WO2007123230A1 - 情報記録媒体及びその製造方法 - Google Patents
情報記録媒体及びその製造方法 Download PDFInfo
- Publication number
- WO2007123230A1 WO2007123230A1 PCT/JP2007/058769 JP2007058769W WO2007123230A1 WO 2007123230 A1 WO2007123230 A1 WO 2007123230A1 JP 2007058769 W JP2007058769 W JP 2007058769W WO 2007123230 A1 WO2007123230 A1 WO 2007123230A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- information
- recording medium
- recording
- atomic
- Prior art date
Abstract
Description
Claims