WO2003078668A1 - Procede pour fabriquer une feuille d'acier galvanisee a chaud de haute resistance, presentant une excellente ductilite et une grande resistance a la fatigue - Google Patents
Procede pour fabriquer une feuille d'acier galvanisee a chaud de haute resistance, presentant une excellente ductilite et une grande resistance a la fatigue Download PDFInfo
- Publication number
- WO2003078668A1 WO2003078668A1 PCT/JP2003/002190 JP0302190W WO03078668A1 WO 2003078668 A1 WO2003078668 A1 WO 2003078668A1 JP 0302190 W JP0302190 W JP 0302190W WO 03078668 A1 WO03078668 A1 WO 03078668A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mass
- hot
- phase
- steel sheet
- temperature
- Prior art date
Description
Claims