WO2002071493A2 - Relaxed silicon germanium platform for high speed cmos electronics and high speed analog - Google Patents
Relaxed silicon germanium platform for high speed cmos electronics and high speed analog Download PDFInfo
- Publication number
- WO2002071493A2 WO2002071493A2 PCT/US2002/003669 US0203669W WO02071493A2 WO 2002071493 A2 WO2002071493 A2 WO 2002071493A2 US 0203669 W US0203669 W US 0203669W WO 02071493 A2 WO02071493 A2 WO 02071493A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- layers
- sige
- relaxed
- semiconductor surface
- Prior art date
Abstract
Description
Claims