WO2007099910A1 - フォトマスクブランク及びフォトマスク、並びにそれらの製造方法 - Google Patents
フォトマスクブランク及びフォトマスク、並びにそれらの製造方法 Download PDFInfo
- Publication number
- WO2007099910A1 WO2007099910A1 PCT/JP2007/053528 JP2007053528W WO2007099910A1 WO 2007099910 A1 WO2007099910 A1 WO 2007099910A1 JP 2007053528 W JP2007053528 W JP 2007053528W WO 2007099910 A1 WO2007099910 A1 WO 2007099910A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- shielding film
- light
- photomask blank
- photomask
- film
- Prior art date
Abstract
遮光膜のウェットエッチング特性を最適化させることで断面形状の良好な遮光膜のパターンを形成することができ、更に、パターンのギザが極めて小さい遮光膜のパターンを形成することができるフォトマスクブランク及びフォトマスクを提供する。 透光性基板上に遮光膜を有するフォトマスクブランクにおいて、前記フォトマスクブランクは、前記遮光膜上に形成されるマスクパターンをマスクにしてウェットエッチング処理により、前記遮光膜をパターニングするフォトマスクの作製方法に対応するウェットエッチング処理用のフォトマスクブランクであって、前記遮光膜は、クロムを含む材料からなり、かつ、X線回折によるCrN(200)の回折ピークから算出される結晶子サイズが10nm以下である。また、前記遮光膜をウェットエッチング処理によりパターニングして前記基板上に遮光膜パターンが形成されたフォトマスクを得る。
Description
明 細 書
フォトマスクブランク及びフォトマスク、並びにそれらの製造方法
技術分野
[0001] 本発明は、遮光膜パターン形成のためのウエットエッチング処理用に遮光膜のゥェ ットエッチング特性を最適化させたフォトマスクブランク及びフォトマスク、並びにそれ らの製造方法に関する。特に、 FPDデバイスを製造するためのフォトマスクブランク、 係るフォトマスクブランクを用いて製造されたフォトマスクに関する。
背景技術
[0002] 一般に、半導体装置や液晶表示装置の製造工程では、フォトリソグラフィ一法を用 いて微細パターンの形成が行われている。この微細パターンの形成には通常、フォト マスクと呼ばれている基板が使用される。このフォトマスクは、一般に透光性のガラス 基板上に、金属薄膜等力 なる遮光性の微細パターンを設けたものであり、このフォ トマスクの製造にぉ 、てもフォトリソグラフィ一法が用いられて 、る。
[0003] フォトリソグラフィ一法によるフォトマスクの製造には、ガラス基板等の透光性基板上 に遮光膜を有するフォトマスクブランクが用いられる。このフォトマスクブランクを用い たフォトマスクの製造は、フォトマスクブランク上に形成されたレジスト膜に対し、所望 のパターン露光を施す露光工程と、所望のパターン露光に従って前記レジスト膜を 現像してレジストパターンを形成する現像工程と、レジストパターンに沿って前記遮光 膜をエッチングするエッチング工程と、残存したレジストパターンを剥離除去する工程 とを有して行われている。上記現像工程では、フォトマスクブランク上に形成されたレ ジスト膜に対し所望のパターン露光を施した後に現像液を供給して、現像液に可溶 なレジスト膜の部位を溶解し、レジストパターンを形成する。また、上記エッチングェ 程では、このレジストパターンをマスクとして、たとえばウエットエッチングによって、レ ジストパターンの形成されて ヽな ヽ遮光膜が露出した部位を溶解し、これにより所望 のマスクパターンを透光性基板上に形成する。こうして、フォトマスクが出来上がる。
[0004] 特許文献 1には、ウエットエッチングに適したマスクブランクとして、透明基板上に、 クロム炭化物を含有するクロム膜を遮光膜として備えたフォトマスクブランクが記載さ
れている。また、特許文献 2には、同じくウエットエッチングに適したマスクブランクとし て、透明基板上に、ハーフトーン材料膜と金属膜との積層膜を有し、この金属膜は、 表面側から透明基板側に向かってエッチングレートが異なる材料で構成される領域 が存在しており、例えば CrNZCrCの金属膜と CrONの反射防止膜からなるハーフ トーン型位相シフトマスクブランクが記載されている。
[0005] ところで、液晶表示装置における例えば、カラーフィルターや TFT (薄膜トランジス タ)アレイ、反射板等の部品を製造するに当たって使用されるフォトマスクは、 LSI用 のフォトマスクに比べて基板サイズが大きい。従って、基板サイズが大きい分、基板サ ィズが小さい場合に比べ、製造原理上の限界面 (製造方法や製造装置に由来する 限界面)の要因、並びに製造条件の変動 (プロセス変動)の要因に基づき、面内及び 基板間において諸特性 (膜組成、膜質、透過率、反射率、光学濃度、エッチング特 性、その他光学特性、膜厚など)のばらつきが生じやすぐこのため面内及び基板間 の諸特性が均一なものが得られずらいといった特色がある。このような特色は、 FPD ( フラットパネルディスプレイ)の更なる大型化 ·高精細化に伴 、増長される傾向にある
[0006] 近年の液晶表示装置の高精細化にともなって、フォトマスクに形成されるパターン の最小線幅は 2〜3 μ m程度であったものが、 1 μ m程度以下まで微細化されてきて いる。そのような状況下において、その他の寸法精度 (線幅公差、トータルピッチ精度 、重ね合わせ精度)もより厳しくなる傾向にある。
また、このように液晶表示装置のパターンを高精細化するには、微細化されたマス クパターンの精度の良好なパターン転写を行う必要がある。このためには、大型の基 板全面に渡って形成されるマスクパターンにギザが生じず、断面形状が良好であるこ とが望まれる。例えば、フォトマスクに形成されるマスクパターンの断面形状は、膜面 に対して略垂直形状であることが望ま 、。
[0007] 特許文献 1 :特公昭 62— 32782号公報
特許文献 2:特許第 2983020号公報
発明の開示
発明が解決しょうとする課題
[0008] 従来、液晶表示装置の製造に使われるフォトマスクの原版となるフォトマスクブラン クとしては、ガラス基板上に酸化クロム (CrO)膜とクロム (Cr)膜を積層した遮光膜が 形成されたものや、ガラス基板上に酸化クロム (CrO)膜とクロム (Cr)膜と酸化クロム( CrO)膜を積層した遮光膜が形成されたものを使用していた。尚、上述の酸化クロム( CrO)膜は、露光光に対する膜面の反射を低減させる反射防止機能を持った反射防 止膜である。
そして、上述のフォトマスクブランクを、硝酸第二セリウムアンモンと過塩素酸と純水 のエツチャントを用いて、遮光膜上に形成されたレジストパターンをマスクにしてゥエツ トエッチングにより遮光膜パターンを形成して、フォトマスクを作製して 、た。
[0009] しかしながら、近年のマスクパターンの微細化が進んで!/、る状況下にお!/、ては、従 来の遮光膜では、マスクパターンのギザ (マスクパターンを平面視したときのパターン エッジラフネス (パターンエッジの凹部と凸部の最大距離) )が無視できな 、状況とな り、また、断面形状が良好 (垂直)なパターンが得られないという問題が生じた。このマ スクパターンにおけるギザや、パターンの断面形状は、フォトマスクを使って液晶表示 装置を作製した場合に、表示むらを引き起こす原因となる。
[0010] そこで本発明は、従来の問題点を解決するべくなされたものであり、その目的とする ところは、遮光膜のウエットエッチング特性を最適化させることで断面形状の良好な遮 光膜のパターンを形成することができ、更に、パターンのギザが極めて小さい遮光膜 のパターンを形成することができるフォトマスクブランク及びフォトマスク、並びにそれ らの製造方法を提供することである。
課題を解決するための手段
[0011] 前述したように、従来は、遮光膜の膜厚や、遮光膜の深さ方向での組成傾斜などの 制約から、ウエットエッチング処理により形成される遮光膜パターンの断面形状を良 好に仕上げることが困難であるとの問題に鑑み、本発明者は鋭意研究した結果、クロ ム系遮光膜を構成するクロムの結晶性と遮光膜のウエットエッチング特性とは相関関 係があることを突き止め、さらにこのクロムの結晶性を制御することにより、遮光膜のゥ エツトエッチング特性を制御して、結果、遮光膜パターンの断面形状が良好な形状と なるようにコントロールでき、またパターンギザが極めて小さくなることを見い出した。
[0012] すなわち、上記課題を解決するため、本発明は以下の構成を有する。
(構成 1)透光性基板上に遮光膜を有するフォトマスクブランクにおいて、前記フォトマ スタブランクは、前記遮光膜上に形成されるマスクパターンをマスクにしてウエットエツ チング処理により、前記遮光膜をパターニングするフォトマスクの作製方法に対応す るウエットエッチング処理用のフォトマスクブランクであって、前記遮光膜は、クロムを 含む材料力もなり、かつ、 X線回折による CrN (200)の回折ピーク力も算出される結 晶子サイズが lOnm以下であることを特徴とするフォトマスクブランクである。
(構成 2)前記遮光膜は、 X線回折法により得られる回折ピークが CrN (200)の回折 ピークと Cr (110)の回折ピークをもつ膜であることを特徴とする構成 1記載のフォトマ スタブランクである。
(構成 3)前記遮光膜は、深さ方向の略全域において窒素 (N)が含まれていることを 特徴とする構成 1又は 2記載のフォトマスクブランクである。
[0013] (構成 4)前記遮光膜の上層部に酸素を含む反射防止層を形成することを特徴とする 構成 1乃至 3の何れか一に記載のフォトマスクブランクである。
(構成 5)前記フォトマスクブランクは、 FPDデバイスを製造するためのフォトマスクブラ ンクであることを特徴とする構成 1乃至 4の何れか一に記載のフォトマスクブランクであ る。
(構成 6)構成 1乃至 5の何れか一に記載のフォトマスクブランクにおける前記遮光膜 を、ウエットエッチング処理によりパターユングして前記透光性基板上に遮光膜バタ ーンが形成されたことを特徴とするフォトマスクである。
[0014] (構成 7)透光性基板上に、クロムを含む材料力もなるターゲットを用いたスパッタリン グ成膜により、クロムを含む遮光膜を形成する工程を有するフォトマスクブランクの製 造方法において、前記フォトマスクブランクは、前記遮光膜上に形成されるレジストパ ターンをマスクにしてウエットエッチング処理により、前記遮光膜をパターニングするフ オトマスクの作製方法に対応するウエットエッチング処理用のフォトマスクブランクであ つて、前記ウエットエッチング処理により形成される遮光膜パターンの断面形状が所 定の形状となるように、前記遮光膜を構成するクロムの結晶性を制御することを特徴 とするフォトマスクブランクの製造方法である。
[0015] (構成 8)前記遮光膜を形成した後、該遮光膜に加わる熱処理条件を調整すること〖こ より前記遮光膜を構成するクロムの結晶性を制御することを特徴とする構成 7記載の フォトマスクブランクの製造方法である。
(構成 9)前記熱処理は、前記遮光膜上に形成するレジスト膜形成前、又はレジスト膜 形成後の加熱処理であることを特徴とする構成 7又は 8記載のフォトマスクブランクの 製造方法である。
(構成 10)前記ウエットエッチング処理により形成される遮光膜パターンの断面形状 が膜面に対して略垂直となる形状であることを特徴とする構成 7乃至 9の何れか一に 記載のフォトマスクブランクの製造方法である。
[0016] (構成 11)前記フォトマスクブランクは、 FPDデバイスを製造するためのフォトマスクブ ランクであることを特徴とする構成 7乃至 10の何れか一に記載のフォトマスクブランク の製造方法である。
(構成 12)構成 7乃至 11の何れか一に記載の製造方法により得られるフォトマスクブ ランクにおける前記遮光膜を、ウエットエッチング処理によりパターユングする工程を 有することを特徴とするフォトマスクの製造方法である。
[0017] 構成 1にあるように、本発明のフォトマスクブランクは、透光性基板上に遮光膜を有 するフォトマスクブランクにおいて、前記フォトマスクブランクは、前記遮光膜上に形成 されるマスクパターンをマスクにしてウエットエッチング処理により、前記遮光膜をパタ 一-ングするフォトマスクの作製方法に対応するウエットエッチング処理用のフォトマ スタブランクであって、前記遮光膜は、クロムを含む材料力もなり、かつ、 X線回折によ る CrN (200)の回折ピーク力も算出される結晶子サイズが lOnm以下である膜とする このように、遮光膜の結晶性を、 CrN (200)の回折ピークから算出される結晶子サ ィズが lOnm以下とすることによって、遮光膜をウエットエッチングによりパターユング した際に、遮光膜パターンのギザも極めて小さくすることが可能となり、更に遮光膜パ ターンの断面形状が良好な形状となる。上記遮光膜パターンのギザを小さくする点に お!、ては、 CrN (200)の回折ピーク力も算出される結晶子サイズがより小さ!/、方が好 ましいが、遮光膜パターンの断面形状や成膜速度などの生産性からは、結晶子サイ
ズは小さすぎても好ましくな 、。上記の点を考慮すると CrN (200)の回折ピークから 算出される結晶子サイズは、 5nm以上 lOnm以下とすることが好ましい。
[0018] また、構成 2にあるように、さらに遮光膜の結晶性は、 X線回折法により得られる回 折ピークが CrN (200)の回折ピークと Cr ( 110)の回折ピークをもつことで、遮光膜パ ターンの形状を制御しやすくなるので好まし 、。
また、構成 3にあるように、遮光膜は、深さ方向の全領域において窒素 (N)を含む 膜とすることで、ウエットエッチング速度を高めることができ、遮光膜上に形成するレジ スト膜の薄膜ィ匕に対応することができるので、より微細かつ高精細な遮光膜パターン を形成することができる。
また、構成 4にあるように、前記遮光膜はその上層部に酸素を含む反射防止層を形 成することができる。このような反射防止層を形成することにより、露光波長における 反射率を低反射率に抑えることができるので、マスクパターンを被転写体に転写する ときに投影露光面との間で多重反射を抑制し、結像特性の低下を抑制することがで きる。
[0019] また、構成 5にあるように、前記フォトマスクブランクは、大型の基板であって、基板 全面に渡って遮光膜パターンの寸法精度が求められる FPDデバイスを製造するた めのフォトマスクブランクに適して!/、る。
また、構成 6にあるように、構成 1乃至 5の何れか一に記載のフォトマスクブランクに おける前記遮光膜を、ウエットエッチング処理によりパターニングして形成された遮光 膜パターンは、断面形状が良好で、かつ遮光膜パターンのギザが極めて小さい良好 なフォトマスクとなる。
[0020] また、構成 7にあるように、透光性基板上に、クロムを含む材料力もなるターゲットを 用いたスパッタリング成膜により、クロムを含む遮光膜を形成する工程を有するフォト マスクブランクの製造方法において、前記フォトマスクブランクは、前記遮光膜上に形 成されるレジストパターンをマスクにしてウエットエッチング処理により、前記遮光膜を パター-ングするフォトマスクの作製方法に対応するウエットエッチング処理用のフォ トマスクブランクであって、前記ウエットエッチング処理により形成される遮光膜パター ンの断面形状が所定の形状となるように、前記遮光膜を構成するクロムの結晶性を
制御する。
このように、遮光膜の結晶性を制御することで、遮光膜のウエットエッチング特性を 制御することができ、これによつて、遮光膜パターンの断面形状が良好な形状となり、 更に遮光膜パターンのギザが極めて小さくなるようにコントロールすることができる。
[0021] たとえば、構成 8にあるように、前記遮光膜を形成した後、該遮光膜に加わる熱処 理条件を調整することにより前記遮光膜を構成するクロムの結晶性を好適に制御す ることがでさる。
ここで、クロムの結晶'性は、例えば CrN (200)の結晶子サイズであり、構成 8にある ように、前記遮光膜を形成した後、該遮光膜に加わる熱処理条件を調整することによ り、前記遮光膜を構成するクロムの結晶子サイズを制御することが好適である。
[0022] また、構成 9にあるように、遮光膜に対する熱処理は、前記遮光膜上に形成するレ ジスト膜形成前、又はレジスト膜形成後の加熱処理である。一般に、フォトマスクブラ ンクの製造工程において、遮光膜形成後に、レジスト膜形成前に行われる付着力向 上を目的としたベータ処理、又はレジスト膜形成後のプリベータ処理が行われる。従 つて、これらの加熱処理条件を調整することにより、遮光膜を構成するクロムの結晶 性 (例えばクロムの結晶子サイズ)を制御することが好適である。
また、構成 10にあるように、前記ウエットエッチング処理により形成される遮光膜パタ ーンの断面形状は、膜面に対して略垂直となる形状であることが望ましぐ本発明に よれば、遮光膜パターンの断面形状を良好にコントロールすることができるため好適 である。
[0023] また、構成 11にあるように、前記フォトマスクブランクは、大型の基板であって、基板 全面に渡って遮光膜パターンの寸法精度が求められる FPDデバイスを製造するた めのフォトマスクブランクに適して!/、る。
また、構成 12にあるように、構成 7乃至 11の何れか一に記載の製造方法により得ら れるフォトマスクブランクにおける前記遮光膜を、ウエットエッチング処理によりパター ユングする工程を有するフォトマスクの製造方法により、ウエットエッチング処理により ノターニングして形成された遮光膜パターンは、断面形状が良好で、かつ遮光膜パ ターンのギザが極めて小さい良好なフォトマスクが得られる。
発明の効果
[0024] 本発明によれば、遮光膜の結晶性を CrN (200)の回折ピーク力 算出される結晶 子サイズを lOnm以下とすることにより、遮光膜のウエットエッチング特性を最適化さ せ、遮光膜パターンの断面形状が良好な形状となり、更には遮光膜パターンのギザ も極めて小さくすることができるフォトマスクブランクを提供することができる。
また、本発明により得られるフォトマスクブランクにおける遮光膜をウエットエッチング 処理を用いてパターユングすることで、断面形状が良好で、かつパターンギザが極め て小さい良好な遮光膜パターンが形成されたフォトマスクを提供することができる。 図面の簡単な説明
[0025] [図 1]本発明により得られるフォトマスクブランクの一実施の形態を示す断面図である
[図 2]フォトマスクブランクを用いたフォトマスクの製造工程を示す断面図である。 符号の説明
[0026] 1 透光性基板
2 遮光膜
3 レジスト膜
2a 遮光膜のパターン
3a レジストパターン
10 フォトマスクブランク
20 フォトマスク
発明を実施するための最良の形態
[0027] 以下、図面を参照して、本発明の実施の形態を詳述する。
図 1は本発明におけるフォトマスクブランクの第一の実施の形態を示す断面図であ る。
図 1のフォトマスクブランク 10は、透光性基板 1上に遮光膜 2を有する FPD作製用 のフォトマスクブランクの形態のものである。
上記フォトマスクブランク 10は、前記遮光膜 2上に形成されるレジストパターンをマ
スクにしてウエットエッチング処理により、前記遮光膜 2をパターユングするフォトマス クの作製方法に対応するウエットエッチング処理用のマスクブランクである。また、前 記遮光膜 2は、透光性基板 1上に、クロムを含むターゲットを用いたスパッタリング成 膜により形成される、クロムを含む遮光膜である。
ここで、透光性基板 1としては、ガラス基板が一般的である。ガラス基板は、平坦度 及び平滑度に優れるため、フォトマスクを使用して被転写基板上へのパターン転写を 行う場合、転写パターンの歪み等が生じな 、で高精度のパターン転写が行える。
[0028] 本発明にお 、て、前記遮光膜 2は、ウエットエッチング処理により形成される遮光膜 パターンのギザが極めて小さぐ且つ断面形状が所定の形状となるように、前記遮光 膜 2を構成するクロムの結晶性を、 CrN (200)の回折ピークから算出される結晶子サ ィズを lOnm以下となるようにしている。さらに、好ましくは、上記結晶子サイズに加え 、遮光膜パターンの形状制御性を高めるために、遮光膜 2を構成するクロムの結晶性 を X線回折法により得られる回折ピーク力 CrN (200)の回折ピークと Cr(l lO)の回 折ピークとなるようにして 、る。
このような、結晶性を有する遮光膜 2とすることで、遮光膜 2のウエットエッチング特 性を制御することができ、これによつて、遮光膜パターンの断面形状が良好で、かつ 遮光膜パターンのギザが極めて小さくすることができる。
遮光膜 2を構成するクロムの結晶性は、たとえば前記遮光膜 2を形成した後、該遮 光膜 2に加わる熱処理条件を調整することにより制御することができる。
[0029] また、遮光膜 2に対する熱処理は、たとえば遮光膜 2上に形成するレジスト膜形成 前、又はレジスト膜形成後の加熱処理である。一般に、フォトマスクブランクの製造ェ 程において、遮光膜形成後に、レジスト膜形成前に行われる付着力向上を目的とし たベータ処理、又はレジスト膜形成後のプリベータ処理が行われる。従って、これらの 加熱処理条件を調整することにより、遮光膜を構成するクロムの結晶性を制御するこ とが好適である。
遮光膜 2の結晶性を X線回折による CrN (200)の回折ピーク力も算出される結晶 子サイズを lOnm以下とし、さらに、 X線回折法により得られる回折ピークが CrN (20 0)の回折ピークと Cr(l lO)の回折ピークをもつ膜とするには、少なくとも遮光膜 2は
クロムと窒素とを含む材料、更に好ましくは、クロムと窒素と炭素を含む材料、更に好 ましくは、クロムと窒素と炭素と酸素を含む材料とし、加熱処理条件としては、 80°C以 上 180°C以下、好ましくは 100°C以上 150°C以下の加熱温度で加熱処理することに より得られる。
[0030] 前述したように、ウエットエッチング処理により形成される遮光膜パターンの断面形 状は、膜面に対して略垂直となる形状であることが望ましい。本発明によれば、遮光 膜 2の結晶性を制御することで、遮光膜 2のウエットエッチング特性を制御することが できる。その結果、遮光膜パターンの断面形状が上記の良好な形状となり、遮光膜 パターンのギザが極めて小さくなるようにコントロールすることができるので、本発明は 好適である。
[0031] 具体的な遮光膜 2の材料としては、クロムと窒素とを含む材料が挙げられ、遮光膜 2 中に含まれるクロム (Cr)の含有量を 1としたときに、深さ方向にお 、て窒素 (N)の含 有量が 0. 5以上の領域と、窒素 (N)の含有量が 0. 5未満の領域が存在するようにす る。例えば、遮光膜としては、透光性基板側力もクロム (Cr)の含有量を 1としたときに 窒素(N)の含有量が 0. 5未満の層と、窒素(N)の含有量が 0. 5以上となる層の積層 膜や、透光性基板側からクロム (Cr)の含有量を 1としたときに窒素 (N)の含有量が 0 . 5以上となる層と、窒素 (N)の含有量が 0. 5未満となる層と、窒素 (N)の含有量力 SO . 5以上となる層の積層膜や、透光性基板側からクロム (Cr)の含有量を 1としたときに 窒素(N)の含有量が 0. 5以上となる層と、窒素(N)の含有量が 0. 5未満となる層の 積層膜が挙げられる。尚、遮光膜が積層膜である場合において、遮光膜中に含まれ るクロム (Cr)や窒素 (N)は、段階的に変化してもよいし、連続的に変化しても良い。 また、遮光膜 2には、更に、酸素、炭素、弗素等の添加元素を含んでも良い。
[0032] 上述の遮光膜における積層膜の中でも、 FPDの製造用に使われる 330mm X 450 mm以上の大型の基板全面に渡ってマスクパターンにギザが生じず、断面形状が良 好となる遮光膜パターンをウエットエッチングにより形成するためには、遮光膜の材料 は、クロムと窒素とを含む材料とし、透光性基板側力もクロム (Cr)の含有量を 1とした ときに窒素(N)の含有量が 0. 5未満の層と、窒素(N)の含有量が 0. 5以上となる層 の積層膜とすることが好まし 、。
[0033] 上記遮光膜 2の形成方法は、特に制約する必要はな 、が、なかでもスパッタリング 成膜法が好ましく挙げられる。スパッタリング成膜法によると、均一で膜厚の一定な膜 を形成することが出来るので、本発明には好適である。透光性基板 1上に、スパッタリ ング成膜法によって上記遮光膜 2を成膜する場合、スパッタターゲットとしてクロム (C r)ターゲットを用い、チャンバ一内に導入するスパッタガスは、アルゴンガスやへリウ ムガスなどの不活性ガスに酸素、窒素もしくは二酸ィ匕炭素、一酸化窒素等のガスを 混合したものを用いる。アルゴンガス等の不活性ガスに酸素ガス或いは二酸ィ匕炭素 ガスを混合したスパッタガスを用いると、クロムに酸素を含む遮光膜を形成することが でき、アルゴンガス等の不活性ガスに窒素ガスを混合したスパッタガスを用いると、ク ロムに窒素を含む遮光膜を形成することができ、またアルゴンガス等の不活性ガスに 一酸ィヒ窒素ガスを混合したスパッタガスを用いると、クロムに窒素と酸素を含む遮光 膜を形成することができる。また、アルゴンガス等の不活性ガスにメタンガスを混合し たスパッタガスを用いると、クロムに炭素を含む遮光膜を形成することができる。
[0034] 上記遮光膜 2の膜厚は、露光光に対して光学濃度が例えば 3. 0以上となるように 設定される。具体的には、 FPDデバイスを製造する際に使用される超高圧水銀灯を 露光光源としたときに、上記遮光膜 2の膜厚は、 200nm以下であることが好ましい。 膜厚が 200nmを超えると、遮光膜 2の基板面内における膜厚ばらつきが大きくなる 傾向となり、遮光膜パターンのパターン精度が悪ィ匕するので好ましくない。尚、遮光 膜 2の膜厚の下限につ 、ては、所望の光学濃度が得られる限りにお 、ては薄くする ことができる。
[0035] また、上記遮光膜 2は、上述の通り積層膜のような多層であることに限られず、単層 でも良い。例えば、遮光膜 2が積層膜である場合において、表層部(上層部)に反射 防止機能を持たせても良い。その場合、反射防止機能を持った反射防止層としては 、例えば、 CrO、 CrCO、 CrNO、 CrCON等の材料が好ましく挙げられる。反射防止 層を設けることによって、露光波長における反射率を例えば、 20%以下、好ましくは 15%以下に抑えることができるので、マスクパターンを被転写体に転写するときに投 影露光面との間で多重反射を抑制し、結像特性の低下を抑制することができる。
[0036] なお、反射防止層は必要に応じて透光性基板側にも設けてもよい。
また、上記遮光膜 2は、クロムと、例えば酸素、窒素、炭素等の元素の含有量が深さ 方向で異なり、表層部の反射防止層と、それ以外の層 (遮光層)で段階的、又は連続 的に組成傾斜した組成傾斜膜としても良い。このような遮光膜を組成傾斜膜とするた めには、例えば前述のスパッタリング成膜時のスパッタガスの種類 (組成)を成膜中に 適宜切替える方法が好適である。
[0037] また、フォトマスクブランクとしては、後述する図 2 (a)にあるように、上記遮光膜 2の 上に、レジスト膜 3を形成した形態であっても構わない。レジスト膜 3の膜厚は、遮光 膜のパターン精度 (CD精度)を良好にするためには、できるだけ薄 、方が好ま 、。 レジスト膜の膜厚の下限は、レジストパターンをマスクにして遮光膜 2をウエットエッチ ングしたときに、レジスト膜が残存するように設定される。
[0038] 次に、図 1に示すフォトマスクブランク 10を用いたフォトマスクの製造方法を説明す る。
このフォトマスクブランク 0を用いたフォトマスクの製造方法は、フォトマスクブランク 1 0の遮光膜 2を、ウエットエッチングを用いてパターユングする工程を有し、具体的に は、フォトマスクブランンク 10上に形成されたレジスト膜に対し、所望のパターン露光 (パターン描画)を施す工程と、所望のパターン露光に従って前記レジスト膜を現像し てレジストパターンを形成する工程と、レジストパターンに沿って前記遮光膜をエッチ ングする工程と、残存したレジストパターンを剥離除去する工程とを有する。
[0039] 図 2は、フォトマスクブランク 10を用いたフォトマスクの製造工程を順に示す断面図 である。
図 2 (a)は、図 1のフォトマスクブランク 10の遮光膜 2上にレジスト膜 3を形成した状 態を示している。尚、レジスト材料としては、ポジ型レジスト材料でも、ネガ型レジスト 材料でも用 、ることができる。
次に、図 2 (b)は、フォトマスクブランク 10上に形成されたレジスト膜 3に対し、所望 のパターン露光 (パターン描画)を施す工程を示す。ノ《ターン露光は、レーザー描画 装置などを用いて行われる。上述のレジスト材料は、レーザーに対応する感光性を有 するものが使用される。
次に、図 2 (c)は、所望のパターン露光に従ってレジスト膜 3を現像してレジストパタ
ーン 3aを形成する工程を示す。該工程では、フォトマスクブランク 10上に形成したレ ジスト膜 3に対し所望のパターン露光を施した後に現像液を供給して、現像液に可溶 なレジスト膜の部位を溶解し、レジストパターン 3aを形成する。
[0040] ウエットエッチングの際使用するエッチング液としては、一般に硝酸第二セリウムァ ンモンに過塩素酸を加えた水溶液が使用される。エッチング液の濃度や温度、処理 時間等のウエットエッチングの条件は、遮光膜のパターン断面特性など力 適宜設定 される。
[0041] 図 2 (e)は、残存したレジストパターン 3aを剥離除去することにより得られたフォトマ スク 20を示す。こうして、本発明により、断面形状の良好な遮光膜パターンが精度良 く形成されたフォトマスクが出来上がる。
なお、本発明は以上説明した実施の形態には限定されない。即ち、透光性基板上 に遮光膜を形成した、所謂バイナリマスク用フォトマスクブランクに限られず、透光性 基板上に露光光を遮光する遮光部と、露光光を透過する透過部と、半透光性領域で あるグレートーン部とを有するグレートーンマスク用フォトマスクブランクであっても良 い。グレートーン部は、露光光に対し所望の透過率となるように材料選定された半透 光性膜であってもよいし、或いは、遮光膜と同じ材料であって、露光光の解像限界以 下の微細な遮光膜パターンであっても良い。半透光性膜パターンが形成されたダレ 一トーンマスクは、半透光性膜パターンが遮光膜パターンの下に形成される半透光 性膜下置きタイプのグレートーンマスクや、半透光性膜パターンが遮光膜パターンの 上に形成される半透光性膜上置きタイプのグレートーンマスクであっても構わない。
[0042] また、本発明にお 、て、透光性基板としては、一般にガラス基板が挙げられ、合成 石英ガラス基板、ソーダライムガラス基板、無アルカリガラス基板などが挙げられる。 また、 FPDデバイスを製造するための透光性基板としては、例えば、 330mm X 45 Ommから 1400mm X 1600mmの大型サイズの基板を言う。
また、本発明において、 FPDデバイスを製造するためのフォトマスクブランク及びフ オトマスクとしては、 LCD (液晶ディスプレイ)、プラズマディスプレイ、有機 EL (エレク トロルミネッセンス)ディスプレイなどの FPDデバイスを製造するためのマスクブランク 及びフォトマスクが挙げられる。
[0043] ここで、 LCD製造用マスクには、 LCDの製造に必要なすべてのフォトマスクが含ま れ、例えば、 TFT (薄膜トランジスタ)、特に TFTチャンネル部やコンタクトホール部、 低温ポリシリコン TFT、カラーフィルター、反射板などを形成するためのフォトマスクが 含まれる。他の表示デバイス製造用マスクには、有機 EL (エレクト口ルミネッセンス) ディスプレイ、プラズマディスプレイなどの製造に必要なすべてのフォトマスクが含ま れる。
実施例
[0044] 以下、実施例により、本発明の実施の形態を更に具体的に説明する。併せて、実 施例に対する比較例についても説明する。
(実施例 1)
大型ガラス基板 (合成石英 10mm厚、サイズ 850mmX 1200mm)上に大型インラ インスパッタリング装置を使用し、膜表面に反射防止膜が形成された遮光膜の成膜を 行った。成膜は、大型インラインスパッタリング装置内に連続して配置された各スぺー ス(スパッタ室)に Crターゲットを各々配置し、まず、 Arガスと Nガスをスパッタリング
2
ガスとして CrN膜を、さらに Arガスと CHガスをスパッタリングガスとして CrC膜を、さ
4
らに Arガスと NOガスをスパッタリングガスとして CrON膜を連続成膜して、 FPD用大 型フォトマスクブランクを作製した。遮光膜は、超高圧水銀ランプの波長である i線 (3 65nm)から g線 (436nm)において、光学濃度で 3. 5となるような膜厚とした。遮光膜 が形成されたガラス基板をホットプレートに載置し、 130°C、 10分間加熱処理を行つ た。加熱処理を終えた遮光膜について、ラザフォード後方散乱分析 (RBS)により深 さ方向における窒素の割合を測定したところ、ガラス基板側力 クロム (Cr)の含有量 を 1としたときに窒素(N)の含有量が 0. 5未満の層と、窒素(N)の含有量が 0. 5以上 となる層の積層膜であって、窒素が遮光膜の表面側力 ガラス基板側に従って、連 続的に減少して ヽる膜であることが確認された。
[0045] また、この遮光膜にっ 、て、 X線回折法により結晶性を測定した。その結果、得られ た遮光膜は、 CrN (200)の回折ピークと Cr ( 110)の回折ピークが確認され、 CrN (2 00)の回折ピーク力も算出される結晶子サイズは、 8nmであった。なお、結晶子サイ ズは、以下に示すシヱラーの式を用いて算出した。
結晶子サイズ (nm) = 0. 9 λ Z j8 cos 0
β = ( β 2 - β 2) 1/2
e 0
ここで、 λ : 0. 15418nm
β:回折ピークの半値幅の補正値 (rad)
β :回折ピークの半値幅の測定値
e
β :半値幅の装置定数 (0. 12° )
0
Θ:ブラッグ角(回折角 2 Θの 1Z2)とした。
[0046] 次に、上記で作製した FPD用大型フォトマスクブランクを用い、洗浄処理 (純水、常 温)後、上記遮光膜上にレーザー描画用フォトレジスト (膜厚 1 μ m)を塗布した後、 加熱処理した。次に、上記レーザー描画用フォトレジストに対して、所定のパターンを レーザー描画した後、現像処理によってレジストパターンを形成し、このレジストパタ ーンをマスクにして、遮光膜をウエットエッチングでパターユングして、 5 μ m幅の通常 パターンと、 1 μ m幅のグレートーンパターン(大型 FPD用露光機の解像限界以下の 微細遮光パターン及び微細透過部カゝらなるパターン)を有する FPD用大型フォトマ スクを作製した。
[0047] この FPD用大型フォトマスクに形成された遮光膜のパターンを、走査型電子顕微 鏡 (SEM)で観察したところ、いずれの遮光膜パターンについても、パターンを平面 視したときのパターンエッジの凹凸(ギザ)は 0. 1 μ m未満と良好であった。また、 FP D用大型フォトマスクの面内のパターン線幅均一性も良好であった。さらに、遮光膜 のパターンの断面形状を観察したところ、断面形状が垂直であり良好であった。
[0048] (実施例 2)
上記実施例 1において、遮光膜成膜後の加熱処理温度を 170°Cとした以外は実施 例 1と同様にして FPD用大型フォトマスクブランク及び、 FPD用大型フォトマスクを作 製した。 FPD用大型フォトマスクブランクにおける遮光膜の結晶性を X線回折法によ り測定したところ、 CrN (200)の回折ピークと Cr ( 110)の回折ピークが確認され、 Cr N (200)の回折ピークから算出される結晶子サイズは、 10nmであった。また、 FPD 用大型フォトマスクの遮光膜パターンについても、パターンを平面視したときのパター ンエッジの凹凸(ギザ)は 0. 1 μ m未満と良好であった。また、 FPD用大型フォトマス
クの面内のパターン線幅均一性も良好であった。さらに、遮光膜のパターンの断面形 状を観察したところ、断面形状が垂直であり良好であった。
[0049] (比較例)
大型ガラス基板 (合成石英 10mm厚、サイズ 850mmX 1200mm)上に大型インラ インスパッタリング装置を使用し、膜表面に反射防止膜が形成された遮光膜の成膜を 行った。成膜は、大型インラインスパッタリング装置内に連続して配置された各スぺー ス(スパッタ室)に Crターゲットを各々配置し、まず、 Arガスと COガスをスパッタリン
2
グガスとして CrO膜を、さら〖こ、 Arガスと Oガスと Nガスをスパッタリングガスとして Cr
2 2
ON膜を連続成膜して、 FPD用大型フォトマスクブランクを作製した。遮光膜は、超高 圧水銀ランプの波長である i線(365nm)から g線 (436nm)において、光学濃度で 3 . 5となるような膜厚とした。遮光膜が形成されたガラス基板について、加熱処理を行 わな力つた。この遮光膜について、ラザフォード後方散乱分析 (RBS)により深さ方向 における窒素の割合を測定したところ、ガラス基板側からクロム (Cr)の含有量を 1とし たときに窒素(N)の含有量が 0. 5未満の層と、窒素(N)の含有量が 0. 5以上となる 層の積層膜であって、窒素が遮光膜の表面側力もガラス基板側に向力つて段階的に 減少して!/ヽる膜であることが確認された。
[0050] また、この遮光膜にっ 、て、 X線回折法により結晶性を測定した。その結果、得られ た遮光膜は、実質的に CrN (200)の回折ピークのみ確認され、 CrN (200)の回折ピ 一タカ 算出される結晶子サイズは、 l lnmであった。
次に、上記実施例 1と同様に、 FPD用大型フォトマスクを作製した。
この FPD用大型フォトマスクに形成された遮光膜のパターンを、走査型電子顕微 鏡 (SEM)で観察したところ、いずれの遮光膜パターンについても、パターンを平面 視したときのパターンエッジの凹凸(ギザ)は 0. 1 μ mをはるかに超えていた。また、 F PD用大型フォトマスクの面内のパターン線幅均一性は悪ィ匕し、遮光膜のパターンの 断面形状を観察したところ、基板側のパターン幅が小さぐ表面側のパターン幅が大 きいパターン形状となり、パターン形状も悪ィ匕する結果となった。
[0051] 上記の実施例 1、 2、比較例の FPD用大型フォトマスクを用いて、 FPDデバイスを 作製し、表示むらを確認したところ、実施例 2の FPD用大型フォトマスクを用いて
作製した FPDデバイスには表示むらはな力つたが、比較例 1の FPD用大型フォトマ スクを用いて作製した FPDデバイスには、フォトマスクのグレートーンパターン部での ギザが原因と思われる表示むらがあることが確認された。
Claims
[1] 透光性基板上に遮光膜を有するフォトマスクブランクにおいて、
前記フォトマスクブランクは、前記遮光膜上に形成されるマスクパターンをマスクに してウエットエッチング処理により、前記遮光膜をパターユングするフォトマスクの作製 方法に対応するウエットエッチング処理用のフォトマスクブランクであって、
前記遮光膜は、クロムを含む材料力 なり、かつ、 X線回折による CrN (200)の回 折ピーク力も算出される結晶子サイズが lOnm以下であることを特徴とするフォトマス クブランク。
[2] 前記遮光膜は、 X線回折法により得られる回折ピークが CrN (200)の回折ピークと Cr( 110)の回折ピークをもつ膜であることを特徴とする請求項 1記載のフォトマスクブ ランク。
[3] 前記遮光膜は、深さ方向の略全域において窒素 (N)が含まれていることを特徴と する請求項 1又は 2記載のフォトマスクブランク。
[4] 前記遮光膜の上層部に酸素を含む反射防止層を形成することを特徴とする請求項
1乃至 3の何れか一に記載のフォトマスクブランク。
[5] 前記フォトマスクブランクは、 FPDデバイスを製造するためのフォトマスクブランクで あることを特徴とする請求項 1乃至 4の何れか一に記載のフォトマスクブランク。
[6] 請求項 1乃至 5の何れか一に記載のフォトマスクブランクにおける前記遮光膜を、ゥ エツトエッチング処理によりパター-ングして前記透光性基板上に遮光膜パターンが 形成されたことを特徴とするフォトマスク。
[7] 透光性基板上に、クロムを含む材料力もなるターゲットを用いたスパッタリング成膜 により、クロムを含む遮光膜を形成する工程を有するフォトマスクブランクの製造方法 において、
前記フォトマスクブランクは、前記遮光膜上に形成されるレジストパターンをマスクに してウエットエッチング処理により、前記遮光膜をパターユングするフォトマスクの作製 方法に対応するウエットエッチング処理用のフォトマスクブランクであって、
前記ウエットエッチング処理により形成される遮光膜パターンの断面形状が所定の 形状となるように、前記遮光膜を構成するクロムの結晶性を制御することを特徴とする
フォトマスクブランクの製造方法。
[8] 前記遮光膜を形成した後、該遮光膜に加わる熱処理条件を調整することにより前 記遮光膜を構成するクロムの結晶性を制御することを特徴とする請求項 7記載のフォ トマスクブランクの製造方法。
[9] 前記熱処理は、前記遮光膜上に形成するレジスト膜形成前、又はレジスト膜形成後 の加熱処理であることを特徴とする請求項 7又は 8記載のフォトマスクブランクの製造 方法。
[10] 前記ウエットエッチング処理により形成される遮光膜パターンの断面形状が膜面に 対して略垂直となる形状であることを特徴とする請求項 7乃至 9の何れか一に記載の フォトマスクブランクの製造方法。
[11] 前記フォトマスクブランクは、 FPDデバイスを製造するためのフォトマスクブランクで あることを特徴とする請求項 7乃至 10の何れか一に記載のフォトマスクブランクの製 造方法。
[12] 請求項 7乃至 11の何れか一に記載の製造方法により得られるフォトマスクブランク における前記遮光膜を、ウエットエッチング処理によりパターユングする工程を有する ことを特徴とするフォトマスクの製造方法。