WO2005080622A1 - Cr-al-steel for high-temperature applications - Google Patents
Cr-al-steel for high-temperature applications Download PDFInfo
- Publication number
- WO2005080622A1 WO2005080622A1 PCT/SE2005/000249 SE2005000249W WO2005080622A1 WO 2005080622 A1 WO2005080622 A1 WO 2005080622A1 SE 2005000249 W SE2005000249 W SE 2005000249W WO 2005080622 A1 WO2005080622 A1 WO 2005080622A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alloy
- applications
- ferritic steel
- alloy according
- steel alloy
- Prior art date
Abstract
Description
Claims