WO2004044342A1 - A hybrid structural module - Google Patents
A hybrid structural module Download PDFInfo
- Publication number
- WO2004044342A1 WO2004044342A1 PCT/AU2003/001519 AU0301519W WO2004044342A1 WO 2004044342 A1 WO2004044342 A1 WO 2004044342A1 AU 0301519 W AU0301519 W AU 0301519W WO 2004044342 A1 WO2004044342 A1 WO 2004044342A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- structural module
- hybrid structural
- resin system
- steel
- filled resin
- Prior art date
Abstract
Description
Claims