WO2002038027A2 - Bande de tissu non-tisse enchevetre par procede hydraulique contenant des materiaux fibreux synthetiques recycles - Google Patents
Bande de tissu non-tisse enchevetre par procede hydraulique contenant des materiaux fibreux synthetiques recycles Download PDFInfo
- Publication number
- WO2002038027A2 WO2002038027A2 PCT/US2001/046761 US0146761W WO0238027A2 WO 2002038027 A2 WO2002038027 A2 WO 2002038027A2 US 0146761 W US0146761 W US 0146761W WO 0238027 A2 WO0238027 A2 WO 0238027A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fibers
- fiber
- nonwoven fabric
- recycled
- hydraulically entangled
- Prior art date
Abstract
Priority Applications (7)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP01990862A EP1358375A2 (fr) | 2000-11-10 | 2001-11-07 | Bande de tissu non-tisse enchevetre par procede hydraulique contenant des materiaux fibreux synthetiques recycles |
BR0115259-9A BR0115259A (pt) | 2000-11-10 | 2001-11-07 | Trama não trançada hidroemaranhada contendo materiais fibrosos sintéticos reciclados |
KR10-2003-7006326A KR20030051792A (ko) | 2000-11-10 | 2001-11-07 | 재생 합성 섬유 재료를 함유하는 수얽힘 부직 웹 |
JP2002540619A JP2004513256A (ja) | 2000-11-10 | 2001-11-07 | リサイクル合成繊維材料を含む水圧交絡された不織ウェブ |
MXPA03003768A MXPA03003768A (es) | 2000-11-10 | 2001-11-07 | Tela no tejida hidroenredada que contiene materiales fibrosos sinteticos reciclados. |
AU3062702A AU3062702A (en) | 2000-11-10 | 2001-11-07 | Hydroentangled nonwoven web containing recycled synthetic fibrous materials |
CA002426027A CA2426027A1 (fr) | 2000-11-10 | 2001-11-07 | Bande de tissu non-tisse enchevetre par procede hydraulique contenant des materiaux fibreux synthetiques recycles |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US24709100P | 2000-11-10 | 2000-11-10 | |
US60/247,091 | 2000-11-10 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2002038027A2 true WO2002038027A2 (fr) | 2002-05-16 |
WO2002038027A3 WO2002038027A3 (fr) | 2002-11-07 |
Family
ID=22933510
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2001/046761 WO2002038027A2 (fr) | 2000-11-10 | 2001-11-07 | Bande de tissu non-tisse enchevetre par procede hydraulique contenant des materiaux fibreux synthetiques recycles |
Country Status (12)
Country | Link |
---|---|
US (1) | US20020115370A1 (fr) |
EP (1) | EP1358375A2 (fr) |
JP (1) | JP2004513256A (fr) |
KR (1) | KR20030051792A (fr) |
CN (1) | CN1473217A (fr) |
AR (1) | AR032772A1 (fr) |
AU (1) | AU3062702A (fr) |
BR (1) | BR0115259A (fr) |
CA (1) | CA2426027A1 (fr) |
MX (1) | MXPA03003768A (fr) |
WO (1) | WO2002038027A2 (fr) |
ZA (1) | ZA200302953B (fr) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7740412B2 (en) | 2005-01-28 | 2010-06-22 | S.C. Johnson & Son, Inc. | Method of cleaning using a device with a liquid reservoir and replaceable non-woven pad |
US7891898B2 (en) | 2005-01-28 | 2011-02-22 | S.C. Johnson & Son, Inc. | Cleaning pad for wet, damp or dry cleaning |
US7976235B2 (en) | 2005-01-28 | 2011-07-12 | S.C. Johnson & Son, Inc. | Cleaning kit including duster and spray |
US8893347B2 (en) | 2007-02-06 | 2014-11-25 | S.C. Johnson & Son, Inc. | Cleaning or dusting pad with attachment member holder |
Families Citing this family (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ITMI20030805A1 (it) * | 2003-04-17 | 2004-10-18 | Orlandi Spa | Non-tessuto a base di fibre esplose o fibre multicomponenti splittabili. |
JP5539661B2 (ja) * | 2008-03-24 | 2014-07-02 | 旭化成ケミカルズ株式会社 | 殺菌消毒剤含有ウェットワイパー |
BRPI1007103A2 (pt) * | 2009-04-30 | 2016-03-01 | Kimberly Clark Co | composito não tecido incluindo material reciclado pós-consumidor |
US20110094691A1 (en) * | 2009-10-25 | 2011-04-28 | Nunn Kayren J | Process for regenerating post-consumer and post-industrial fibers |
MX2017015258A (es) * | 2015-06-29 | 2018-02-19 | Kimberly Clark Co | Toallita humeda dispersable y metodo de fabricacion. |
EP3367862B2 (fr) * | 2015-10-30 | 2023-05-03 | Kimberly-Clark Worldwide, Inc. | Procédé de fabrication de produits d'essuyage |
KR102493024B1 (ko) * | 2016-04-04 | 2023-01-30 | 킴벌리-클라크 월드와이드, 인크. | 낮은 린트 및 높은 유체 흡수성 및 방출 특성을 갖는 세정 제품 |
WO2018075522A1 (fr) * | 2016-10-17 | 2018-04-26 | The Procter & Gamble Company | Articles contenant des structures fibreuses |
WO2018075516A1 (fr) | 2016-10-17 | 2018-04-26 | The Procter & Gamble Company | Articles contenant des structures fibreuses dotés de propriétés pertinentes pour les consommateurs |
FI12853Y1 (fi) * | 2019-09-30 | 2020-12-30 | Suominen Corp | Kuitukankaan valmistuslinja |
CN111074445A (zh) * | 2020-01-03 | 2020-04-28 | 启东和安无纺材料有限公司 | 一种无纺布的制造方法及适用于该方法的装置 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4808467A (en) * | 1987-09-15 | 1989-02-28 | James River Corporation Of Virginia | High strength hydroentangled nonwoven fabric |
EP0492554A1 (fr) * | 1990-12-21 | 1992-07-01 | Kimberly-Clark Corporation | Etoffe non tissée composite avec une haute teneur en poudre de fibres, méthode de réalisation et utilisation |
EP0560556A1 (fr) * | 1992-03-12 | 1993-09-15 | New Oji Paper Co., Ltd. | Procédé pour la production d'un non-tissé pour l'essuyage |
WO1996006222A1 (fr) * | 1994-08-22 | 1996-02-29 | Sca Hygiene Paper Ab | Materiau non tisse comprenant une certaine proportion de fibres recyclees provenant de dechets de non tisses et/ou de textiles |
Family Cites Families (27)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US1815007A (en) * | 1928-08-06 | 1931-07-14 | Midwest Fulton Machine Co | Beater engine |
US1831004A (en) * | 1931-01-27 | 1931-11-10 | Bertram C Hope | Beater roll adjuster and indicator |
US1980253A (en) * | 1933-04-03 | 1934-11-13 | Cassius M Bryan | Paper making apparatus |
US2666369A (en) * | 1952-05-29 | 1954-01-19 | Nicholas J Niks | Method of making soft papers adaptable to impregnation |
US3485706A (en) * | 1968-01-18 | 1969-12-23 | Du Pont | Textile-like patterned nonwoven fabrics and their production |
US3849241A (en) * | 1968-12-23 | 1974-11-19 | Exxon Research Engineering Co | Non-woven mats by melt blowing |
DE1950669C3 (de) * | 1969-10-08 | 1982-05-13 | Metallgesellschaft Ag, 6000 Frankfurt | Verfahren zur Vliesherstellung |
US3821068A (en) * | 1972-10-17 | 1974-06-28 | Scott Paper Co | Soft,absorbent,fibrous,sheet material formed by avoiding mechanical compression of the fiber furnish until the sheet is at least 80% dry |
US3890220A (en) * | 1973-12-26 | 1975-06-17 | Kimberly Clark Co | Fiber waste reclaim system and method |
US4100324A (en) * | 1974-03-26 | 1978-07-11 | Kimberly-Clark Corporation | Nonwoven fabric and method of producing same |
US4366111A (en) * | 1979-12-21 | 1982-12-28 | Kimberly-Clark Corporation | Method of high fiber throughput screening |
US4340563A (en) * | 1980-05-05 | 1982-07-20 | Kimberly-Clark Corporation | Method for forming nonwoven webs |
US4735682A (en) * | 1985-02-21 | 1988-04-05 | James River-Norwalk, Inc. | Method for recovery of cellulosic fibers containing latex solids from latex bonded broke |
US4767586A (en) * | 1986-01-13 | 1988-08-30 | Kimberly-Clark Corporation | Apparatus and method for forming a multicomponent integral laid fibrous web with discrete homogeneous compositional zones, and fibrous web produced thereby |
US4931355A (en) * | 1988-03-18 | 1990-06-05 | Radwanski Fred R | Nonwoven fibrous hydraulically entangled non-elastic coform material and method of formation thereof |
US4879170A (en) * | 1988-03-18 | 1989-11-07 | Kimberly-Clark Corporation | Nonwoven fibrous hydraulically entangled elastic coform material and method of formation thereof |
CH678366A5 (fr) * | 1989-03-08 | 1991-08-30 | Frama Ag | |
US5322225A (en) * | 1991-05-23 | 1994-06-21 | Diatec Recycling Technologies Ltd. | Process of recycling of disposable diapers and the machine components thereof |
US5328759A (en) * | 1991-11-01 | 1994-07-12 | Kimberly-Clark Corporation | Process for making a hydraulically needled superabsorbent composite material and article thereof |
US5151320A (en) * | 1992-02-25 | 1992-09-29 | The Dexter Corporation | Hydroentangled spunbonded composite fabric and process |
US5382400A (en) * | 1992-08-21 | 1995-01-17 | Kimberly-Clark Corporation | Nonwoven multicomponent polymeric fabric and method for making same |
DE4333547A1 (de) * | 1993-10-01 | 1995-04-06 | Hoechst Ag | Verfahren zur Verwertung von Reststoffen enthaltend cellulosische Fasern und aus synthetischen Polymeren |
US5573841A (en) * | 1994-04-04 | 1996-11-12 | Kimberly-Clark Corporation | Hydraulically entangled, autogenous-bonding, nonwoven composite fabric |
US6022818A (en) * | 1995-06-07 | 2000-02-08 | Kimberly-Clark Worldwide, Inc. | Hydroentangled nonwoven composites |
US5687916A (en) * | 1995-11-06 | 1997-11-18 | Kimberly-Clark Worldwide, Inc. | Method of nonwoven reclaim |
US6159882A (en) * | 1997-09-09 | 2000-12-12 | Boricel Corporation | Nonwoven fibrous product |
US6103061A (en) * | 1998-07-07 | 2000-08-15 | Kimberly-Clark Worldwide, Inc. | Soft, strong hydraulically entangled nonwoven composite material and method for making the same |
-
2001
- 2001-11-05 US US10/012,766 patent/US20020115370A1/en not_active Abandoned
- 2001-11-07 JP JP2002540619A patent/JP2004513256A/ja active Pending
- 2001-11-07 MX MXPA03003768A patent/MXPA03003768A/es not_active Application Discontinuation
- 2001-11-07 AU AU3062702A patent/AU3062702A/xx not_active Withdrawn
- 2001-11-07 EP EP01990862A patent/EP1358375A2/fr not_active Withdrawn
- 2001-11-07 KR KR10-2003-7006326A patent/KR20030051792A/ko not_active Application Discontinuation
- 2001-11-07 WO PCT/US2001/046761 patent/WO2002038027A2/fr active IP Right Grant
- 2001-11-07 CN CNA018186246A patent/CN1473217A/zh active Pending
- 2001-11-07 CA CA002426027A patent/CA2426027A1/fr not_active Abandoned
- 2001-11-07 BR BR0115259-9A patent/BR0115259A/pt not_active Application Discontinuation
- 2001-11-09 AR ARP010105256A patent/AR032772A1/es not_active Application Discontinuation
-
2003
- 2003-04-15 ZA ZA200302953A patent/ZA200302953B/en unknown
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4808467A (en) * | 1987-09-15 | 1989-02-28 | James River Corporation Of Virginia | High strength hydroentangled nonwoven fabric |
EP0492554A1 (fr) * | 1990-12-21 | 1992-07-01 | Kimberly-Clark Corporation | Etoffe non tissée composite avec une haute teneur en poudre de fibres, méthode de réalisation et utilisation |
EP0560556A1 (fr) * | 1992-03-12 | 1993-09-15 | New Oji Paper Co., Ltd. | Procédé pour la production d'un non-tissé pour l'essuyage |
WO1996006222A1 (fr) * | 1994-08-22 | 1996-02-29 | Sca Hygiene Paper Ab | Materiau non tisse comprenant une certaine proportion de fibres recyclees provenant de dechets de non tisses et/ou de textiles |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7740412B2 (en) | 2005-01-28 | 2010-06-22 | S.C. Johnson & Son, Inc. | Method of cleaning using a device with a liquid reservoir and replaceable non-woven pad |
US7891898B2 (en) | 2005-01-28 | 2011-02-22 | S.C. Johnson & Son, Inc. | Cleaning pad for wet, damp or dry cleaning |
US7976235B2 (en) | 2005-01-28 | 2011-07-12 | S.C. Johnson & Son, Inc. | Cleaning kit including duster and spray |
US8893347B2 (en) | 2007-02-06 | 2014-11-25 | S.C. Johnson & Son, Inc. | Cleaning or dusting pad with attachment member holder |
Also Published As
Publication number | Publication date |
---|---|
AR032772A1 (es) | 2003-11-26 |
AU3062702A (en) | 2002-05-21 |
CN1473217A (zh) | 2004-02-04 |
JP2004513256A (ja) | 2004-04-30 |
ZA200302953B (en) | 2004-04-15 |
MXPA03003768A (es) | 2003-07-28 |
BR0115259A (pt) | 2004-01-20 |
WO2002038027A3 (fr) | 2002-11-07 |
KR20030051792A (ko) | 2003-06-25 |
CA2426027A1 (fr) | 2002-05-16 |
US20020115370A1 (en) | 2002-08-22 |
EP1358375A2 (fr) | 2003-11-05 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CA2425947A1 (fr) | Structures composites non-tissees hydroentremelees contenant des materiaux fibreux synthetiques recycles | |
AU2002228255B2 (en) | Method of recycling bonded fibrous materials and synthetic fibers and fiber-like materials produced thereof | |
CA1307104C (fr) | Procede d'enchevetrement ou jet d'eau, et produit connexe | |
EP1551628B1 (fr) | Procede de fabrication d'un tissu composite non tisse et tissu produit conformement a ce procede | |
US5106457A (en) | Hydroentangled nonwoven fabric containing synthetic fibers having a ribbon-shaped crenulated cross-section and method of producing the same | |
WO2002038027A2 (fr) | Bande de tissu non-tisse enchevetre par procede hydraulique contenant des materiaux fibreux synthetiques recycles | |
AU2002228255A1 (en) | Method of recycling bonded fibrous materials and synthetic fibers and fiber-like materials produced thereof | |
WO2010125545A2 (fr) | Composite non tissé comprenant une matière recyclée après consommation | |
KR20130137008A (ko) | 재생 셀룰로오스 섬유를 포함하는 부직포 복합체 | |
US20030171056A1 (en) | Hydroentangled nonwoven web containing recycled synthetic fibrous materials | |
AU2002230627B2 (en) | Hydroentangled nonwoven web containing recycled synthetic fibrous materials | |
AU2002230632B2 (en) | Hydroentangled nonwoven composite structures containing recycled synthetic fibrous materials | |
JP2003519298A (ja) | 複合不織布及びその製造処理方法 | |
AU2002230627A1 (en) | Hydroentangled nonwoven web containing recycled synthetic fibrous materials | |
AU2002230632A1 (en) | Hydroentangled nonwoven composite structures containing recycled synthetic fibrous materials | |
JPH04263699A (ja) | バリヤー性不織布とその製造法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
AK | Designated states |
Kind code of ref document: A3 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A3 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2003/02953 Country of ref document: ZA Ref document number: 2002230627 Country of ref document: AU Ref document number: 200302953 Country of ref document: ZA |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2426027 Country of ref document: CA |
|
WWE | Wipo information: entry into national phase |
Ref document number: PA/a/2003/003768 Country of ref document: MX |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2002540619 Country of ref document: JP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 018186246 Country of ref document: CN Ref document number: 1020037006326 Country of ref document: KR |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2001990862 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 1020037006326 Country of ref document: KR |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
WWP | Wipo information: published in national office |
Ref document number: 2001990862 Country of ref document: EP |
|
WWG | Wipo information: grant in national office |
Ref document number: 2002230627 Country of ref document: AU |