WO2005095691A1 - 織布およびその織布加工品 - Google Patents
織布およびその織布加工品 Download PDFInfo
- Publication number
- WO2005095691A1 WO2005095691A1 PCT/JP2005/006430 JP2005006430W WO2005095691A1 WO 2005095691 A1 WO2005095691 A1 WO 2005095691A1 JP 2005006430 W JP2005006430 W JP 2005006430W WO 2005095691 A1 WO2005095691 A1 WO 2005095691A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- woven fabric
- sheath
- thermoplastic resin
- component
- melting point
- Prior art date
Abstract
Description
Claims