WO2005021245A1 - レーザー溶着方法 - Google Patents
レーザー溶着方法 Download PDFInfo
- Publication number
- WO2005021245A1 WO2005021245A1 PCT/JP2004/011732 JP2004011732W WO2005021245A1 WO 2005021245 A1 WO2005021245 A1 WO 2005021245A1 JP 2004011732 W JP2004011732 W JP 2004011732W WO 2005021245 A1 WO2005021245 A1 WO 2005021245A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- laser
- laser light
- resin
- resin member
- white
- Prior art date
Abstract
Description
Claims