WO2007117663A2 - Expandable polyolefin compositions and insulated vehicle parts containing expanded polyolefin compositions - Google Patents
Expandable polyolefin compositions and insulated vehicle parts containing expanded polyolefin compositions Download PDFInfo
- Publication number
- WO2007117663A2 WO2007117663A2 PCT/US2007/008690 US2007008690W WO2007117663A2 WO 2007117663 A2 WO2007117663 A2 WO 2007117663A2 US 2007008690 W US2007008690 W US 2007008690W WO 2007117663 A2 WO2007117663 A2 WO 2007117663A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- weight
- ethylene
- thermally expandable
- cavity
- Prior art date
Abstract
Description
Claims