WO2007085622A1 - Feuchtigkeitshärtende zusammensetzungen enthaltend silanfunktionelle polymere und aminosilan-addukte mit guter haftung - Google Patents
Feuchtigkeitshärtende zusammensetzungen enthaltend silanfunktionelle polymere und aminosilan-addukte mit guter haftung Download PDFInfo
- Publication number
- WO2007085622A1 WO2007085622A1 PCT/EP2007/050700 EP2007050700W WO2007085622A1 WO 2007085622 A1 WO2007085622 A1 WO 2007085622A1 EP 2007050700 W EP2007050700 W EP 2007050700W WO 2007085622 A1 WO2007085622 A1 WO 2007085622A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- moisture
- group
- silane
- composition according
- groups
- Prior art date
Abstract
Description
Claims