WO2006117986A1 - 眼鏡レンズの切削方法及び眼鏡レンズ - Google Patents
眼鏡レンズの切削方法及び眼鏡レンズ Download PDFInfo
- Publication number
- WO2006117986A1 WO2006117986A1 PCT/JP2006/307747 JP2006307747W WO2006117986A1 WO 2006117986 A1 WO2006117986 A1 WO 2006117986A1 JP 2006307747 W JP2006307747 W JP 2006307747W WO 2006117986 A1 WO2006117986 A1 WO 2006117986A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lens
- film
- cutting
- spectacle lens
- chlorinated
- Prior art date
Abstract
撥水性薄膜を施したレンズ表面に、塩素化ポリプロピレン又は塩素化ポリエチレンからなる樹脂製被膜を形成する工程と、該樹脂製被膜上にレンズ加工用両面テープを貼着する工程と、前記レンズを切削加工する工程とを有する眼鏡レンズの切削方法、並びに、撥水性薄膜を施したレンズ表面に、塩素化ポリプロピレン又は塩素化ポリエチレンからなる樹脂製被膜を形成してなる眼鏡レンズであり、撥水性を有するレンズを眼鏡枠入れの玉型加工等の切削加工を行う際に、軸ずれを引き起こすことがない眼鏡レンズの切削方法及び眼鏡レンズを提供する。
Description
明 細 書
眼鏡レンズの切削方法及び眼鏡レンズ
技術分野
[0001] 本発明は、目艮鏡レンズの切削方法及び眼鏡レンズに関し、特に眼鏡レンズを加工 する際に軸ずれを起こすことが無レ、眼鏡レンズの切削方法及び眼鏡レンズに関する 背景技術
[0002] 眼鏡レンズは、円形の厚版レンズを眼鏡枠の形状に合わせるように玉型に切削加 ェして使用される。一方、眼鏡レンズの表面には傷防止のためのハードコート膜や反 射防止膜の他に最表層に水ャケ防止のための撥水性膜が施されている。近年、撥 水性を備えた滑り性の良い水ャケ防止膜が多く用いられるようになつている。レンズ を玉型加工する際に、前述したような撥水性が良好なレンズ表面に、従来法によるェ チレン一ビュルアセテートコポリマーなどからなるレンズ加工用両面テープを用いて 加工を行った場合、レンズ表面の滑りが良いために、レンズ表面とサクシヨンカップ又 はレンズ加工用両面テープの間で滑りが起こり、軸ずれが生じやすい。このため滑り 性の良好な表面を持つレンズに対しては、一般的に、ポリエステルなどのフィルムで 作製される粘着テープをレンズ片面または両面に貼り、その上からサクシヨンカップ 又はレンズ加工用両面テープを貼着することで軸ずれを防止している (特許文献 1参 照)。
[0003] し力 ながら、特許文献 1に記載の方法では、レンズの曲率半径が小さい形状の表 面に粘着テープを貼った場合は粘着テープにしわが入ったり、レンズ表面と粘着テ ープの間に空気が入ったりすることで、玉型カ卩ェ時に粘着テープの付着力低下を引 き起こし、加工軸ずれを生じる場合がある。また粘着テープの大きさが加工玉型より 大きいと、加工時にレンズと研削ツールの隙間にテープが挟まり、加工精度を低下さ せ、加工機の冷却水の排水口にテープ力卩ェ片が詰まるなどの問題が生じるため、一 般的には粘着テープの大きさは切削されたレンズ形状より小さくなつている。このため レンズ表面と粘着テープの接触面積が小さくなり、レンズ度数が高いレンズなどのよう
に加工時の負荷抵抗が大きい場合は、軸ずれを引き起こす場合がある。
また、特許文献 1に開示されている粘着テープを使用した方法では、前もってレン ズ度数の測定、光学中心及び乱視軸のマーキングを行レ、、その後に粘着テープを 貼付する工程となるため、取り扱い時にキズを生じる機会が多くなる。
さらに、撥水性の良好なレンズの表面は水系やアルコール系の液体の濡れ性が悪 ぐレンズ表面で塗膜溶液が弾かれ、均一な透明膜を塗布することが難しいという問 題があった。
また、特許文献 2には、軸ずれ防止手段として、レンズの表面に塗布することにより 、レンズ表面に密着固定される被膜を形成するための被膜形成剤と、所定強度を有 する支持体と前記被膜上に貼着可能な粘着剤を少なくとも有する粘着テープ力 構 成されるキットを用いることが開示され、前記被膜形成剤は合成樹脂と溶剤を含有し 、合成樹脂として酢酸ビニルカ 溶剤としてメタノールが好ましいと開示されている。 し力 ながら、特許文献 2記載のように、合成樹脂として酢酸ビュルを、溶剤としてメ タノールを用いて被膜を形成した場合、皮膜に凹凸が生じて均一な膜が形成できず 、皮膜形成後、レンズメーターによる度数測定が困難という課題を有していた。
このような状況下において、撥水性を備え、滑り性の高いレンズの加工時に軸ずれ を抑え、作業効率の良い切削加工方法が望まれていた。
特許文献 1:特開 2004-122302号公報
特許文献 2:特開 2004-122238号公報
発明の開示
発明が解決しょうとする課題
[0004] 本発明は前記の課題を解決するためなされたもので、撥水性を有するレンズを眼 鏡枠に入れるための玉型加工等の切削加工を行う際に、軸ずれを引き起こすことが なぐ作業効率の良い眼鏡レンズの切削方法及び眼鏡レンズを提供することを目的と するものである。
課題を解決するための手段
[0005] 本発明者等は、前記目的を達成するために鋭意研究を重ねた結果、撥水性薄膜 を施したレンズ表面に、塩素化ポリプロピレン又は塩素化ポリエチレンからなる樹脂
製被膜を形成することにより、軸ずれを引き起こすことがなく眼鏡レンズが切削でき、 前記樹脂製被膜は透明性を有するために、玉型加工等の切削加工を行う際に、被 膜が形成された状態で度数測定、マーキングが行えるため、傷付きも防止されること を見いだし、本発明を完成するに至ったものである。
[0006] すなわち、本発明は、撥水性薄膜を施したレンズ表面に、塩素化ポリプロピレン又 は塩素化ポリエチレン力 なる樹脂製被膜を形成する工程と、該樹脂製被膜上にレ ンズ加工用両面テープを貼着する工程と、前記レンズを切削加工する工程とを有す る眼鏡レンズの切削方法、並びに、撥水性薄膜を施したレンズ表面に、塩素化ポリプ ロピレン又は塩素化ポリエチレン力 なる樹脂製被膜を形成してなる眼鏡レンズを提 供するものである。
発明の効果
[0007] 本発明の眼鏡レンズの切削方法によれば、撥水性を有する眼鏡レンズを切削加工 する際に、軸ずれを引き起こすことがなく正確な加工ができる。
図面の簡単な説明
[0008] [図 1]レンズの軸ずれを評価する基準となる中心ずれ距離及び軸ずれ角を説明する 図である。
発明を実施するための最良の形態
[0009] 本発明の眼鏡レンズの切削方法は、撥水性薄膜を施したレンズ表面に、塩素化ポ リプロピレン又は塩素化ポリエチレンからなる樹脂製被膜を形成する工程と、該樹脂 製被膜上にレンズ加工用両面テープを貼着する工程と、前記レンズを切削加工する 工程とを有する。
また、本発明の眼鏡レンズは、撥水性薄膜を施したレンズ表面に、塩素化ポリプロ ピレン又は塩素化ポリエチレンからなる樹脂製被膜を形成してなるものである。 本発明に用いられるレンズとしては、特に限定されず、ガラスレンズ、プラスチックレ ンズのいずれにも適用でき、硬化膜や反射防止膜等が施されていてもよい。この硬 化膜の材料としては、特に限定されず、公知の有機ケィ素化合物及び金属酸化物コ ロイド粒子よりなるコーティング組成物を使用することができる。前記反射防止膜の材 質及び形成方法は特には限定されず、従来より知られている無機酸化物よりなる単
層、多層膜を使用することができる。
また、レンズ表面に施される撥水性薄膜の種類及び形成方法は、特に限定されず
、例えば、特開 2005-3817号公報に記載されているような含フッ素シラン化合物等の 撥水処理剤を用いて、真空蒸着等の公知の方法で形成すればよい。また、前記樹 脂製被膜が撥水性薄膜から、より容易に剥がれやすくするため、撥水性薄膜は、撥 水性に加え良好な撥油性を兼ね備えた材質力 なることが好ましい。
[0010] 前記塩素化ポリプロピレン力 なる樹脂製被膜は、塩素化ポリプロピレンと溶媒とを 含有した塩素化ポリプロピレン溶液からなる被膜形成剤を用いて形成されると好まし ぐ前記塩素化ポリエチレン力 なる樹脂製被膜は、塩素化ポリエチレンと溶媒とを含 有した塩素化ポリエチレン溶液からなる被膜形成剤を用いて形成されると好ましい。 以下、塩素化ポリプロピレン溶液と塩素化ポリエチレン溶液を総称して被膜形成剤 ということがある。
[0011] 本発明で用いる被膜形成剤は、レンズ表面に樹脂製被膜を形成するための溶液で あり、被膜形成剤における塩素化ポリプロピレン及び塩素化ポリエチレン (溶質)の濃 度は、それぞれについて被膜形成剤全量を基準にして、通常 5〜40質量%、好まし くは 15〜25質量%である。また、塩素化ポリプロピレン、塩素化ポリエチレンの重量 平均分子量は、通常 4〜: 10万、好ましくは 6〜8万である。また、被膜形成剤の固形 分濃度は、通常 5〜40質量%、好ましくは 15〜25質量%である。
前記塩素化ポリエチレンとはポリエチレンに塩素を付加させたもの、塩素化ポリプロ ピレンとはポリプロピレンに塩素を付加させたものである。
前記塩素化ポリプロピレン、塩素化ポリエチレンに対する溶媒としては、特に限定さ れないが、例えば、芳香族炭化水素、塩素化炭化水素、エステル類、ケトン類及び 脂環式炭化水素を有する脂肪族炭化水素化合物から選ばれる一種以上を用いれば 好ましい。
前記芳香族炭化水素の例としては、トルエン、キシレン等が挙げられ、前記塩素化 炭化水素の例としては、塩化メチル、塩化メチレン、クロロホノレム、トリクロロエチレン、 テトラクロロエチレン等が挙げられ、前記エステル類の例としては、酢酸エステル類、 プロピオン酸エステル類等が挙げられ、前記ケトン類の例としては、メチルェチルケト
ン、メチルイソプチルケトン、ジイソプチルケトン、アセトン等が挙げられ、前記脂環式 炭化水素を含有する脂肪族炭化水素の例としては、シクロへキサン、メチノレシクロへ キサン、ェチルシクロへキサン等が挙げられる。
[0012] また、本発明で用レ、る被膜形成剤は、必要に応じ、界面活性剤を添加しても良ぐ シリコーン系界面活性剤及び Z又はフッ素系界面活性剤が好ましレ、。界面活性剤を 添加することにより、形成被膜に凹凸がな より均一な膜となり、度数測定がより容 易になる。
前記界面活性剤の添加量としては、被膜形成剤全量を基準にして、通常 0. 01〜5 質量%、好ましくは 0. 1〜:!質量%である。
前記シリコーン系界面活性剤としては、下記一般式(1)〜(4)の様な例が挙げられ 、重合度及び変性率を変えることにより、低粘度液状から高粘度ペースト状、又は固 体状のシリコーンにすることができ、また有機基 Xにより任意の親水性を付与すること ができる。
[0013] [化 1]
(側鎖変性型)
CH3 X
(CH3)3SiO(SiO)m(SiO)nSi(CH3)3
CH3 CH3
(両末端変性型)
CH3 CH3 CH3
X_ SiO(SiO)mSi— X
H3 0Η3 Η3
(両末端側鎖変性型)
H3し X CH3
X- SiO(SiO)m(SiO)nSi-X
GH3 H3 0H3 CH3 前記各一般式(1)〜(4)において、 mは 1以上の整数、 nは 1以上の整数である。 有機基 Xとしては、下記ポリエーテル系、ポリグリセリン系、ピロリドン系、ベタイン系 、硫酸塩、リン酸塩及び 4級ァミン塩等が挙げられる。
ポリエーテル系:— C H〇(C H O) (C H〇) R[aは 1以上の整数、 bは 1以上の整数
3 6 2 4 a 3 6 b
、 Rは有機基である。 ]
ポリグリセリン系:— C H 0(CH CH(OH)CH〇) H[cは 1以上の整数。 ]
3 6 2 2 c
ピロリドン系:
ベタイン系: 一 C H N+(CH ) CH COO"
硫酸塩: C H 0(C H〇) SO Na[aは 1以上の整数。 ]
リン酸塩: C H 0(C H O) PO Na[aは 1以上の整数。 ]
[化 3] o
II
一 C3H60 (C2H40) a— P— ONa
OH
[aは 1以上の整数。 ]
4級ァミン塩: -C H N+(CH ) -Of
[0015] また、前記フッ素系界面活性剤としては、例えば、ァニオン系、ノニオン系、カチォ ン系、両性イオン系等が挙げられる。
[0016] 以上のような被膜形成剤を用いて、撥水性薄膜を施したレンズ表面に、樹脂製被 膜を形成するが、樹脂製被膜の形成方法としては、例えば、スピンコーティング法や 浸漬塗布法を用いることができ、浸漬塗布法で形成することが好ましい。具体的には 浸漬塗布法により、通常、上昇速度 50mm/min〜: 1000mm/min、好ましくは 15 0mm/min〜600mmZminで、レンズの切削加工もしくは玉型加工に用いる軸部 材によりレンズが固定される部分よりも広い面積に塗布するが、取り扱いキズを減らす という観点からはレンズ全面に塗布することが好ましい。塗布後、溶媒が揮発するとレ ンズ表面に密着固定された樹脂製被膜が形成される。
なお、従来、透明性を有する被膜を得るためには、被膜の膜厚ムラをなくし、膜中 への気泡を排除する必要があった力 本発明では塩素化ポリプロピレン又は塩素化 ポリエチレンを上記のような高揮発性の溶媒に溶解させた溶液を用いることで、例え
ば、浸漬後の引き上げ時にレンズ表面に形成された被膜力 の溶媒の揮発が早いた め、塗布溶液の粘度が高くなり、撥水膜による弾きは抑えられる。このため溶液の粘 度も必要以上に高くする必要がなぐ均一で透明な膜を得ることが可能となる。
[0017] 本発明においては、前記樹脂製被膜が形成された後、該樹脂製被膜上にレンズ加 ェ用両面テープを貼着し、レンズの切削加工を行う。
レンズ加工用両面テープとしては、特に限定されず公知のものを用いればよぐ例 えば、商品名:リーブテープ (住友 3M (株)製)、商品名:ブロッキングパット (株式会社 サイモン製)等が知られてレ、る。
また、レンズを切削する加工機械としては、特に限定されず公知の機械を用いればよ ぐ眼鏡小売店等で使用されている機械や、加工業者が使用している機械を使用す ること力 Sできる。
切削加工後の眼鏡レンズにおいて、樹脂製被膜が不要の場合には、樹脂製被膜の 端を指でつまむなどして容易にはがすことができる。
実施例
[0018] 以下、本発明を実施例を用いてより具体的に説明するが、本発明はこれらの実施 例に限定されるものではない。
実施例 1
(1)反射防止膜付プラスチックレンズの作製
プラスチックレンズとして、ジエチレングリコールビスァリルカーボネート重合体系レ ンズ (HOYA (株)製 Hi— Lux (商品名)、屈折率 1. 499、度数 0. 00)を用い、この プラスチックレンズ基材上に、特開昭 63— 10640号公報に開示されている硬化膜を 施した。具体的には、 SiO濃度 40%のコロイダルシリカ(スノーテックス— 40、水分
2
散シリカ、 日産化学 (株)製) 240質量部に、 0. 5N塩酸 2. 0質量部、酢酸 20質量部 をカロえた溶液を、 35°Cにして攪拌しながら、 y—グリシドキシプロピルトリメトキシシラ ン (3官能有機ケィ素化合物) 95質量部を滴下し、室温にて 8時間攪拌し、室温にて 16時間放置した。この加水分解溶液に、メチルセ口ソルブ 80質量部、イソプロピルァ ルコーノレ 120質量部、ブチルアルコール 40質量部、アルミニウムァセチルアセトン 1 6質量部、シリコーン系界面活性剤(NUCシルウエット Y— 7006 (商品名)、 日本ゥニ
力(株)製) 0. 2質量部、紫外線吸収剤(チヌビン P (商品名)、チバガイギー製) 0. 1 質量部を加えて、 8時間攪拌後、室温にて 24時間熟成させコーティング組成物を得 た。該組成物を、引き上げ速度 15cm/minで浸漬法により塗布、室温にて 15分放 置後、 120°Cで 2時間加熱硬化して硬化膜を施した。
次に、前記硬化膜上に真空蒸着法 (真空度 2. 67 X 10"3Pa (2 X 10"5Torr) )によ り、二酸化ケイ素からなる下地層(屈折率 1. 46、膜厚 0. 5 λ ( λは 550nm) )を形成 し、該下地層の上に、プラスチックレンズに酸素イオンビームを照射するイオンビーム アシスト法で得られる二酸化チタン力らなる層(膜厚 0. 06え)、真空蒸着法で得られ る二酸化ケイ素からなる層(膜厚 0. 12え)、さらにイオンビームアシスト法で得られる 二酸化チタン力 なる層(膜厚 0. 06え)よりなる 3層等価膜である第 1層(屈折率 1. 7 0、膜厚 0. 24 λ )を形成した。この第 1層の上に、イオンビームアシスト法により二酸 化チタン力 なる第 2層(屈折率 2. 40、膜厚 0. 5 λ )を形成し、該第 2層の上に、真 空蒸着法 (真空度 2. 67 X 10— 3Pa (2 X 10— 5Torr) )により二酸化ケイ素からなる第 3 層(屈折率 1. 46、膜厚 0. 25え)を形成して、反射防止膜付きプラスチックレンズを 得た。このレンズは直径 75mmの円形で、視感反射率は 0. 4%であった。
(2)撥水性薄膜の形成
前記(1)で得られたプラスチックレンズの凹凸両面に、撥水処理剤として下記化合 物 (A)及び溶媒としてメタキシレンへキサフロライド(C H (CF ) )を用いて、下記の
6 4 3 2
ようにしてフッ素防汚コーティングが施されたレンズを作製した。
(CH O) SiCH CH CH OCH CF (OC F ) (OCF ) OCF CH OCH CH CH
3 3 2 2 2 2 2 2 4 p 2 q 2 2 2 2 2
Si (OCH ) · · · (A)
3 3
(式中、 p = 22、 q = 22、繰り返し単位(〇C F )及び(〇CF )の配列はランダムであり
2 4 2
、化合物 (A)は 3次元構造の硬化物である。 )
化合物(A)を 0. 30mlしみ込ませたステンレス製焼結フィルター(糸田孔径 80〜100 a m、直径 18mm φ、厚さ 3mm)を真空蒸着装置内にセットし、以下 (I)、 (II)の条件 で電子銃を用いて該焼結フィルター全体を加熱して、前記反射防止膜付プラスチッ クレンズに撥水性薄膜を形成した。このレンズの度数は _ 7. 00D、視感反射率は 0 . 4%であった。
(I)真空度: 3. 1 X 10 〜8. 0 X 10 Pa (2. 3 X 10 〜6. 0 X 10 Torr)
(II)電子銃の条件
[0020] (3)樹脂製被膜の形成
被膜形成剤として、固形分濃度 20質量%となるように、溶質として重量平均分子量 6〜8万の塩素化ポリプロピレン、溶媒としてトルエン及びシクロへキサンを含有する 被膜形成剤(商品名:スーパークロン 日本製紙ケミカル (株)製)を使用して(2)で得 られたプラスチックレンズを、常温で浸漬塗布法により下降速度を 300mm/min、 上昇速度を 300mm/minとして被膜形成剤を全面に塗布し、 15分間常温乾燥させ てプラスチックレンズに樹脂製被膜を形成した。
(4)プラスチックレンズの評価
上記(1 )〜(3)の操作を繰り返し、プラスチックレンズのサンプノレを 10枚作製し下記 (i)及び(ii)の評価を行った。
(i)度数変化の測定
樹脂製被膜形成前と形成後のプラスチックレンズのサンプノレについてレンズメータ 一にて度数の測定を行った結果を表 1に示す。
(ii)軸ずれの測定
レンズの光学中心を通るよう、横方向 (X軸)及び縦方向 (Y軸)に 2本の線を直交する ように設ける。レンズの光学中心にレンズ加工用両面テープ (商品名:リーブテープ( 住友 3M (株)製)の基準点が来るように、前記テープを貼り付ける。その後、 HOYA ( 株)製の玉摺り加工機(商品名: AE _ 3000)を用いてレンズの玉型加工を行レ、、レ ンズ加工前と加工後のレンズ力卩ェ用両面テープの基準点間の直線間距離及び角度 を測定し、それぞれ中心ずれ距離 (A (mm) )、軸ずれ角(Θ (° ) )とした(図 1参照)。 図 1において、点線が加工前の直行座標、実線が加工後の直行座標を示す。得られ た結果を表 2に示す。
なお、表 2中、中心ずれ距離 Aが 0. 5mm以上を X、 0. 5mm未満を〇として記載 した。
[0021] 比較例 1
実施例 1において、樹脂製被膜の代わりに眼鏡用レンズの両面にポリエステル製フ イルム (商品名: AT— 22 ビッグテクノス (株)製)を貼り付け、その上の凸面に両面加 ェ用テープ (リーブテープ (住友 3M (株)製))を貼り付けた以外は同様にして、プラス チックレンズのサンプルを 10枚作製し(4)の(i)及び(Π)の評価を行った。それらの結 果を表 1及び 2に示す。
ただし、比較例 1においては、(4)の (i)の測定は、樹脂製被膜形成前と形成後の プラスチックレンズのサンプルの代わりに、ポリエステル製フィルムの貼り付け前と貼り 付け後のサンプルについてレンズメーターにて度数の測定を行った。
[0022] 比較例 2
実施例 1において、樹脂製被膜を形成せず、眼鏡用レンズの凸面に両面加工用テ ープ (リーブテープ (住友 3M (株)製))のみを貼り付けた以外は同様にして、プラスチッ クレンズのサンプルを 10枚作製し (4)の(ii)の評価を行った結果を表 2に示す。
[0023] [表 1] 表 1
※Sは度数を表し、単位は Dである。
[0024] 表 1の結果より、実施例 1のプラスチックレンズでは:樹脂製被膜形成の前後で度数
表示差が大きくずれるものは無かった。これに対し、比較例 1のプラスチックレンズで はポリエステル製フィルムの貼り付け前後で度数表示差が大きぐ度数の誤表示とな るものがあるため、フィルムやテープ貼り付け後に正確な度数測定を行うことはできな レ、。なお、通常は、フィルムやテープを張る位置を決めるためにレンズメーターを使 用するため、何の印も無い状態で正確な位置にフィルムやテープを張ることは不可 能である。
以上の結果より、実施例 1のように樹脂製被膜を形成することにより、正確な度数測 定が行えることが確認された。
[表 2] 表 2
表 2の結果より、実施例 1のプラスチックレンズでは、 10枚すべてについて中心ず れ及び軸ずれが発生しな力つた。一方、比較例 1では中心ずれはないが、軸ずれが 起きたものがあった。比較例 2では、全てのレンズで中心ずれ、軸ずれがおきた。また 、実施例 1のプラスチックレンズは玉型加工後の撥水性が劣化することなく維持され ていた。
また、玉型加工終了後、実施例 1のプラスチックレンズの樹脂製被膜の端を指でつ まんで剥がすと、加工後のレンズはレンズ表面に汚れの無いきれいな状態となり、そ の後も洗浄を必要としないため、取り扱い傷を減らすことが可能となった。
[0027] 実施例 2
実施例 1において、被膜形成剤に、シリコーン系界面活性剤 (Y_ 7006 (商品名)、 (東レ 'ダウコーユング社製))を 0. 1質量%添加した以外は全て同様にしてプラスチ ックレンズに樹脂製被膜を形成し、実施例 1の(4)と同様にプラスチックレンズを評価 したところ実施例 1と同様の結果が得られた。
比較例 3
実施例 1において、実施例 1で用いた被膜形成剤の代わりに、合成樹脂として変性 酢酸ビニル樹脂を 25〜35質量%、溶剤としてメタノールを 65〜75質量%含有する 被膜形成剤 (Three Bond 1401 (商品名)、(株)スリーボンド製)を用いた以外は同様 にしてプラスチックレンズに樹脂製被膜を形成したところ、レンズ表面に凹凸ができて しまい、実施例 1の(4)の(1)と同様にプラスチックレンズの度数測定を行なった結果 、レンズメーターにおける度数表示値が誤数値となった。
産業上の利用可能性
[0028] 本発明の眼鏡レンズの切削方法によれば、撥水性を有する眼鏡レンズを玉型カロェ 等の切削加工する際に、軸ずれを弓 Iき起こすことがなく正確な加工ができる。このた め、実用的な眼鏡レンズの切削方法として有用である。
Claims
[1] 撥水性薄膜を施したレンズ表面に、塩素化ポリプロピレン又は塩素化ポリエチレン 力 なる樹脂製被膜を形成する工程と、該樹脂製被膜上にレンズ加工用両面テープ を貼着する工程と、前記レンズを切削加工する工程とを有する眼鏡レンズの切削方 法。
[2] 前記樹脂製被膜が浸漬塗布法により形成されるものである請求項 1に記載の眼鏡 レンズの切削方法。
[3] 前記塩素化ポリプロピレン力 なる樹脂製被膜が、塩素化ポリプロピレンと、芳香族 炭化水素、塩素化炭化水素、エステル類、ケトン類及び脂環式炭化水素を有する脂 肪族炭化水素化合物から選ばれる一種以上の溶媒とを含有した塩素化ポリプロピレ ン溶液からなる被膜形成剤を用いて形成されるものである請求項 1に記載の眼鏡レ ンズの切削方法。
[4] 前記塩素化ポリエチレン力 なる樹脂製被膜が、塩素化ポリエチレンと、芳香族炭 化水素、塩素化炭化水素、エステル類、ケトン類及び脂環式炭化水素を有する脂肪 族炭化水素化合物から選ばれる一種以上の溶媒とを含有した塩素化ポリエチレン溶 液からなる被膜形成剤を用いて形成されるものである請求項 1に記載の眼鏡レンズの 切削方法。
[5] 前記樹脂製被膜が界面活性剤を含有する請求項 1に記載の眼鏡レンズの切削方 法。
[6] 前記撥水性薄膜が撥油性を兼ね備えた請求項 1に記載の眼鏡レンズの切削方法
[7] 前記レンズが反射防止膜を有する請求項 1に記載の眼鏡レンズの切削方法。
[8] 撥水性薄膜を施したレンズ表面に、塩素化ポリプロピレン又は塩素化ポリエチレン 力もなる樹脂製被膜を形成してなる眼鏡レンズ。
[9] 前記樹脂製被膜が界面活性剤を含有する請求項 8に記載の眼鏡レンズ。
[10] 前記レンズが反射防止膜を有する請求項 8に記載の眼鏡レンズ。