WO2005081915A2 - Appareil et procede de fabrication d'un film pouvant etre utilise pour appliquer du vernis et de la couleur sur un objet - Google Patents
Appareil et procede de fabrication d'un film pouvant etre utilise pour appliquer du vernis et de la couleur sur un objet Download PDFInfo
- Publication number
- WO2005081915A2 WO2005081915A2 PCT/US2005/005522 US2005005522W WO2005081915A2 WO 2005081915 A2 WO2005081915 A2 WO 2005081915A2 US 2005005522 W US2005005522 W US 2005005522W WO 2005081915 A2 WO2005081915 A2 WO 2005081915A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- varnish
- layer
- coating roller
- onto
- Prior art date
Abstract
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/US2005/005522 WO2005081915A2 (fr) | 2004-02-23 | 2005-02-22 | Appareil et procede de fabrication d'un film pouvant etre utilise pour appliquer du vernis et de la couleur sur un objet |
CNA2005800127730A CN1946571A (zh) | 2004-02-23 | 2005-02-22 | 用于制造施用清漆和颜料到物体上的膜的设备和方法 |
EP05713901A EP1732769A4 (fr) | 2004-02-23 | 2005-02-22 | Appareil et procede de fabrication d'un film pouvant etre utilise pour appliquer du vernis et de la couleur sur un objet |
EP05005641A EP1619022A1 (fr) | 2004-02-23 | 2005-03-15 | Procédé de fabrication d'un film qui peut être employé pour appliquer un vernis et une couleur sur un objet |
EP05005644A EP1618967A1 (fr) | 2004-02-23 | 2005-03-15 | Appareil pour appliquer un vernis sur un film |
EP05005642A EP1618966A1 (fr) | 2004-02-23 | 2005-03-15 | Appareil pour fabriquer un film qui peut être employé pour appliquer un vernis et une couleur sur un objet |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US54673604P | 2004-02-23 | 2004-02-23 | |
US60/546,736 | 2004-02-23 | ||
PCT/US2005/005522 WO2005081915A2 (fr) | 2004-02-23 | 2005-02-22 | Appareil et procede de fabrication d'un film pouvant etre utilise pour appliquer du vernis et de la couleur sur un objet |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2005081915A2 true WO2005081915A2 (fr) | 2005-09-09 |
WO2005081915A3 WO2005081915A3 (fr) | 2006-04-06 |
Family
ID=38812821
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2005/005522 WO2005081915A2 (fr) | 2004-02-23 | 2005-02-22 | Appareil et procede de fabrication d'un film pouvant etre utilise pour appliquer du vernis et de la couleur sur un objet |
Country Status (3)
Country | Link |
---|---|
EP (1) | EP1732769A4 (fr) |
CN (1) | CN1946571A (fr) |
WO (1) | WO2005081915A2 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2014150116A1 (fr) * | 2013-03-15 | 2014-09-25 | Illinois Tool Works Inc. | Feuilles de transfert utilisant un traitement par plasma pour remplacer la couche de décollement |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102555415B (zh) * | 2011-12-30 | 2014-08-06 | 西安交通大学 | 一种机床测量用光栅尺保护膜的涂覆方法 |
US20200064520A1 (en) * | 2018-08-22 | 2020-02-27 | GM Global Technology Operations LLC | Smart multifunctional lens coatings |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0573676A1 (fr) | 1992-05-19 | 1993-12-15 | General Electric Plastics B.V. | Utilisation d'une bande de support ayant des propriétés de décollage pour l'application de laque et de teinture sur un substrat |
EP1053793A1 (fr) | 1999-05-17 | 2000-11-22 | Argotec Lacksysteme GmbH | Procédé pour l'application d' une peinture et d'un décor sur un objet et procédé et dispositif pour appliquer une peinture, un décor et un adhésif sur un film |
Family Cites Families (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4352706A (en) * | 1981-08-31 | 1982-10-05 | Miller Lee H | Process for applying a metallic image in register to a document of value |
ES2036071T3 (es) * | 1990-05-08 | 1993-05-01 | Polytrend Gesellschaft Fur Polymere Werkstoffe & Oberflachentechnik Mbh | Procedimiento y dispositivo para la transferencia de un dibujo de colores sobre un substrato de plastico o un substrato de plastico decorado. |
DE4404128A1 (de) * | 1993-02-19 | 1994-08-25 | Gao Ges Automation Org | Sicherheitsdokument und Verfahren zu seiner Herstellung |
DE4421559C2 (de) * | 1994-06-20 | 1998-05-20 | Osmetric Entwicklungs Und Prod | Verfahren zum Herstellen einer Beschichtung, die eine Struktur aufweist, auf einem Substrat sowie Beschichtung |
US6277229B1 (en) * | 1995-08-25 | 2001-08-21 | Avery Dennison Corporation | Image transfer sheets and a method of manufacturing the same |
GB9702064D0 (en) * | 1997-01-31 | 1997-03-19 | De La Rue Holographics Ltd | Manufacture of security tapes and security threads |
EP0993876B1 (fr) * | 1998-10-13 | 2004-03-03 | Bush Industries, Inc. | Procédé d'application d'un décor coloré sur un substrat |
ES2213247T3 (es) * | 1998-10-13 | 2004-08-16 | Bush Industries, Inc. | Procedimiento para la decoracion de color de un objeto. |
-
2005
- 2005-02-22 EP EP05713901A patent/EP1732769A4/fr not_active Withdrawn
- 2005-02-22 CN CNA2005800127730A patent/CN1946571A/zh active Pending
- 2005-02-22 WO PCT/US2005/005522 patent/WO2005081915A2/fr active Application Filing
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0573676A1 (fr) | 1992-05-19 | 1993-12-15 | General Electric Plastics B.V. | Utilisation d'une bande de support ayant des propriétés de décollage pour l'application de laque et de teinture sur un substrat |
EP1053793A1 (fr) | 1999-05-17 | 2000-11-22 | Argotec Lacksysteme GmbH | Procédé pour l'application d' une peinture et d'un décor sur un objet et procédé et dispositif pour appliquer une peinture, un décor et un adhésif sur un film |
Non-Patent Citations (1)
Title |
---|
See also references of EP1732769A4 |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2014150116A1 (fr) * | 2013-03-15 | 2014-09-25 | Illinois Tool Works Inc. | Feuilles de transfert utilisant un traitement par plasma pour remplacer la couche de décollement |
Also Published As
Publication number | Publication date |
---|---|
CN1946571A (zh) | 2007-04-11 |
WO2005081915A3 (fr) | 2006-04-06 |
EP1732769A2 (fr) | 2006-12-20 |
EP1732769A4 (fr) | 2009-07-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP7113853B2 (ja) | オブジェクトの装飾のための装置および方法 | |
CN107531042B (zh) | 用于施用箔的方法、施用设备和印刷设备 | |
US10807357B2 (en) | Method and apparatus for cold-stamping onto three-dimensional objects | |
EP0993963B1 (fr) | Procédé d'impression en continu d'un film plastique, dispositif pour sa mise en oeuvre et film plastique imprimé obtenu par le procédé | |
US5645639A (en) | Apparatus for applying a protective finish to a web | |
US8501316B2 (en) | Process for printing wax release layer | |
EP0428628A1 (fr) | Unite d'impression laminaire de rev tement de substrats plats | |
EP1732769A2 (fr) | Appareil et procede de fabrication d'un film pouvant etre utilise pour appliquer du vernis et de la couleur sur un objet | |
EP0604075A2 (fr) | Production d'un substrat avec revêtement dur | |
EP1827800A2 (fr) | Articles decores | |
JPS6232626Y2 (fr) | ||
EP1618967A1 (fr) | Appareil pour appliquer un vernis sur un film | |
EP1618966A1 (fr) | Appareil pour fabriquer un film qui peut être employé pour appliquer un vernis et une couleur sur un objet | |
KR102142428B1 (ko) | 무한 확장 가능한 경계 라인을 구비한 프로텍트 시트지 구조 시스템 | |
JP2010099969A (ja) | 転写箔の製造方法 | |
JP2521202B2 (ja) | 印刷物の光沢加工装置 | |
US20100038021A1 (en) | Device and method for applying decoration, which adheres to a film, to a multidimentional object | |
JPH054920B2 (fr) | ||
JP2004017305A (ja) | フィルム転写方式による表面加工方法及びフィルム転写表面加工印刷物 | |
JPH1191298A (ja) | 曲面転写方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2005713901 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 200580012773.0 Country of ref document: CN |
|
WWP | Wipo information: published in national office |
Ref document number: 2005713901 Country of ref document: EP |