DESCRIPTION SILICA GLASS CONTAINING Ti02 AND OPTICAL MATERIAL FOR EUV
LITHOGRAPHY TECHNICAL FIELD The present invention relates to a silica glass containing Ti02 (hereinafter referred to as Ti02-Si02 glass) and a process for its production. Particularly, it relates to Ti02-Si02 glass to be used for an optical material for an exposure device to be used for EUV lithography and a process for its production. In the present invention, EUV (Extreme Ultra Violet) light means light having a waveband in a soft X-ray region or in a vacuum ultraviolet region and specifically means light having a wavelength of from 0.2 to 100 nm. BACKGROUND ART
Heretofore, in photolithography, it is common to employ an exposure device to transfer a fine circuit pattern onto a wafer to produce an integrated circuit . Along with high integration and high functionality of integrated circuits, microsizing of integrated circuit has been progressing, and an exposure device is required to form an image of a circuit pattern on a wafer with a high resolution in a deep focal depth, whereby blue shift of the exposure light source is in progress. The exposure light source has been advanced from the conventional g-line (wavelength: 436 nm) , i-line (wavelength: 365 nm) or KrF excimer laser (wavelength:
248 nm) , and now an ArF excimer laser (wavelength: 193 nm) is being used. Further, in order to be prepared for an integrated circuit for the next generation where the line width of a circuit pattern will be less than 100 nm, it is considered to be prospective to employ a F2 laser (wavelength: 157 nm) as the exposure light source, but it is considered that even this can not cover beyond a generation of a line width of 70 nm.
Under these circumstances, a lithographic technique employing typically a light having a wavelength of 13 nm among EUV light (extreme ultraviolet light) as the exposure light source, has attracted attention, as it may be applied to the printing of feature sizes of 50 nm and smaller. The image-forming principle of the EUV lithography (hereinafter referred to as "EUVL") is the same as the conventional photolithography to such an extent that a mask pattern is transferred by means of an optical projection system. However, in the energy region of EUV light, there is no material to let the light pass therethrough. Accordingly, a refraction optical system can not be used, and an optical system will be required to be a reflection optical system in all cases.
The optical material for the exposure device to be used for EUVL will be a photomask, a mirror or the like, and it is basically constituted of (1) a base material, (2) a reflective multilayer formed on the base material and (3) an absorber layer formed on the reflective
multilayer. For the multilayer, it is studied to form layers of Mo/Si alternately, and for the absorber layer, it is studied to use Ta or Cr as the layer-forming material. As the base material, a material having a low thermal expansion coefficient is required so that no strain will be formed even under irradiation with EUV light, and a glass having a low thermal expansion coefficient is being studied.
Ti02-Si02 glass is known to be a very low thermal expansion material having a coefficient of thermal expansion (CTE) smaller than quartz glass, and the coefficient of thermal expansion can be controlled by the Ti02 content in the glass, whereby it is possible to obtain a zero expansion glass having a coefficient of thermal expansion being close to zero. Accordingly,
Ti02-Si02 glass is prospective as a material to be used for an optical material for the exposure device for EUVL .
In a conventional method for preparing Ti02-Si02 glass, firstly, a silica precursor and a titania precursor are, respectively, converted into a vapor form, and then mixed. Such a vapor form mixture is feeded into a burner and thermally decomposed to form Ti02-Si02 glass particles. Such Ti02-Si02 glass particles will be deposited in a refractory container and at the same time will be melted to form Ti02-Si02 glass. However, Ti02- Si02 glass prepared by this method has had a periodical fluctuation of the Ti02/Si02 ratio, which appears as
striped striae with a 100 to 200 μm pitch.
Further, U.S. Patent application publication No. 2002/157421 discloses a method which comprises forming a Ti02-Si02 porous glass body, converting it to a glass body, and then obtaining a mask substrate therefrom. The striped striae of the Ti02-Si02 glass are considered to form as the difference in the refractive index increases due to the periodical fluctuation of the Ti02/Si02 ratio in the glass material. When it is to be used as an optical material for the exposure device for EVUL, the Ti02-Si02 glass is required to be polished so that the glass will have an ultra, smooth surface. However, in the Ti02-Si02 glass, at the portion where the Ti02/Si02 compositional ratio is different, the mechanical and chemical properties of the glass vary depending upon the composition, whereby the polishing rate tends to be non-uniform, and it is difficult to finish so that the glass surface after polishing will be ultra smooth. Further, if a Ti02-Si02 glass having striped striae with a 100 to 200 μm pitch, is polished,
"waving" will be formed on the glass surface with a pitch of the same degree as the striae pitch, whereby it is very difficult to obtain ultra smooth surface.
In recent years, it has been pointed out that it is necessary to reduce MSFR (Mid-Spatial Frequency
Roughness) having a waving pitch of from 10 μm to 1 mm, as an extremely important characteristic required for an
optical material for the exposure device for EUVL. When a conventional Ti02-Si02 glass is polished, it has a waving with a 100 to 200 μm pitch for the above-mentioned reason, whereby it has been very difficult to reduce MSFR.
Accordingly, in order to finish so that the glass surface after polishing will be ultra smooth, as an optical material for the exposure device for EUVL, it is considered effective to minimize the fluctuation of the Ti02/Si02 ratio of the Ti02-Si02 glass to make the polishing rate constant at the glass surface, and to reduce the striae pitch to a level of at most 10 μm to reduce MSFR.
Further, even with a Ti0-Si02 glass substrate having the same level of smoothness (Roughness (rms)), rough surface of a glass whose striae pitch is smaller can be polished efficiently in a short time, and can be finished to be ultra smooth easily.
Further, it is important to make the Ti02/Si02 ratio uniform in the Ti02-Si02 glass, with a view to minimizing the fluctuation of the coefficient of thermal expansion within the glass. Accordingly, in addition to minimizing the fluctuation of the Ti02/Si02 ratio in the small areas so-called striae, it is preferred to minimize the fluctuation of the Ti02/Si02 ratio in the entire region of the material .
DISCLOSURE OF THE INVENTION
Embodiment 1 of the present invention provides a silica glass containing Ti02, characterized in that the fluctuation of the refractive index (Δn) is at most 2xl0~4 within an area of 30 mm x 30 mm in at least one plane .
Embodiment 2 provides the silica glass containing Ti02 according to Embodiment 1, wherein the fluctuation of the refractive index (Δn) is at most 2xl0~4 within an area of 30 mm x 30 mm in each of two orthogonal planes.
Embodiment 3 provides a silica glass containing Ti02, characterized in that the Ti02 concentration is at least 1 mass%, and the difference between the maximum value and the minimum value of the Ti02 concentration is at most 0.06 masε% within an area of 30 mm x 30 mm in at least one plane .
Embodiment 4 provides the silica glass containing Ti02 according to Embodiment 3, wherein the difference between the maximum value and the minimum value of the Ti02 concentration is at most 0.06 mass% within an area of 30 mm x 30 mm in each of two orthogonal planes.
Embodiment 5 provides a silica glass containing Ti02, characterized in that the Ti02 concentration is at least 1 mass%, and the striae pitch is at most 10 μm. Embodiment 6 provides the silica glass containing Ti02 according to Embodiment 1 , 2 , 3 or 4 , wherein the striae pitch is at most 10 μm.
Embodiment 7 provides an optical material for EUV lithography, characterized in that it is made of a silica glass containing Ti02 and the fluctuation of the refractive index (Δn) is at most 2xl0~4 in a plane perpendicular to the incident light direction.
Embodiment 8 provides the optical material for EUV lithography according to Embodiment 7, wherein there is no striae which cause a fluctuation of the refractive index (Δn) exceeding 2xl0~4 in a plane perpendicular to the incident light direction.
Embodiment 9 provides an optical material for EUV lithography, characterized in that it is made of a silica glass containing Ti02, wherein the Ti02 concentration is at least 1 mass%, and the difference between the maximum value and the minimum value of the Ti02 concentration is at most 0.06 mass% in a plane perpendicular to the incident light direction.
Embodiment 10 provides the optical material for EUV lithography according to Embodiment 9, wherein there is no striae which cause a difference between the maximum value and the minimum value of the Ti02 concentration, exceeding 0.06 mass% in a plane perpendicular to the incident light direction.
Embodiment 11 provides the optical material for EUV lithography according to any one of Embodiments 6 to 10, wherein the striae pitch is at most 10 μm.
Embodiment 12 provides an optical material for EUV
lithography employing the silica glass containing Ti02, as defined in any one of Embodiments 1 to 6.
According to the present invention, it is possible to obtain Ti02-Si02 glass having a small surface roughness . Accordingly, it is very useful as a material for a component constituting an optical system to be used for EUVL. BEST MODE FOR CARRYING OUT THE INVENTION
Ti02-Si02 glass is known to have a coefficient of thermal expansion which changes depending upon the concentration of Ti02 contained, and the coefficient of thermal expansion of Ti02-Si02 glass containing about 7 mass% of Ti02 becomes substantially zero at near room temperature . The Ti02-Si02 glass of the present invention is preferably a silica glass containing from 1 to 12 mass% of Ti02. If the content of Tiθ2 is less than 1%, zero expansion may not be accomplished, and if it exceeds 12 mass%, the coefficient of thermal expansion is likely to be negative. The content of Ti02 is more preferably from 5 to 9 mass%.
The striae pitch is preferably at most 10 μm, more preferably at most 7 μm. If the striae pitch exceeds 10 μm, it tends to be difficult to reduce MSFR of the polished surface. In this specification, "the fluctuation of the Ti02 concentration" is defined to be the difference between the maximum value and the minimum
value of the Ti02 concentration in one plane. The fluctuation of the Ti02 concentration in each area of 30 mm x 30 mm, that is small area, is preferably at most 0.06 mass%, more preferably at most 0.04 mass%. If the fluctuation of the Ti02 concentration exceeds 0.06 mass%, it tends to be difficult to obtain an adequate smoothness by polishing. A process for producing a Ti02-Si02 glass having the fluctuation of the Ti0 concentration controlled to be within 0.06 mass%, is as follows. Ti02- Si02 glass particles (soot) obtained by flame hydrolysis or thermal decomposition of a Si precursor and a Ti precursor as glass-forming materials, by a soot process, are deposited and grown on a target to obtain a porous Ti02-Si02 glass body, and the obtained porous Ti02-Si02 glass body is heated to a vitrification temperature to obtain a verified Tiθ2-Si0 glass body. The target made of quartz glass may, for example, be used for this process .
The present inventors have investigated the relationship between the rotational speed of the target in the step of obtaining the porous Ti02-Si02 glass body and the striae pitch of the obtained Tiθ2-Siθ2 glass body in detail. As a result, they have found that as the rotational speed of the target becomes high, the fluctuation of the Ti02 concentration in the Ti02-Si02 glass body becomes small, and the striae pitch is reduced.
Specifically, a rotational speed of the target at the step of obtaining the porous Tiθ2-Si02 glass body is preferably adjusted to be at least 25 rpm, more preferably at least 50 rpm, particularly preferably at least 100 rpm. The fluctuation of the Ti02 concentration in the Ti02-Si02 glass body will be at most 0.06 mass%, and the striae pitch will be at most 10 μm by this method .
In this method, it is more preferred to stabilize the supply of the raw materials as the glass-forming materials, with a view to reducing the degree and pitch of the striae.
The striae observed in a Ti02-Siθ2 glass, are attributable to the fluctuation of the Ti02/Si02 ratio. Further, if the Ti02/Si02 ratio fluctuates, the absolute refractive index of glass will fluctuate. For example, at a portion where the Ti02 concentration is high, the refractive index tends to be high as compared with a portion where the Ti02 concentration is low. The present inventors have measured the absolute refractive indices of several Ti02-Si02 glasses having different Ti02 concentrations and have found that the following relation is satisfied between the Ti02 concentration and the refractive index within a range where the Ti02 concentration is at most 12 mass%. Absolute refractive index = 3.27 x 10~3 x Ti02 concentration (mass%) + 1.459 (1)
By using the formula (1) , it will be possible to calculate the fluctuation of the Ti02 concentration (ΔTi02) from the fluctuation of the refractive index (Δn) of the Ti02-Si02 glass. Specifically, when the fluctuation of the refractive index (Δn) is 200 ppm, the fluctuation of the Ti02 concentration (ΔTi02) is 0.06 mass% .
The method of obtaining the striae pitch is as follows. The fluctuation of the refractive index (Δn) in the plane is measured, and the distance from the portion where the refractive index is high to the portion where the refractive index is low, is measured by means of a microscope .
The method for measuring the fluctuation of the refractive index (Δn) is different as between the case of the fluctuation of the refractive index in small areas (Δni) , and the case of the fluctuation of the refractive index in a broad area (Δn2) , as shown hereinafter.
The fluctuation of the refractive index in small areas (Δni) so-called striae, is measured as follows.
From the Ti02-Si0 glass body, a cube of about 40 mm x 40 mm x 40 mm is, for example, cut out, and each side of the cube is sliced in a thickness of 1 mm to obtain a plate- shaped Ti02-Si02 glass block of 30 mm x 30 mm x l mm. By a Fizeau interferometer, a helium neon laser beam is vertically irradiated to an area of 30 mm x 30 mm of this glass block, and the refractive index distribution within
the area is examined by magnifying to 2 mm x 2 mm, for example, where the striae can be sufficiently observed, and the fluctuation of the refractive index (Δn) is measured. In a case where an area of 30 mm x 30 mm is directly measured, it is possible that the size of one pixel in CCD of the interferometer is not smaller than the width of the striae sufficiently, so that the striae may not be detected. Therefore, the entire area of 30 mm x 30 mm is divided into a lot of small areas at a level of, for example, 2 mm x 2 mm, and the fluctuation of the refractive index (Δ i) in each small area, is measured, and the maximum value is taken as the fluctuation of the refractive index (Δn) in an area of 30 mm x 30 mm. For example, in a case of CCD having 512x480 valid pixels, one pixel corresponds to about 4 square μm in a visual field of 2 mm x 2 mm. Accordingly, striae with a pitch of at least 10 μm can be sufficiently detected, but striae smaller than this may not be detected sometime. Therefore, in a case where striae of at most 10 μm are to be measured, it is advisable to set at least that one pixel corresponds to at most 1 to 2 square μm. In Examples in this specification, the fluctuation of the refractive index (Δni) was measured so that one pixel corresponds to about 2 square μm by measuring an area of 2 mm x 2 mm by means of CCD having 900x900 valid pixels. On the other hand, the fluctuation of the refractive
index in a broad area such as an area irradiated with EUV light to be used for exposure (Δn2) , is measured as follows. A formed Ti02-Si02 glass body of 160 mm x 160 mm x 150 mm is sliced into a block of 7 mm in thickness to obtain a Ti02-Si02 glass block of 160 mm x 160 mm x 7 mm. By a Fizeau interferometer, a helium neon laser beam is vertically irradiated to the face of 160 mm x 160 mm of this glass block, and the refractive index distribution within an area of 100 mm x 100 mm is examined, and the fluctuation of the refractive index (Δn2) is measured. In Examples in this specification, the fluctuation of the refractive index (Δn ) was measured so that one pixel corresponds to about 300 to 400 square μm by measuring an area of 100 mm x 100 mm by means of CCD having 320x240 valid pixels. In this case, the refractive index difference in an area of about 1 mm can be measured.
By the above-mentioned method for measuring the fluctuation of the refractive index in small areas (Δni) , the absolute value of the refractive index can not be measured, and only the refractive index difference can be obtained. Accordingly, if the divided small areas are measured without directly measuring the entire area irradiated with EUV light to be used for exposure, the refractive indices at both ends of the material can not be compared, and it is possible that the fluctuation of the refractive index is estimated to be small .
Therefore, the fluctuation of the refractive index is measured over the entire area irradiated with EUV light to be used for exposure, and the measured value is taken as the fluctuation of the refractive index in a plane perpendicular to the incident direction (Δn) .
When the fluctuation of the refractive index in small areas is measured by the above-mentioned method on the same face, if the fluctuation of the refractive index in the small areas (Δni) is larger than the fluctuation of the refractive index in the entire area (Δn2) , the fluctuation of the refractive index in the small areas (Δni) is taken as the fluctuation of the refractive index in the plane perpendicular to the incident direction (Δn) . Further, it is very important to make the Ti0 /Siθ2 ratio uniform in a broad area such as an area irradiated with EUV light to be used for exposure when the Ti02-Si02 glass is used as a material for the exposure device for EUVL, with a view to minimizing the fluctuation of the coefficient of the thermal expansion within the material. This fluctuation of the Ti02/Si02 ratio causes the refractive index of glass. Accordingly, the fluctuation of the refractive index may be used as an index for the uniformity of the Ti02-Si02 composition. Δn in the plane perpendicular to the incident light direction is preferably within a range of 2xl0"4, more preferably within 1.5xl0"4, particularly preferably
within 1. OxlO"4.
Further, it is very important to make the Ti02/Si02 ratio uniform in the small areas like 30 mm x 30 mm, with a view to polishing the glass surface ultra smooth. Δn in an area of 30 mm x 30 mm is preferably within 2xl0-4, more preferably within 1.5xl0-4, particularly preferably within l.OxlO-4, most preferably within 0.5xl0~4. If Δn exceeds the above range, the polishing rate will not be constant depending upon the position, and it tends to be difficult to finish so that the glass surface after polishing will be ultra smooth surface.
If the Tiθ2~Si02 glass having a striae pitch of at most 10 μm or the Ti02-Si02 glass of which a fluctuation of the Ti02 concentration is at most 0.06 mass%, obtained by the present invention, is cut into a size of 160 mm x 160 mm x 7 mm, and then, an area of 160 mm x 160 mm is polished, the value of MSFR (Mid-Spatial Frequency Roughness) which has a waving pitch within a range of from 10 μm to 1 mm and is an index showing smoothness of a polished surface, will be a roughness (rms) of at most 1.5 nm, which is suitable for an optical material for the exposure device for EUVL.
Further, with the Ti02-Si02 glass having a striae pitch of at least 10 μm or the Ti02-Si02 glass having a fluctuation of the Ti02 concentration being at least 0.06 mass%, it is difficult to bring MSFR of the polished surface to be at most 1.5 nm, whereby such a glass tends
to be inadequate for an optical material for the exposure device for EUVL.
Further, in a Ti0-Si02 glass having striae, the fluctuation of the Ti0 /Si02 ratio or Δn usually becomes largest at the portion having the striae. Accordingly, in such a case, if the fluctuation of the refractive index or the fluctuation of the Ti0 /Si02 ratio is reduced in an area of 30 mm x 30 mm in at least one plane, by reducing the degree of the striae, it is possible to reduce the fluctuation of the Ti02/Si02 ratio or the fluctuation of the refractive index in each of two orthogonal planes simultaneously.
By using the Ti02-Si02 glass of the present invention, it becomes easy to obtain an optical material for EUV lithography, which is made of the Ti02-Si02 glass and wherein the fluctuation of the refractive index (Δn) is at most 2xl0~4 in a plane perpendicular to the incident light direction.
Further, in the present invention, the degree of the striae itself is reduced, whereby it is possible to easily obtain an optical material for EUV lithography which is made of the Ti02-Si02 glass and wherein the striae are not present which cause the fluctuation of the refractive index (Δn) to exceed 2xl0~4 in a plane perpendicular to the incident light direction.
Further, by using the Ti02-Si02 glass of the present invention, it is possible to easily obtain an optical
material for EUV lithography which is made of the Ti02- Si02 glass having a Ti02 concentration of at least 1 mass% and wherein the difference between the maximum value and the minimum value of the Ti02 concentration is at most 0.06 mass%, in a plane perpendicular to the incident light direction.
Further, it is likewise possible to easily obtain an optical material for EUV lithography which is made of the Ti02-Si02 glass having a Ti02 concentration of at least 1 mass% and wherein the striae are not present which cause the difference between the maximum value and the minimum value of the Ti0 concentration to exceed 0.06 mass% in a plane perpendicular to the incident light direction.
Further, in a wide temperature range of from 0 to 100°C, the Ti02-Si02 glass can be made to be a zero expansion glass, of which the coefficient of thermal expansion is within a range of 0±200 ppb/°C. Further, in a case where the fictive temperature of the Ti02-Siθ2 glass is at most 1,100°C, the temperature range wherein the coefficient of the thermal expansion shows substantially zero, can be made wider. And within a range of from -50 to 150°C, the coefficient of the thermal expansion can be made to be within a range of O± 200 ppb/°C. Further, when the optical material for EUVL is prepared, by adjusting so that striae will be parallel to patterning surface, it is also possible to reduce the
fluctuation of the Ti02/Si02 ratio or the fluctuation of the refractive index in a plane perpendicular to the incident light direction and to reduce MSFR.
The coefficient of thermal expansion is measured within a range of from -150 to +200°C by means of a laser interferometer type expansion meter (LIX-1, by manufactured by ULVAC-RIKO, Inc.).
The fluctuation of the coefficient of thermal expansion is measured as follows . A Ti0-Si02 glass block of 160 mm x 160 mm x 150 mm is cut and divided into small pieces of Ti02-Si02 glass of 20 mm x 20 mm x 10 mm. The coefficient of thermal expansion of each small piece is measured in accordance with the above-mentioned method, to obtain the fluctuation of the coefficient of thermal expansion of the Ti02-Si02 glass block of 160 mm x 160 mm x 30 mm.
Further, the optical material for EUV lithography is required to have a small fluctuation of the coefficient of thermal expansion. With the Ti02-Si0 glass of the present invention, the difference between the maximum value and the minimum value of the Tiθ2 concentration is at most 0.06 mass%, so the fluctuation of the coefficient of thermal expansion of the Ti02-Si02 glass of the present invention obtained by a calibration curve will be at most about ±5 ppb/°C at room temperature. Thus, the Ti02-Si02 glass of the present invention can be made to have a fluctuation of the coefficient of thermal
expansion being, for example, at most ±5 ppb/°C at room temperature, and as such, is suitable for an optical material for EUV lithography.
The following process can be employed for producing the Ti02-Si02 glass of the present invention. Step (a)
Ti02-Si02 glass particles obtained by flame hydrolysis of a Si precursor and a Ti precursor as glass- forming materials, are deposited and grown on a rotating target to obtain a porous Ti02-Siθ2 glass body (the target as disclosed, for example, in JP-B-63-24973 ) . The glass-forming materials are not particularly limited so long as they are materials capable of being gasified. However, the Si precursor may, for example, be a silicon halide compound, such as a chloride such as SiCl4,
SiHCl3, SiH2Cl2 or SiH3Cl, a fluoride such as SiF4, SiHF3 or SiH2F2, a bromide such as SiBr4 or SiHBr3 or an iodide such as Sil4, or an alkoxy silane represented by RnSi(0R)4-n (wherein R is a Cι_4 alkyl group, and n is an integer of from 0 to 3), and the Ti precursor may, for example, be a titanium halide compound such as TiCl4 or TiBr4, or a titanium alkoxide represented by RnSi(OR)4_n (wherein R is a C1-4 alkyl group, and n is an integer of from 0 to 3) . Further, as the Si precursor and the Ti precursor, a compound of Si and Ti, such as a silicon- titanium alkoxide, may also be used. Further, the target may not be limited to a rod shape, and a plate-shaped
substrate may be employed. Step (b)
The porous Ti02-Si02 glass body is heated to a vitrification temperature for vitrification to obtain a vitrified Ti0-Si02 glass body. In this specification, the vitrification means a state where the porous glass body is densified to such an extent that void spaces can no longer be detected by an optical microscope, and the vitrification temperature means the temperature at which the porous glass body can be densified until void can no longer be detected by an optical microscope. The vitrification temperature is usually from 1,400 to
1,700°C, particularly preferably from 1,450 to 1,650°C. The atmosphere is preferably an atmosphere of 100% inert gas such as helium or an atmosphere containing an inert gas such as helium, as the main component. The pressure may be a reduced pressure or a normal pressure .
Especially in the case of a normal pressure, helium gas may be employed. In the case of a reduced pressure, a pressure of at most 13,000 Pa is preferred. In this specification, "Pa" is meant for an absolute pressure i.e. not a gauge pressure.
Step (c)
The vitrified Tiθ2-Si02 glass body obtained in step (b) is heated to a temperature above near the softening temperature and formed into a desired shape to obtain a formed Ti02-Si02 glass body. The temperature for forming
is preferably from 1,500 to 1,800°C. If it is lower than 1,500°C, no substantial deadweight transformation takes place, since the viscosity of the Ti02-Si02 glass is high, and growth of cristobalite being a crystalline phase of Si02 or growth of rutile or anatase being a crystalline phase of Ti02 takes place, thus leading to so-called devitrification. If the temperature exceeds 1,800°C, vaporization of Si0 tends to be not negligible. Step (d) The fictive temperature of the Ti02-Si02 glass is controlled by carrying out annealing treatment wherein the formed Ti02-Si02 glass body obtained in step (c) is held at a temperature of from 600 to 1,200°C for at least 5 hours, and then, the temperature is lowered to not higher than 500°C at an average cooling rate of at most 10°C/hr. After the temperature is lowered to not higher than 500°C, the glass body may be cooled. The atmosphere in such a case is preferably an atmosphere of 100% inert gas such as helium, argon or nitrogen or an atmosphere containing such an inert gas as the main component, or an atmosphere of air, and the pressure is preferably a reduced pressure or a normal pressure.
Now, the present invention will be described in further detail with reference to Examples. However, it should be understood that the present invention is by no means restricted to such specific Examples. In the glass compositions in the following Examples, Ti02=7.4 mass%,
and Si02=92.6 mass%, in all cases. EXAMPLE 1
Ti0-Si02 glass particles obtained by gasifying TiCl4 and SiCl4 as glass-forming materials for Ti02-Si02 glass, respectively, then mixing them and feeding them to heat hydrolysis (flame hydrolysis) in oxyhydrogen flame, were deposited and grown on a target made of quartz glass rotating at a rate of 25 rpm, to form a porous Ti0-Si02 glass body having a diameter of 80 mm and a length of about 100 mm (step (a)).
The obtained porous Ti0-Si02 glass body was heated to 1,550°C in an atmosphere of 100% He and held at this temperature for 10 hours for vitrification to obtain a vitrified Ti02-Si02 glass body (step (b) ) . The obtained vitrified Ti02-Si02 glass body was heated to 1,600°C i.e. higher than the softening point for deadweight transformation and formed into a block shape of 50 mm x 50 mm x 10 mm (step '(c) ) . The obtained block was set in an electric furnace and held at 950°C for 100 hours. Then, the temperature was lowered to
500°C at a rate of 5°C/hr, and then the block was cooled to room temperature (step (d) ) to obtain Ti02-Si0 glass. EXAMPLE 2
In the step (a) in Example 1, the Ti02-Si02 glass particles were deposited and grown on a target made of quartz glass rotating at a rate of 100 rpm. Other than this, in the same manner as in Example 1, Ti02-Si02 glass
was obtained. EXAMPLE 3
In the step (a) in Example 1, the Ti02-Si02 glass particles were deposited and grown on a target made of quartz glass rotating at a rate of 250 rpm. Other than this, in the same manner as in Example 1, Ti02-Si0 glass was obtained. EXAMPLE 4
In the step (a) in Example 1, the Ti0-Si02 glass particles were deposited and grown on a target made of quartz glass rotating at a rate of 5 rpm. Other than this, in the same manner as in Example 1, Ti02-Si0 glass was obtained. EXAMPLE 5 Ti02-Si02 glass particles obtained by gasifying TiCl4 and SiCl4 as glass-forming materials for Ti02-Si02 glass, respectively, then mixing them and feeding them to heat hydrolysis (flame hydrolysis) in oxyhydrogen flame, were deposited and grown on a target made of quartz glass rotating at a rate of 25 rpm, to form a porous Ti0-Si02 glass body having a diameter of 30 mm and a length of 80 cm (step (a) ) .
The obtained porous Ti02-Si02 glass body was heated to 1,430°C in an atmosphere of 100% He and held at this temperature for 2 hours for vitrification to obtain a vitrified Ti02-Si0 glass body (step (b) ) .
Further, it was heated to 1,680°C i.e. higher than
the softening point for deadweight transformation and formed into a block shape of 160 mm x 160 mm x 150 mm (step (c) ) . Then, it was sliced into a block of 7 mm in thickness. The obtained block of 160 mm x 160 mm x 7 mm was set in an electric furnace and held at 950°C for 100 hours. Then, the temperature was lowered to 500°C at a rate of 5°C/hr, and then the block was cooled to room temperature (step (d) ) to obtain Ti02-Si02 glass.
The evaluation was carried out in accordance with the above-mentioned measuring methods, respectively. The results of evaluation of Examples 1 to 5 are summarized in Table 1. Here, Examples 1, 2, 3 and 5 are Examples of the present invention, and Example 4 is a Comparative Example.
Table 1
tSJ
In Examples 1 and 2 , the striae pitch is not more than 10 μm, and in at least one plane, the fluctuation of the refractive index in small areas is not more than 200 ppm, and the fluctuation of the Ti02 concentration is not more than 0.06 mass%. The fluctuation of the refractive index or the fluctuation of the Ti02 concentration are attributable to the striae, and the strength of the striae is reduced in Examples 1 and 2 , whereby MSFR can easily be reduced by polishing and it will be possible to be ultra smooth surface.
Further, with these samples, it is seen that also in at least one plane orthogonal thereto, the fluctuation of the refractive index is not more than 200 ppm, and the fluctuation of the Ti02 concentration is not more than 0.06 mass%.
In Example 3 , the presence of striae can be visually confirmed, and by the measurement microscope, the striae pitch was confirmed to be 1 μm, but the fluctuation of the refractive index could not be detected by the above- mentioned method. Accordingly, it is considered that the fluctuation of the refractive index is not more than 50 ppm, and the fluctuation of the Ti02 concentration is not more than 0.06 mass%. Accordingly, in Example 3, MSFR can be reduced more easily, and it is possible to obtain ultra smooth surface.
In Example 4, the striae pitch is at least 10 μm, the fluctuation of the refractive index in small areas is
at least 200 ppm, and the fluctuation of the Ti02 concentration is at least 0.06 mass% . The degree of striae was very high, and it was difficult to reduce MSFR by polishing. In Example 5, the fluctuation of the refractive index in a broad area is not more than 200 ppm, and it becomes possible to obtain an optical material for EUV lithography wherein the fluctuation of the refractive index (Δn) is at most 2xl0~4 in a plane perpendicular to the incident light direction.