WO2008050486A1 - Matériau de conditionnement en papier stratifié et son procédé de production - Google Patents
Matériau de conditionnement en papier stratifié et son procédé de production Download PDFInfo
- Publication number
- WO2008050486A1 WO2008050486A1 PCT/JP2007/001167 JP2007001167W WO2008050486A1 WO 2008050486 A1 WO2008050486 A1 WO 2008050486A1 JP 2007001167 W JP2007001167 W JP 2007001167W WO 2008050486 A1 WO2008050486 A1 WO 2008050486A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- packaging material
- barrier
- layer
- laminated packaging
- resin
- Prior art date
Description
明 細 書
紙積層包装材料及びその製造方法
技術分野
[0001 ] 本発明は、 本発明は、 紙コア層、 バリヤ一層及び植物由来の材料を有する食 品用積層包装材料及びその製造方法に関する。
背景技術
[0002] 牛乳、 ジュース、 ミネラルウォーターなどの飲料を収容する包装紙容器は、 折目線が付けられ、 外観デザィンが印刷されたゥェブ状包装積層材料から得 られる。
包装紙容器を製造するために、 先ず、 ウェブ状包装積層材料を長手方向の縦 シールによりチューブ状に成形する。 チューブ状包装材料内に食品を充填す る。 チューブ状包装材料を横断方向に横シールして切断する。 折目線に沿つ て折畳んで最終形状に成形する。 その最終形状には、 レンガ状、 正四面体形 状などがある。
[0003] バリア性が要求される場合、 積層包装材料は、 通常、 熱可塑性材料最内層 （ ポリエチレン樹脂層） 、 バリア層のアルミ箔層、 紙コア層及びポリエチレン 樹脂最外層を有する。 アルミ箔以外の酸素バリア層としては、 無機蒸着層を 有するプラスチックフィイルム、 酸素/くリァ性樹脂であるエチレンビニルァ ルコール共重合体 （E V O H ) や M X D 6ナイロンなどを積層した単層、 バ リァ樹脂フィルムを積層した、 あるいは上記樹脂を共押出して積層した多層 が使用されている。 酸素バリア層を積層する通常の方法として、 バリア樹脂 のフィルムを接着剤でコア層に積層する方法、 溶融バリア樹脂をコア層面に 押出して積層する方法がある。
[0004] コア層の紙は、 典型的な植物由来の材料である。 しかし、 その他の積層材料 、 熱可塑性材料 （ポリエチレン樹脂など） 及び、 酸素バリア性樹脂の多くは 、 石油由来の材料である。 環境負荷低減のために、 植物由来の材料をより多 <使用することが望まれている。
[0005] 植物由来の原料モノマーから重合したプラスチック （バイオマスポリマ一） として、 ポリ乳酸 （P L A ) 、 ポリグリコール酸、 ポリコハク酸 （P A S ) 、 ポリ酪酸 （P B A ) などが知られている。 植物由来の原料であるので、 本 来的に生分解性である。
植物由来の原料モノマーから重合したプラスチックを用いた包装要材料とし ては、 植物性繊維を含有する基材の表面にポリ乳酸またはその誘導体を被覆 した生分解性複合材料、 包装容器 （特許第 2 5 1 3 0 9 1号公報） 、 乳酸ポ リマーと 2個以上のカルポン酸エステル基を有する可塑剤とを含むフィルム であって、 水蒸気透過度が 5 0〜3 0 0 g /m 2 ■ 2 4 h r、 厚さが 1 0〜5 0 O mである食品包装用フィルム。 （特許第 3 1 7 8 6 9 2号公報） 、 脂 肪族多価アルコール類、 脂肪族多塩基酸類（コハク酸）、 あるいはさらにヒド 口キシカルボン酸類を縮合反応して得られる脂肪族ポリエステルからなる耐 衝撃性に優れた分解性容器 （特許第 3 3 6 0 7 6 2号公報） （特許文献参照
) などがある。
[0006] 特許文献 1 ：特表 2 0 0 3— 5 0 8 2 7 4号公報
特許文献 2：特許第 2 5 1 3 0 9 1号公報
特許文献 3：特許第 3 1 7 8 6 9 2号公報
特許文献 4：特許第 3 3 6 0 7 6 2号公報
発明の開示
発明が解決しょうとする課題
[0007] 食品用紙積層包装材料の主要な構成材料として植物由来の材料を用いる積層 包装材料、 酸素バリア性に優れた生分解性積層包装材料、 数少ない工程でバ リア積層包装材料を製造する方法、 石油由来の接着剤を必須とせず、 積層体 の構造をシンプルにすることができ、 積層体の厚みを薄くすることができる バリア積層包装材料を製造する方法、 薄いバリア層であってもピンホール等 の欠陥の発生がないバリァ積層包装材料を製造する方法を提供することを目 的とする。
課題を解決するための手段
[0008] この課題を解決するこの発明の食品用積層包装材は、 紙コア層、 バリア層及 び熱可塑性樹脂層を含む積層包装材料であって、 バリア層が、 ポリビニルァ ルコールからなり、 熱可塑性樹脂層が、 植物原料プラスチックを含み、 溶融 押出し可能特性を有する樹脂組成物からなる、 ことを特徴とする。
[0009] この発明の好ましい態様において、 バリア層が、 ポリビニルアルコールと、 微小な層状珪酸塩、 すなわち、 微小な無機薄片状化合物又は粘土鉱物とから なる。
[0010] この発明の好ましい態様において、 熱可塑性樹脂層の樹脂組成物が、 0. 9
1 0〜0. 925の平均密度、 3〜 1 5のメルトフローレイシォ （M F R) 及び、 1. 55〜 1. 75のスウェリング率 （S R) を有する。
[0011] この発明の好ましい態様において、 熱可塑性樹脂層の樹脂組成物が、 0. 9
1 0〜0. 925の平均密度及び 5〜 20のメルトフ口一レイシォ （M F R ) を有する高 M F R植物原料プラスチックと、 0. 9 1 0〜0. 925の平 均密度及び 1. 55〜 1. 75のスウェリング率 （S R) を有するを有する 高 S R植物原料プラスチックとを含む。
[0012] この発明の好ましい態様において、 熱可塑性樹脂層の樹脂組成物が、 生分解 性可塑剤を含有して、 0. 9 1 0〜0. 925の平均密度、 3〜 1 5のメル トフ口一レイシォ （M F R) 及び、 1. 55〜 1. 75のスウェリング率 （ S R) を有する。
[0013] この課題を解決するこの発明の積層包装材料の製造方法は、 バリア樹脂の分 散液又は溶液を含むバリア樹脂液をバリア層として紙コア層に塗布し、 バリ ァ層を乾燥してバリア樹脂液中の分散剤又は溶媒を除去し、 乾燥バリヤ一層 面に植物原料プラスチックを含む樹脂組成物を押出して熱可塑性樹脂層を形 成する、 ことを特徴とする。
[0014] この発明の好ましい態様において、 バリア樹脂が、 ポリビニルアルコールで 発明の効果
[0015] 以上の本発明によれば、 以下の有利な効果が得られる。
この発明において紙積層包装材料は、 紙コア層、 バリア層及び熱可塑性樹脂 層を含む積層包装材料であって、 バリア層が、 ポリビニルアルコールからな り、 熱可塑性樹脂層が、 植物原料プラスチックを含み、 溶融押出し可能特性 を有する樹脂組成物からなる。 上記の主要な構成材料として植物由来の材料 を用いることができる。
[001 6] 紙コア層に熱可塑性樹脂層によって積層されたバリア層のポリビニルアルコ ールが、 優れた酸素バリア性を呈し、 微小な層状珪酸塩、 すなわち、 微小な 無機薄片状化合物又は粘土鉱物、 所謂ナノクレイがポリビニルアルコールに 添加されることにより、 更に優れた酸素バリァ性を発揮することができる。 熱可塑性樹脂層の樹脂組成物が、 押出し加工にする優れた平均密度、 メルト フローレイシォ （M F R ) 及び、 スウェリング率 （S R ) を有するので、 ド ローダウン性、 ネックィンに優れ高速に積層包装材料を製造することができ る。
[001 7] 積層包装材料の製造方法は、 バリア樹脂液をバリア層として紙コア層に塗布 し、 バリア層を乾燥し、 植物原料プラスチックを押出して熱可塑性樹脂層を 形成するので、 数少ない工程でバリァ積層包装材料を製造することができる 。 また、 石油由来の接着剤を必須とせず、 積層体の構造をシンプルにするこ とができ、 積層体の厚みを薄くすることができる。 しかも、 薄いバリア層で あってもピンホール等の欠陥を発生させない。
発明を実施するための最良の形態
[0018] 以下、 本発明の実施の形態について詳細に説明する。
この発明において紙積層包装材料は、 紙コア層、 バリア層及び熱可塑性樹脂 層を含む積層包装材料であって、 バリア層が、 ポリビニルアルコールからな り、 熱可塑性樹脂層が、 植物原料プラスチックを含み、 溶融押出し可能特性 を有する樹脂組成物からなる。
[001 9] 本発明においてコア層が、 紙基材である。
紙基材として用いられる板紙には、 一般に包装材料の原材料として用いられ ているものが使用可能である、 坪量 （単位面積あたりの重量） として 150g/m2
以上 400g/m2以下のものが使用できる。 しかしこの範囲に限定されることはな <、 場合によっては 30g/m2以上 150g/m2未満のグラシン紙などの薄葉紙に加工 を行い、 これを他の紙基材、 あるいはシートやフィルムなどの樹脂基材と積 層加工を行うことも可能である。
材質における制限はなく、 また表面の平滑性を向上させたクレーコ一ト塗布 紙などを用いてもよい。 紙加工時において、 一般的にはコロナ処理や火炎処 理などの表面処理が行われるが、 本発明においても加工時にこのような表面 処理を必要に応じて行ってもよい。
[0020] 本発明においてバリア層が、 ポリビニルアルコールからなる。 ポリビニルァ ルコール系樹脂である。
ここで、 ポリビニルアルコール系樹脂とは、 酢酸ェチルを単独あるいは共重 合させて得られたポリマーのビニル基をけん化して得られる樹脂である。 ポ リビニルアルコール樹脂は、 酢酸ビニルモノマーを重合されて得られたポリ 酢酸ビニルのビニル基をヒド口キシル基にけん化させて得られる水溶性の樹 脂であり、 重合度やけん化率の異なる多くの種類が存在する。 実際の樹脂に は重合度やけん化率の調整のみならず、 物性、 加工性を調整するために各種 の変性も行われるが、 重合度 5 0 0 - 2 5 0 0、 けん化率 6 9 . 5〜9 9 . 8 5 m o I %の範囲にあるビニルアルコール樹脂が使用できる。
[0021 ] この発明に好ましい態様において、 バリア層は、 ポリビニルアルコールとそ れに均一に分散された微小な層状珪酸塩とから成る。
好ましくは、 バリア層中に、 平均粒径が 1〜8 0ミクロンの範囲内にあり、 かつ 3 0 0ミクロン以上の粒径を含まない層状珪酸塩を 0 . 1〜 1 0重量0 /0 含有し、 層状珪酸塩は、 層間距離が 5 0オングストローム以上に実質的に均 —に分散している。
例えば、 バリア層用の樹脂は、 重合プロセスにおいて、 単量体中の粘土鉱物 を拡散させ重合することによって、 調製され、 このプロセスは、 極めて細か い構造およびポリマーの中に十分に分散された珪酸塩微小板を生成する。
[0022] このような層状珪酸塩の原料としては、 珪酸マグネシウムまたは珪酸アルミ
二ゥムの層から構成される層状フイロ珪酸鉱物を例示することができる。 層状珪酸塩の配合量は、 ポリマーに対して 0. 05〜 1 5重量％が好ましく 、 0. 1〜 1 0重量％がさらに好ましい。
好ましい態様において、 N a、 K、 L i及び C aを除く金属イオン （例えば 、 A g、 Z n、 C o、 C d、 C uから選ばれた金属イオン） 又はその金属化 合物を層間に有する層状珪酸塩 （粘土鉱物） を用いることができる。 この層 状珪酸塩自体が、 緑膿菌、 大腸菌、 黄色ブドウ球菌などの種々の微生物に対 して優れた抗菌性を備える。 従って、 この層状珪酸塩を含有する包装積層材 料にもこの抗菌性が付与される。
[0023] 本発明において熱可塑性樹脂層が、 植物原料プラスチックを含み、 溶融押出 し可能特性を有する樹脂組成物からなる。
本発明において熱可塑性樹脂層に用いられる植物原料プラスチックとしては 、 ポリ乳酸 （P LA) 、 ポリグリコール酸、 ポリコハク酸 （PAS) 、 ポリ 酪酸 （P BA) などがある。 本発明においては、 溶融押出し可能特性を有す る樹脂組成物である。
より具体的には、 熱可塑性樹脂層の樹脂組成物が、 0. 9 1 0〜0. 925 の平均密度、 3〜 1 5のメルトフローレイシォ （M F R) 及び、 1. 55〜 1. 75のスウェリング率 （S R) を有する。
[0024] 溶融押出し可能特性を有する樹脂にするためには、 第 1に植物原料プラスチ ック自体にこの特性を付与するようにポリマ一設計する、 第 2に 2種以上の 植物原料プラスチックをプレンドしてこの特性が付与されるようにプレンド 設計する、 第 3に特定の植物原料プラスチックにこの特性を付与するように 改質剤などを添加する、 などの方法がとることができる。
[0025] 第 2の方法では、 好ましい態様において、 熱可塑性樹脂層の樹脂組成物が、 0. 9 1 0〜0. 925の平均密度及び 5〜20のメルトフローレイシォ （ M F R) を有する高 M F R植物原料プラスチックと、 0. 9 1 0〜0. 92 5の平均密度及び 1. 55〜1. 75のスウェリング率 （S R) を有するを 有する高 S R植物原料プラスチックとをプレンドする。
[0026] 第 3の方法では、 好ましい態様において、 熱可塑性樹脂層の樹脂組成物が、 例えば、 ロジンのような生分解性可塑剤を含有して、 0. 9 1 0〜0. 92 5の平均密度、 3〜 1 5のメルトフローレイシォ （M F R) 及び、 1. 55 〜1. 75のスウェリング率 （S R) を有する。
[0027] この発明において、 押出し加工性 （ドローダウン性、 ネックイン） を評価す る上で、 重要なパラメ一ターが、 M F R、 S R、 密度である。 M F R (M e I t F l ow R a t e)は、 1 90度 C、 2. 1 6 k gの荷重で、 2 mm 径のノズルから 1 0分間、 押し出したときの数値で、 この数値が高いほど、 流動性 （押出し加工におけるドローダウン性 （高速加工性） ） が高い。 また 、 S R (Sw e l l i n g R a t i o) は、 M F R測定において、 1 90 度 C、 2. 1 6 k gの荷重で、 2mm径のノズルから 1 0分間、 押し出した とき、 そのストランドがどれだけ膨らむかを見る。 この数値が 1を超える場 合、 膨らみ、 1未満の場合、 収縮する。
[0028] この発明の積層包装材料の製造方法は、 ポリビニルアルコールのバリア樹脂 の分散液又は溶液を含むバリア樹脂液をバリア層として紙コア層に塗布し、 バリア層を乾燥してバリア樹脂液中の分散剤又は溶媒を除去し、 乾燥バリヤ 一層面に植物原料プラスチックを含む樹脂組成物を押出して熱可塑性樹脂層 を形成する。
[0029] バリア樹脂液は、 バリア樹脂を分散剤に分散し、 又は溶媒に溶解して調製す ることができる。
本発明の好ましい態様において、 分散剤及び溶媒は水性である。 塗布液 （バ リア樹脂液） は、 ポリビニルアルコール系樹脂を水または水とアルコールの 混合溶媒に溶解させたものであり、 乾燥工程において有害な有機溶媒の揮発 もないことから、 環境面、 安全面においても優れた加工方法である。
し力、し、 本発明では、 加工性や塗膜物性の改良のために必要に応じて溶液/ 分散媒に種々の無機、 有機物を添加することも可能である。 また塗布液も上 記に限定されるものではなく、 樹脂を他の溶媒に溶解あるいは乳化分散させ たものを用いることも可能である。
[0030] 塗布方法については、 溶液/分散液のスプレーコーティングや、 スクリーン 印刷ゃグラビア印刷などの印刷と同様の工程で塗布ができる。 グラビアロー ルを用いた転写方式を使用することで連続的に効率よく加工を行うことでき る。 溶液/分散液を転写ロールに薄く転写し、 そのロールを紙基材表面に密 着させることで樹脂を紙基材に転写する。
塗布後の材料は引き続き熱乾燥炉に導入され、 そこで乾燥される。 塗布され るポリビニルアルコール系樹脂のバリア樹脂液は、 例えば、 乾燥後重量での 0 . 5g/m2以上、 10g/m2以下である。
[0031 ] 本発明における押出し工程では、 乾燥バリヤ一層面に熱可塑性樹脂を押出し てその熱可塑性樹脂層 （最内層及び最外層） を形成するを示す。
具体的には、 バリヤ一層を有するコア層のウェブは、 押出し機を用いてゥェ ブの両外側に対し押出し可能な熱可塑性樹脂を同時に積層しながら 2本の回 転ローラーの間のニップに通して、 積層包装材料を得る。
紙加工包装材料には防水性やヒートシール性を持たせるため、 紙基材の両外 面にポリエチレンをコーティングすることが一般的である。 本発明において も紙基材コア層のバリア層の反対側にポリエチレンをコ一ティングして用い ることができる。
押出し加工は一般的な紙基材への樹脂の押出し加工と同様になされる。 紙基 材へのコ口ナ処理等の表面処理を必要に応じて行つてもよい。
[0032] <実施例 >
実施例 1
6種の牛乳容器用原紙 （坪量約 310g/m2) の漂白原紙に、 乾燥重量で 2g/m2の 2 重量％スメクタイ ト含有ポリビニルアルコールのバリア樹脂水性溶液を塗布 し乾燥する。
塗布乾燥後に、 23°C、 0%RH条件下における酸素透過量を測定する。 サンプル 1〜 6については酸素透過量は、 610cc/m2. day. atm〜6010cc/m2. day. atmであ る。
[0033] (酸素バリア性の評価）
材料の酸素バリア性は、 J I S K-7126に準拠して評価する。 具体的には酸素透 過量測定装置を用いて測定を行う。 アルミ箔のような物理的なバリア層と異 なり、 樹脂系のバリア材の酸素バリア性は温度や湿度依存性があるため、 必 要に応じて測定条件を設定する。 一般的には酸素透過率が 50cc/m2. day. atm以 下の材料を用いて成形された容器であれば実用上酸素/ リァ性を有する容器 であるため、 本発明では 50cc/m2. day. atmを酸素透過性有無の判断基準とする
[0034] 従って、 上記結果から、 単にバリア樹脂液を塗布し乾燥しただけではバリア 性を得ることができない。
次いで、 バリア層の上に 15g/m2で、 ポリ乳酸と改質剤の脂肪族芳香族ポリエス テルとのブレンド物 （密度 0. 924g/cm3、 M F R 1 0、 S R 1 . 6 ) を押出しラ ミネ一卜する。 得られるサンプルについて。 23°C、 90%RH条件下にて酸素透過 量を測定する。 いずれも 50cc/m2. day. atm以下となり、 良好なバリァ性を示す 材料である。
[0035] 比較例 1
牛乳容器用原紙の漂白原紙に、 バリア樹脂水性溶液を塗布することなく、 原 紙上に 2 O g/m2の低密度ポリェチレンの押出し加工を行った以外、 実施例 1 と 同様に包装材料を得る。 良好なバリア性を示さない材料である。
[0036] なお、 本発明は前記実施の形態に限定されるものではなく、 本発明の趣旨に 基づいて種々変形させることが可能であり、 それらを本発明の範囲から排除 するものではない。
産業上の利用可能性
[0037] この発明の積層包装材料及びその製造方法は、 牛乳、 ジュース、 ミネラルウ オーターなどの飲料、 流動食品などの包装容器に適用できる。
Claims
[1] 紙コア層、 バリア層及び熱可塑性樹脂層を含む積層包装材料であって、 該バリア層が、 ポリビニルアルコールからなり、
該熱可塑性樹脂層が、 植物原料プラスチックを含み、 溶融押出し可能特性を 有する樹脂組成物からなる、 食品用積層包装材。
[2] 前記バリア層が、 ポリビニルアルコールと、 微小な層状珪酸塩とからなる、 請求項 1記載の食品用積層包装材。
[3] 前記熱可塑性樹脂層の樹脂組成物が、 0. 91 0〜0. 925の平均密度、 3〜 1 5のメルトフローレイシォ （M F R) 及び、 1. 55〜1. 75のス ウェリング率 （S R) を有する、 請求項 1記載の食品用積層包装材。
[4] 前記熱可塑性樹脂層の樹脂組成物が、 0. 91 0〜0. 925の平均密度及 び 5〜20のメルトフローレイシォ （MFR) を有する高 M F R植物原料プ ラスチックと、 0. 91 0〜0. 925の平均密度及び 1. 55〜1. 75 のスウェリング率 （S R) を有するを有する高 S R植物原料プラスチックと を含む、 請求項 1記載の食品用積層包装材。
[5] 前記熱可塑性樹脂層の樹脂組成物が、 生分解性可塑剤を含有して、 0. 91 0〜0. 925の平均密度、 3〜1 5のメルトフローレイシォ （MFR) 及 び、 1. 55〜1. 75のスウェリング率 （S R) を有する、 請求項 1記載 の食品用積層包装材。
[6] バリア樹脂の分散液又は溶液を含むバリア樹脂液をバリア層として紙コア層 に塗布し、 該バリア層を乾燥して該バリア樹脂液中の分散剤又は溶媒を除去 し、 乾燥バリヤ一層面に植物原料プラスチックを含む樹脂組成物を押出して 該熱可塑性樹脂層を形成する、
ことを特徴とする積層包装材料の製造方法。
[7] 前記バリア樹脂液が、 ポリビニルアルコールと、 微小な層状珪酸塩とからな る、 請求項 6記載の積層包装材料の製造方法。
[8] 前記バリア樹脂液を前記コア層に直接に塗布する、 請求項 6記載の積層包装 材料の製造方法。