WO2003033781A1 - Low temperature epitaxial growth of quaternary wide bandgap semiconductors - Google Patents
Low temperature epitaxial growth of quaternary wide bandgap semiconductors Download PDFInfo
- Publication number
- WO2003033781A1 WO2003033781A1 PCT/US2002/033134 US0233134W WO03033781A1 WO 2003033781 A1 WO2003033781 A1 WO 2003033781A1 US 0233134 W US0233134 W US 0233134W WO 03033781 A1 WO03033781 A1 WO 03033781A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- group
- film
- epitaxial
- semiconductor
- Prior art date
Abstract
Description
Claims