WO2005113440A1 - Composition zéolitique d'aluminosilicate cristallin: uzm-15 - Google Patents
Composition zéolitique d'aluminosilicate cristallin: uzm-15 Download PDFInfo
- Publication number
- WO2005113440A1 WO2005113440A1 PCT/US2004/012153 US2004012153W WO2005113440A1 WO 2005113440 A1 WO2005113440 A1 WO 2005113440A1 US 2004012153 W US2004012153 W US 2004012153W WO 2005113440 A1 WO2005113440 A1 WO 2005113440A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- zeolite
- value
- uzm
- varies
- group
- Prior art date
Abstract
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/US2004/012153 WO2005113440A1 (fr) | 2004-04-20 | 2004-04-20 | Composition zéolitique d'aluminosilicate cristallin: uzm-15 |
JP2007509432A JP5027655B2 (ja) | 2004-04-20 | 2004-04-20 | 結晶性アルミノシリケートゼオライト質組成物:uzm−15 |
CN200480043384XA CN1972868B (zh) | 2004-04-20 | 2004-04-20 | 结晶铝硅酸盐沸石组合物:uzm-15 |
EP04750374A EP1742875A1 (fr) | 2004-04-20 | 2004-04-20 | Composition zéolitique d'aluminosilicate cristallin: uzm-15 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/US2004/012153 WO2005113440A1 (fr) | 2004-04-20 | 2004-04-20 | Composition zéolitique d'aluminosilicate cristallin: uzm-15 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2005113440A1 true WO2005113440A1 (fr) | 2005-12-01 |
Family
ID=34957944
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2004/012153 WO2005113440A1 (fr) | 2004-04-20 | 2004-04-20 | Composition zéolitique d'aluminosilicate cristallin: uzm-15 |
Country Status (4)
Country | Link |
---|---|
EP (1) | EP1742875A1 (fr) |
JP (1) | JP5027655B2 (fr) |
CN (1) | CN1972868B (fr) |
WO (1) | WO2005113440A1 (fr) |
Cited By (24)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7674941B2 (en) | 2004-04-16 | 2010-03-09 | Marathon Gtf Technology, Ltd. | Processes for converting gaseous alkanes to liquid hydrocarbons |
US7838708B2 (en) | 2001-06-20 | 2010-11-23 | Grt, Inc. | Hydrocarbon conversion process improvements |
US7847139B2 (en) | 2003-07-15 | 2010-12-07 | Grt, Inc. | Hydrocarbon synthesis |
US7880041B2 (en) | 2004-04-16 | 2011-02-01 | Marathon Gtf Technology, Ltd. | Process for converting gaseous alkanes to liquid hydrocarbons |
US7883568B2 (en) | 2006-02-03 | 2011-02-08 | Grt, Inc. | Separation of light gases from halogens |
US7964764B2 (en) | 2003-07-15 | 2011-06-21 | Grt, Inc. | Hydrocarbon synthesis |
US7998438B2 (en) | 2007-05-24 | 2011-08-16 | Grt, Inc. | Zone reactor incorporating reversible hydrogen halide capture and release |
US8008535B2 (en) | 2004-04-16 | 2011-08-30 | Marathon Gtf Technology, Ltd. | Process for converting gaseous alkanes to olefins and liquid hydrocarbons |
US8053616B2 (en) | 2006-02-03 | 2011-11-08 | Grt, Inc. | Continuous process for converting natural gas to liquid hydrocarbons |
US8173851B2 (en) | 2004-04-16 | 2012-05-08 | Marathon Gtf Technology, Ltd. | Processes for converting gaseous alkanes to liquid hydrocarbons |
US8198495B2 (en) | 2010-03-02 | 2012-06-12 | Marathon Gtf Technology, Ltd. | Processes and systems for the staged synthesis of alkyl bromides |
US8273929B2 (en) | 2008-07-18 | 2012-09-25 | Grt, Inc. | Continuous process for converting natural gas to liquid hydrocarbons |
US8282810B2 (en) | 2008-06-13 | 2012-10-09 | Marathon Gtf Technology, Ltd. | Bromine-based method and system for converting gaseous alkanes to liquid hydrocarbons using electrolysis for bromine recovery |
CN102811950A (zh) * | 2010-03-31 | 2012-12-05 | 环球油品公司 | Uzm-37硅铝酸盐沸石 |
US8367884B2 (en) | 2010-03-02 | 2013-02-05 | Marathon Gtf Technology, Ltd. | Processes and systems for the staged synthesis of alkyl bromides |
US8436220B2 (en) | 2011-06-10 | 2013-05-07 | Marathon Gtf Technology, Ltd. | Processes and systems for demethanization of brominated hydrocarbons |
RU2500619C2 (ru) * | 2008-09-30 | 2013-12-10 | Юоп Ллк | Алюмосиликатный цеолит uzm-35, способ его получения и применения |
US8642822B2 (en) | 2004-04-16 | 2014-02-04 | Marathon Gtf Technology, Ltd. | Processes for converting gaseous alkanes to liquid hydrocarbons using microchannel reactor |
US8802908B2 (en) | 2011-10-21 | 2014-08-12 | Marathon Gtf Technology, Ltd. | Processes and systems for separate, parallel methane and higher alkanes' bromination |
US8815050B2 (en) | 2011-03-22 | 2014-08-26 | Marathon Gtf Technology, Ltd. | Processes and systems for drying liquid bromine |
US8829256B2 (en) | 2011-06-30 | 2014-09-09 | Gtc Technology Us, Llc | Processes and systems for fractionation of brominated hydrocarbons in the conversion of natural gas to liquid hydrocarbons |
US9193641B2 (en) | 2011-12-16 | 2015-11-24 | Gtc Technology Us, Llc | Processes and systems for conversion of alkyl bromides to higher molecular weight hydrocarbons in circulating catalyst reactor-regenerator systems |
US9206093B2 (en) | 2004-04-16 | 2015-12-08 | Gtc Technology Us, Llc | Process for converting gaseous alkanes to liquid hydrocarbons |
US11918973B1 (en) | 2022-08-22 | 2024-03-05 | Sinanen Zeomic Co., Ltd. | Heavy metal adsorbent, water purification material, and method of manufacturing heavy metal adsorbent |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7687423B2 (en) * | 2008-06-26 | 2010-03-30 | Uop Llc | Selective catalyst for aromatics conversion |
US7985886B1 (en) * | 2010-03-31 | 2011-07-26 | Uop Llc | Aromatic alkylation process using UZM-37 aluminosilicate zeolite |
JP5613694B2 (ja) * | 2012-01-19 | 2014-10-29 | ユーオーピー エルエルシー | 結晶性アルミノシリケートゼオライト質組成物:uzm−15 |
WO2014003909A1 (fr) * | 2012-06-29 | 2014-01-03 | Uop Llc | Tamis moléculaires de métallophosphate, procédé de préparation et utilisation |
US8618343B1 (en) * | 2012-12-12 | 2013-12-31 | Uop Llc | Aromatic transalkylation using UZM-39 aluminosilicate zeolite |
US11278874B2 (en) * | 2018-11-30 | 2022-03-22 | Johnson Matthey Public Limited Company | Enhanced introduction of extra-framework metal into aluminosilicate zeolites |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4209498A (en) * | 1976-11-05 | 1980-06-24 | Imperial Chemical Industries Limited | Silica-containing material FU-1 |
US4495303A (en) * | 1983-11-29 | 1985-01-22 | Mobil Oil Corporation | Process for making zeolite ZSM-45 with a dimethyldiethylammonium directing agent |
US5000932A (en) * | 1986-10-24 | 1991-03-19 | Exxon Research And Engineering Company | Mazzite-type zeolite, ECR-15, and a process for preparing it |
US6419895B1 (en) * | 2000-11-03 | 2002-07-16 | Uop Llc | Crystalline aluminosilicate zeolitic composition: UZM-4 |
US6613302B1 (en) * | 2000-11-03 | 2003-09-02 | Uop Llc | UZM-5, UZM-5P and UZM-6: crystalline aluminosilicate zeolites and processes using the same |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1079780C (zh) * | 1996-06-28 | 2002-02-27 | 太原工业大学 | 一种y型沸石的制备方法 |
-
2004
- 2004-04-20 JP JP2007509432A patent/JP5027655B2/ja not_active Expired - Fee Related
- 2004-04-20 WO PCT/US2004/012153 patent/WO2005113440A1/fr active Application Filing
- 2004-04-20 CN CN200480043384XA patent/CN1972868B/zh not_active Expired - Fee Related
- 2004-04-20 EP EP04750374A patent/EP1742875A1/fr not_active Withdrawn
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4209498A (en) * | 1976-11-05 | 1980-06-24 | Imperial Chemical Industries Limited | Silica-containing material FU-1 |
US4495303A (en) * | 1983-11-29 | 1985-01-22 | Mobil Oil Corporation | Process for making zeolite ZSM-45 with a dimethyldiethylammonium directing agent |
US5000932A (en) * | 1986-10-24 | 1991-03-19 | Exxon Research And Engineering Company | Mazzite-type zeolite, ECR-15, and a process for preparing it |
US6419895B1 (en) * | 2000-11-03 | 2002-07-16 | Uop Llc | Crystalline aluminosilicate zeolitic composition: UZM-4 |
US6613302B1 (en) * | 2000-11-03 | 2003-09-02 | Uop Llc | UZM-5, UZM-5P and UZM-6: crystalline aluminosilicate zeolites and processes using the same |
Cited By (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7838708B2 (en) | 2001-06-20 | 2010-11-23 | Grt, Inc. | Hydrocarbon conversion process improvements |
US8415512B2 (en) | 2001-06-20 | 2013-04-09 | Grt, Inc. | Hydrocarbon conversion process improvements |
US7847139B2 (en) | 2003-07-15 | 2010-12-07 | Grt, Inc. | Hydrocarbon synthesis |
US7964764B2 (en) | 2003-07-15 | 2011-06-21 | Grt, Inc. | Hydrocarbon synthesis |
US8232441B2 (en) | 2004-04-16 | 2012-07-31 | Marathon Gtf Technology, Ltd. | Process for converting gaseous alkanes to liquid hydrocarbons |
US7880041B2 (en) | 2004-04-16 | 2011-02-01 | Marathon Gtf Technology, Ltd. | Process for converting gaseous alkanes to liquid hydrocarbons |
US9206093B2 (en) | 2004-04-16 | 2015-12-08 | Gtc Technology Us, Llc | Process for converting gaseous alkanes to liquid hydrocarbons |
US8008535B2 (en) | 2004-04-16 | 2011-08-30 | Marathon Gtf Technology, Ltd. | Process for converting gaseous alkanes to olefins and liquid hydrocarbons |
US8642822B2 (en) | 2004-04-16 | 2014-02-04 | Marathon Gtf Technology, Ltd. | Processes for converting gaseous alkanes to liquid hydrocarbons using microchannel reactor |
US8173851B2 (en) | 2004-04-16 | 2012-05-08 | Marathon Gtf Technology, Ltd. | Processes for converting gaseous alkanes to liquid hydrocarbons |
US7674941B2 (en) | 2004-04-16 | 2010-03-09 | Marathon Gtf Technology, Ltd. | Processes for converting gaseous alkanes to liquid hydrocarbons |
US8053616B2 (en) | 2006-02-03 | 2011-11-08 | Grt, Inc. | Continuous process for converting natural gas to liquid hydrocarbons |
US7883568B2 (en) | 2006-02-03 | 2011-02-08 | Grt, Inc. | Separation of light gases from halogens |
US8921625B2 (en) | 2007-02-05 | 2014-12-30 | Reaction35, LLC | Continuous process for converting natural gas to liquid hydrocarbons |
US7998438B2 (en) | 2007-05-24 | 2011-08-16 | Grt, Inc. | Zone reactor incorporating reversible hydrogen halide capture and release |
US8282810B2 (en) | 2008-06-13 | 2012-10-09 | Marathon Gtf Technology, Ltd. | Bromine-based method and system for converting gaseous alkanes to liquid hydrocarbons using electrolysis for bromine recovery |
US8273929B2 (en) | 2008-07-18 | 2012-09-25 | Grt, Inc. | Continuous process for converting natural gas to liquid hydrocarbons |
US8415517B2 (en) | 2008-07-18 | 2013-04-09 | Grt, Inc. | Continuous process for converting natural gas to liquid hydrocarbons |
RU2500619C2 (ru) * | 2008-09-30 | 2013-12-10 | Юоп Ллк | Алюмосиликатный цеолит uzm-35, способ его получения и применения |
US8198495B2 (en) | 2010-03-02 | 2012-06-12 | Marathon Gtf Technology, Ltd. | Processes and systems for the staged synthesis of alkyl bromides |
US8367884B2 (en) | 2010-03-02 | 2013-02-05 | Marathon Gtf Technology, Ltd. | Processes and systems for the staged synthesis of alkyl bromides |
US9133078B2 (en) | 2010-03-02 | 2015-09-15 | Gtc Technology Us, Llc | Processes and systems for the staged synthesis of alkyl bromides |
CN102811950A (zh) * | 2010-03-31 | 2012-12-05 | 环球油品公司 | Uzm-37硅铝酸盐沸石 |
CN102811950B (zh) * | 2010-03-31 | 2015-01-07 | 环球油品公司 | Uzm-37硅铝酸盐沸石 |
US8815050B2 (en) | 2011-03-22 | 2014-08-26 | Marathon Gtf Technology, Ltd. | Processes and systems for drying liquid bromine |
US8436220B2 (en) | 2011-06-10 | 2013-05-07 | Marathon Gtf Technology, Ltd. | Processes and systems for demethanization of brominated hydrocarbons |
US8829256B2 (en) | 2011-06-30 | 2014-09-09 | Gtc Technology Us, Llc | Processes and systems for fractionation of brominated hydrocarbons in the conversion of natural gas to liquid hydrocarbons |
US8802908B2 (en) | 2011-10-21 | 2014-08-12 | Marathon Gtf Technology, Ltd. | Processes and systems for separate, parallel methane and higher alkanes' bromination |
US9193641B2 (en) | 2011-12-16 | 2015-11-24 | Gtc Technology Us, Llc | Processes and systems for conversion of alkyl bromides to higher molecular weight hydrocarbons in circulating catalyst reactor-regenerator systems |
US11918973B1 (en) | 2022-08-22 | 2024-03-05 | Sinanen Zeomic Co., Ltd. | Heavy metal adsorbent, water purification material, and method of manufacturing heavy metal adsorbent |
Also Published As
Publication number | Publication date |
---|---|
JP2007533587A (ja) | 2007-11-22 |
CN1972868A (zh) | 2007-05-30 |
JP5027655B2 (ja) | 2012-09-19 |
CN1972868B (zh) | 2010-04-21 |
EP1742875A1 (fr) | 2007-01-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2005113440A1 (fr) | Composition zéolitique d'aluminosilicate cristallin: uzm-15 | |
US7713513B2 (en) | High silica zeolites: UZM-8HS | |
US6890511B2 (en) | Crystalline aluminosilicate zeolitic composition: UZM-15 | |
EP1756004B1 (fr) | Zeolites uzm-5hs a forte teneur en silice | |
KR101617564B1 (ko) | Uzm-39 알루미노실리케이트 제올라이트 | |
KR100958149B1 (ko) | Uzm-8 및 uzm-8hs 결정질 알루미노실리케이트제올라이트 조성물 및 이 조성물을 이용하는 방법 | |
US7344694B2 (en) | UZM-12 and UZM-12HS: crystalline aluminosilicate zeolitic compositions and processes for preparing and using the compositions | |
WO2004039725A2 (fr) | Composition zeolitique d'aluminosilicate cristalline uzm-4m | |
WO2003068679A1 (fr) | Composition cristalline zéolitique d'aluminosilicate: uzm-9 | |
WO2010074889A2 (fr) | Famille de compositions d'aluminosilicates cristallins uzm-26, procédé de préparation et procédés d'utilisation de ces compositions | |
US6982074B2 (en) | High silica zeolites: UZM-5HS | |
US20040182744A1 (en) | High silica zeolites: UZM-8HS | |
US6752980B1 (en) | UZM-16: a crystalline aluminosilicate zeolitic material | |
US8268290B2 (en) | UZM-29 family of crystalline zeolitic compositions and a method of preparing the compositions | |
WO2013096072A2 (fr) | Synthèse de zéolites par conversion en couches | |
JP5118482B2 (ja) | Uzm−16:結晶性アルミノシリケートゼオライト質材料 | |
US8017824B2 (en) | Hydrocarbon conversion processes using UZM-29 and UZM-29HS crystalline zeolitic compositions | |
JP5613694B2 (ja) | 結晶性アルミノシリケートゼオライト質組成物:uzm−15 | |
RU2340555C2 (ru) | Кристаллическая алюмосиликатная цеолитная композиция uzm-15 | |
JP5646366B2 (ja) | Uzm−16:結晶性アルミノシリケートゼオライト質材料 | |
EP2462060A2 (fr) | Famille uzm-29 de compositions zéolithiques cristallines et procédé de préparation des compositions | |
RU2340552C2 (ru) | Uzm-16: кристаллический алюмосиликатный цеолитный материал |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): BW GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
DPEN | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed from 20040101) | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2007509432 Country of ref document: JP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWW | Wipo information: withdrawn in national office |
Country of ref document: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2004750374 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2006140799 Country of ref document: RU |
|
WWE | Wipo information: entry into national phase |
Ref document number: 200480043384.X Country of ref document: CN |
|
WWP | Wipo information: published in national office |
Ref document number: 2004750374 Country of ref document: EP |