Issoire | Alliage aluminium cuivre lithium a resistance mecanique et tenacite ameliorees |
WO2010149873A1 (fr) * | 2009-06-25 | 2010-12-29 | Alcan Rhenalu | Alliage aluminium cuivre lithium a resistance mecanique et tenacite ameliorees |
US8845827B2 (en) | 2010-04-12 | 2014-09-30 | Alcoa Inc. | 2XXX series aluminum lithium alloys having low strength differential |
EP2558564A1 (fr) | 2010-04-12 | 2013-02-20 | Alcoa Inc. | Alliages d'aluminium lithium de série 2xxx à faible différentiel de résistance |
EP3404123A1 (fr) * | 2010-04-12 | 2018-11-21 | Arconic Inc. | Alliages d'aluminium lithium de série 2xxx a faible différential de résistance |
RU2598423C2 (ru) * | 2010-04-12 | 2016-09-27 | Алкоа Инк. | Алюминий-литиевые сплавы серии 2ххх, имеющие низкую разность прочностей |
EP2558564A4 (fr) * | 2010-04-12 | 2015-07-15 | Alcoa Inc | Alliages d'aluminium lithium de série 2xxx à faible différentiel de résistance |
US10435774B2 (en) * | 2010-04-12 | 2019-10-08 | Arconic Inc. | 2XXX series aluminum lithium alloys having low strength differential |
US20150000799A1 (en) * | 2010-04-12 | 2015-01-01 | Alcoa Inc. | 2xxx series aluminum lithium alloys having low strength differential |
US8999079B2 (en) | 2010-09-08 | 2015-04-07 | Alcoa, Inc. | 6xxx aluminum alloys, and methods for producing the same |
US9249484B2 (en) | 2010-09-08 | 2016-02-02 | Alcoa Inc. | 7XXX aluminum alloys, and methods for producing the same |
CN103168110A (zh) * | 2010-09-08 | 2013-06-19 | 美铝公司 | 改进的铝-锂合金及其生产方法 |
AU2011226797B2 (en) * | 2010-09-08 | 2012-04-19 | Alcoa Inc. | Improved aluminum-lithium alloys, and methods for producing the same |
US9359660B2 (en) | 2010-09-08 | 2016-06-07 | Alcoa Inc. | 6XXX aluminum alloys, and methods for producing the same |
US9194028B2 (en) | 2010-09-08 | 2015-11-24 | Alcoa Inc. | 2xxx aluminum alloys, and methods for producing the same |
WO2012085359A3 (fr) * | 2010-12-20 | 2012-09-13 | Constellium France | Alliage aluminium cuivre lithium à résistance en compression et ténacité améliorées |
FR2969177A1 (fr) * | 2010-12-20 | 2012-06-22 | Alcan Rhenalu | Alliage aluminium cuivre lithium a resistance en compression et tenacite ameliorees |
US20120152415A1 (en) * | 2010-12-20 | 2012-06-21 | Constellium France | Aluminum copper lithium alloy with improved resistance under compression and fracture toughness |
KR102003569B1 (ko) | 2011-02-17 | 2019-07-24 | 아르코닉 인코포레이티드 | 2xxx 계열 알루미늄 리튬 합금 |
EP2675933A4 (fr) * | 2011-02-17 | 2014-10-22 | Alcoa Inc | Alliages d'aluminium-lithium de la série 2xxx |
EP2675933A2 (fr) * | 2011-02-17 | 2013-12-25 | Alcoa Inc. | Alliages d'aluminium-lithium de la série 2xxx |
EP3187603A1 (fr) * | 2011-02-17 | 2017-07-05 | Arconic Inc. | Alliages d'aluminium-lithium de la série 2xxx |
KR20140010074A (ko) * | 2011-02-17 | 2014-01-23 | 알코아 인코포레이티드 | 2xxx 계열 알루미늄 리튬 합금 |
EP2675933B1 (fr) | 2011-02-17 | 2017-02-08 | Alcoa Inc. | Alliages d'aluminium-lithium de la série 2xxx |
US9926620B2 (en) | 2012-03-07 | 2018-03-27 | Arconic Inc. | 2xxx aluminum alloys, and methods for producing the same |
FR2989387A1 (fr) * | 2012-04-11 | 2013-10-18 | Constellium France | Alliage aluminium cuivre lithium a resistance au choc amelioree |
US9945010B2 (en) | 2012-04-11 | 2018-04-17 | Constellium Issoire | Aluminum-copper-lithium alloy with improved impact resistance |
WO2013153292A1 (fr) | 2012-04-11 | 2013-10-17 | Constellium France | Alliage aluminium cuivre lithium à résistance au choc améliorée |
EP2847361B1 (fr) | 2012-05-09 | 2017-01-11 | Alcoa Inc. | Alliages d'aluminium lithium de série 2xxx |
RU2659529C2 (ru) * | 2012-05-09 | 2018-07-02 | Арконик Инк. | Алюминий-литиевые сплавы серии 2ххх |
US9458528B2 (en) | 2012-05-09 | 2016-10-04 | Alcoa Inc. | 2xxx series aluminum lithium alloys |
WO2013169901A1 (fr) * | 2012-05-09 | 2013-11-14 | Alcoa Inc. | Alliages d'aluminium lithium de série 2xxx |
EP2937435A4 (fr) * | 2012-12-21 | 2016-09-07 | Kawasaki Heavy Ind Ltd | Procédé de fabrication d'un composant façonné en alliage d'aluminium destiné à un aéronef et composant façonné destiné à un aéronef |
US9587298B2 (en) | 2013-02-19 | 2017-03-07 | Arconic Inc. | Heat treatable aluminum alloys having magnesium and zinc and methods for producing the same |
EP2981632B1 (fr) | 2013-04-03 | 2017-08-02 | Constellium Issoire | Tôles minces en alliage d'aluminium-cuivre-lithium pour la fabrication de fuselages d'avion |
US10501835B2 (en) | 2013-04-03 | 2019-12-10 | Constellium Issoire | Thin sheets made of an aluminium-copper-lithium alloy for producing airplane fuselages |
US20160144946A1 (en) * | 2013-06-21 | 2016-05-26 | Constellium Issoire | Extrados structural element made from an aluminium copper lithium alloy |
KR102260797B1 (ko) * | 2013-06-21 | 2021-06-07 | 콩스텔리움 이수와르 | 알루미늄 구리 리튬 합금으로 제조된 외호면 구조 요소 |
US11472532B2 (en) | 2013-06-21 | 2022-10-18 | Constellium Issoire | Extrados structural element made from an aluminium copper lithium alloy |
KR20160040464A (ko) * | 2013-06-21 | 2016-04-14 | 콩스텔리움 이수와르 | 알루미늄 구리 리튬 합금으로 제조된 외호면 구조 요소 |
CN106795595A (zh) * | 2014-10-03 | 2017-05-31 | 伊苏瓦尔肯联铝业 | 用于制造飞机机身的各向同性铝‑铜‑锂合金板 |
RU2716722C2 (ru) * | 2014-10-26 | 2020-03-16 | КАЙЗЕР АЛЮМИНУМ ФАБРИКЕЙТЕД ПРОДАКТС, ЭлЭлСи | Алюминиево-литиевые сплавы с высокой прочностью, высокой деформируемостью и низкой стоимостью |
EP3072984B1 (fr) | 2015-03-27 | 2017-07-05 | Otto Fuchs KG | Alliage d'al-cu-mg-li et produit allié ainsi produit |
EP3072984B2 (fr) † | 2015-03-27 | 2020-05-06 | Otto Fuchs KG | Alliage d'al-cu-mg-li et produit allié ainsi produit |
US12043887B2 (en) | 2015-12-18 | 2024-07-23 | Novelis Inc. | High strength 6xxx aluminum alloys and methods of making the same |
US11920229B2 (en) | 2015-12-18 | 2024-03-05 | Novelis Inc. | High strength 6XXX aluminum alloys and methods of making the same |
CN115584403A (zh) * | 2015-12-18 | 2023-01-10 | 诺维尔里斯公司 | 高强度6xxx铝合金和其制备方法 |
EP3411508B1 (fr) | 2016-02-03 | 2020-04-08 | Constellium Issoire | Tôles épaisses en alliage al cu li à propriétés en fatigue améliorées |
EP3414352B1 (fr) | 2016-02-09 | 2019-12-04 | Aleris Rolled Products Germany GmbH | Produit travaillé en alliage al-cu-li-mg-mn-zn |
WO2017137260A1 (fr) * | 2016-02-09 | 2017-08-17 | Aleris Rolled Products Germany Gmbh | Produit d'alliage corroyé à base d'al-cu-li-mg-mn-zn |
DE202017100517U1 (de) | 2017-01-31 | 2018-05-03 | Aleris Rolled Products Germany Gmbh | Al-Cu-Li-Mg-Mn-Zn Knetlegierungsprodukt |
CN106893911A (zh) * | 2017-02-27 | 2017-06-27 | 广东省材料与加工研究所 | 一种高强耐热Al‑Cu系铝合金及其制备方法 |
CN106884129A (zh) * | 2017-03-14 | 2017-06-23 | 广州金邦液态模锻技术有限公司 | 一种用于挤压铸造铝合金转向节的热处理工艺 |
CN108118271B (zh) * | 2017-12-08 | 2019-08-06 | 北京星航机电装备有限公司 | 一种异形铝合金舱段热处理变形控制方法 |
CN108118271A (zh) * | 2017-12-08 | 2018-06-05 | 北京星航机电装备有限公司 | 一种异形铝合金舱段热处理变形控制方法 |
US20210310108A1 (en) * | 2018-05-02 | 2021-10-07 | Constellium Issoire | Aluminum-copper-lithium alloy having improved compressive strength and improved toughness |
WO2019211547A1 (fr) | 2018-05-02 | 2019-11-07 | Constellium Issoire | Alliage aluminium cuivre lithium a resistance en compression et tenacite ameliorees |
WO2019211546A1 (fr) | 2018-05-02 | 2019-11-07 | Constellium Issoire | Procede de fabrication d'un alliage aluminium cuivre lithium a resistance en compression et tenacite ameliorees |
WO2020097169A1 (fr) * | 2018-11-07 | 2020-05-14 | Arconic Inc. | Alliages d'aluminium-lithium de la série 2xxx |
WO2020102441A3 (fr) * | 2018-11-14 | 2020-08-20 | Arconic Inc. | Alliages d'aluminium 7xxx améliorés |
CN111020425A (zh) * | 2019-12-25 | 2020-04-17 | 辽宁忠旺集团有限公司 | 一种2系铝合金热处理工艺 |
CN113981280A (zh) * | 2021-11-01 | 2022-01-28 | 北京理工大学 | 一种低密度高强高弹性模量的铝锂合金及制备方法 |
Also Published As
Publication number | Publication date |
---|---|
RU2481412C2 (ru) | 2013-05-10 |
CN103266246B (zh) | 2016-09-21 |
CN103266246A (zh) | 2013-08-28 |
CA2700250C (fr) | 2016-06-28 |
RU2013102512A (ru) | 2014-07-27 |
CN101855376A (zh) | 2010-10-06 |
CN101855376B (zh) | 2013-06-05 |
DE202008018370U1 (de) | 2013-04-30 |
DE112008002522T5 (de) | 2010-08-26 |
CA2700250A1 (fr) | 2009-03-26 |
RU2627085C2 (ru) | 2017-08-03 |
RU2010110350A (ru) | 2011-09-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CA2700250C (fr) | Produit en alliage ai-cu-li qui convient pour une application aerospatiale | |
US8002913B2 (en) | AA7000-series aluminum alloy products and a method of manufacturing thereof | |
US9890448B2 (en) | Al—Zn—Mg alloy product with reduced quench sensitivity | |
US8608876B2 (en) | AA7000-series aluminum alloy products and a method of manufacturing thereof | |
EP2121997B1 (fr) | Produit en alliage al-cu adapté à une application aérospatiale | |
KR102580143B1 (ko) | 7xxx-시리즈 알루미늄 합금 제품 | |
US10472707B2 (en) | Al—Zn—Mg—Cu alloy with improved damage tolerance-strength combination properties | |
JP4535731B2 (ja) | 静的機械的特性/耐損傷性の調和が向上したal−zn−mg−cu合金製品 | |
US7666267B2 (en) | Al-Zn-Mg-Cu alloy with improved damage tolerance-strength combination properties | |
EP3414352B1 (fr) | Produit travaillé en alliage al-cu-li-mg-mn-zn | |
EP3911777B1 (fr) | Produit en alliage d'aluminium de la série 7xxx | |
WO2022107065A1 (fr) | Procédé de fabrication de produits en alliage d'aluminium de série 2xxx |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 200880107556.3 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 08802260 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2010110350 Country of ref document: RU |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2700250 Country of ref document: CA Ref document number: 1573/CHENP/2010 Country of ref document: IN |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1120080025223 Country of ref document: DE |
|
RET | De translation (de og part 6b) |
Ref document number: 112008002522 Country of ref document: DE Date of ref document: 20100826 Kind code of ref document: P |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 08802260 Country of ref document: EP Kind code of ref document: A1 |