WO2003006364A2 - Zeolite ssz-59 - Google Patents

Zeolite ssz-59 Download PDF

Info

Publication number
WO2003006364A2
WO2003006364A2 PCT/US2002/021019 US0221019W WO03006364A2 WO 2003006364 A2 WO2003006364 A2 WO 2003006364A2 US 0221019 W US0221019 W US 0221019W WO 03006364 A2 WO03006364 A2 WO 03006364A2
Authority
WO
WIPO (PCT)
Prior art keywords
methyl
zeolite
catalyst
cation
oxide
Prior art date
Application number
PCT/US2002/021019
Other languages
French (fr)
Other versions
WO2003006364A3 (en
Inventor
Saleh Elomari
Original Assignee
Chevron U.S.A. Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US09/905,461 external-priority patent/US6464956B1/en
Priority claimed from US09/905,351 external-priority patent/US6547958B1/en
Priority claimed from US09/905,353 external-priority patent/US6461578B1/en
Application filed by Chevron U.S.A. Inc. filed Critical Chevron U.S.A. Inc.
Priority to EP02748044A priority Critical patent/EP1409402A4/en
Priority to AU2002318478A priority patent/AU2002318478A1/en
Priority to JP2003512143A priority patent/JP4383856B2/en
Publication of WO2003006364A2 publication Critical patent/WO2003006364A2/en
Publication of WO2003006364A3 publication Critical patent/WO2003006364A3/en

Abstract

The present invention relates to new crystalline zeolite SSZ-59 prepared using a N-methyl-N-[(1-phenylcyclopentyl)methyl!heptamethyleneiminium cation, N-methyl-N-[(1-(4-chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[1-(4-chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[(1-phenylcyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[(1-phenylcyclopentyl)methyl]piperidinium cation or N-methyl-N-[(1-(4-chlorophenyl)cyclopentyl)methyl]piperidinium cation templating agent, and processes employing SSZ-59 in a catalyst.

Description

ZEOLITE SSZ-59 BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to new crystalline zeolite SSZ-59 and a method for preparing SSZ-59 using a N-methyl-N-[(l - phenylcyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l- phenylcyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-((l- phenylcyclopentyl)methyl]piperidinium cation or N-methyl-N-[( 1 -(4- chlorophenyl)cyclopentyl)methyl]piperidinium cation templating agent or structure directing agent (SDA). State of the Art Because of their unique sieving characteristics, as well as their catalytic properties, crystalline molecular sieves and zeolites are especially useful in applications such as hydrocarbon conversion, gas drying and separation. Although many different crystalline molecular sieves have been disclosed, there is a continuing need for new zeolites with desirable properties for gas separation and drying, hydrocarbon and chemical conversions, and other applications. New zeolites may contain novel internal pore architectures, providing enhanced selectivities in these processes. Crystalline aluminosilicates are usually prepared from aqueous reaction mixtures containing alkali or alkaline earth metal oxides, silica, and alumina. Crystalline borosilicates are usually prepared under similar reaction conditions except that boron is used in place of aluminum. By varying the synthesis conditions and the composition of the reaction mixture, different zeolites can often be formed. SUMMARY OF THE INVENTION The present invention is directed to a family of crystalline molecular sieves with unique properties, referred to herein as "zeolite SSZ-59" or simply "SSZ-59". Preferably, SSZ-59 is obtained in its silicate, aluminosilicate, titanosilicate, vanadosilicate or borosilicate form. The term "silicate" refers to a zeolite having a high mole ratio of silicon oxide relative to aluminum oxide, preferably a mole ratio greater than 100, including zeolites comprised entirely of silicon oxide. As used herein, the term "aluminosilicate" refers to a zeolite containing both alumina and silica and the term "borosilicate" refers to a zeolite containing oxides of both boron and silicon. In accordance with this invention, there is provided a zeolite having a mole ratio greater than about 20 of an oxide of a first tetravalent element to an oxide of a second tetravalent element different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof and having, after calcination, the X-ray diffraction lines of Table II. Further, in accordance with this invention, there is provided a zeolite having a mole ratio greater than about 20 of an oxide selected from silicon oxide, germanium oxide and mixtures thereof to an oxide selected from aluminum oxide, gallium oxide, iron oxide, boron oxide, titanium oxide, indium oxide, vanadium oxide and mixtures thereof and having, after calcination, the X-ray diffraction lines of Table II below. The present invention further provides such a zeolite having a composition, as synthesized and in the anhydrous state, in terms of mole ratios as follows: YO2/WcOd 20 - 150 M2 n/YO2 0.01 - 0.03 Q/YO2 0.02 - 0.05 wherein Y is silicon, germanium or a mixture thereof; W is aluminum, gallium, iron, boron, titanium, indium, vanadium or mixtures thereof; c is 1 or 2; d is 2 when c is 1 (i.e., W is tetravalent) or d is 3 or 5 when c is 2 (i.e., d is 3 when W is trivalent or 5 when W is pentavalent); M is an alkali metal cation, alkaline earth metal cation or mixtures thereof; n is the valence of M (i.e., 1 or 2); and Q is a N-methyl-N-[(l- phenylcyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l- phenylcyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-((l- phenylcyclopentyl)methyl]piperidinium cation or N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]piperidinium cation. In accordance with this invention, there is also provided a zeolite prepared by thermally treating a zeolite having a mole ratio of an oxide selected from silicon oxide, germanium oxide and mixtures thereof to an oxide selected from aluminum oxide, gallium oxide, iron oxide, boron oxide, titanium oxide, indium oxide, vanadium oxide and mixtures thereof greater than about 20 at a temperature of from about 200°C to about 800°C, the thus-prepared zeolite having the X-ray diffraction lines of Table II. The present invention also includes this thus-prepared zeolite which is predominantly in the hydrogen form, which hydrogen form is prepared by ion exchanging with an acid or with a solution of an ammonium salt followed by a second calcination. Also provided in accordance with the present invention is a method of preparing a crystalline material comprising an oxide of a first tetravalent element and an oxide of a second tetravalent element which is different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof, said method comprising contacting under crystallization conditions sources of said oxides and a templating agent comprising a N-methyl-N-[(l -phenylcyclopentyl)methyl]heptamethyleneiminium cation, N-methyl- N-[(l-(4-chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N- [(l-phenylcyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-((l - phenylcyclopentyl)methyl]piperidinium cation or N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]piperidinium cation. The present invention provides a process for converting hydrocarbons comprising contacting a hydrocarbonaceous feed at hydrocarbon converting conditions with a catalyst comprising the zeolite of this invention. The zeolite may be predominantly in the hydrogen form. It may also be substantially free of acidity. Further provided by the present invention is a hydrocracking process comprising contacting a hydrocarbon feedstock under hydrocracking conditions with a catalyst comprising the zeolite of this invention, preferably predominantly in the hydrogen form. This invention also includes a dewaxing process comprising contacting a hydrocarbon feedstock under dewaxing conditions with a catalyst comprising the zeolite of this invention, preferably predominantly in the hydrogen form. The present invention also includes a process for improving the viscosity index of a dewaxed product of waxy hydrocarbon feeds comprising contacting the waxy hydrocarbon feed under isomerization dewaxing conditions with a catalyst comprising the zeolite of this invention, preferably predominantly in the hydrogen form. The present invention further includes a process for producing a C20+ lube oil from a C 0+ olefin feed comprising isomerizing said olefin feed under isomerization conditions over a catalyst comprising at least one Group Vffl metal and the zeolite of this invention. The zeolite may be predominantly in the hydrogen form. In accordance with this invention, there is also provided a process for catalytically dewaxing a hydrocarbon oil feedstock boiling above about 350°F and containing straight chain and slightly branched chain hydrocarbons comprising contacting said hydrocarbon oil feedstock in the presence of added hydrogen gas at a hydrogen pressure of about 15-3000 psi with a catalyst comprising at least one Group VIII metal and the zeolite of this invention, preferably predominantly in the hydrogen form. The catalyst may be a layered catalyst comprising a first layer comprising at least one Group VIII metal and the zeolite of this invention, and a second layer comprising an aluminosilicate zeolite which is more shape selective than the zeolite of said first layer. Also included in the present invention is a process for preparing a lubricating oil which comprises hydrocracking in a hydrocracking zone a hydrocarbonaceous feedstock to obtain an effluent comprising a hydrocracked oil, and catalytically dewaxing said effluent comprising hydrocracked oil at a temperature of at least about 400°F and at a pressure of from about 15 psig to about 3000 psig in the presence of added hydrogen gas with a catalyst comprising at least one Group VIII metal and the zeolite of this invention. The zeolite may be predominantly in the hydrogen form. Further included in this invention is a process for isomerization dewaxing a raffinate comprising contacting said raffinate in the presence of added hydrogen with a catalyst comprising at least one Group VIII metal and the zeolite of this invention. The raffinate may be bright stock, and the zeolite may be predominantly in the hydrogen form. Also included in this invention is a process for increasing the octane of a hydrocarbon feedstock to produce a product having an increased aromatics content comprising contacting a hydrocarbonaceous feedstock which comprises normal and slightly branched hydrocarbons having a boiling range above about 40°C and less than about 200°C, under aromatic conversion conditions with a catalyst comprising the zeolite of this invention made substantially free of acidity by neutralizing said zeolite with a basic metal. Also provided in this invention is such a process wherein the zeolite contains a Group VIII metal component. Also provided by the present invention is a catalytic cracking process comprising contacting a hydrocarbon feedstock in a reaction zone under catalytic cracking conditions in the absence of added hydrogen with a catalyst comprising the zeolite of this invention, preferably predominantly in the hydrogen form. Also included in this invention is such a catalytic cracking process wherein the catalyst additionally comprises a large pore crystalline cracking component. This invention further provides an isomerization process for isomerizing C4 to C7 hydrocarbons, comprising contacting a feed having normal and slightly branched C4 to C7 hydrocarbons under isomerizing conditions with a catalyst comprising the zeolite of this invention, preferably predominantly in the hydrogen form. The zeolite may be impregnated with at least one Group VIII metal, preferably platinum. The catalyst may be calcined in a steam/air mixture at an elevated temperature after impregnation of the Group VIII metal. Also provided by the present invention is a process for alkylating an aromatic hydrocarbon which comprises contacting under alkylation conditions at least a molar excess of an aromatic hydrocarbon with a C2 to C 0 olefin under at least partial liquid phase conditions and in the presence of a catalyst comprising the zeolite of this invention, preferably predominantly in the hydrogen form. The olefin may be a C2 to C4 olefin, and the aromatic hydrocarbon and olefin may be present in a molar ratio of about 4: 1 to about 20: 1, respectively. The aromatic hydrocarbon may be selected from the group consisting of benzene, toluene, ethylbenzene, xylene, naphthalene, naphthalene derivatives such as dimethylnaphthalene or mixtures thereof. Further provided in accordance with this invention is a process for transalkylating an aromatic hydrocarbon which comprises contacting under transalkylating conditions an aromatic hydrocarbon with a polyalkyl aromatic hydrocarbon under at least partial liquid phase conditions and in the presence of a catalyst comprising the zeolite of this invention, preferably predominantly in the hydrogen form. The aromatic hydrocarbon and the polyalkyl aromatic hydrocarbon may be present in a molar ratio of from about 1 : 1 to about 25:1, respectively. The aromatic hydrocarbon may be selected from the group consisting of benzene, toluene, ethylbenzene, xylene, or mixtures thereof, and the polyalkyl aromatic hydrocarbon may be a dialkylbenzene. Further provided by this invention is a process to convert paraffins to aromatics which comprises contacting paraffins under conditions which cause paraffins to convert to aromatics with a catalyst comprising the zeolite of this invention, said catalyst comprising gallium, zinc, or a compound of gallium or zinc. In accordance with this invention there is also provided a process for isomerizing olefins comprising contacting said olefin under conditions which cause isomerization of the olefin with a catalyst comprising the zeolite of this invention. Further provided in accordance with this invention is a process for isomerizing an isomerization feed comprising an aromatic C8 stream of xylene isomers or mixtures of xylene isomers and ethylbenzene, wherein a more nearly equilibrium ratio of ortho-, meta- and para-xylenes is obtained, said process comprising contacting said feed under isomerization conditions with a catalyst comprising the zeolite of this invention. The present invention further provides a process for oligomerizing olefins comprising contacting an olefin feed under oligomerization conditions with a catalyst comprising the zeolite of this invention. This invention also provides a process for converting lower alcohols and other oxygenated hydrocarbons comprising contacting said lower alcohol or other oxygenated hydrocarbon with a catalyst comprising the zeolite of this invention under conditions to produce liquid products. Further provided in accordance with the present invention is a process for the production of higher molecular weight hydrocarbons from lower molecular weight hydrocarbons comprising the steps of: (a) introducing into a reaction zone a lower molecular weight hydrocarbon- containing gas and contacting said gas in said zone under C2+ hydrocarbon synthesis conditions with the catalyst and a metal or metal compound capable of converting the lower molecular weight hydrocarbon to a higher molecular weight hydrocarbon; and (b) withdrawing from said reaction zone a higher molecular weight hydrocarbon containing stream. In accordance with the present invention there is provided an improved process for the reduction of oxides of nitrogen contained in a gas stream in the presence of oxygen wherein said process comprises contacting the gas stream with a zeolite, the improvement comprising using as the zeolite a zeolite having a mole ratio greater than about 20 of an oxide of a first tetravalent element to an oxide of a second tetravalent element different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof and having, after calcination, the X-ray diffraction lines of Table II. The zeolite may contain a metal or metal ions (such as cobalt, copper or mixtures thereof) capable of catalyzing the reduction of the oxides of mtrogen, and may be conducted in the presence of a stoichiometric excess of oxygen. In a preferred embodiment, the gas stream is the exhaust stream of an internal combustion engine. DETAILED DESCRIPTION OF THE INVENTION The present invention comprises a family of crystalline, zeolites designated herein "zeolite SSZ-59" or simply "SSZ-59". SSZ-59 is believed to be a large pore zeolite. As used herein, the term "large pore" means having an average pore size diameter greater than about 6.0 Angstroms, preferably from about 6.5 Angstroms to about 7.5 Angstroms. In preparing SSZ-59 zeolites, a N-methyl-N-[(l- phenylcyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l- phenylcyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-((l- phenylcyclopentyl)methyl]piperidinium cation or N-methyl-N-[(l -(4- chlorophenyl)cyclopentyl)methyl]piperidinium cation is used as a crystallization template. In general, SSZ-59 is prepared by contacting an active source of one or more oxides selected from the group consisting of monovalent element oxides, divalent element oxides, trivalent element oxides, and tetravalent element oxides with the N-methyl-N-[(l- phenylcyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l -(4- chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l- phenylcyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[( 1 -(4- chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-((l- phenylcyclopentyl)methyl]piperidinium cation or N-methyl-N-[(l -(4- chlorophenyl)cyclopentyl)methyl]piperidinium cation templating agent. SSZ-59 is prepared from a reaction mixture having the composition shown in Table A below. TABLE A Reaction Mixture Typical Preferred YO2/WaOb > 20 35 - 70 OH-/YO2 0.1 - 0.5 0.15 - 0.3 Q/YO2 0.05 - 0.5 0.1 - 0.2 M2 n/YO2 0.02 - 0.04 0.1 - 0.25 H2O/YO 20 - 80 25 - 40 where Y, W, Q, M and n are as defined above, and a is 1 or 2, and b is 2 when a is 1 (i.e., W is tetravalent) and b is 3 when a is 2 (i.e., W is trivalent). In practice, SSZ-59 is prepared by a process comprising: (a) preparing an aqueous solution containing sources of at least one oxide capable of forming a crystalline molecular sieve and a N-methyl-N-[(l - phenylcyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation, N-methyl-N- [(l-phenylcyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation, N-methyl-N-((l- phenylcyclopentyl)methyl]piperidinium cation or N-methyl-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]piperidinium cation having an anionic counterion which is not detrimental to the formation of SSZ-59; (b) maintaining the aqueous solution under conditions sufficient to form crystals of SSZ-59; and (c) recovering the crystals of SSZ-59. Accordingly, SSZ-59 may comprise the crystalline material and the templating agent in combination with metallic and non-metallic oxides bonded in tetrahedral coordination through shared oxygen atoms to form a cross-linked three dimensional crystal structure. The metallic and non-metallic oxides comprise one or a combination of oxides of a first tetravalent element(s), and one or a combination of a second tefravalent element(s) different from the first tetravalent element(s), trivalent element(s), pentavalent element(s) or mixture thereof. The first tetravalent element(s) is preferably selected from the group consisting of silicon, germanium and combinations thereof. More preferably, the first tetravalent element is silicon. The second tetravalent element (which is different from the first tetravalent element), trivalent element and pentavalent element is preferably selected from the group consisting of aluminum, gallium, iron, boron, titanium, indium, vanadium and combinations thereof. More preferably, the second trivalent or tetravalent element is aluminum or boron. Typical sources of aluminum oxide for the reaction mixture include aluminates, alumina, aluminum colloids, aluminum oxide coated on silica sol, hydrated alumina gels such as Al(OH)3 and aluminum compounds such as A1C13 and A12(S04)3. Typical sources of silicon oxide include silicates, silica hydrogel, silicic acid, fumed silica, colloidal silica, tetra-alkyl orthosilicates, and silica hydroxides. Boron, as well as gallium, germanium, titanium, indium, vanadium and iron, can be added in forms corresponding to their aluminum and silicon counterparts. A source zeolite reagent may provide a source of aluminum or boron. In most cases, the source zeolite also provides a source of silica. The source zeolite in its dealuminated or deboronated form may also be used as a source of silica, with additional silicon added using, for example, the conventional sources listed above. Use of a source zeolite reagent as a source of alumina for the present process is more completely described in U.S. Patent No. 5,225,179, issued July 6, 1993 to Nakagawa entitled "Method of Making Molecular Sieves", the disclosure of which is incorporated herein by reference. Typically, an alkali metal hydroxide and/or an alkaline earth metal hydroxide, such as the hydroxide of sodium, potassium, lithium, cesium, rubidium, calcium, and magnesium, is used in the reaction mixture; however, this component can be omitted so long as the equivalent basicity is maintained. The templating agent may be used to provide hydroxide ion. Thus, it may be beneficial to ion exchange, for example, the halide for hydroxide ion, thereby reducing or eliminating the alkali metal hydroxide quantity required. The alkali metal cation or alkaline earth cation may be part of the as-synthesized crystalline oxide material, in order to balance valence electron charges therein. The reaction mixture is maintained at an elevated temperature until the crystals of the SSZ-59 zeolite are formed. The hydrothermal crystallization is usually conducted under autogenous pressure, at a temperature between 100°C and 200°C, preferably between 135°C and 160°C. The crystallization period is typically greater than 1 day and preferably from about 3 days to about 20 days. Preferably, the zeolite is prepared using mild stirring or agitation. During the hydrothermal crystallization step, the SSZ-59 crystals can be allowed to nucleate spontaneously from the reaction mixture. The use of SSZ-59 crystals as seed material can be advantageous in decreasing the time necessary for complete crystallization to occur. In addition, seeding can lead to an increased purity of the product obtained by promoting the nucleation and/or formation of SSZ-59 over any undesired phases. When used as seeds, SSZ-59 crystals are added in an amount between 0.1 and 10% of the weight of silica used in the reaction mixture. Once the zeolite crystals have formed, the solid product is separated from the reaction mixture by standard mechanical separation techniques such as filtration. The crystals are water- washed and then dried, e.g., at 90°C to 150°C for from 8 to 24 hours, to obtain the as-synthesized SSZ-59 zeolite crystals. The drying step can be performed at atmospheric pressure or under vacuum. SSZ-59 as prepared has a mole ratio of an oxide selected from silicon oxide, germanium oxide and mixtures thereof to an oxide selected from aluminum oxide, gallium oxide, iron oxide, boron oxide, titanium oxide, indium oxide, vanadium oxide and mixtures thereof greater than about 20; and has, after calcination, the X-ray diffraction lines of Table II below. SSZ-59 further has a composition, as synthesized (i.e., prior to removal of the templating agent from the zeolite) and in the anhydrous state, in terms of mole ratios, shown in Table B below. TABLE B As-Svnthesized SSZ-59 YO2/WcOd > 20 M2/n/YO2 0.01 - 0.03 Q/YO2 0.02 - 0.05 where Y, W, c, d, M and Q are as defined above. SSZ-59 can be made essentially aluminum free, i.e., having a silica to alumina mole ratio of ∞. A method of increasing the mole ratio of silica to alumina is by using standard acid leaching or chelating treatments. However, essentially aluminum-free SSZ- 59 can be synthesized directly using essentially aluminum-free silicon sources as the main tetrahedral metal oxide component, if boron is also present. SSZ-59 can also be prepared directly as either an aluminosilicate or a borosilicate. Lower silica to alumina ratios may also be obtained by using methods which insert aluminum into the crystalline framework. For example, aluminum insertion may occur by thermal treatment of the zeolite in combination with an alumina binder or dissolved source of alumina. Such procedures are described in U.S. Patent No. 4,559,315, issued on December 17, 1985 to Chang et al. It is believed that SSZ-59 is comprised of a new framework structure or topology which is characterized by its X-ray diffraction pattern. SSZ-59 zeolites, as-synthesized, have a crystalline structure whose X-ray powder diffraction pattern exhibit the characteristic lines shown in Table I and is thereby distinguished from other zeolites. TABLE I
As-Svnthesized SSZ-59
2 Theta a) D Relative Intensity (b)
6.1 14.5 M
7.2 12.3 S
8.3 10.6 S
14.4 6.14 w
15.7 5.64 w
17.1 5.18 w
18.45 4.80 w
20.75 4.28 vs
22.45 3.96 M
25.3 3.52 M
27.5 3.24 W
35.75 2.51 W
(a) ± 0.2 ^ The X-ray patterns provided are based on a relative intensity scale in which the strongest line in the X-ray pattern is assigned a value of 100: W(weak) is less than 20; M(medium) is between 20 and 40; S(strong) is between 40 and 60; VS(very strong) is greater than 60.
Table LA below shows the X-ray powder diffraction lines for as-synthesized SSZ- including actual relative intensities.
TABLE IA
Two Theta d-spacing (A) Intensity JVIo x 100
6.07 14.54 37
7.20 12.26 45
8.28 10.68 55
14.42 6.140 12
15.71 5.638 6
16.72 Sh 5.298 5
17.10 5.181 14
17.93 Sh 4.942 3
18.24 Sh 4.860 9
18.46 4.804 11
19.33 4.589 3
20.75 4.278 100
21.31 Sh 4.165 6 21.95 4.047 7
22.45 3.957 24
22.99 3.866 3
24.76 3.593 10
25.30 3.517 18
25.54 Sh 3.485 14
26.23 3.395 8
27.22 Sh 3.274 7
27.47 3.244 15
29.09 3.067 2
29.67 3.009 3
30.21 2.956 6
31.09 2.875 5
32.17 2.780 6
33.05 2.708 2
33.55 2.669 2
34.48 2.599 4
35.76 2.509 15
37.00 2.427 2
(a) ± 0.2
After calcination, the SSZ-59 zeolites have a crystalline structure whose X-ray powder diffraction pattern include the characteristic lines shown in Table II: TABLE II
Calcined SSZ-59
2 Theta(a) d Relative Intensity
6.1 14.5 VS
7.2 12.3 vs
8.3 10.6 VS
15.7 5.64 w
17.1 5.18 M
18.5 4.79 w
20.7 4.29 s
22.4 3.97 w
25.2 3.53 M
27.5 3.24 W
35.6 2.52 w
(a) ± 0.2 Table IIA below shows the X- -ray powder diffraction lines for calcined SSZ-59 including actual relative intensities.
TABLE IIA
Two Theta (deg.)(a) d-spacing (A) Intensity I/Io x 100
6.11 14.46 87
7.20 12.27 74
8.28 10.67 100
10.54 8.391 2
15.69 5.642 5
17.09 5.185 12
18.24 Sh 4.859 5
18.53 4.785 10
19.28 4.600 3
20.71 4.286 65
21.50 Sh 4.129 2
21.90 Sh 4.055 3
22.40 3.966 16
24.11 3.688 2
24.84 Sh 3.581 7
25.24 3.526 20
25.53 Sh 3.486 11
26.20 3.399 4
27.19 Sh 3.277 2
27.53 3.237 7
29.66 3.009 2
30.22 2.955 3
32.14 2.783 3
33.02 2.711 2
34.49 2.599 1
35.64 2.517 9
36.83 2.439 2
37.11 2.421 1
39.56 2.277 1
(a) ± 0.2 The X-ray powder diffraction patterns were determined by standard techniques. The radiation was the K-alpha/doublet of copper. The peak heights and the positions, as a function of 2Θ where θ is the Bragg angle, were read from the relative intensities of the peaks, and d, the interplanar spacing in Angstroms corresponding to the recorded lines, can be calculated. The variation in the scattering angle (two theta) measurements, due to instrument error and to differences between individual samples, is estimated at ± 0.20 degrees. The X-ray diffraction pattern of Table I is representative of "as-synthesized" or "as-made" SSZ-59 zeolites. Minor variations in the diffraction pattern can result from variations in the silica-to-alumina or silica-to-boron mole ratio of the particular sample due to changes in lattice constants. In addition, sufficiently small crystals will affect the shape and intensity of peaks, leading to significant peak broadening. Representative peaks from the X-ray diffraction pattern of calcined SSZ-59 are shown in Table II. Calcination can also result in changes in the intensities of the peaks as compared to patterns of the "as-made" material, as well as minor shifts in the diffraction pattern. The zeolite produced by exchanging the metal or other cations present in the zeolite with various other cations (such as H+ or NH4 ) yields essentially the same diffraction pattern, although again, there may be minor shifts in the interplanar spacing and variations in the relative intensities of the peaks. Notwithstanding these minor perturbations, the basic crystal lattice remains unchanged by these treatments. Crystalline SSZ-59 can be used as-synthesized, but preferably will be thermally treated (calcined). Usually, it is desirable to remove the alkali metal cation by ion exchange and replace it with hydrogen, ammonium, or any desired metal ion. The zeolite can be leached with chelating agents, e.g., EDTA or dilute acid solutions, to increase the silica to alumina mole ratio. The zeolite can also be steamed; steaming helps stabilize the crystalline lattice to attack from acids. The zeolite can be used in intimate combination with hydrogenating components, such as tungsten, vanadium molybdenum, rhenium, nickel cobalt, chromium, manganese, or a noble metal, such as palladium or platinum, for those applications in which a hydrogenation-dehydrogenation function is desired. Metals may also be introduced into the zeolite by replacing some of the cations in the zeolite with metal cations via standard ion exchange techniques (see, for example, U.S. Patent Nos. 3,140,249 issued July 7, 1964 to Plank et al; 3,140,251 issued July 7, 1964 to Plank et al.; and 3,140,253 issued July 7, 1964 to Plank et al.). Typical replacing cations can include metal cations, e.g., rare earth, Group LA, Group IIA and Group VIII metals, as well as their mixtures. Of the replacing metallic cations, cations of metals such as rare earth, Mn, Ca, Mg, Zn, Cd, Pt, Pd, Ni, Co, Ti, Al, Sn, and Fe are particularly preferred. The hydrogen, ammonium, and metal components can be ion-exchanged into the SSZ-59. The zeolite can also be impregnated with the metals, or, the metals can be physically and intimately admixed with the zeolite using standard methods known to the art. Typical ion-exchange techniques involve contacting the synthetic zeolite with a solution containing a salt of the desired replacing cation or cations. Although a wide variety of salts can be employed, chlorides and other halides, acetates, nitrates, and sulfates are particularly preferred. The zeolite is usually calcined prior to the ion- exchange procedure to remove the organic matter present in the channels and on the surface, since this results in a more effective ion exchange. Representative ion exchange techniques are disclosed in a wide variety of patents including U.S. Patent Nos. 3,140,249 issued on July 7, 1964 to Plank et al.; 3,140,251 issued on July 7, 1964 to Plank et al.; and 3,140,253 issued on July 7, 1964 to Plank et al. Following contact with the salt solution of the desired replacing cation, the zeolite is typically washed with water and dried at temperatures ranging from 65 °C to about 200°C. After washing, the zeolite can be calcined in air or inert gas at temperatures ranging from about 200°C to about 800°C for periods of time ranging from 1 to 48 hours, or more, to produce a catalytically active product especially useful in hydrocarbon conversion processes. Regardless of the cations present in the synthesized form of SSZ-59, the spatial arrangement of the atoms which form the basic crystal lattice of the zeolite remains essentially unchanged. SSZ-59 can be formed into a wide variety of physical shapes. Generally speaking, the zeolite can be in the form of a powder, a granule, or a molded product, such as extrudate having a particle size sufficient to pass through a 2-mesh (Tyler) screen and be retained on a 400-mesh (Tyler) screen. In cases where the catalyst is molded, such as by extrusion with an organic binder, the aluminosilicate can be extruded before drying, or, dried or partially dried and then extruded. SSZ-59 can be composited with other materials resistant to the temperatures and other conditions employed in organic conversion processes. Such matrix materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and metal oxides. Examples of such materials and the manner in which they can be used are disclosed in U.S. Patent No. 4,910,006, issued May 20, 1990 to Zones et al., and U.S. Patent No. 5,316,753, issued May 31, 1994 to Nakagawa, both of which are incorporated by reference herein in their entirety. Hydrocarbon Conversion Processes SSZ-59 zeolites are useful in hydrocarbon conversion reactions. Hydrocarbon conversion reactions are chemical and catalytic processes in which carbon containing compounds are changed to different carbon containing compounds. Examples of hydrocarbon conversion reactions in which SSZ-59 are expected to be useful include hydrocracking, dewaxing, catalytic cracking and olefin and aromatics formation reactions. The catalysts are also expected to be useful in other petroleum refining and hydrocarbon conversion reactions such as isomerizing n-paraffins and naphthenes, polymerizing and oligomerizing olefinic or acetylenic compounds such as isobutylene and butene-1, reforming, isomerizing polyalkyl substituted aromatics (e.g., m-xylene), and disproportionating aromatics (e.g., toluene) to provide mixtures of benzene, xylenes and higher methylbenzenes and oxidation reactions. Also included are rearrangement reactions to make various naphthalene derivatives, and forming higher molecular weight hydrocarbons from lower molecular weight hydrocarbons (e.g., methane upgrading). The SSZ-59 catalysts may have high selectivity, and under hydrocarbon conversion conditions can provide a high percentage of desired products relative to total products. SSZ-59 zeolites can be used in processing hydrocarbonaceous feedstocks. Hydrocarbonaceous feedstocks contain carbon compounds and can be from many different sources, such as virgin petroleum fractions, recycle petroleum fractions, shale oil, liquefied coal, tar sand oil, synthetic paraffins from NAO, recycled plastic feedstocks and, in general, can be any carbon containing feedstock susceptible to zeolitic catalytic reactions. Depending on the type of processing the hydrocarbonaceous feed is to undergo, the feed can contain metal or be free of metals, it can also have high or low nitrogen or sulfur impurities. It can be appreciated, however, that in general processing will be more efficient (and the catalyst more active) the lower the metal, nitrogen, and sulfur content of the feedstock. The conversion of hydrocarbonaceous feeds can take place in any convenient mode, for example, in fluidized bed, moving bed, or fixed bed reactors depending on the types of process desired. The formulation of the catalyst particles will vary depending on the conversion process and method of operation.
Other reactions which can be performed using the catalyst of this invention containing a metal, e.g., a Group VIII metal such platinum, include hydrogenation-dehydrogenation reactions, denitrogenation and desulfurization reactions.
The following table indicates typical reaction conditions which may be employed when using catalysts comprising SSZ-59 in the hydrocarbon conversion reactions of this invention. Preferred conditions are indicated in parentheses.
Figure imgf000018_0001
Several hundred atmospheres Gas phase reaction 3 Hydrocarbon partial pressure 4 Liquid phase reaction 5 WHSV Other reaction conditions and parameters are provided below. Hydrocracking Using a catalyst which comprises SSZ-59, preferably predominantly in the hydrogen form, and a hydrogenation promoter, heavy petroleum residual feedstocks, cyclic stocks and other hydrocrackate charge stocks can be hydrocracked using the process conditions and catalyst components disclosed in the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No. 5,316,753. The hydrocracking catalysts contain an effective amount of at least one hydrogenation component of the type commonly employed in hydrocracking catalysts. The hydrogenation component is generally selected from the group of hydrogenation catalysts consisting of one or more metals of Group VIB and Group VIII, including the salts, complexes and solutions containing such. The hydrogenation catalyst is preferably selected from the group of metals, salts and complexes thereof of the group consisting of at least one of platinum, palladium, rhodium, iridium, ruthenium and mixtures thereof or the group consisting of at least one of nickel, molybdenum, cobalt, tungsten, titanium, chromium and mixtures thereof. Reference to the catalytically active metal or metals is intended to encompass such metal or metals in the elemental state or in some form such as an oxide, sulfide, halide, carboxylate and the like. The hydrogenation catalyst is present in an effective amount to provide the hydrogenation function of the hydrocracking catalyst, and preferably in the range of from 0.05 to 25% by weight. Dewaxing SSZ-59, preferably predominantly in the hydrogen form, can be used to dewax hydrocarbonaceous feeds by selectively removing straight chain paraffins. Typically, the viscosity index of the dewaxed product is improved (compared to the waxy feed) when the waxy feed is contacted with SSZ-59 under isomerization dewaxing conditions. The catalytic dewaxing conditions are dependent in large measure on the feed used and upon the desired pour point. Hydrogen is preferably present in the reaction zone during the catalytic dewaxing process. The hydrogen to feed ratio is typically between about 500 and about 30,000 SCF/bbl (standard cubic feet per barrel), preferably about 1000 to about 20,000 SCFYbbl. Generally, hydrogen will be separated from the product and recycled to the reaction zone. Typical feedstocks include light gas oil, heavy gas oils and reduced crudes boiling above about 350°F. A typical dewaxing process is the catalytic dewaxing of a hydrocarbon oil feedstock boiling above about 350°F and containing straight chain and slightly branched chain hydrocarbons by contacting the hydrocarbon oil feedstock in the presence of added hydrogen gas at a hydrogen pressure of about 15-3000 psi with a catalyst comprising SSZ-59 and at least one Group VIII metal. The SSZ-59 hydrodewaxing catalyst may optionally contain a hydrogenation component of the type commonly employed in dewaxing catalysts. See the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No. 5,316,753 for examples of these hydrogenation components. The hydrogenation component is present in an effective amount to provide an effective hydrodewaxing and hydroisomerization catalyst preferably in the range of from about 0.05 to 5% by weight. The catalyst may be run in such a mode to increase isodewaxing at the expense of cracking reactions. The feed may be hydrocracked, followed by dewaxing. This type of two stage process and typical hydrocracking conditions are described in U.S. Patent No. 4,921,594, issued May 1, 1990 to Miller, which is incorporated herein by reference in its entirety. SSZ-59 may also be utilized as a dewaxing catalyst in the form of a layered catalyst. That is, the catalyst comprises a first layer comprising zeolite SSZ-59 and at least one Group VIII metal, and a second layer comprising an aluminosilicate zeolite which is more shape selective than zeolite SSZ-59. The use of layered catalysts is disclosed in U.S. Patent No. 5,149,421, issued September 22, 1992 to Miller, which is incorporated by reference herein in its entirety. The layering may also include a bed of SSZ-59 layered with a non-zeolitic component designed for either hydrocracking or hydrofmishing. SSZ-59 may also be used to dewax raffmates, including bright stock, under conditions such as those disclosed in U. S. Patent No. 4,181,598, issued January 1, 1980 to Gillespie et al., which is incorporated by reference herein in its entirety. It is often desirable to use mild hydrogenation (sometimes referred to as hydrofinishing) to produce more stable dewaxed products. The hydrofmishing step can be performed either before or after the dewaxing step, and preferably after. Hydrofinishing is typically conducted at temperatures ranging from about 190°C to about 340°C at pressures from about 400 psig to about 3000 psig at space velocities (LHSV) between about 0.1 and 20 and a hydrogen recycle rate of about 400 to 1500 SCF/bbl. The hydrogenation catalyst employed must be active enough not only to hydrogenate the olefins, diolefins and color bodies which may be present, but also to reduce the aromatic content. Suitable hydrogenation catalyst are disclosed in U. S. Patent No. 4,921,594, issued May 1, 1990 to Miller, which is incorporated by reference herein in its entirety. The hydrofinishing step is beneficial in preparing an acceptably stable product (e.g., a lubricating oil) since dewaxed products prepared from hydrocracked stocks tend to be unstable to air and light and tend to form sludges spontaneously and quickly. Lube oil may be prepared using SSZ-59. For example, a C20+ lube oil may be made by isomerizing a C20+ olefin feed over a catalyst comprising SSZ-59 in the hydrogen form and at least one Group VIII metal. Alternatively, the lubricating oil may be made by hydrocracking in a hydrocracking zone a hydrocarbonaceous feedstock to obtain an effluent comprising a hydrocracked oil, and catalytically dewaxing the effluent at a temperature of at least about 400°F and at a pressure of from about 15 psig to about 3000 psig in the presence of added hydrogen gas with a catalyst comprising SSZ-59 in the hydrogen form and at least one Group VIII metal. Aromatics Formation SSZ-59 can be used to convert light straight run naphthas and similar mixtures to highly aromatic mixtures. Thus, normal and slightly branched chained hydrocarbons, preferably having a boiling range above about 40°C and less than about 200°C, can be converted to products having a substantial higher octane aromatics content by contacting the hydrocarbon feed with a catalyst comprising SSZ-59. It is also possible to convert heavier feeds into BTX or naphthalene derivatives of value using a catalyst comprising SSZ-59. The conversion catalyst preferably contains a Group VIXI metal compound to have sufficient activity for commercial use. By Group VIII metal compound as used herein is meant the metal itself or a compound thereof. The Group VIII noble metals and their compounds, platinum, palladium, and iridium, or combinations thereof can be used. Rhenium or tin or a mixture thereof may also be used in conjunction with the Group VIII metal compound and preferably a noble metal compound. The most preferred metal is platinum. The amount of Group VIII metal present in the conversion catalyst should be within the normal range of use in reforming catalysts, from about 0.05 to 2.0 weight percent, preferably 0.2 to 0.8 weight percent. It is critical to the selective production of aromatics in useful quantities that the conversion catalyst be substantially free of acidity, for example, by neutralizing the zeolite with a basic metal, e.g., alkali metal, compound. Methods for rendering the catalyst free of acidity are known in the art. See the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No. 5,316,753 for a description of such methods. The preferred alkali metals are sodium, potassium, rubidium and cesium. The zeolite itself can be substantially free of acidity only at very high silica: alumina mole ratios. Catalytic Cracking Hydrocarbon cracking stocks can be catalytically cracked in the absence of hydrogen using SSZ-59, preferably predominantly in the hydrogen form. When SSZ-59 is used as a catalytic cracking catalyst in the absence of hydrogen, the catalyst may be employed in conjunction with traditional cracking catalysts, e.g., any aluminosilicate heretofore employed as a component in cracking catalysts. Typically, these are large pore, crystalline aluminosilicates. Examples of these traditional cracking catalysts are disclosed in the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No 5,316,753. When a traditional cracking catalyst (TC) component is employed, the relative weight ratio of the TC to the SSZ-59 is generally between about 1:10 and about 500:1, desirably between about 1:10 and about 200:1, preferably between about 1:2 and about 50:1, and most preferably is between about 1:1 and about 20:l. The novel zeolite and/or the traditional cracking component may be further ion exchanged with rare earth ions to modify selectivity. The cracking catalysts are typically employed with an inorganic oxide matrix component. See the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No. 5,316,753 for examples of such matrix components. Isomerization The present catalyst is highly active and highly selective for isomerizing C4 to C hydrocarbons. The activity means that the catalyst can operate at relatively low temperature which thermodynamically favors highly branched paraffins. Consequently, the catalyst can produce a high octane product. The high selectivity means that a relatively high liquid yield can be achieved when the catalyst is run at a high octane. The present process comprises contacting the isomerization catalyst, i.e., a catalyst comprising SSZ-59 in the hydrogen form, with a hydrocarbon feed under isomerization conditions. The feed is preferably a light straight run fraction, boiling within the range of 30°F to 250°F and preferably from 60°F to 200°F. Preferably, the hydrocarbon feed for the process comprises a substantial amount of C4 to C7 normal and slightly branched low octane hydrocarbons, more preferably C5 and C6 hydrocarbons. It is preferable to carry out the isomerization reaction in the presence of hydrogen. Preferably, hydrogen is added to give a hydrogen to hydrocarbon ratio (H2 HC) of between 0.5 and 10 H2/HC, more preferably between 1 and 8 H /HC. See the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No. 5,316,753 for a further discussion of isomerization process conditions. A low sulfur feed is especially preferred in the present process. The feed preferably contains less than 10 ppm, more preferably less than 1 ppm, and most preferably less than 0.1 ppm sulfur. In the case of a feed which is not already low in sulfur, acceptable levels can be reached by hydrogenating the feed in a presaturation zone with a hydrogenating catalyst which is resistant to sulfur poisoning. See the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No. 5,316,753 for a further discussion of this hydrodesulfurization process. It is preferable to limit the nitrogen level and the water content of the feed. Catalysts and processes which are suitable for these purposes are known to those skilled in the art. After a period of operation, the catalyst can become deactivated by sulfur or coke. See the aforementioned U.S. Patent No. 4,910,006 and U.S. Patent No. 5,316,753 for a further discussion of methods of removing this sulfur and coke, and of regenerating the catalyst. The conversion catalyst preferably contains a Group VIII metal compound to have sufficient activity for commercial use. By Group VIII metal compound as used herein is meant the metal itself or a compound thereof. The Group VIII noble metals and their compounds, platinum, palladium, and iridium, or combinations thereof can be used. Rhenium and tin may also be used in conjunction with the noble metal. The most preferred metal is platinum. The amount of Group VIII metal present in the conversion catalyst should be within the normal range of use in isomerizing catalysts, from about 0.05 to 2.0 weight percent, preferably 0.2 to 0.8 weight percent. Alkylation and Transalkylation SSZ-59 can be used in a process for the alkylation or transalkylation of an aromatic hydrocarbon. The process comprises contacting the aromatic hydrocarbon with a C2 to C16 olefin alkylating agent or a polyalkyl aromatic hydrocarbon transalkylating agent, under at least partial liquid phase conditions, and in the presence of a catalyst comprising SSZ-59. SSZ-59 can also be used for removing benzene from gasoline by alkylating the benzene as described above and removing the alkylated product from the gasoline. For high catalytic activity, the SSZ-59 zeolite should be predominantly in its hydrogen ion form. It is preferred that, after calcination, at least 80% of the cation sites are occupied by hydrogen ions and/or rare earth ions. Examples of suitable aromatic hydrocarbon feedstocks which may be alkylated or transalkylated by the process of the invention include aromatic compounds such as benzene, toluene and xylene. The preferred aromatic hydrocarbon is benzene. There may be occasions where naphthalene or naphthalene derivatives such as dimethylnaphthalene may be desirable. Mixtures of aromatic hydrocarbons may also be employed. Suitable olefins for the alkylation of the aromatic hydrocarbon are those containing 2 to 20, preferably 2 to 4, carbon atoms, such as ethylene, propylene, butene-1, trans-butene-2 and cis-butene-2, or mixtures thereof. There may be instances where pentenes are desirable. The preferred olefins are ethylene and propylene. Longer chain alpha olefins may be used as well. When transalkylation is desired, the transalkylating agent is a polyalkyl aromatic hydrocarbon containing two or more alkyl groups that each may have from 2 to about 4 carbon atoms. For example, suitable polyalkyl aromatic hydrocarbons include di-, tri- and tetra-alkyl aromatic hydrocarbons, such as diethylbenzene, triethylbenzene, diethylmethylbenzene (diethyltoluene), di-isopropylbenzene, di-isopropyltoluene, dibutylbenzene, and the like. Preferred polyalkyl aromatic hydrocarbons are the dialkyl benzenes. A particularly preferred polyalkyl aromatic hydrocarbon is di-isopropylbenzene. When alkylation is the process conducted, reaction conditions are as follows. The aromatic hydrocarbon feed should be present in stoichiometric excess. It is preferred that molar ratio of aromatics to olefins be greater than four-to-one to prevent rapid catalyst fouling. The reaction temperature may range from 100°F to 600°F, preferably 250°F to 450°F. The reaction pressure should be sufficient to maintain at least a partial liquid phase in order to retard catalyst fouling. This is typically 50 psig to 1000 psig depending on the feedstock and reaction temperature. Contact time may range from 10 seconds to 10 hours, but is usually from 5 minutes to an hour. The weight hourly space velocity (WHS V), in terms of grams (pounds) of aromatic hydrocarbon and olefin per gram (pound) of catalyst per hour, is generally within the range of about 0.5 to 50. When transalkylation is the process conducted, the molar ratio of aromatic hydrocarbon will generally range from about 1 : 1 to 25 : 1 , and preferably from about 2 : 1 to 20: 1. The reaction temperature may range from about 100°F to 600°F, but it is preferably about 250°F to 450°F. The reaction pressure should be sufficient to maintain at least a partial liquid phase, typically in the range of about 50 psig to 1000 psig, preferably 300 psig to 600 psig. The weight hourly space velocity will range from about 0.1 to 10. U.S. Patent No. 5,082,990 issued on January 21, 1992 to Hsieh, et al. describes such processes and is incorporated herein by reference. Conversion of Paraffins to Aromatics SSZ-59 can be used to convert light gas C2-C6 paraffins to higher molecular weight hydrocarbons including aromatic compounds. Preferably, the zeolite will contain a catalyst metal or metal oxide wherein said metal is selected from the group consisting of Groups IB, LTJB, VIII and IIIA of the Periodic Table. Preferably, the metal is gallium, niobium, indium or zinc in the range of from about 0.05 to 5% by weight. Xylene Isomerization SSZ-59 may also be useful in a process for isomerizing one or more xylene isomers in a C8 aromatic feed to obtain ortho-, meta-, and para-xylene in a ratio approaching the equilibrium value. In particular, xylene isomerization is used in conjunction with a separate process to manufacture para-xylene. For example, a portion of the para-xylene in a mixed C8 aromatics stream may be recovered by crystallization and centrifugation. The mother liquor from the crystallizer is then reacted under xylene isomerization conditions to restore ortho-, meta- and para-xylenes to a near equilibrium ratio. At the same time, part of the ethylbenzene in the mother liquor is converted to xylenes or to products which are easily separated by filtration. The isomerate is blended with fresh feed and the combined stream is distilled to remove heavy and light by- products. The resultant C8 aromatics stream is then sent to the crystallizer to repeat the cycle. Optionally, isomerization in the vapor phase is conducted in the presence of 3.0 to 30.0 moles of hydrogen per mole of alkylbenzene (e.g., ethylbenzene). If hydrogen is used, the catalyst should comprise about 0.1 to 2.0 wt.% of a hydrogenation/dehydrogenation component selected from Group VIII (of the Periodic Table) metal component, especially platinum or nickel. By Group VIII metal component is meant the metals and their compounds such as oxides and sulfides. Optionally, the isomerization feed may contain 10 to 90 wt.% of a diluent such as toluene, trimethylbenzene, naphthenes or paraffins. Oligomerization It is expected that SSZ-59 can also be used to oligomerize straight and branched chain olefins having from about 2 to 21 and preferably 2-5 carbon atoms. The oligomers which are the products of the process are medium to heavy olefins which are useful for both fuels, i.e., gasoline or a gasoline blending stock and chemicals. The oligomerization process comprises contacting the olefin feedstock in the gaseous or liquid phase with a catalyst comprising SSZ-59. The zeolite can have the original cations associated therewith replaced by a wide variety of other cations according to techniques well known in the art. Typical cations would include hydrogen, ammonium and metal cations including mixtures of the same. Of the replacing metallic cations, particular preference is given to cations of metals such as rare earth metals, manganese, calcium, as well as metals of Group II of the Periodic Table, e.g., zinc, and Group VIII of the Periodic Table, e.g., nickel. One of the prime requisites is that the zeolite have a fairly low aromatization activity, i.e., in which the amount of aromatics produced is not more than about 20% by weight. This is accomplished by using a zeolite with controlled acid activity [alpha value] of from about 0.1 to about 120, preferably from about 0.1 to about 100, as measured by its ability to crack n-hexane. Alpha values are defined by a standard test known in the art, e.g., as shown in U.S. Patent No. 3,960,978 issued on June 1, 1976 to Givens et al. which is incorporated totally herein by reference. If required, such zeolites may be obtained by steaming, by use in a conversion process or by any other method which may occur to one skilled in this art. Condensation of Alcohols SSZ-59 can be used to condense lower aliphatic alcohols having 1 to 10 carbon atoms to a gasoline boiling point hydrocarbon product comprising mixed aliphatic and aromatic hydrocarbon. The process disclosed in U.S. Patent No. 3,894,107, issued July 8, 1975 to Butter et al., describes the process conditions used in this process, which patent is incorporated totally herein by reference. The catalyst may be in the hydrogen form or may be base exchanged or impregnated to contain ammonium or a metal cation complement, preferably in the range of from about 0.05 to 5% by weight. The metal cations that may be present include any of the metals of the Groups I through VIII of the Periodic Table. However, in the case of Group IA metals, the cation content should in no case be so large as to effectively inactivate the catalyst, nor should the exchange be such as to eliminate all acidity. There may be other processes involving treatment of oxygenated substrates where a basic catalyst is desired. Methane Upgrading Higher molecular weight hydrocarbons can be formed from lower molecular weight hydrocarbons by contacting the lower molecular weight hydrocarbon with a catalyst comprising SSZ-59 and a metal or metal compound capable of converting the lower molecular weight hydrocarbon to a higher molecular weight hydrocarbon. Examples of such reactions include the conversion of methane to C2+ hydrocarbons such as ethylene or benzene or both. Examples of useful metals and metal compounds include lanthanide and or actinide metals or metal compounds. These reactions, the metals or metal compounds employed and the conditions under which they can be run are disclosed in U.S. Patents No. 4,734,537, issued March 29, 1988 to Devries et al.; 4,939,311, issued July 3, 1990 to Washecheck et al.; 4,962,261, issued October 9, 1990 to Abrevaya et al.; 5,095,161, issued March 10, 1992 to Abrevaya et al.; 5,105,044, issued April 14, 1992 to Han et al.; 5,105,046, issued April 14, 1992 to Washecheck; 5,238,898, issued August 24, 1993 to Han et al; 5,321,185, issued June 14, 1994 to van der Vaart; and 5,336,825, issued August 9, 1994 to Choudhary et al, each of whicfh is incorporated herein by reference in its entirety. SSZ-59 may be used for the catalytic reduction of the oxides of nitrogen in a gas stream. Typically, the gas stream also contains oxygen, often a stoichiometric excess thereof. Also, the SSZ-59 may contain a metal or metal ions within or on it which are capable of catalyzing the reduction of the mtrogen oxides. Examples of such metals or metal ions include copper, cobalt and mixtures thereof. One example of such a process for the catalytic reduction of oxides of nitrogen in the presence of a zeolite is disclosed in U.S. Patent No. 4,297,328, issued October 27, 1981 to Ritscher et al., which is incorporated by reference herein. There, the catalytic process is the combustion of carbon monoxide and hydrocarbons and the catalytic reduction of the oxides of nitrogen contained in a gas stream, such as the exhaust gas from an internal combustion engine. The zeolite used is metal ion-exchanged, doped or loaded sufficiently so as to provide an effective amount of catalytic copper metal or copper ions within or on the zeolite. In addition, the process is conducted in an excess of oxidant, e.g., oxygen. EXAMPLES The following examples demonstrate but do not limit the present invention. The templating agents indicated in Table C below are used in these examples. TABLE C N-Methyl-N-[(1 -phenylcyclopentyl)methyl]piperidinium
Figure imgf000028_0001
(Template A)
N-Methyl-N-[(l-(4-chlorophenyl)cyclopentyl)methyl]piperidinium cation
Figure imgf000028_0002
(Template B)
N-Methyl-N-[(1 -phenylcyclopentyl)methyl]heptamethyleneiminium cation
Figure imgf000028_0003
(Template C)
N-Methyl-N-[(l-(4-chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation
Figure imgf000029_0001
(Template D)
N-Methyl-N-[(l-phenylcyclopentyl)methyl]hexamethyleneiminium cation
Figure imgf000029_0002
(Template E) N-Methyl-N-[( 1 -(4-chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation
Figure imgf000029_0003
(Template F)
The anion (X") associated with the cation may be any anion which is not detrimental to the formation of the zeolite. Representative anions include halogen, e.g., fluoride, chloride, bromide and iodide, hydroxide, acetate, sulfate, tefrafluoroborate, carboxylate, and the like. Hydroxide is the most preferred anion. EXAMPLE 1 Synthesis of N-methyl-N-[(l-phenylcvclopentyl methvnpiperidinium cation (Template A) The templating agent was synthesized from the commercially available starting materials according to the synthetic sequence scheme shown below.
Figure imgf000030_0001
Synthesis of the starting amide(phenylcyclopentyl piperidyl ketone) To a mechanically stirred solution of piperidine (85.15 gm; 1 mole) and triethylamine (126.5 gm; 1.25 mole) in 800 ml anhydrous benzene in a 2-liter three-neck round bottom reaction a 215 gm (1.03 mole) of 1-phenylcyclopentanecarbonyl chloride (synthesis of this compound is described below), dissolved in 100 ml benzene, were added drop wise via an addition funnel at 0°C over a period of 20 minutes. The resulting mixture (a solution with tan-colored solids) was allowed to gradually warm up to room temperature and continued to stir over night. The resulting Mixture was transferred to a 2-liter separatory funnel and diluted with 600ml ethyl acetate. The mixture was washed three times with water (300 ml each) and once with 300 ml saturated sodium chloride solution. The organic phase was dried over anhydrous magnesium sulfate, filtered and concentrated at reduced pressure on a rotary evaporator to give 241 gm of the desired amide (pure by NMR analysis) as a tan-colored solid.
Reduction of phenylcyclopentyl piperidyl ketone to the corresponding N-[(l- phenylcyclopentvDmethyl] piperidine
To a mechanically stirred suspension of lithium aluminum hydride (37.95 gm; 1 mole) in 1000 ml anhydrous tetrahydrofuran (THF) at 0°C (ice-water bath) in a 2-liter 3- neck flask, the amide (128.7 gm, 0.5 mole) dissolved in 200 ml anhydrous THF was added drop-wise via an addition funnel. Once the addition was completed, the ice-water bath was removed and the reaction was stirred for 0.5 hrs at room temperature. The reaction was, then, heated at reflux for 3 hrs. The heat source was removed and once the reaction mixture cooled down to room temperature , the mixture was cooled to 0°C by means of an ice-water bath. The mixture was diluted with 500 ml ethyl ether and the reaction was worked up by adding 225 ml of 15% aqueous NaOH solution drop-wise via an addition funnel. The resulting bi-phasic (colorless liquid and white precipitate) solution was filtered though a fritted-glass funnel The filtrate was dried over anhydrous magnesium sulfate, filtered and concentrated at reduced pressure on a rotary evaporator to give 118 gm of the desired amine (pure by NMR analysis) as a pale yellow_oil.
Quaternization (synthesis of N-methyl-N-f (1 -phenylcvclopentvDmethyllpiperidinium iodide). To a mechanically stirred solution of [(1 -phenylcyclopentyl)methyl]piperidine (115 gm; 0.47 mole) in 1000 ml methanol (ACS reagent), methyl iodide (100 gm; 0.7 mole) were added. The resulting mixture was stirred for 48 hrs. Then an additional 35 gm (0.5 mole equivalent) of methyl iodide was added and the reaction was heated for 1 hr. The resulting solution was concentrated under reduced pressure on a rotary evaporator to give 175 gm of a tan solid material. The obtained solid was re-crystallized by dissolving in hot isopropyl alcohol and allowed to re-crystallize overnight. Re- crystallization afforded 171 gm of the product (NMR analysis) as shinny white needles.
Ion Exchange (making N-methyl-N-r(l-phenylcvclopentyl methyl]piperidinium hydroxide). To a gently stirred solution of 100 gm (0.26 mole) of methyl(((phenyl)cyclopentyl)methyl)piperidinium iodide in 400 ml de-ionized water in a plastic bottle, 325 gm of Ion-Exchange Resin-OH (BIO RAD®) were added and the mixture was let to stir at room temperature overnight. The mixture was filtered through a fritted-glass funnel and the solids were rinsed with additional 75ml of water. A small aliquot from the filtrate was titrated with 0. IN HC1 to indicate a total yield of 0.22 mole of OH ions (hence 0.22 of N-methyl-N-[(l-phenylcyclopentyl)methyl]piperidinium hydroxide).
Synthesis of l-phenylcyclopentanecarbonyl chloride The carboxylic acid chlorides used in the synthesis of the parent amides were all synthesized as described below. In a 1-liter 3-neck flask, 200 gm (1.05 mole) of 1- phenylcyclopentanecarboxylic acid (ACROS ORGANICS) was added drop-wise to stirring excess of thionyl chloride (Aldrich) under nitrogen. The resulting mixture was heated at reflux for two hrs. The reaction was further stirred at room temperature overnight. The resulting brown-red solution was concentrated at reduced pressure and heat on a rotary evaporator to remove excess thionyl chloride. The reaction yielded 216 gm of a lachrymator substance whose 1H-NMR and 13C-NMR spectra were ideal for the desired acid chloride. EXAMPLE 2 Synthesis of templating agent N-methyl-N-[(l-(4- chlorophenyl)cvclopentyl)methyl]piperidinium cation (Template B
N-methyl-N-[(l -(4-chlorophenyl)cyclopentyl)methyl]piperidinium cation was synthesized using the above procedure starting from piperidine and l-(4- chlorophenyl)cyclopentanecarbonyl chloride.
Figure imgf000032_0001
EXAMPLE 3 Synthesis of templating agent N-methyl-N-[Yl- phenylcvclopentyl)methyl]heptamethyleneiminium cation (Template C)
N-methyl-N-[(l-phenylcyclopentyl)methyl]heptamethyleneiminium cation was synthesized using the above procedure starting from heptametheleneimine and 1- phenylcyclopentanecarbonyl chloride
Figure imgf000032_0002
EXAMPLE 4 Synthesis of N-methyl-N-r(l-(4- chlorophenyl cyclopentyl methyl]heptamethyleneiminium cation (Template D N-methyl-N-[(l-(4-chlorophenyl)cyclopentyl)methyl]heptamethyleneiminium cation was synthesized using the above procedure starting from heptametheleneimme and. l-(4-chlorophenyl)cyclopentanecarbonyl chloride.
Figure imgf000033_0001
EXAMPLE 5 Synthesis of templating agent N-mefhyl-N-lYl- phenylcyclopentyl methyl]hexamethyleneiminium cation (Template E)
N-methyl-N-[(l -phenylcyclopentyl)methyl]hexamethyleneiminium cation was synthesized using the above procedure starting from hexametheleneimine and 1- phenylcyclopentanecarbonyl chloride
Figure imgf000033_0002
EXAMPLE 6 Synthesis of N-mett_yl-N-ITl-(4- chlorophenyl cvclopentyl)methyl]hexamethyleneiminium cation (Template F)
N-methyl-N-[(l-(4-chlorophenyl)cyclopentyl)methyl]hexamethyleneiminium cation was synthesized using the above procedure starting from hexametheleneimine and l-(4-chlorophenyl)cyclopentanecarbonyl chloride
Figure imgf000033_0003
EXAMPLE 7 Synthesis of Boron-SSZ-59 In a 23-cc Teflon liner, 6.48 gm of 0.46 M solution (aqueous) of the templating agent N-methyl-N-[(l-phenylcyclopentyl)methyl]piperidinium hydroxide (Template A, 3 mmol) were mixed with 1.2 gm of 1.ON NaOH (1.2 mmol) and 4.3 gm of de-ionized water. To this mixture, 0.06 gm of sodium borate decahydrate were added and stirred until completely dissolved. To this mixture, 0.9 gm of CAB-O-SIL M-5 amorphous fumed silica (~ 14.7 mmol SiO2) were added. The mixture was thoroughly stirred and the resulting gel was capped off and placed in steel Parr autoclave and heated in an oven at 160°C while tumbling at 43 rpm. The progress of the reaction was monitored by Scanning Electron Microscopy at intervals of 6 days. Once completed (after heating for 12 days), the pasty reaction mixture was filtered through a fritted glass funnel. The collected solid was rinsed with water (1 liter) and air-dried overnight. The solids were further dried in an oven at 120°C for 2hrs. The reaction yielded 0.9 gm of SSZ-59 as a white powder. Table IVA below shows the synthesis of Boron-SSZ-59 at varying SiO2/B2O3 ratios. The data presented in Table IVA is obtained from attempts at making the borosilicate version of SSZ-59 at differentSiO2/B2O3 ratios while keeping Si02 to other reagent constant using Template A as structure directing agent.
Table JVA*
Figure imgf000034_0001
Figure imgf000035_0001
*SiO /OH for all runs was 3.5; H2O/SiO2 for all runs was 44 The XRD data appears in Table III below.
TABLE III
Two Theta(a) d-spacing (A) intensity I/Io x 100
6.07 14.54 37
7.20 12.26 45
8.28 10.68 55
14.42 6.140 12
15.71 5.638 6
16.72 Sh 5.298 5
17.10 5.181 14
17.93 Sh 4.942 3
18.24 Sh 4.860 9
18.46 4.804 11
19.33 4.589 3
20.75 4.278 100
21.31 Sh 4.165 6
21.95 4.047 7
22.45 3.957 24
22.99 3.866 3
24.76 3.593 10
25.30 3.517 18
25.54 Sh 3.485 14
26.23 3.395 8
27.22 Sh 3.274 7
27.47 3.244 15
29.09 3.067 2
29.67 3.009 3
30.21 2.956 6
31.09 2.875 5
32.17 2.780 6
33.05 2.708 2
33.55 2.669 2
34.48 2.599 4
35.76 2.509 15
37.00 2.427 2
(a) ± 0.2 EXAMPLE 8 Synthesis of Aluminum-SSZ-59 In a 23-cc Teflon liner, 6.75 gm of 0.34 M solution (aqueous) of the templating agent N-methyl-N- [( 1 -phenylcyclopentyl)methyl]heptamethyleneiminium hydroxide (Template C, 2.25 mmol) were mixed with 1.5 gm of 1.ON NaOH (1.5 mmol). To this mixture, 0.25 gm of Union Carbide's LZ-Y52 zeolite were added. Then, 0.8 gm of CAB- O-SIL M-5 (- 13 mmol SiO2) were added. The mixture was thoroughly stirred and the resulting gel was capped off and placed in steel Parr autoclave and heated in an oven at 160°C while tumbling at 43 rpm. The progress of the reaction was monitored by Scanning Electron Microscopy at intervals of 6 days. Once completed (after heating for 6 days), the pasty looking reaction mixture was filtered through a fritted glass funnel. The collected solid was rinsed with water (1 liter) and air-dried overnight. The solids were further dried in an oven at 120°C for 2 hrs. The reaction yielded 0.75 gm of SSZ-59 as a white powder. Analysis by XRD shows the product to be SSZ-59. SSZ-59 is made in a similar manner using in turn B, D, E and F as the templating agent. Example 9 Calcination of SSZ-59 The material from Example 8 is calcined in the following manner. A thin bed of material is heated in a muffle furnace from room temperature to 120°C at a rate of 1°C per minute and held at 120°C for three hours. The temperature is then ramped up to 540°C at the same rate and held at this temperature for 5 hours, after which it is increased to 594°C and held there for another 5 hours. A 50/50 mixture of air and nitrogen is passed over the zeolite at a rate of 20 standard cubic feet per minute during heating. The X-ray diffraction data for the product is provided in Table TV below. TABLE TV
Two Theta (deg.)( ) d-spacing (A) Intensity I/Io x 100
6.11 14.46 87
7.20 12.27 74
8.28 10.67 100
10.54 8.391 2
15.69 5.642 5
17.09 5.185 12 18.24 Sh 4.859 5
18.53 4.785 ' 10
19.28 4.600 3
20.71 4.286 65
21.50 Sh 4.129 2
21.90 Sh 4.055 3
22.40 3.966 16
24.11 3.688 2
24.84 Sh 3.581 7
25.24 3.526 20
25.53 • Sh 3.486 11
26.20 3.399 4
27.19 Sh 3.277 2
27.53 3.237 7
29.66 3.009 2
30.22 2.955 3
32.14 2.783 3
33.02 2.711 2
34.49 2.599 1
35.64 2.517 9
36.83 2.439 2
37.11 2.421 1
39.56 2.277 1
(a) ± 0.2 Example 10 NH4 Exchange Ion exchange of calcined SSZ-59 material (prepared in Example 8) is performed using NH4NO3 to convert the zeolite from its Na+ form to the NH4 + form, and, ultimately, the ϊ form. Typically, the same mass of NBUNO3 as zeolite is slurried in water at a ratio of 25-50: 1 water to zeolite. The exchange solution is heated at 95°C for 2 hours and then filtered. This procedure can be repeated up to three times. Following the final exchange, the zeolite is washed several times with water and dried. This NH4 + form of SSZ-59 can then be converted to the H+ form by calcination (as described in Example 9) to 540°C. Example 11 Constraint Index Determination The hydrogen form of the zeolite of Example 8 (after treatment according to Examples 9 and 10) is pelletized at 2-3 KPSI, crushed and meshed to 20-40, and then > 0.50 gram is calcined at about 540°C in air for four hours and cooled in a desiccator. 0.50 Gram is packed into a 3/8 inch stainless steel tube with alundurn on both sides of the zeolite bed. A Lindburg furnace is used to heat the reactor tube. Helium is introduced into the reactor tube at 10 cc/min. and at atmospheric pressure. The reactor is heated to about 315°C, and a 50/50 (w/w) feed of n-hexane and 3-methylpentane is introduced into the reactor at a rate of 8 μl/min. Feed delivery is made via a Brownlee pump. Direct sampling into a gas chromatograph begins after 10 minutes of feed introduction. The Constraint Index value is calculated from the gas chromatographic data using methods known in the art, and is found to be 0.27, which suggests a large pore zeolite. At 315°C and 10 minutes on stream, feed conversion was greater than 62%. SSZ-59 has a very high cracking activity, indicative of strongly acidic sites. Example 12 Hydrocracking of n-Hexadecane A sample of SSZ-59 as prepared in Example 8 was treated as in Examples 9 and 10. Then a sample was slurried in water and the pH of the slurry was adjusted to a pH of -10 with dilute ammonium hydroxide. To the slurry was added a solution of Pd(NH3)4(NO3)2 at a concentration which would provide 0.5 wt. % Pd with respect to the dry weight of the zeolite sample. This slurry was stirred for 48 hours at 100°C. After cooling, the slurry was filtered through a glass frit, washed with de-ionized water, and dried at 100°C. The catalyst was then calcined slowly up to 900°F in air and held there for three hours. The calcined catalyst was pelletized in a Carver Press and crushed to yield particles with a 20/40 mesh size range. Sized catalyst (0.5 g) was packed into a V" OD tubing reactor in a micro unit for n-hexadecane hydroconversion. Table Vffl gives the run conditions and the products data for the hydrocracking test on n-hexadecane. After the catalyst was tested with n-hexadecane, it was titrated using a solution of butyl amine in hexane. The temperature was increased and the conversion and product data evaluated again under titrated conditions. The results shown in Table V show that SSZ-59 is effective as a hydrocracking catalyst. Table V
Figure imgf000039_0001

Claims

WHAT IS CLAIMED IS:
1. A zeolite having a mole ratio greater than about 20 of an oxide of a first tetravalent element to an oxide of a second tetravalent element which is different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof and having, after calcination, the X-ray diffraction lines of Table II.
2. A zeolite having a mole ratio greater than about 20 of an oxide selected from the group consisting of silicon oxide, germanium oxide and mixtures thereof to an oxide selected from aluminum oxide, gallium oxide, iron oxide, boron oxide, titanium oxide, indium oxide, vanadium oxide and mixtures thereof, and having, after calcination, the X-ray diffraction lines of Table II.
3. A zeolite according to Claim 2 wherem the oxides comprise silicon oxide and aluminum oxide.
4. A zeolite according to Claim 2 wherein the oxides comprise silicon oxide and boron oxide.
5. A zeolite according to Claim 1 wherein said zeolite is predominantly in the * hydrogen form.
6. A zeolite according to Claim 1 wherein said zeolite is substantially free of acidity.
7. A zeolite having a composition, as synthesized and in the anhydrous state, in terms of mole ratios as follows:
YO2/WcOd > 20 M2 n/YO2 0.01 - 0.03 Q/YO2 0.02 - 0.05
wherein Y is silicon, germanium or a mixture thereof; W is aluminum, gallium, iron, boron, titanium, indium, vanadium or mixtures thereof; c is 1 or 2; d is 2 when c is 1 or d is 3 or 5 when c is 2; M is an alkali metal cation, alkaline earth metal cation or mixtures thereof; π is the valence of ; and Q is a N-methyl-N-[(l- phenylcyclopentyl)rnethyl]heptaιnemyleneimiτ]ii- cation, N-methyl-N-[(l~(4- c orophenyl)cyclopentyl)memyl]heptarrιemyleneimiιιiuιn cation, N-rnethyI-N-[(l- (4-chlorophenyl)cyclopentyl)methyl]hexamethyletiejmiTitum cation, N-methyl-N- [(l-phenylcyclopentyl)methyl]hexamethyleneirπraium cation, N-methyl-N-[(l- ρhenylcyclopent l)methyl]ρiρeridinium cation or N-methyl-N-[(l-(4- cblorophenyl)cyclopentyl)methyl]piperidinium cation.
8. A zeolite according to Claim 7 wherein Q is a N-methyl-N-[(l- phenylcyclopentyl)memyl]heptamethyleneiminium cation.
9. A zeolite according to Claim 7 herei Q is N-metbyl-N-[(l-(4- cMorophenyl)cyclopentyl)methyl]heρtamethyleιieiιrjiniι.ιιn cation.
10. A zeolite according to Claim 7 wherein Q is a N-methyI-N-[(l-(4- chlorophenyl)cyclopentyl)methyl]hexamethyleneimOTum cation.
11. A zeolite according to Claim 7 wherein Q is a N-methyl-N-[(l- phenylcyclopentyl)raethyl]hexamethyleueimiτύum cation.
12. A zeolite according to Claim 7 wherein Q is a N-methyl-N-[(l- phenylcyclopentyl)r ethyl]piperidinium cation.
13. A zeolite according to Claim 7 wherein Q is a N-methyl-N-[(l-(4- cMorophenyl)cyclopentyl)metiiyl]piperidimum cation.
14. A zeolite according to Claim 7 wherein W is aluminum and Y is silicon.
15. A zeolite according to Claim 7 wherein W is boron and Y is silicon.
16. A method of preparing a crystalline material comprising an oxide of a first tefravalent element and an oxide of a second tetravalent element which is different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof, said method comprising contacting under crystallization conditions sources of said oxides; and a templating agent comprising a N-methyl-N-[(l- phenylcyclopentyl)methyl]heptamemylenenι ir-iuin cation, N-ttιethγl-N-[(l-(4- chlorophenyl)cyclopentyl)n ethyl]heptamethylenchninium cation, N-methyl-N-[(l- (4-chlorophenyl)cyclopentyl)methyl]hex-ιme ylenehrιirdum cation, N-methyl-N- [(1 -phenylcyclopentyl)memyI]hexamethyIeneiminium cation, N-methyl-N-[(l - phenylcyclopentyl)methyl]piperidirιium cation or N-methyl-N-[( 1 -(4- chlorophenyl)cyclopentyl)methyl]piperJdmium cation.
17- The method according to Claim 16 wherein the first tetravalent element is selected from the group consisting of silicon, germanium and combinations thereof.
18. The method according to Claim 16 wherein the second tetravalent element, trivalent element or pentavalent element is selected from the group consisting of aluminum, gallium, iron, boron, titanium, indium, vanadium and combinations thereof.
1 - The method according to Claim 18 wherein the second tetravalent element or trivalent element is selected from the group consisting of aluminum, boron, titanium and combinations thereof.
20. The method according to Claim 19 wherein the first tetravalent element is silicon.
21. The method of Claim 16 wherein the crystalline material has, after calcination, the X-ray diffraction lines of Table II.
22. The method of Claim 16 wherein the templating agent is a N-methyl-N-[(l - ρhenyIcyclopentyl)methyl]heptamemyleneirninium cation.
23. The method of Claim 16 wherein the templating agent is a N-methyl-[(l -(4- chlorophenyl)cyclopentyl)memyl]heptamethyleneiminium cation.
24. The method of Claim 16 wherem the templating agent is a N-methyl-N-[(l-(4- c orophenyl)cyclopentyl)methyl]bexamethyleneimirιium cation.
25. The method of Claim 16 wherein the templating agent is a N-methyl-N-[( i - phenylcyclopentyl)metiιyl]hexamemyleneiminiτιm cation.
26. The method of Claim 16 wherein the templating agent is a N-methyl-N-[(l - phenyl)cyclopentyl)methyl]piperidinivmi cation.
27. The method of Claim 16 wherein the templating agent is a N-methyl-N-[(l -(4- chlorophenyl)cyclopentyl)methyl]piperidinium cation.
28. A process for converting hydrocarbons comprising contacting a hydrocarbonaceous feed at hydrocarbon converting conditions with a catalyst comprising a zeolite having a mole ratio greater than about 20 of an oxide of a first tetravalent element to an oxide of a second tetravalent element which is different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof and having, after calcination, the X-ray diffraction lines of Table II.
29. The process of Claim 28 wherein the zeolite is predominantly in the hydrogen form.
30. The process of Claim 28 wherein the zeolite is substantially free of acidity,
31. The process of Claim 28 wherein the process is a hydrocracking process comprising contacting the catalyst with a hydrocarbon feedstock under hydrocracking conditions.
32. The process of Claim 31 wherem the zeolite is predominantly in the hydrogen form.
33. The process of Claim 28 wherein the process is a dewaxing process comprising contacting the catalyst with a hydrocarbon feedstock under dewaxing conditions.
34. The process of Claim 33 wherein the zeolite is predominantly in the hydrogen form.
35. The process of Claim 28 wherein the process is a process for improving the viscosity index of a dcwaxed product of waxy hydrocarbon feeds comprising contacting the catalyst with a waxy hydrocarbon feed under isomerization dewaxing conditions.
36. The process of Claim 35 wherem the zeolite is predominantly in the hydrogen form.
37. The process of Claim 28 wherein the process is a process for producing a C20+ lube oil from a C2o+ olefin feed comprising isomerizing said olefin feed under isomerization conditions over the catalyst.
38. The process of Claim 37 wherein the zeolite is predominantly in the hydrogen form.
39- The process of Claim 37 wherein the catalyst further comprises at least one Group VΪIΪ metal.
40. The process of Claim 28 wherein the process is a process for catalytically dewaxing a hydrocarbon oil feedstock boiling above about 350°F and containing straight chain and slightly branched chain hydrocarbons comprising contacting said hydrocarbon oil feedstock in the presence of added hydrogen gas at a hydrogen pressure of about 15-3000 psi under dewaxing conditions with the catalyst.
41. The process of Claim 40 wherein the zeolite is predominantly in the hydrogen form.
42. The process of Claim 40 wherein the catalyst further comprises at least one Group VIII metal.
43. The process of Claim 40 wherein said catalyst comprises a layered catalyst comprising a first layer comprising the zeolite and at least one Group VIII metal, and a second layer comprising an aluminosilicate zeolite which is more shape selective than the zeolite of said first layer,
44, The process of Claim 28 wherein the process is a process for preparing a lubricating oil which comprises: hydrocracking in a hydrocracking zone a hydrocarbonaceous feedstock to obtain an effluent comprising a hydrocracked oil; and
catalytically dewaxing said effluent comprising hydrocracked oil at a temperature of at least about 400°F and at a pressure of from about 15 psig to about 3000 psig in the presence of added hydrogen gas with the catalyst.
45. The process of Claim 44 wherein the zeolite is predominantly in the hydrogen form.
46. The process of Claim 44 wherein the catalyst further comprises at least one Group VJJJ metal.
47. The process of Claim 28 wherein the process is a process for isomerization dewaxing a raffinate comprising contacting said raffinate in the presence of added hydrogen under isomerization dewaxing conditions with the catalyst.
48. The process of Claim 47 wherein the zeolite is predominantly in the hydrogen form,
49. The process of Claim 47 wherein the catalyst further comprises at least one Group Vm metal.
50. The process of Claim 47 wherein the raffinate is bright stock.
51. The process of Claim 28 wherem the process is a process for increasing the octane of a hydrocarbon feedstock to produce a product having an increased aromatics content comprising contacting a hydrocarbonaceous feedstock which comprises normal and slightly branched hydrocarbons having a boiling range above about 40°C and less than about 200"C under aromatic conversion conditions with the catalyst.
52. The process of Claim 51 wherein the zeolite is substantially free of acid.
53. The process of Claim 51 wherein the zeolite contains a Group VIII metal component.
54. The process of Claim 28 wherein the process is a catalytic cracking process comprising contacting a hydrocarbon feedstock in a reaction zone under catalytic cracking conditions in the absence of added hydrogen with the catalyst.
55. The process of Claim 54 wherein the zeolite is predominantly in the hydrogen form
56. The process of Claim 54 wherein the catalyst additionally comprises a large pore crystallin e cracking component.
57. The process of Claim 28 wherein the process is an isomerization process for isomerizing C4 to C7 hydrocarbons, comprising contacting a feed having normal and slightly branched C4 to C7 hydrocarbons under isomerizing conditions with the catalyst.
58. The process of Claim 57 wherein the zeolite i$ predominantly in the hydrogen form.
5 . The process of Claim 57 wherein the zeolite has been impregnated with at least one Group VIII metal.
60. The process of Claim 57 wherein the catalyst has been calcined in a steam/air mixture at an elevated temperature after impregnation of the Group VH1 metal.
61. The process of Claim 59 wherein the Group VJII metal is platinum.
62. The process of Claim 28 wherein the process is a process for alkylating an aromatic hydrocarbon which comprises contacting under alkylation conditions at least a molar excess of an aromatic hydrocarbon with a C2 to C20 olefin under at least partial liquid phase conditions and in the presence of the catalyst.
63. The process of Claim 62 wherein the zeolite is predominantly in the hydrogen form.
64. The process of Claim 62 wherein the olefin is a C2 to C_. olefin.
65. The process of Claim 64 wherein the aromatic hydrocarbon and olefin are present in a molar ratio of about 4:1 to about 20:1, respectively.
66. The process of Claim 64 wherein the aromatic hydrocarbon is selected from the group consisting of benzene, toluene, ethylbenzene, xylene, naphthalene, naphthalene derivatives, dimethylnaphthaleπe or mixtures thereof.
67. The process of Claim 28 wherein the process is a process for transalkylating an arom atic hydrocarbon which comprises contacting under transalkylating conditions an aromatic hydrocarbon with a polyalkyl aromatic hydrocarbon under at least partial liquid phase conditions and in the presence of the catalyst.
68 , The process of Claim 67 wherein the zeolite is predominantly in the hydrogen form.
69. The process of Claim 67 wherein the aromatic hydrocarbon and the polyalkyl aromatic hydrocarbon are present in a molar ratio of from about 1:1 to about 25:1, respectively.
70. The process of Claim 67 wherein the aromatic hydrocarbon is selected from the group consisting of benzene, toluene, ethylbenzene, xylene, or mixtures thereof.
71. The process of Claim 67 wherein the polyalkyl aromatic hydrocarbon is a dialkylbenzene.
72. The process of Claim 28 wherein the process is a process to convert paraffins to aromatics which comprises contacting paraffins under conditions which cause paraffins to convert to aromatics with a catalyst comprising the zeolite and gallium, zinc, or a compound of gallium or zinc.
73. The process of Claim 28 wherein the process is a process for isomerizing olefins comprising contacting said olefin under conditions which cause isomerization of the olefin with the catalyst.
74. The process of Claim 28 wherein the process is a process for isomerizing an isomerization feed comprising an aromatic Cg stream of xylene isomers or mixtures of xylene isomers and ethylbenzene, wherein a more nearly equilibrium ratio of ortho-, meta and para-xylenes is obtained, said process comprising contacting said feed under isomerization conditions with the catalyst.
75. The process of Claim 28 wherein the process is a process for oligomerizing olefins comprising contacting an olefin feed under oligomerization conditions with the catalyst.
76. A process for converting lower alcohols and other oxygenated hydrocarbons comprising contacting said lower alcohol or other oxygenated hydrocarbon under conditions to produce liquid products with a catalyst comprising a zeolite having a mole ratio greater than about 20 of an oxide of a first tetravalent element to an oxide of a second tetravalent element which is different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof and having, after calcination, the X-ray diffraction lines of Table II.
77. The process of Claim 28 wherein the process is a process for the production of higher molecular weight hydrocarbons from lower molecular wei ght hydrocarbons comprising the steps of:
(a) introducing into a reaction zone a lower molecular weight hydrocarbon- containing gas and contacting said gas in said zone under C2+ hydrocarbon synthesis conditions with the catalyst and a metal or metal compound capable of converting the lower molecular weight hydrocarbon to a higher molecular weight hydrocarbon; and
b) withdrawing from said reaction zone a higher molecular weight hydrocarbon- containing stream.
78. The process of Claim 77 wherein the metal or metal compound comprises a Ianthanide or actinide metal or metal compound.
79. The process of Claim 77 wherein the lower molecular weight hydrocarbon is methane.
80. In a process for the reduction of oxides of nitrogen contained in a gas stream in the presence of oxygen wherein said process comprises contacting the gas stream with a zeolite, the improvement comprising using as the zeolite a zeolite having a mole ratio greater than about 20 of an oxide of a first tetravalent element to an oxide of a second tetravalent element which is different from said first tetravalent element, trivalent element, pentavalent element or mixture thereof and having, after calcination, the X-ray diffraction lines of Table JX
81. The process of Claim 80 wherein said zeolite contains a metal or metal ions capable of catalyzing the reduction of the oxides of nitrogen.
82. The process of Claim 81 wherein the metal is copper, cobalt or mixtures thereof.
83. The process of Claim 81 wherein the gas stream is the exhaust stream of an internal combustion engine.
PCT/US2002/021019 2001-07-13 2002-07-03 Zeolite ssz-59 WO2003006364A2 (en)