WO2005038878A2 - Developer-soluble materials and methods of using the same in via-first dual damascene applications - Google Patents
Developer-soluble materials and methods of using the same in via-first dual damascene applications Download PDFInfo
- Publication number
- WO2005038878A2 WO2005038878A2 PCT/US2004/034495 US2004034495W WO2005038878A2 WO 2005038878 A2 WO2005038878 A2 WO 2005038878A2 US 2004034495 W US2004034495 W US 2004034495W WO 2005038878 A2 WO2005038878 A2 WO 2005038878A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- layer
- group
- substrate
- polymer
- Prior art date
Abstract
Description
Claims