WO2002102605A2 - Application of images to surfaces - Google Patents
Application of images to surfaces Download PDFInfo
- Publication number
- WO2002102605A2 WO2002102605A2 PCT/GB2002/002459 GB0202459W WO02102605A2 WO 2002102605 A2 WO2002102605 A2 WO 2002102605A2 GB 0202459 W GB0202459 W GB 0202459W WO 02102605 A2 WO02102605 A2 WO 02102605A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- image
- adhesive
- reinforcing
- adhesive properties
- Prior art date
Abstract
Description
Claims