WO2006009229A1 - 固体リン酸触媒およびそれを用いたオレフィンの二量化方法 - Google Patents

固体リン酸触媒およびそれを用いたオレフィンの二量化方法 Download PDF

Info

Publication number
WO2006009229A1
WO2006009229A1 PCT/JP2005/013427 JP2005013427W WO2006009229A1 WO 2006009229 A1 WO2006009229 A1 WO 2006009229A1 JP 2005013427 W JP2005013427 W JP 2005013427W WO 2006009229 A1 WO2006009229 A1 WO 2006009229A1
Authority
WO
WIPO (PCT)
Prior art keywords
phosphoric acid
mass
olefin
acid
reaction
Prior art date
Application number
PCT/JP2005/013427
Other languages
English (en)
French (fr)
Inventor
Tatsuo Hamamatsu
Nobuhiro Kimura
Tsutomu Takashima
Takashi Morikita
Original Assignee
Nippon Oil Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Oil Corporation filed Critical Nippon Oil Corporation
Priority to US11/632,369 priority Critical patent/US7741527B2/en
Priority to KR1020077000811A priority patent/KR101121822B1/ko
Priority to CA2574229A priority patent/CA2574229C/en
Priority to EP05766288A priority patent/EP1769847A4/en
Publication of WO2006009229A1 publication Critical patent/WO2006009229A1/ja

Abstract

本発明により、オレフィン二量化反応において高い反応活性および二量体選択性が得られる固体リン酸触媒およびそれを用いる効率的なオレフィンの二量化方法が提供される。　すなわち、珪酸質担体にリン酸を担持して成り、担持されたリン酸中のオルトリン酸の比率がリン原子換算で６０モル％以上である固体リン酸触媒が提供される。前記固体リン酸触媒は、珪酸質担体にリン酸水溶液を接触したのち乾燥させて調製されものであって、その調製工程が１００℃未満である。さらに、前記触媒に、オレフィン含有原料を接触させる方法が提供され、前記方法においてオレフィン含有原料中に水を１０～１０００質量ｐｐｍ含有させる方法、前記方法において固体リン酸触媒にオレフィン含有原料を液相で接触させる、および前記方法においてオレフィンが炭素数３～７のモノオレフィンである等の方法が提供される。

Description

删書 固体リン Μ¾およびそれを用いた才レフィンのニ量ィ 法 擁分野
本発明は、 担体にリン酸を插寺して成る固体リン およびそれを用いたォレフィ ンの選択的二量化方法に関する。 背景鎌
ォレフィンのオリゴマ一は各 Mffl途に用いられており、 特に レフィン （例 えば、 プロピレン、 n—ブテン、 イソブテン、 ペンテ の二量体は、 ガソリンの高 オクタン価¾ や化学中間 IT料として である。 ォレフィンのニ量化を含む才リゴマ —化は、 翻嫌を用いて行われ、 これまで数多くの職がなされている。 として は、 薩、 フツイは素、 リン酸、 塩化アルミニウム及びフッ化ホウ 、 非晶質または 結晶質アルミノシリケ一ト、 粘土、 イオン 3 ^脂、 混合酸化物、 担体付き酸などの固 体酸が慣用 β勺な例として挙げられ 安価で簡便な纖プロセスが 能である固体リン酸 «についても種々検討されている。 例えば、 1 0 0°C以上の力 件で調製された固体リン m«を用いてプロピレンを オリゴマー化する方法 （特 や、 リン酸と 原料の無定形混合物を 2 5 0 〜4 5 0°C、 水蒸^?雛 3〜5 0モル％の条件で結尉匕して調製した羅（シリコンォ ルトホスフェートおよびシリコンピロホスフェートからなる を用いてプロピレン をオリゴマー化する方法 （特 H2) が開示されている。 また、 固体リン翻 のリン酸の縮合度が、ォレフィンのオリゴマー化反応の活性に影 響をおよぼすこと から知られており、 例えば、 固体リン MMを水に浸潰して溶 出する リン^^ (オノレトリン酸、 ピロリン酸などの非縮合または^ I合のリン 酸） の賺に対する質量比が小さい讓（嫌されたリン酸中のオルトリン酸の比率が、 リン原子露で多くても 4 6モル％髓） を用いて、 C 3および C 4等のォレフィンを オリゴマー化する例が開示されている （特 R«3、 非特 しかしながら、 上記の の固体リン を用いるォレフィンのオリゴマー化は、 いずれもォレフィンのニ量化を主目的としたものではないうえに、 «の固体リン纖 媒では才レフィンの高重合物の副生が避けられず、 ォレフィンのニ量体を選択的に得る ことは困難であつ/こ。 なお、 リン膨 Κ^Μ^作においては、 時間、 、 等の操作条件にもよるが、 職 工程で »されたオルトリン酸の縮合が進行し易い。 これは一 iBBt!麦でも同様に縮合 が進行しやすい。 特に後記するように、 全リン酸中のオルトリン酸謎が低いと縮合が 進行しやすい。 また、 これ 記したように特言^ #3でも記載しているが、 ー 合 した高縮合のリン酸では、 水に非常に緩隱にしか溶解しない （特言 «3、 段落 0 0 3 6、 後段) 。 つまり高縮合のリン酸の加水分解は実際上はその進行が緩 I曼であるのであ る。
換訂れば、 赚のリン 時操作では、 全リン酸中のオルトリン酸 MSが低 いこともあり、 結果として縮合がt行し易ぐ 高縮合のリン酸の担時量が多くならざる を得ない。 そのため、 上記した （ されたリン酸中のオルトリン酸の比率が、 リン原 子騰で多くても 4 6モル％程度） の：^、 実際のオルトリン酸の比率は、 たとえオル トリン酸が生成しているとしても縮合が進行するために理論値としての駄値 （4 6モ ル％程度） よりもはるかに少ないと予想される。 そして乾^ X程で一 合して担持さ れた高縮合のリン酸は、 その後に、 系中で液状、 ガス状の水と誦しても加水 されるとしてもオレトリン酸に戻るの« ^、ずしも容易ではないということであり、 さら に謂麦のオルトリン酸では、 全リン酸中のオルトリン廳 ISが低レ^^はもちろん、 たとえ該 が くとも SJS条件によってはオルトリン酸の縮合が i亍する可食 I生もあ る。
特言 1 ： ム、平 8— 2 9 2 5 1号么
特言^ «2： 平 7— 5 9 3 0 1 報
特言 ΐ«3：特開 2 0 0 1— 1 9 9 9 0 7号 非特 fR¾ l： "Applied Catalysis A： General", 1993, 97, p.177-196 発明の開示
ォレフィンのニ量化 において高い 活性および二量体 生を示す固体リン酸 ¾を iiftし、 効率的な才レフィンのニ量イ^法を ίΐ#ττることにある。
本発明の第 1は、 担体にリン酸 （加水飾によりリン酸となるものを含む。 以下同 じ。 ) を膽して成り、 賺されたリン酸中のオルトリン酸の比率がリン原子騰で 6
0モル％以上であることを mとする固体リン m»sである。
本発明の第 2は、 担体にリン 醒を雄したのち観させて調製されたものであ つて、 その調製工程が 1 0 0°C未満であることを猶とする本発明の第 1に記載の固体 リン翻螩である。
本発明の第 3は、 本発明の第 1または第 2の固体リン に、 ォレフィ： ^有原料 を皿させることを,とする才レフィンのニ量 f ^法である。
本発明の第 4は、 本発明の第 3において、 ォレフィ ^有廳中に水を 1 0〜1 0 0 0質量 p pm含 ることを ^とする方法である。
本発明の第 5は、 本発明の第 3または第 4において、 固体リン^ Kにォレフィ ^ 有 料を液相で機させることを體とする方法である。
本発明の第 6は、 本発明の第 3ないし第 5のいずれかにおいて、 ォレフィンが炭素数 3〜7のモノォレフィンであることを置とする方法である。 発明の効果
本発明の固体リン^ ¾は、 特にォレフィン二量化反応に適しており、 活性および二 量傳: 性が く、 が長いため、 効率的にォレフィン二量体を製造することが できる。 発明を実施するための最良の形態
以下に本発明をさらに詳しく説明する。
本発明に用いる固体リン ^ ^の担体としては、 リン酸を嫌できるものであれば特 に制限はないが、 好ましくは、 珪藻土、 滴虹、 繊毛 ¾±、 キーゼルグール、 カオリン、 フラー土、 人工多? シリ力などの^ R担体およびその混合物の成形品を挙げること ができる。 担体を成形する:^、 十分な弓艘、 m , 比表 ®¾を与える目的でいか なる? 条件でも力焼を行うことができる。 成形の方法および成形品の开狱については 特に制限が無ぐ 例えば打誠形、 押出し成形、 スプレードライ、 転動微立， 油中 等の方法で、 粒状、 板状、 ペレット状の各 «舰本とすることができ、 mo. 5〜
5mm@¾とすることが きる。 リン酸としては、 具体的には、 オルトリン酸およびその縮合物 （ピロリン酸、 ポリリ ン酸等） カ举げられる。攝操作には、 加水連によりリン酸となるもの （リン酸前駆 体） 、 例えば、 数 1〜8のアルコールのリン酸エステル等も棚することが^5きる。 また、 それらの混合物でもよい。 賺中の担体に対するリン酸の割合 （リン酸はオルトリン酸として計算し、 オルトリ ン酸]^のリン酸については、 に加水 したときに生 るオルトリン酸に する。 以下、 「リン Mt*J という。 ） は、 1 0〜2 0 0質量％、 好ましくは 3 0〜 1 2 0質量％である。 少ない場合はォレフインの二量化反応の活性が低く、 多い場合に は反 液中へのリン酸の溶出が大きくなり機器装置の腐食の問題が発生するので好まし くない。 本発明においては、 担体に Sitされたリン酸中のオルトリン酸とその他の縮合したポ リリン^との比率が 要である。 すなわち、 リン酸中のオルトリン酸の比率が、 リン 原子購で 6 0モル％以上、 好ましくは 7 0モル％以上、 より好ましくは 8 0モル％以 上であるときに、 ォレフィンのニ量化反応において優れた活性および二量体選択性が発 現する。
リン酸中のオルトリン酸の比率が、 リン原子 で 6 0モル％以上の ±l^r、 オルトリ ン酸の縮合の進行が非常に緩 I曼となるが、 6 0モル％より小さい： tj^は、 オルトリン酸 の縮合の進行が速ぐ ォレフィンの二量化反応の急激な活性低下を引き起こす。 ォレフ ィンのニ量化反応において高い活性および二量体魔性を翻間膽するためには、 触 媒のリン酸中のオル卜リン酸の比率が 6 0モル％以上の;!態でォレフィンを させる こと力肝要である。 賺のリン酸中のオルトリン酸の比率を測 ¾r る手段については特に P跪は無いが、 リン核 (^P)の固 f繊^ ^口,！^法が最も適した方法である。 リン酸のリン核の化学 シフト備纖合度に応じて高腿にシフトし、 オルトリン酸を O p pmとした齢、 ピ 口リン酸は一 1 1. 8 p pm、 ポリリン酸は一 2 4. 3 p pm付近に観測される。 これ らのシグナルを波形分離して 比を求めることにより、 リン 合糸！ ^を調べること が きる。
上記測定中およびその嘿 (前処衝においては、 腿が水分と誦しないようにする 必要がある。 上記測定中およびその請 (前処衝において水分と漏すると、 羅中の 縮合リン酸の"^が加水連してオルトリン酸に変化してしまうため、 正確に測 ¾Tる こと力 ?きなくなる。 方法としては、 担体をリン 激液に浸漬したのち乾燥する方法や、 担体 とリン を混合して得られたペーストを成形 ·草纖する方法力 ましく用いられ る。
前者の方法は、 二量化反応の際に羅中のリン酸が反 液中に溶け出すことによってリ ン酸担持量;^減少、した 、 «の再浸漬によりリン酸を することが、できるの で特に好ましい。 後者の方法の:^、 成形の方法および成形品の颜犬については、 担体 の成形と同様に行うことができる。 賺調製に関して、 担体をリン^:賺に浸漬したのち観させて膽させる方法に ついて具体的に説明する。 賺調製に麵する装置については特に ρ跪は無ぐ "^的 な回分槽を用いることが きるが、 ォレフィンのニ量化反応を実施する反応器を用いれ ば、 匪調製と同時に «« ^が きる。 浸漬に用いるリン 溶液の髓は、 特に制 限はないが通常約 1 0〜 8 0質量％で、 目的とするリン酸賺量により変化させること が きる。 例えば、 リン酸 iSt* 7 0質量％とするためには、 担体の表面濃の性状にもよるが、 リン 赚の？鐘 «®常 3 5〜4 5質量％離である。 浸漬時間は、 通常 1時間驗 またはそれ以上であれば特に問題ない。 浸漬温度は 1 0 0°C未満、 好ましくは 5 0°C以 下である。 1 0 0°C以上の高 件では、 リン酸中のオルトリン酸の！；摔が小さくなる 恐れがあるので好ましくない。 また、 、¾が低すぎると凝固して浸漬できなくなるので、 0 °C以上、 さらには 1 5 °C以上が好ましい。 浸漬後、 ろ過などの 自妨法で魏のリン^ K溶液を鉄した後に、 余分な水分の 随を蒸発観により戯行うことが きる。大気中に放置してもよいし、 気ィ機を用 いてもよい。 皐燥に用いる気体は、 ¾ ^件において気体 態であれば特に 15跪されな ぃカ 空気、 ガス、 7_素ガス、 ^数 1〜5の!^口炭 fb!K素ガス力 «である。 ま た、 気体中には！^口量以下の水蒸気が含まれていても良い。 例えば、 室温において、 約 2. 5 以下の水蒸気を含む空気を用レ τ¾ ^を行うこと力 s きる。 ¾«®ま 1 0 0°C未満、 好ましくは 5 0°C以下である。 1 0 0°C以上では、 リン酸の縮合が急 に 起こり、 リン酸中のオルトリン酸の比率が低下するので好ましくない。 また、 が低 すぎると皐腦率が悪くなるので、 0°C以上、 さらには 5 °C以上が好ましい。 嫌時間 および気体の ¾1は、 腿によるリン酸の縮合の進^合を確認しながら、 リン酸中の オルトリン酸の比率が爾己した割合の範囲内、 例えば、 リン原子騰で 6 0モル％未満 とならないように細周 t る。 リン酸の縮合力雄行した高縮合リン^ ¾は、 再浸漬 処理によって低縮合 4え態 （オルトリン酸の比率が 6 0モル％以上の忧態） に戻し、 これ を使用すること力 きる。 ォレフィ ^有 IT料の才レフィンとしては、 数 3〜 7のモノォレフィンカ で あり、 纖状、 分岐状およ 状のいずれでもよく、 目的 物に応じて職でも混合 物でも用いることが きる。 具体的にはプロピレン、 ブテン類 （1—ブテン、 シス一 2 ーブテン、 トランス一 2—ブテン、 イソプチレン） 、 ノルマルペンテ^、 イソペンテ ン類、 シクロペンテ;^、 ノルマルへキセン類、 イソへキセン類、 シクロへキセン類、 ノルマルヘプテン類、 イソヘプテン類、 シクロヘプテ ¾を挙げることが きる。 なお、 ォレフィンの二量化とは、 應ォレフイン 2モルの （ォレフイン混合 料の:^に は、 異なる原料ォレフィン同士の も含む。 ) によりォレフィン 1モルが生^ "Tるこ とを意味する。 本発明では、 枓ォレフインとして、 例えばブテン類カ18¾に用いられる。
得られるブテン類の二量体のうち、 ィソォクテンはガソリンの高オクタン価凝才 料 として有用である。 また高 のジイソプチレンは、 ォクチルフエノー イソノナン 酸などの機能化学製品の原料として有用な化合物である。
ブテ ^の二量体の ¾ ^を行う^、 ブテン類の一種を職で^ fflすることもできる が、 ブテン類の数種が 意の割合で混合された物を翻することもできる。 ブテ >mの 糸滅は、 その二量化物の用途およ ^求特性 （オクタン価指数など） に応じて調整する ことが好ましい。 また、 その要求特性を満足する範囲において、 他のォレフィン、 例え ばプロピレンならびに it 状、 分岐状およ 状のペンテン類、 へキセ： ^1、 ヘプテン 類等を含んでいても差し支えない。
ォレフィ 有原料の供緇原は、 特に制限はないが、 例えば F C Cプロセスで生産さ れるォレフィン留分、 ナフサクラッカーで生産される留分からジェン を抽出や 的水素化によって]^したォレフィン留分、 コ一力オフガス留分、 素 生成物な どが挙げられ またこれらを任意の割合で混合したものでも良い。 更にそれらに対し蒸 留などの の方法を用いて、 特定の留分の含有量を増減させて調整しても良い。 例え ば、 ナフサクラッカーで生 βΤΤる C 4留分からブタジエンを抽出したラフィネートゃ F C C— C 4留分を蒸留 （または反応蒸留） し、 カレマルブテン類およびノルマルブタン を除いたィソブチレンを髙 に含有するィソブチレンーィソブタン留分を用いること が きる。 これらの留分をブテン類の二量化反応に用いる:！^、 反応に を及ぼさな い程度であれば、 ブタジエン等の不純物が ^まれていても差し支えない。 また、 反応熱を する目的で、 溶媒を含むォレフィン含有 IT料を使用することが きる。 溶媒は、 二量化 as条件において液体であって、 固体リン に対して本質的 に不活性であれば何でもよい。 例えば、 n—パラフィン、 イソパラフィン、 ナフテン類、 芳香猴などの炭化水素を用いることができる。 上記ラフイネ一トゃ C 4留中のブタン等 の 口炭ィは素も溶媒として作用する。 溶媒の量としては、 ォレフィンと溶媒を含むォ レフィン含有 料の総量に占めるォレフィンの割合が、 1〜 7 0質量％、 好ましくは 1 0〜6 5質量％、 より好ましくは 1 5〜6 0質量％となる量である。 溶媒の量が多すぎ ると生産性が低下し、 少なすぎると P激効率が低くなる。 本発明においては、 固体リン M にォレフィ 有原料を液相で ¾ させることが 好ましい。 目では、 コーキングの発生により、 ォレフィン二量化反応の活性および二 量 #選択性が氐下し、 が短くなるおそれが ¾>るので好ましくない。 ォレフィンのニ量化反応に用いる反 および反応形式には特に制限はなぐ 槽型反 応 によるバッチ式、 セミバッチ式、 镜¾1式反応や、 固定床、 流動床、 移動床の流 通反 による遙镜颜式反応などを翻することが きる。 反応 は、 0〜3 0 0°C、 好ましくは 2 0〜2 0 0°Cである。 0°Cより βでは十分な反応藤が得られず、 3 0 0°Cより高温で « J反応が多くなるので好ましくない。 反応圧力は、 常圧〜 2 0M P a力 ましく、 低圧では反応系が液相を維持できなくなるおそれがあり、 高圧では設 備コストが増大するので好ましくない。 WHS V ( 1時間あたりの担体質量に対する供 給 I 料質 *) は、 0. l S O O h r—1 好ましくは 1〜1 5 O h r -1である。 WH S Vが小さいと 率が ぐ 大きいと反応が 行しないので好ましくない。 前記したようにリン酸中のオリレトリン酸の比率がリン原子 で 6 0モル％以上では オルトリン酸の縮合の進行が非常に綾 I曼となるが、 それでも反応条件によっては、 二量 化反応の進行とともに徐々に «中のオリレ卜リン酸の縮合力 することが、ある。
そこで儘中のオルトリン酸の縮合の進行を防止するために、 反応系中に水分を雜 させることが好ましい。 水分の供給方法としては特に制限はなぐ 混 置によってォ レフィ 有原料に所 の水を溶解させて反応 に供給する方法など力寧げられる。 ォレフイ^有]！1料中の水分量は、 1 0 ~ 1 0 0 0質量 p pm、 好ましくは 3 0〜5 0 0質量 p pm、 より好ましくは 5 0〜3 0 0質量 p pmである。
上記範囲よりも水; が少なレ驗は、 廳のリン酸中のオルトリン酸の比率が比較 的短時間で 6 0モル％未満となるので、 生髓カ犒くなり生産性が低下する。一 方、 水分量が多い齡は、 翻の水分 （特に原料液の 口水^ *を超える分の水） が触 媒中のリン酸を溶出させ、 そのため活性が低下するので好ましくない。 なお、 このよう に溶出により腿中のリン酸が減少した齢は、 脇系内 にリン酸を 加して ¾ϋ¾¾·Τることも可能である。 難例 1
逢藻土の押出し 品（1. 6mm(i) x 2mm) 1 2. 0 gを 1 0 Om 1ビーカーに 入った 31質量％リン^ K溶液 6 Om lに浸漬した。 1時間浸漬後、 メッシュフィ レタ —上で水藤を |5鉄し、 M 5° ¾ 50%の室内にて放置車 ^ii 作を 2時間行い、 固体リン m»SAを調製した。 漏某についてリン (31P)の固体核 法による 分析を行ったところ、 膽されたリン酸の糸賊 （リン原子騰のモル％、 以下同じ。 ) は、 オルトリン酸 8 5 %、 ピロリン酸 1 5 %で、 ポリリン酸は被していなかった。 ま た、 中和滴定の結果、 賺中のリン酸量は、 オルトリン酸騰で 20質量％であり、 触 媒のス洗によるリン酸^ ¾および ¾ ^の結果、 «中の担体の割合は 7 7. 5質量％で あった。 従ってリン酸担腿は 2 5. 8質量％となる。
固体リン翻嫌 Aの 2 gを管形ステンレス鋼反応器 (内径 8mm)に充填し、 反応器の 上部よりイソフ'チレン含有原料（イソブチレン 3 0質量％、 n-ブテン 5質量％、 n -へ キサン 6 5質量％、 水 2 5 0質量 111) を 40 gZh (WHS V= 2 6 h—り でフィ —ドし、 下部より反鎌を抜き出しながら二量化反応を 3 0日間薩して難した。 圧 力は 1.0MPa、 角顯の?渡は 8 0°Cとし、 液相 4え態を纖した。 反応結果を表 1に、 反 応腿の のリン酸の糸賊を表 3に示す。 難例 2
珪藻土の押出し 品（lmm<i x 2mm) 3. O gを、 管形ステンレス鋼反腿 (内 径 8 mm)に挿入した。 反応 下部より 3 1質量％リン^薩を、 全ての纏土が浸 漬される量だけ導入し、 1時間後に ϋΓ 下部よりリン 謹を ί鉄した。 次に、 反 雄上部より 2髓％の水分を含む ガスを室温 (2 5°C)、 1 LZHで 9 0分間フィ —ドして下部より排出し、 皐體作を行った。 反 から^ Mり出された固体リン酸 羅 Βについて、 難例 1と同様にして分析を行ったところ、 膽されたリン酸の誠 はオルトリン酸 8 7 %、 ピロリン酸 1 3 %で、 ポリリン酸は擁していなかった。 また。 中のリン (オルトリン^^) は、 1 9質*%、 «中の担体の割合は 7 7. 7質量％であり、 U iiif*½2 4. 4質量％となった。 なお、 反応 中に残った触 mm. 8 6 gとなった。
次に、 反応 の上部よりイソブチレ ^有原料 （イソブチレン 3 0質量％、 n-ブテ ン 5質量％、 11^\キサン6 5質訾ん 7K2 5 OM pm) を 4 0 g/h (WHS V= 2 8 h一1) でフィードし、 下部より反)^液を抜き出しながら二量化反応を 3 0日間 镜 して雄した。 圧力は 1. OMP a、 の髓は 8 0°Cとし、 液相; (え態を膽した。 反応結果を表 1に、 樹麦の ¾のリン酸の を表 3に示す。 難例 3
料«をイソブチレン 3 5質量％、 η~^\キサン 6 5質量％、 7Κ2 5 0質量 p pm とした以外は、 ^例 1と同様にして二量化反応を実施した。 反) iS 果を表 1に、
Figure imgf000011_0001
ン酸の誠を表 3に示す。 難例 4
原料組成をイソブチレン 8質量％、 n-ブテン 2 7質量％、 n-へキサン 6 5質量％、 7K2 5 OOTp pm, 圧力を 2. OMP a、 謹層の温度を 1 4 5 °Cとした以外は、 実 施例 1と同様にして二量化跡を鐘した。 結果を表 1に、 反編菱の ¾のリ ン酸の誠を表 3に示す。 謹例 5
原料賊を n—ブテン 3 5質量％、 n-へキサン 6 5質量％、 水 2 5 0質量 p pm、 圧 力を 2. OMP a、 « の温度を 1 4 5°Cとした以外は、 例 1と同様にして二量 化反応を «した。 果を表 1に、 ^の ^のリン酸の «を表 3に示す。 鎌例 6
珪藻土の押出し戲品（ΙπιιηΦ X 2mm) 3. 0 gを、 管形ステンレス鋼反 (内 径 8 mm)に挿入した。 反応 下部より 3 1質量％リン 謹を、 全ての珪藻土が浸 漬される量だけ導入し、 1時間後に反応 下部よりリン 霞を P鉄した。 次に、 反 応 上部より ガスを室温 (25。C)、 1L/Hで 60分間フィードして下部より 排出し、 車^^作を行った。 反膨から ~«り出された固体リン m»cについて、 難例 1と同様にして分析を行ったところ、 纖されたリン酸の糸滅〖*tルトリン酸 8 0%、 ピロリン酸 20%で、 ポリリン酸は旅していなかった。 また。賺中のリン酸 量 （オルトリン は 19質量％、 讓中の担体の割合は 78. 3質量％であり、 リン酸賺量は 24. 3質量％となった。 なお、 反応 中に残った は 1. 93g となった。
次に、 反 の上部より、 水を実質的に含まないイソブチレ 有 料（イソブチレ ン 30質量％、 n-ブテン 5質量％、 n-へキサン 65質量％) を 40g/h (WHSV = 26h-') でフィードし、 下部より抜き出しながら二量化反応を 30日間連镜して実 施した。 圧力は 1. 0MPa、 觸某層の は 80 °Cとし、 液相状態を纖した。 反応 結果を表 1に、 反応謝美の のリン酸の誠を表 3に示す。 難例 7
原料 をイソペンテン 20質量％、 n—ペンテン 20質量％、 シクロペンテン 10 質量％、 n ンタン 50質量％、 X25 OMppm, 圧力 2. OMPa、 Mの 温 を 145°Cとした以外は、 例 1と同様にして二量化反応を実施した。反応結果 を表 1に、 反応謝麦の^ hのリン^ を表 3に示す。 麵例 8
原料«をイソプチレン 20質量％、 n-ブテン 3質量％、 イソペンテン 7質量％、 n -ペンテン 10質量％、 n-へキサン 60質量％、 7j 25 OKMppm, 圧力 1. 5M Pa、 匪層の を120 とした は、 難例 1と同様にして二量化反応を ¾g した。 反応糸吉果を表 1に、 反 ϋδϋί麦の^:のリン を表 3に示す。
[比翻 1 ]
Figure imgf000012_0001
1 ot:の オーブン内 作を行った は^例 1 と同様の操作を行い、 固体リン を調製した。 匪について、 麵例 1と同様に して分析を行ったところ、 ,されたリン酸の «は才レ卜リン酸 57%、 ピロリン酸 3 8 %、 ポリリン酸 5 %であった。 また、 謹中のリン (オレトリン^^) は 2 0質量％、 «中の担体の割合は 8 0. 5質量％であり、 リン酸 TO量は 2 4. 8質 量％となった。 固体リン を用いて、 難例 1と同様にして二量化 を雄し た。 反応結果を表 2に、 前後の のリン酸の誠を表 4に示す。
[比湖 2]
リン^ K«P敍後に、 例 2と同様の方法で、 リン に浸潰して水溶液を
P鉄した iW ;に対し、 反応 上部より 2 0 0°Cの草 S S素ガスを 1 LZHで 1時間フ イードし Cf部より排出し)て車漏作を行つた は雄例 2と同様の操作を行つた。 反) ΐ器から取り出された固体リン翻蝶 Εについて、 «例 1と同様にして分析を行つ たところ、 攝されたリン酸の糸滅はオレトリン酸 2 5 %、 ピロリン酸 3 9 %、 ポリリ ン酸 3 6 %であった。 また、 賺中のリン隨 （オルトリン酸購） は 1 8質量％、 触 媒中の担体の割合は 8 3. 3質量％であり、 リン酸 量は 2 1. 6質量％となった。 次に、 反応 に残った 1. 8 gの匪を用いて難例 2と同様にして、 二量化反応を 鍾した。 結果を表 2に、 反麵轰の のリン酸の誠を表 4に示す。
[比翻 3]
原料糸賊をイソプチレン 3 5質量％、 n—へキサン 6 5質量％、 7 2 5 OMp pm とした は、 比翻 1と同様にして二量化跡を雄した。 脇結果を表 2に、 反応 謙の のリン酸の糸滅を表 4に示す。
[比較训
原料組成をイソプチレン 8質量％、 n-ブテン 2 7質量％、 n-へキサン 6 5質量％、 7K2 5 OM*p pm, 圧力を 2. O MP a、 の を 1 4 5T3とした は、 比 觀 1と同様にして二量化反応を魏した。 反 果を表 2に、 反編麦の のリ ン酸の繊を表 4に示す。 原料 «を11 -ブテン 35質量％、 n-へキサン 65質量％、 τΚ250®gp m, 圧 力を 2. 0MPa、 « の温度を 145°Cとした以外は、 比較例 2と同様にして二量 化反応を難した。 二量化生 勿が全く得られなかったため、 反応を 5時間で終了した。 反応結果を表 2に、 反歸の ¾ のリン酸の糸滅を表 4に示す。
Figure imgf000015_0001
表 2 反応 is果
比較例
1 2 3 4 5
5 時間 ォレフィ ン転 49 32 55 41 0 後 化率％
二 量 体 選 択 85 64 77 87 率％
二量体収率％ 42 20 42 36 0
30 曰 ォレフィ ン転 40 22 41 21 後 化率％
二 量 体 選 択 67 50 63 75 率％
.二量体収率％ 27 1 1 26 16 ——
'表 3
Figure imgf000016_0001
表 4 反応前後の触媒のリ ン酸組成（リ ン原子換算のモル％) 比較例
1 2 3 4 5 反 J心前 オルトリ ン酸 57 25 57 57 26 ピ口リ ン酸 38 39 38 38 40 ポリ リン酸 5 36 5 5 34
30 曰 オルトリ ン酸 42 13 35 45 .
後 ピ口リ ン酸 46 31 45 47
ポリ リン酸 12 56 20 8
産業上の利用可能性
本発明の固体リン ^^は、 ォレフィンの二量化 にも、 ォレフィンのフ j m¾¾や 芳麵匕合物のアルキル化 as等の Mを用いる各 応においても棚することが でさる。

Claims

請求の範囲
1. 担体にリン酸 水^^によりリン酸となるものを含む。 以下同じ。 ) を纖 して成り、 s ^されたリン酸中のオルトリン酸の比率がリン原子鍵で 6 0モル％以上 であることを とする固体リン^^。
2. 担体にリン^ K職を纖したのち難させて調製されたものであって、 その 調 S C程が 1 0 0°C未満であることを赚とする請求項 1に記載の固体リン^^。
3. 請求項 1または 2に記載の固体リン «に、 ォレフィ ^有原料を纖させ ることを とする才レフィンのニ量ィ匕方法。
4. 才レフィン含有原料中に水を 1 0〜； L 0 0 0質量 p pm含有 ることを と する請求項 3に記載の方法。
5. 固体リン自 に才レフィン含有原料を液ネ させることを,とする請 求項 3または 4に記載の方法。
6. ォレフィンが炭素数 3〜 7のモノォレフィンであることを!^とする請求項 3 〜 5のいずれかに記載の方法。
PCT/JP2005/013427 2004-07-16 2005-07-13 固体リン酸触媒およびそれを用いたオレフィンの二量化方法 WO2006009229A1 (ja)