WO2004014983A1 - 水性難燃性ポリエステル樹脂、同樹脂を含有する樹脂組成物、および同樹脂組成物で処理された繊維製品 - Google Patents
水性難燃性ポリエステル樹脂、同樹脂を含有する樹脂組成物、および同樹脂組成物で処理された繊維製品 Download PDFInfo
- Publication number
- WO2004014983A1 WO2004014983A1 PCT/JP2003/001403 JP0301403W WO2004014983A1 WO 2004014983 A1 WO2004014983 A1 WO 2004014983A1 JP 0301403 W JP0301403 W JP 0301403W WO 2004014983 A1 WO2004014983 A1 WO 2004014983A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water
- polyester resin
- retardant polyester
- solubility
- flame
- Prior art date
Abstract
Description
Claims